The effect of morphology and doping on photoluminescence of ZnO nanostructures

In this work, optical properties of ZnO nanostructures prepared by chemical vapor deposition under different conditions were investigated. ZnO nanostructures were characterized by electron microscopy and photoluminescence. A high intensity green emission and a narrow UV emission band are observed in photoluminescence spectra of ZnO nanostructures related to the below-band-gap and band-edge that their intensities depend on the morphology of the nanostructures. It is considered that the green emission is originated from structural defects. In addition, the influence of thermal treatment and dopants such as iron and copper, on the photoluminescence (PL) properties of the ZnO nanostructures was investigated.     

Effect of growth temperature on the ZnO nanowires prepared by thermal heating of Zn powders

ZnO nanowires have been synthesized by heating Zn powders under nitrogen (N₂) gas atmosphere. The influence of the growth temperature on the morphology, structure, and photoluminescence (PL) properties of ZnO nanowires has been investigated. At the higher-temperature growth process, thinner nanowires have been obtained. Interestingly, it is observed that the variation of growth temperature has significantly affected the photoluminescence spectra of the ZnO nanowires, showing an enhancement in the relative intensity of the green to UV emission bands with the increase of the growth temperature. In addition, the oxygen sensing properties of the as-synthesized ZnO nanowires were tested.     

Nanocrystalline ZnO film deposited by ultrasonic spray on textured silicon substrate as an anti-reflection coating layer

A ZnO thin film was successfully synthesized on glass, flat surface and textured silicon substrates by chemical spray deposition. The textured silicon substrate was carried out using two solutions (NaOH/IPA and Na₂CO₃). Textured with Na₂CO₃ solution, the sample surface exhibits uniform pyramids with an average height of 5 μm. The properties and morphology of ZnO films were investigated. X-ray diffraction (XRD) spectra revealed a preferred orientation of the ZnO nanocrystalline film along the c-axis where the low value of the tensile strain 0.26% was obtained. SEM images show that all films display a granular, polycrystalline morphology. The morphology of the ZnO layers depends dramatically on the substrate used and follows the contours of the pyramids on the substrate surface. The average reflectance of the textured surface was found to be around 13% and it decreases dramatically to 2.57% after deposition of a ZnO antireflection coating. FT-IR peaks arising from the bonding between Zn–O are clearly represented using a silicon textured surface. A very intense photoluminescence (PL) emission peak is observed for ZnO/textured Si, revealing the good quality of the layer. The PL peak at 380.5 nm (UV emission) and the high-intensity PL peak at 427.5 nm are observed and a high luminescence occurs when using a textured Si substrate.     

Optical properties of ZnO nanoparticles synthesized by varying the sodium hydroxide to zinc acetate molar ratios using a Sol-Gel process

Material property dependence on the OH⁻/Zn²⁺ molar ratio of the precursor was investigated by varying the amount of NaOH during synthesis of ZnO. It was necessary to control the water content and temperature of the mixture to ensure the reproducibility. It was observed that the structural properties, particle size, photoluminescence intensity and wavelength of maximum intensity were influenced by the molar ratio of the precursor. The XRD spectra for ZnO nanoparticles show the entire peaks corresponding to the various planes of wurtzite ZnO, indicating a single phase. UV measurements show the absorption that comes from the ZnO nanoparticles in visible region. The absorption edge of these ZnO nanoparticles are shifted to higher energies and the determined band gap energies are blue shifted as the OH⁻/Zn² molar ration increases, due to the quantum confinement effects. The photoluminescence characterization of the ZnO nanostructures exhibited a broad emission band centred at green (600 nm) region for all molar ratios except for OH⁻/Zn²⁺ = 1.7 where a second blue emission around 468 nm was also observed. The photoluminescence properties of ZnO nanoparticles were largely determined by the size and surface properties of the nanoparticles.     

