Peak effect and oxygen ordering in YBa2Cu3O7−δ single crystals

We have investigated the second magnetization peak in pure YBa₂Cu₃O_7−δ single crystals with various oxygen contents (6.91<7−δ<6.97) and degrees of oxygen vacancy ordering, as achieved by low (1 bar) and high (100 bar) oxygen pressure annealing. Although the position of the peak changes drastically with oxygen stoichiometry, no dependence on the distribution of oxygen vacancies has been found for temperatures below 70 K. For T>70 K, however, ordering effects become important as demonstrated by the disappearance of the peak for the high pressure annealed samples. These results suggest that while at low temperatures, pinning of the vortex system by clusters or a more homogeneous distribution of oxygen vacancies is similar, at elevated T, the former are much stronger pinning sites leading to larger hysteresis and the presence of the peak.     

Study on the superconducting composite material formation in the system Bi2Sr2CaCu2O8+x/Al-containing phases

Phase evolution in the Bi---Sr---Ca---Cu---Al---O system was studied. Two Al-containing phases BiSr_1.5Ca_0.5Al₂O_z and (Sr_1−xCa_x)₃Al₂O₆ (x = 0.4 − 0.45) were determined to be chemically compatible with Bi_2.18Sr₂CaCu₂O_8+x (Bi-2212) at temperatures of the samples processing. The phase equilibria in the title system were investigated above the solidus temperature. The BiSr_1.5Ca_0.5Al₂O_z was found to be in equilibrium only with the melt and the (Sr_1−xCa_x)₃Al₂O₆ phase. This latter aluminate equilibrated with Ca,Sr cuprates, CaO, the Cu-free phase, and the liquid. The melting and solidification in Bi-2212, doped with the aluminate, corresponded to the reversible reaction Bi-2212 + BiSr_1.5Ca_0.5Al₂O_z ↔ (Sr_1−xCa_x)₃Al₂O₆ + liquid. Two sets of superconducting composite materials with initial compositions Bi-2212 + nBiSr_1.5Ca_0.5Al₂O_z and Bi-2212 + m(Sr_1−xCa_x)₃Al₂O₆ were prepared by solidification from the partial melt. The former material was composed mostly of large Bi-2212 lamellas separated by the BiSr_1.5Ca_0.5Al₂O_z phase, which destroyed superconducting links between Bi-2212 grains. The latter material consisted of a Bi-2212 polycrystalline matrix with high concentration of small (ca. 3 μm) grains of (Sr_1−xCa_x)₃Al₂O₆ imbedded in Bi-2212 lamellas. The Bi-2212 + m(Sr_1−xCa_x)₃Al₂O₆ materials displayed a trend to enhance flux pinning at T = 60 K with the increase of aluminate phase content.     

Magnetic properties of the Bi1.95Sr2.05−xLaxCuOy (Bi-2201) superconducting phase

We have investigated the reversible mixed-state magnetization M of three lanthanum substituted Bi_1.95Sr_2.05−xLa_xCuO_y (Bi-2201) ceramic samples having different critical temperatures T_c ranging from 20.0 to 35.5 K. As for the Bi₂Sr₂CaCu₂O_8+δ (Bi-2212) phase, we found that anisotropy of Bi-2201 is large. A manifestation of this anisotropy is the field independent magnetization M^* observed at a temperature T^*. In the framework of the London model, and including thermal fluctuations of vortices, we found for the temperature dependence of the penetration depth λ_ab(T) = λ_ab(0)[1 − (T/T_c0)ⁿ]^−1/2, with n 1.7 and λ_ab (T = 0) 4000 Å. The estimated upper critical fields μ₀H_c2,c are of the order of 10 T. We observe a peculiar negative slope M/T at low temperature and sufficiently high external magnetic field. This feature seems to be a characteristic of the Bi-2201 phase. However, we do not know whether it is associated with the superconducting mixed-state. A small amount of magnetic impurities could also be responsible for this behavior. Finally, the behavior of the reversible magnetization of the Bi-2201 samples investigated, which are situated at the optimal and in the overdoped region, did not indicate any unusual temperature dependence for the upper critical field H_c2,c.     

Vortex matter phase transition in the C15-Laves-phase superconductor CeRu2: comparison with Bi-2212

We present a comparative study of peak-effect in DC magnetization in single-crystal samples of CeRu₂ and Bi-2212. While the PE in Bi-2212 can be associated with the second-order phase transition from Bragg-glass to vortex-glass, the PE in CeRu₂ is anomalous and can be understood as accompanying a first-order phase transition in the vortex matter.     

