分子束外延生长Fe/Fe50Mn50双层膜的交换偏置

利用表面磁光克尔效应和铁磁共振对分子束外延生长的Fe/Fe₅₀Mn₅₀双层膜的交换偏置场和矫顽力进行了研究,实验结果表明,当反铁磁层厚度小于55nm时 ,不出现交换偏置,而当大于这一厚度时,出现交换偏置;大约在7nm时,达到极大值.随着 反铁磁层厚度的继续增大,偏置场和矫顽力随Fe₅₀Mn₅₀膜厚的增大 而下降.铁磁共振实验结果表明样品的磁性存在单向各向异性.并对上述结果进行了讨论. 关键词： 分子束外延 50Mn₅₀')" href="#">Fe/Fe₅₀Mn₅₀ 双层膜 交换偏置     

具有垂直各向异性(Pt/Co)n/FeMn多层膜的交换偏置

采用磁控溅射方法制备了以Pt为缓冲层和保护层的具有垂直各向异性(Pt/Co)n/FeMn多层膜.研究结果表明,多层膜的垂直交换偏置场Hex和反铁磁层厚度的关系与其具有平面各向异性的交换偏置场随反铁磁层厚度变化趋势相近.随着铁磁层调制周期数的增加,垂直交换偏置场Hex相应减小,并且与铁磁层的调制周期数近似成反比关系.(Pt/Co)3/FeMn的垂直交换偏置场Hex已经达到22.3kA/m.为了进一步提高Hex,在Co/FeMn的界面插入Pt层,当Pt层厚度为0.4nm时,Hex达到最大值39.8kA/m.     

铁磁/反铁磁双层膜系统中交换各向异性及其厚度依赖性

研究铁磁/反铁磁双层膜系统中交换偏置场和矫顽场的冷却磁场依赖性.结果表明,随着冷却磁场的增加,交换偏置场由负值向正值转变.在转变点附近,矫顽场有-个特别的增强,并达到最大值.结果同相关实验-致.研究铁磁层和反铁磁层厚度对交换偏置场和矫顽场的影响.发现,正负交换偏置场和矫顽场随着铁磁层厚度的增大而减小,但随反铁磁层厚度的变化关系复杂.在正交换偏置场的情形,随反铁磁层厚度的增大,交换偏置场增强,矫顽场减弱;在负交换偏置场的情形,随反铁磁层厚度的增大,交换偏置场减弱,矫顽场增强.     

具有垂直各向异性(Pt/Co)n/FeMn多层膜的交换偏置

采用磁控溅射方法制备了以Pt为缓冲层和保护层的具有垂直各向异性(Pt/Co)_n/ FeMn多层膜.研究结果表明，多层膜的垂直交换偏置场H_ex和反铁磁层厚度的关 系与其具有平面各向异性的交换偏置场随反铁磁层厚度变化趋势相近.随着铁磁层调制周期 数的增加，垂直交换偏置场H_ex相应减小，并且与铁磁层的调制周期数近似成反 比关系.(Pt/Co)₃/FeMn的垂直交换偏置场H_ex已经达到22.3kA/m.为 关键词： 交换偏置 垂直各向异性 多层膜     

成分和厚度的依赖

通过调整Mn的成分，系统地研究了Ni81Fe19/Ni100-xMnx双层膜的磁学性质，特别是交换偏置场(Hex)的变化.当Ni100-xMnx中Mn的原子百分比在534%到600%之间时，对于150nm的Ni81Fe19，得到了最大的交换偏置场175kA/m，同时由于Mn对Ni81Fe19层的扩散所造成的磁矩的降低小于20%；高角x射线衍射证明Ni100-xMnx的晶格常数随着Mn成分的改变而变化，Mn含量越多，其晶格常数越大；制备态Ni100-xMnx膜晶格常数与θ相NiMn膜晶格常数的接近程度与NiMn膜θ相形成的容易程度相对应.也研究了交换偏置场随着Ni１００-xMnx厚度的变化，第一次得到了当Ni100-xMnx中Mn的原子百分比为706%时，Ni81Fe19(150nm)/Ni100-xMnx(90nm)双层膜在经过240℃，5h退火后，可以有80kA/m的交换偏置场，此时铁磁层磁矩的大小几乎不变. 关键词： Ni81Fe19/Ni100-xMnx 交换偏置场     

