Electrochemical reduction of Bi2Sr2Ca1Cu2O8 superconductor single crystals

Single crystals and polycrystalline pellets of the high-temperature cuprate superconductor Bi₂Sr₂Ca₁Cu₂O₈ were doped at room temperature by electrochemical reduction at > 95% Coulombic efficiency using lithium dopant ions in propylene carbonate electrolyte. Cyclic voltammetry and potential step measurements on single crystals suggest an unusual reduction mechanism, with a diffusion coefficient for Li⁺ in the c-axis direction of bulk superconductor of ca. 3 × 10^?11 cm²s^?1. Sintered pellets of polycrystalline powder could be doped more rapidly, with an apparent diffusion coefficient of 7 × 10^?8 cm²s^?1. X-ray susceptibility analysis show extensive disordering occurs on heavy Li doping, with a first-order transition from a crystalline/superconducting to an amorphous/non-superconducting phase. Single, crystals of Bi₂Sr₂Ca₁Cu₂O₈ exhibited a color change on reduction from metallic gray to golden bronze. The reduced material was highly air-sensitive, forming a hydroxide surface film on exposure to ambient atmosphere.