Effects of 230 MeV Au irradiation on Bi2Sr2CaCu2Ox

Bi₂Sr₂CaCu₂O_x tapes were irradiated using 230 MeV Au¹⁴⁺ ions. Columnar defects were presumably produced due to irradiation. Zero-field-cooling (ZFC) magnetization increased up to a fluence of 1.6 × 10¹¹ Au⁺/cm², but field-cooling (FC) magnetization decreased, indicating the strong pinning effects resulting from the columnar defects. The critical current density as well as the irreversibility field, obtained from the hysteresis loops, were enhanced. Irreversibility fields are fitted by H_irr = A exp(−T/T_A). An effective activation energy for flux motion was obtained from the measurements of magnetization relaxation. The features of flux pinning as a result of the columnar defects were compared with those of point defects brought about by 120 MeV O⁷⁺ irradiation.     

Field-induced pinning effect of Nd(Ba1−xNdx)2Cu3O7−δ single crystals grown by the traveling-solvent floating-zone method

We have studied the superconducting properties of Nd(Ba_1−xNd_x)₂Cu₃O_7−δ (Nd123, x ≈ 0.1) single crystals grown by the traveling-solvent floating-zone method under 0.1% O₂ in Ar atmosphere. The enhancement of the magnetization with increasing field is observed in the hysteresis (M-H) loop in fields both parallel and perpendicular to the c-axis of the Nd123 single crystals as well as in the bulk crystals prepared by the oxygen-controlled-melt-growth (OCMG) method. The composition variation of Ba/Nd is observed in the matrix of Nd123 crystals by an analytical TEM equipped with a cold field-emission gun. It turns out that the enhancement is due to the field-induced pinning effect ascribed to the weak superconducting Nd---Ba substitution regions in the Nd123 matrix.     

Field induced flux pinning in Nd1+xBa2−xCu3O7−δ single crystal

The flux pinning behavior of a Nd_1+xBa_2−xCu₃O_7−δ (Nd123) single crystal, which exhibited a peak effect, has been studied by monitoring the time decay of the magnetic moment. The apparent pinning energy (U₀^*) was deduced from flux creep data on the basis of the Anderson-Kim model. The magnetic field dependence of U₀^* showed maxima at peak fields which depended on the temperatures, in a similar manner to those of critical current densities. In addition, the temperature dependence of U₀^* showed several features. To explain the increase in U₀^* with the field as well as its temperature and field dependence, we made a numerical calculation by introducing an additional pinning energy which increased with increasing field. The results are in good agreement with the experimental data, especially at temperatures above 60 K, where the contribution of field induced pinning centers is believed to be dominant.     

Unusual resistivity broadening in the mixed state of NdBa2Cu3O7−δ crystals grown by a crystal-pulling technique

In order to clarify the origin of a strong peak effect in the magnetization curve of NdBa₂Cu₃O_7−δ crystals, we investigated the superconductivity transition behavior of the in-plane resistivity in static magnetic fields up to 8 T. Comparing the results for the samples exhibiting and not exhibiting the peak effect, we found that the former (peak effect sample) shows lower resistivity above the vortex melting temperature. This implies that the pinning force is effective in the vortex liquid state. We also found that the normal state resistivity behaviors of some samples were unusual, indicating inhomogeneous current flow. These results suggest an existence of sheet-like pinning centers perpendicular to the conduction planes.     

Angular dependence of the magnetization curves and interlayer Josephson coupling in Bi2Sr2CaCu2O8

Magnetization curves were measured for Bi₂Sr₂CaCu₂O₈ crystals which were irradiated with 5.8 GeV Pb ions along the c direction or at 45° with respect to it. Each ion produces continuous columnar that crosses the sample and yields a unidirectional pinning center. The density of the defects in the various samples ranges from 10¹⁰ to 2.5 X 10¹¹ ions/cm². In all the irradiated samples the width of the magnetization curves is found to be the largest for fields along the defects indicating that when the field is at other directions the vortices are tilted away from the defects. This manifests the important role of the Josephson coupling between the CuO₂ planes. We also report on accelerated flux escape around zero magnetization and around zero field, particularly in samples with a high dose of irradiation.     