退火对多晶ZnO薄膜结构与发光特性的影响

用射频反应溅射法在Si（111）衬底上制备了C轴取向的多晶ZnO薄膜，通过不同温度的退火处理，研究了退火对多晶ZnO薄膜结构和发光特性的影响.由x射线衍射得知，随退火温度的升高，晶粒逐渐变大，薄膜中压应力由大变小至出现张应力.光致发光测量发现，样品在430nm附近有一光致发光峰, 峰的强度随退火温度升高而减弱，联合样品电阻率随退火温度升高而逐渐变大的测量及能级图，推测出ZnO薄膜中的蓝光发射主要来源于锌填隙原子缺陷能级与价带顶能级间的跃迁. 关键词： ZnO薄膜 退火 光致发光 射频反应溅射     

Synthesis and characterization of ZnO-Ag core-shell nanocomposites with uniform thin silver layers

This paper presents an investigation on the synthesis and characterization of ZnO-Ag core-shell nanocomposites. ZnO nanorods were employed as core material for Ag seeds, and subsequent nucleation and growth of reduced Ag by formaldehyde formed the ZnO-Ag core-shell nanocomposites. The ZnO-Ag nanocomposites were annealed at different temperature to improve the crystallinity and binding strength of Ag nanoparticles. The morphology, microstructure and optical properties of the ZnO-Ag core-shell nanocomposites were characterized by X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy, energy-dispersive X-ray spectroscopy, ultraviolet-visible (UV-vis) absorption and photoluminescence measurement. It was demonstrated that very small face-center-cubic Ag nanoparticles were coated on the surface of ZnO nanorods. The ultraviolet absorption and surface plasmon absorption band of ZnO-Ag core-shell nanocomposites exhibited some redshifts relative to pure ZnO nanorods and monometallic Ag nanoparticles. The coating of Ag nanocrystals onto the ZnO nanorods completely quenched the photoluminescence. These observations reflected the strong interfacial interaction between ZnO nanorods and Ag nanoparticles. The effect of Ag coating thickness on the morphology and optical properties of ZnO-Ag core-shell nanocomposites was also investigated. Moreover, the growth mechanism of ZnO-Ag core-shell nanocomposites was also proposed and discussed in detail.     

LiGaO2衬底上ZnO外延膜的结构与光学特性

采用磁控溅射法在(001),(100)及(010)LiGaO2衬底上制备了ZnO薄膜,通过X射线衍射(XRD)、原子力显微镜(AFM)、透过光谱以及光致发光谱(PL)对薄膜的结构、形貌及光学性质进行了表征.结果表明LiGaO2衬底不同晶面上制备的ZnO薄膜具有不同的择优取向,在(001)、(100)及(010)LiGaO2上分别获得了[001]、[1100]及[1120]取向的ZnO薄膜;不同取向的ZnO薄膜表面形貌差异较大;薄膜在可见光波段具有较高的透过率;在ZnO薄膜的光致发光谱中只观察到了位于378 nm的紫外发射峰,而深能级发射几乎观察不到,(1100)取向的薄膜紫外发射峰强度最大,半高宽也最小,薄膜光致发光件质的差异丰要和晶粒尺寸有关.     

Photoluminescence investigation of ZnO:P nanoneedle arrays on InP substrate by pulsed laser deposition

Phosphorus-doped ZnO nanoneedle arrays were prepared by phosphorus diffusion from InP substrate using a pulsed laser deposition (PLD) technique. The optical properties of ZnO nanoneedle were investigated by photoluminescence (PL) spectroscopy. Low-temperature photoluminescence spectrum measurements exhibited five acceptor-related emission peaks. The excitation intensity and temperature dependent photoluminescence spectra confirmed that the emission peaks corresponded to neutral-acceptor bound exciton, free electron to acceptor, donor-acceptor pairs, and their first and second photon replicas transitions. Acceptor-binding energy was determined to be 135-167 meV, which agrees well with the best-fitting result of the temperature dependent photoluminescence measurements and is reasonable in terms of theoretic prediction in ZnO.     