(Ni0.81Fe0.19)1-xCrx作为种子层对NiFe/FeMn交换偏置的影响

采用一种新的种子层材料:(Ni081Fe019)1-xCrx,通过改变种子层中Cr原子的含量,使得在其上生长的NiFeFeMn双层膜的织构和晶粒尺寸产生极大的差异,系统研究了NiFeFeMn双层膜中FeMn晶粒尺寸和织构对交换偏置的影响.实验结果表明,在FeMn的γ相(111)织构较好的前提下,交换偏置场的大小与织构的差异没有关系;FeMn的晶粒尺寸对交换偏置场有很大影响,较小的反铁磁层晶粒对交换偏置场有利,过大的反铁磁层晶粒不利于交换偏置场.将(Ni081Fe019)05Cr05与传统的种子层材料Ta进 关键词： 交换偏置 晶粒尺寸 织构 种子层     

铁磁/反铁磁双层膜系统中的磁畴动力学行为

比较了铁磁单层膜与铁磁/反铁磁双层膜结构中的磁畴演化行为, 发现由于反铁磁层膜对铁磁层膜的耦合作用使得系统的磁畴壁厚度、 磁畴壁等效质量、磁畴壁移动速度等发生了改变, 系统的矫顽场增强, 并出现了交换偏置场. 文章具体研究了反铁磁层耦合作用下其磁畴壁厚度、 等效质量以及磁畴壁移动速度等与反铁磁层的净磁化、 磁各向异性、界面耦合强度以及温度等的关系; 并研究了其对铁磁/反铁磁双层膜中的交换偏置场、矫顽场的影响. 进而 从磁畴结构的形成及其演化上揭示了铁磁/反铁磁双 层膜中出现交换偏置以及矫顽场增加的物理机制.     

交换偏置系统中的反铁磁磁化与自旋波

采用自由能变分法研究了铁磁/反铁磁双层膜系统在反铁磁层存在净磁化下的自旋波谱.本模型中铁磁薄层具有单轴磁晶各向异性和立方磁晶各向异性,反铁磁层仅具有单轴磁晶各向异性,但厚度有限,推导出了系统铁磁共振频率的表达式.结果表明：系统的自旋波谱分光学模和声学模两种,其中光学模仅在反铁磁层存在净磁化时得到激发.自旋波谱可按外磁场强度的变化情况分为强弱两支;区分强磁场和弱磁场的临界场依赖于铁磁/反铁磁间的交换作用,反铁磁层的磁化强度以及反铁磁层的厚度等.交换偏置场对光学模的影响明显于声学模,而反铁磁的净磁化和其厚度对系统的影响紧密联系,难以区分.但当反铁磁层净磁化很小可忽略时,系统只存在声学模激发. 关键词： 铁磁/反铁磁双层膜 反铁磁层净磁化 光学模 声学模     

非磁性掺杂下的铁磁/反铁磁系统中的交换偏置和矫顽场

采用Monte Carlo方法,分别讨论了在铁磁/反铁磁双层膜和铁磁/反铁磁单层混合膜中,掺入非磁性物质后,掺杂浓度对交换偏置以及矫顽场的影响.计算结果表明:随着掺杂浓度的增大,双层膜和单层膜交换偏置都有先增大后减小的现象,而其矫顽场则先减小后增大.在相同掺杂浓度下,对随机掺杂和规则掺杂两种不同掺杂方式的结果比较发现:铁磁/反铁磁双层膜中,规则掺杂下产生的交换偏置和矫顽场都得到了增强;对于单层混合膜,随机掺杂下的交换偏置更强,规则掺杂下的矫顽场更大.研究发现对于双层膜规则掺杂可明显地导致其磁滞回线的不对称性,说明铁磁/反铁磁系统中磁滞回线的不对称性与界面自旋微结构密切相关.     

Cr/Ru/PtCo/Ru/PtCo/Ru介质中底层Ru厚度对磁记录特性影响的研究

讨论了Cr/Ru（1）/PtCo（稳定层）/Ru（2）/PtCo（记录层）/Ru（3） 结构的矫顽力Hc_c与层间反铁磁耦合交换场Hex_ex随Ru（1）与Ru（2）厚度变 化的规律.研究发现 ，样品的矫顽力及交换场随Ru（1）厚度增加而增大， 这可能是由Ru（1）hcp结构引起的. 矫顽力及交换场在Ru（2）厚度为08nm处有峰值. 关键词： 磁记录 反铁磁耦合     

Influence of Zr(50)Cu(50) thin film metallic glass as buffer layer on the structural and optoelectrical properties of AZO films

Aluminum-doped ZnO(AZO) thin films with thin film metallic glass of Zr(50)Cu(50) as buffer are prepared on glass substrates by the pulsed laser deposition. The influence of buffer thickness and substrate temperature on structural, optical, and electrical properties of AZO thin film are investigated. Increasing the thickness of buffer layer and substrate temperature can both promote the transformation of AZO from amorphous to crystalline structure, while they show(100)and(002) unique preferential orientations, respectively. After inserting Zr(50)Cu(50) layer between the glass substrate and AZO film, the sheet resistance and visible transmittance decrease, but the infrared transmittance increases. With substrate temperature increasing from 25℃ to 520℃, the sheet resistance of AZO(100 nm)/Zr(50)Cu(50)(4 nm) film first increases and then decreases, and the infrared transmittance is improved. The AZO(100 nm)/Zr(50)Cu(50)(4 nm) film deposited at a substrate temperature of 360℃ exhibits a low sheet resistance of 26.7 ?/, high transmittance of 82.1% in the visible light region, 81.6% in near-infrared region, and low surface roughness of 0.85 nm, which are useful properties for their potential applications in tandem solar cell and infrared technology.     