Low temperature magnetocaloric effects in Dy1Ba2Cu3O7−δ and Y1Ba2Cu3O7−δ high-Tc single crystals

The heat release has been measured in high temperature superconductors during and after a change of the external magnetic field μ₀H_a ≤ 0.5 T applied parallel to the c-axis at 0.1 K ≤ T ≤ 0.45 K. Two Y123 and one Dy123 twinned single crystals were investigated. An analysis of the heat release based on the Bean model and on a model for thin superconductors in perpendicular geometry recently proposed by Brandt et al. has been carried out. During field sweep we measured ∝ H_a²dH_a/dt. This dependence can be understood within the Bean model for longitudinal geometry. The critical current densities obtained with this method are in good agreement with those from magnetization measurements. We also present measurements, and a first quantitative analysis, of dissipation due to the time relaxation of the flux line lattice after a field sweep. For the heat release a t⁻¹ dependence has been found which corresponds to a logarithmic time dependence of the magnetization. The normalized relaxation rate we obtained is in agreement with literature values.     

用自助熔剂法生长Bi2Sr2CaCu2Oy单晶的特点

用Ｂｉ₂Ｏ₃作自助熔剂，对Ｂｉ-２２１２单晶的生长特点作了较为细致的实验研究．就助熔剂含量、热循环、坩锅的污染、熔体的非共熔性、各向异性生长速度以及Ｂｉ-２２０１相的共生等晶体生长中普遍存在的诸多问题进行了深入的探讨     

Irreversibility line and anisotropy of magnetic melt textured Y1Ba2Cu3O7−δ studied by AC susceptibility

Magnetically melt textured YBa₂Cu₃O_7−δ samples have been studied by AC initial susceptibility measurements in the low field limit. The critical dynamic fields h^*_c and the relative position of the irreversibility line and of the critical line show that magnetic melt texturing leads to the creation of strong pinning sites. The anisotropy factor A is in agreement with the value obtained from magnetization under high DC fields. The A values are lower than in single cystals, but in agreement with the important orientation effects introduced by magnetic field texturing. These values also are typical of fabrication techniques involving a melting at some stage.     

Dynamic softening of vortex lines in YBa2Cu3O7−δ single crystals

Transport measurements in the mixed state of oxygen-deficient YBa₂Cu₃O_7−δ single crystals using the flux transformer configuration show that the flux liquid changes with increasing anisotropy from strongly correlated to uncorrelated in the field direction. For intermediate coupling, the current inducing loss of vortex correlation has a maximum near the irreversibility temperature. Thus, an effective softening of vortex lines with decreasing temperature is detected. We propose a simple model that accounts for this behavior by including the effects of the pinning potential on the dynamics of vortices.     

Phase separation in YBa2Cu3O7−δ single crystals near δ = 0

X-ray diffraction, resistivity, AC and DC magnetization data on high-quality single crystals of YBa₂Cu₃O_7−δ are presented. We demonstrate that for δ<0.08, the (0 0 l) diffraction lines are split into two, indicating that at these high oxygen concentrations the crystals are no longer single phase but actually consist of two (or more) different phases with slightly different c-axis parameters. In the two-phase region, the electrical resistivity and the AC and DC magnetic susceptibilities show a broadening of the superconducting transition. This broadening is thought to be due to the proximity effect or strains in two finely dispersed phases with slightly different transition temperatures.     

Electrochemical reduction of Bi2Sr2Ca1Cu2O8 superconductor single crystals

Single crystals and polycrystalline pellets of the high-temperature cuprate superconductor Bi₂Sr₂Ca₁Cu₂O₈ were doped at room temperature by electrochemical reduction at > 95% Coulombic efficiency using lithium dopant ions in propylene carbonate electrolyte. Cyclic voltammetry and potential step measurements on single crystals suggest an unusual reduction mechanism, with a diffusion coefficient for Li⁺ in the c-axis direction of bulk superconductor of ca. 3 × 10⁻¹¹ cm²s⁻¹. Sintered pellets of polycrystalline powder could be doped more rapidly, with an apparent diffusion coefficient of 7 × 10⁻⁸ cm²s⁻¹. X-ray susceptibility analysis show extensive disordering occurs on heavy Li doping, with a first-order transition from a crystalline/superconducting to an amorphous/non-superconducting phase. Single, crystals of Bi₂Sr₂Ca₁Cu₂O₈ exhibited a color change on reduction from metallic gray to golden bronze. The reduced material was highly air-sensitive, forming a hydroxide surface film on exposure to ambient atmosphere.     