Dominant ultraviolet-blue photoluminescence of ZnO embedded into synthetic opal

The temperature-dependent photoluminescence (PL) characteristics of zinc oxide (ZnO) embedded into the voids of synthetic opal were studied. ZnO was infiltrated into opal from aqueous solution with zinc nitrate precursor followed by thermal annealing. The PL spectra of the ZnO powder exhibit very high and broad emission peaks in the green region due to crystal defects, such as oxygen vacancies and zinc ion interstitials. In contrast to the PL spectra of ZnO powder, nanocrystals of ZnO embedded into the voids of FCC packed opal matrix exhibit dominant ultraviolet (UV)-blue and rapidly decreasing green PL emissions with decreasing temperature. The temperature-dependent PL characteristics show that the green band suppression in the ZnO nanocrystals is due to the influence of photonic crystal. The infiltration of nanoparticles into synthetic opal may be used for the fabrication of polycrystalline ZnO with dominant UV-blue PL. These results indicate that the luminescent materials embedded into photonic crystal may be promising for the fabrication of the RGB pixels in full-color displays.     

Effect of Mn doping on the structural and optical properties of sol-gel derived ZnO nanoparticles

Un-doped and Mn-doped ZnO nanoparticles were successfully synthesized in an ethanolic solution by using a sol-gel method. Material properties of the samples dependence on preparation conditions and Mn concentrations were investigated while other parameters were controlled to ensure reproducibility. It was observed that the structural properties, particle size, band gap, photoluminescence intensity and wavelength of maximum intensity were influenced by the amount of Mn ions present in the precursor. The XRD spectra for ZnO nanoparticles show the entire peaks corresponding to the various planes of wurtzite ZnO, indicating a single phase. The diffraction peaks of doped samples are slightly shifted to lower angles with an increase in the Mn ion concentration, signifying the expansion of the lattice constants and increase in the band gap of ZnO. All the samples show the absorption in the visible region. The absorbance spectra show that the excitonic absorption peak shifts towards the lower wavelength side with the Mn-doped ZnO nanoparticles. The PL spectra of undoped ZnO consist of UV emission at 388 nm and broad visible emission at 560 nm with varying relative peak intensities. The doping of ZnO with Mn quenches significantly the green emission while UV luminescence is slightly affected.     

Preparation and optical properties of ZnO@PPEGMA nanoparticles

The poly(poly(ethylene glycol) methyl ether monomethacrylate) (PPEGMA) grafted zinc oxide (ZnO) nanoparticles were successfully prepared via the surface-initiated atom transfer radical polymerizations (ATRP) from the surfaces functionalized ZnO nanoparticles. The 2-bromoisobutyrate (BIB) was immobilized onto the surface of the ZnO nanoparticles through the reaction between 2-bromoisobutyryl bromide (BIBB) and the hydroxyl groups on nanoparticles, serving as the initiator to induce the ATRP of poly(ethylene glycol) monomethacrylate (PEGMA). Well-defined polymer chains were grown from the surfaces to yield hybrid nanoparticles comprised of ZnO cores and PPEGMA polymer shells having multifunctional end groups. The structure and morphology of the nanoparticles were characterized using Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), X-ray diffraction (XRD) and transmission electron microscopy (TEM). The optical properties of the nanoparticles were investigated by UV-vis absorption spectroscopy and photoluminescence spectroscopy (PL). The results showed that the dispersion and near-band edge (NBE) emission of ZnO nanoparticles could be improved by the grafted PPEGMA polymer segments.     

Effect of barium doping on the physical properties of zinc oxide nanoparticles elaborated via sonochemical synthesis method

The aim of this work is to study the effect of barium (Ba) doping on the optical, morphological and structural properties of ZnO nanoparticles. Undoped and Ba-doped ZnO have been successfully synthesized via sonochemical method using zinc nitrate, hexamethylenetetramine (HMT) and barium chloride as starting materials. The structural characterization by XRD and FTIR shows that ZnO nanoparticles are polycrystalline with a standard hexagonal ZnO wurtzite crystal structure. Decrease in lattice parameters from diffraction data shows the presence of Ba²⁺ in the ZnO crystal lattice. The morphology of the ZnO nanoparticles has been determined by scanning electron microscopy (SEM). Incorporation of Ba was confirmed from the elemental analysis using EDX. Optical analysis depicted that all samples exhibit an average optical transparency over 80%, in the visible range. Room-temperature photoluminescence (PL) spectra detected a strong ultraviolet emission at 330 nm and two weak emission bands were observed near 417 and 560 nm. Raman spectroscopy analysis of Ba-doped samples reveals the successful doping of Ba ions in the host ZnO.     