Evidence for pinning by (Sr,Ca)2CuOy particles in partial-melting processed bulk Bi2Sr2CaCu2O8+δ ceramics

Flux distributions of partial-melting processed Bi₂Sr₂CaCu₂O_8+δ ceramics are obtained using magneto-optic imaging. In remanent states (μ₀H_a=0 T), large amounts of trapped flux are observed along (Sr,Ca)₂CuO_y particles embedded in the Bi₂Sr₂CaCu₂O_8+δ matrix. Despite the relatively large size of these particles (up to 30 μm), the pinning effect is similar to that of Y₂BaCuO₅ particles in melt-processed YBa₂Cu₃O_7−δ. Furthermore, we discuss how the pinning capability of non-superconducting particles of different sizes and densities will show up in magneto-optic images.     

Bi_2Sr_2CaCu_2O_(8+δ)单晶的钉扎力标度和磁通钉扎机制

测量了 Bi2 Sr2 Ca Cu2 O8+δ单晶不同温度下的磁化曲线。根据 Bean临界态模型得到了不同温度下的钉扎力密度 FP 对磁场的依赖关系 ,发现在不同温度下的钉扎力密度可以标度在同一条曲线上。标度函数和最大钉扎力所对应的磁场与不可逆场 Hirr的比值都表明 Si2 Sr2 Ca Cu2 O8+δ单晶在磁通玻璃态的钉扎机制主要是正常相面钉扎。     

Surface versus bulk pinning in a HgBa2Ca2Cu3O8+x ceramics

Flux creep measurements on a HgBa₂Ca₂Cu₃O_8+x ceramics are reported. The results of the magnetic relaxation measurements are analyzed both by assuming that the pinning is due to the existence of a surface barrier or exclusively caused by bulk pinning. The action of both the surface and the bulk barriers is evidenced. At 70 K, a very high critical current density of the surface currents is determined, which is higher than the critical current density of the bulk. The field and temperature dependence of the pinning behaviour reflects mainly bulk pinning in 2D. The measurements were repeated after 4 and 12 months to investigate the influence of aging. A destruction of the superconducting properties of the grain boundaries accompanied by a degradation of the surfaces of the grains with time is proved.     

The weak center nature and their pinning anisotropy of radiation damage defects in Y1Ba2Cu3O7−δ single crystals

A field induced weak pinning center, in MeV proton irradiated Y₁Ba₂Cu₃O_7−δ (YBCO) single crystal and in ⁶Li-doped sintered YBCO exposed to thermal neutron irradiation, has been identified. The pinning contribution of those radiation caused weak centers (RWCs) showed strong field dependence, which resembles that of the common weak centers of oxygen deficient regions (OWCs) in most of the bulk YBCO materials. The radiation dose dependence of the pinning enhancement, in proton irradiated single crystal, showed strong angular dependence, when the field orientation relative to the crystal was changed. This is believed to be due to the different flux line size (orξ) in different directions, and the so caused volume or line pinning effects. No angular dependence has been observed in neutron irradiated YBCO, which is polycrystalline in nature.     

Vortex pinning in polycrystalline Eu1.5Ce0.5Sr2Cu2NbO10 from rotational magnetic measurements

Rotational magnetization-vector measurements were carried out on a superconducting polycrystalline disk of EuCSCNO. The results at 4.2 K and low fields resemble recent results for YBa₂Cu₃O_7−δ (YBCO) and Ba_0.57K_0.43BiO₃ (BKBO) in revealing a broad distribution in the strength of the vortex pinning torques. This resemblance extends to higher fields, where it was found that the average pinning torque per vortex (τ_p), which is directly related to the critical current density, decreases steadily with increasing field in a manner consistent with vortex bundling. Quantitatively, however, the values of τ_p for EuCSCNO are smaller by an order of magnitude than those for YBCO but are only moderately smaller than those for BKBO. This comparison supports the notion that the vortex pinning may derive in part from deviations from oxygen stoichiometry, which are normally present in YBCO but are essentially absent in EuCSCNO and BKBO. Moreover, as in YBCO and BKBO, the τ_p in EuCSCNO at fixed field is found to diminish rapidly as the temperature rises towards T_c.