Relationship between crystal morphology and photoluminescence in polynanocrystalline lead sulfide thin films

Thin films of lead sulfide (PbS) nanoparticles were grown on corning glass and Si(1 0 0) substrates by polyethylene glycol-assisted chemical bath deposition (CBD) method. This paper compares the morphology and the luminescence properties (PL) of the deposited thin films in the presence (or absence) of PEG300 and investigates the effect of deposition temperatures. Surface morphology and photoluminescence properties of samples were analyzed. The PL data show a blue-shift from the normal emission at ∼2900 nm in PbS bulk to ∼360 nm in nanoparticles of PbS thin films. Furthermore, the PL emission of the films obtained without the addition of PEG300 (type 1) was slightly shifted from that of the films obtained in presence of PEG300 (type 2) from ∼360 to ∼470 nm. The blue-shifting of the emission wavelengths from 2900 to ∼360 or 470 nm is attributed to quantum confinement of charge carriers in the restricted volume of nanoparticles, while the shift between the two types of PbS nanoparticles thin films is speculated to be due to an increase in the defect concentration. The blue-shift increased with increase of the deposition temperature, which suggests that there has been a relative depletion in particle sizes during the CBD of the films at higher temperatures. The PbS nanocrystalline thin films obtained in the presence of PEG300 at 60 °C exhibit a high blue luminescence.     

Size-dependent visible photoluminescence from ZnO nanoparticles prepared via SiO2 network

This study reports a simple method for the synthesis of different size of wurtzite ZnO nanoparticles in assistance of tetraethyl orthosilicate (TEOS). With the increase of the amount of TEOS added, the average size of ZnO nanoparticles was found decreased from ∼14.6 to ∼1.9 nm by characterization of X-ray diffraction (XRD) and high-resolution electron microscopy (HRTEM). The growth of ZnO nanoparticles is proposed to be controlled by the density of the SiO₂ chain mesh which is determined by TEOS amount in precursor. Ultraviolet–visible (UV–VIS) absorption and photoluminescence (PL) spectra show both shift to higher energy in cut-off edge and in visible emission bands respectively. The electron transition process in the mechanism of the visible emission shift was described and related to quantum size effect in ZnO nanoparticles.     

Effect of Fe-doping on the structural,morphological and optical properties of ZnO nanoparticles synthesized by solution combustion process

The effect of Fe-doping on the structural, morphological and optical properties of ZnO nanoparticles synthesized by simple solution combustion process are reported. The powder XRD pattern indicates that the Fe-doped ZnO samples exhibit primary and secondary phases. The primary phase indicates the hexagonal wurtzite structure with the average crystalline size of around 25–50 nm and the secondary phase is associated with the face centered cubic structure of magnetite iron oxide. The elemental composition of pure and Fe-doped samples are evaluvated by EDX. The results of FE-SEM and HR-TEM cleary show that particles morphology have changed with respect to the incorporation of doping agent and particles are in aggregating nature. The vibrational properties of the synthesized ZnO nanoparticles are investigated by Raman scattering technique and it exhibits that the influence of Fe-doping significantly modify the lattice vibrational characteristics in ZnO sites. The optical properties of the Fe-doped ZnO nanoparticles are carried out by UV–vis absorption and PL spectra. The results of PL spectra show the near-band edge related emission as well as strong blue emissions in the Fe-doped ZnO nanoparticles.     

退火对ZnO薄膜的结构和光学性质的影响

采用射频磁控溅射法在Si衬底上制备了高c轴择优取向的ZnO薄膜,研究了退火对ZnO薄膜的晶粒尺度和发光光谱的影响。XRD结果显示退火可以改善ZnO薄膜的结构特性,PL谱结果显示退火对ZnO薄膜的发光强度产生很大影响。     

Ex situ synthesis and optical properties of ZnO-PbS nanocomposites

Zinc oxide (ZnO) and lead sulphide (PbS) nanoparticles separately synthesized by a precipitation method were combined by an ex situ route to prepare ZnO-PbS nanocomposites with different molar ratios of ZnO and PbS. The structure and morphology of the ZnO, PbS and ZnO-PbS samples were analyzed with X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM). A UV-vis spectrophotometer was used to collect the absorption and 325 nm He-Cd and 488 nm Ar lasers were used to collect the photoluminescence data from the samples. ZnO nanoparticles showed a broad and stable emission peak at ∼570 nm, while a strongly quantum confined emission from PbS nanoparticles was detected at ∼1344-1486 nm. The ZnO-PbS nanocomposites exhibited dual emission in the visible and near-infrared (NIR) regions that is associated with defects and recombination of excitonic centres in the ZnO and PbS nanoparticles, respectively. The PL intensity of the visible emission from the ZnO-PbS nanocomposite was shown to increase when the ZnO to PbS molar ratio was 5:1 and the emission was almost quenched at molar ratios of 1:1 and 1:5. For different molar ratios of ZnO to PbS, the PL intensity of the NIR emission from the ZnO-PbS nanocomposites was more intense than that of PbS nanoparticles.     

脉冲激光沉积方法制备ZnO薄膜生长参量对发光特性的影响

用脉冲激光沉积（PLD）方法在Si（111）衬底上制备了ZnO薄膜。以325nmHe-Cd激光器为光源对薄膜进行了荧光光谱分析,用X射线衍射仪（XRD）和原子力显微镜（AFM）分别对薄膜的结构和形貌进行了分析。脉冲激光沉积方法的主要生长参量为氧压、激光重复频率、生长温度和激光能量。通过控制这些参量变量,研究了这些参量对ZnO薄膜发光特性的影响,得到了用于紫外发光的ZnO薄膜生长的优化条件：发现在温度为650℃左右、氧压50Pa左右、频率5Hz左右的范围内能得到半峰全宽较窄,强度较大的紫外发光峰。分析认为紫外峰主要是由激子辐射复合发光形成的,绿光带主要和Ozn的存在密切相关,氧空位是蓝光发射的重要原因。     

六角锥状ZnO纳米结构的生长机理、结构及光学性能(英文)

利用醋酸锌[Zn(CH3COO)2·2H2O]和六次甲基四胺(C6H12N4)以一定比例配置成反应溶液,通过水热合成法制备了六角锥状ZnO纳米结构。同时,使用了扫描电子显微镜(SEM)、X射线衍射和选区电子衍射(SAED),对样品的形貌与结构进行了分析。结果表明,样品形貌成六角锥状结构,并且在[002]方向择优生长。通过对样品的光学性能测试,由PL光谱分析可知,样品在379nm处有一个较强的紫外发光峰,并且在可见光区域产生了一些较弱的可见光发射峰,表明制备的六角锥状ZnO纳米结构的晶体质量不是很好。除此之外,对六角锥状ZnO的生长机理也进行了讨论。     

Study of ZnO-coated SnO2 nanostructures synthesized by a two-step process

We investigated the influence of the ZnO coating on the properties of one-dimensional (1D) nanostructures of SnO₂. We have employed X-ray diffraction, scanning electron microscope, transmission electron microscope and photoluminescence (PL) spectroscopy to characterize both as-synthesized and ZnO-coated products. We observed that deposition process of ZnO by using an atomic layer deposition technique resulted in the SnO₂ core/ZnO shell structure. The photoluminescence of the ZnO-coated products exhibited broad bands in the UV and green region, suggesting a possible contribution of the emission from the ZnO outlayers.