Cu50Ni50合金快速凝固的分子动力学模拟

采用分子动力学模拟的方法研究了Cu₅₀Ni₅₀合金在不同冷却速度下的凝固过程,利用均方位移、径向分布函数和结构可视化等方法分析其微观结构.并对凝固模型进行拉伸模拟,通过应力应变曲线和直观结构变化分析其性能.研究表明：冷却速度对Cu₅₀Ni₅₀合金凝固形成的结构有较大影响,随着冷却速度的升高,凝固形成的结构中晶体含量减少,在较低的冷却速度下,如冷却1×10¹²K/s时,Cu₅₀Ni₅₀合金凝固形成晶体结构;在较高的冷却速度下,如1×10¹⁴K/s时,Cu₅₀Ni₅₀合金凝固形成非晶体结构,且非晶Cu₅₀Ni₅₀合金的抗拉性能要优于晶体Cu₅₀Ni₅₀合金.     

Fe和Co元素在铁磁性形状记忆合金Mn50Ni25－xFe(Co)xGa25中的作用

为了进一步改善材料的性能和探索新的材料，将Mn₂NiGa合金中的Ni元素分别用Fe和Co替代，制备了Mn₅₀Ni_25-xFe(Co)_xGa₂₅系列合金. 研究了Fe和Co元素对Mn₂NiGa合金的结构、马氏体相变行为、磁性和机械性能等方面的影响. 关键词： 铁磁形状记忆合金 Heusler合金 50Ni_25-xFe(Co)_xGa₂₅')" href="#">Mn₅₀Ni_25-xFe(Co)_xGa₂₅     

Deformations of multiparameter quantum gl(N)

Multiparameter quantum gl(N) is not a rigid structure. This Letter defines an essential deformation as one that cannot be interpreted in terms of a similarity transformation, nor as a perturbation of the parameters. All the equivalence classes of first-order essential deformations are found, as well as a class of exact deformations. This work provides quantization of all the classical Lie bialgebra structures (constantr-matrices) found by Belavin and Drinfeld for sl(n). A special case, that requires the Hecke parameter to be a cubic root of unity, stands out.     

Enhanced orbital magnetism in Fe(50)Pt(50) nanoparticles

X-ray absorption and magnetic circular dichroism spectra at both the Fe and Pt L(3,2) edges were measured on wet-chemically synthesized monodisperse Fe(50)Pt(50) particles with a mean diameter of 6.3 nm before and after complete removal of the organic ligands and the oxide shell covering the particles by soft hydrogen plasma resulting in a pure metallic state. After thermal treatment of the metallic particles, the coercive field increased by a factor of 6, the orbital magnetic moment at the Fe site increased by 330% and is reduced at the Pt site by 30%, while the effective spin moments did not change. A decrease of the frequency of oscillations in the extended x-ray absorption fine structure at the Pt L(3,2) edges provides evidence for crystallographic changes towards the L1(0) phase.     

A Complete Analysis of Clarity (C50) Using I-SIMPA to Maintain Ideal Conditions in an Acoustic Chamber

In any closed environment considered, it can be seen that the acoustic parameters are inherently not constant over the entire area considered. In a closed environment, it is ideally preferred to maintain the acoustic parameters as constant so that there exists better quality of sound leading to better auditory perception with respect to the audience. Practically, some of the acoustic parameters like reverberation time and clarity do not strictly pertain to the pattern obtained theoretically. In this paper, simulations are carried out using I-SIMPA under different values of Sound Transmission Class (STC), source position, distribution and the chamber dimensions and provides an insight into the behaviour of these acoustic parameters and the appropriate values that have to be infused into the system to build the chamber. The acoustic environment is modelled keeping an actual closed room in mind and testing is done with respect to different values of surface absorption coefficients (practically indicated using Sound Transmission Class) and dimensions to determine ideal conditions.     

Interrelations between quantum groups and reflection equation (braided) algebras

We show that the differential complex _B over the braided matrix algebra BM _q (N) represents a covariant comodule with respect to the coaction of the Hopf algebra _A which is a differential extension of GL _q (N). On the other hand, the algebra _A is a covariant braided comodule with respect to the coaction of the braided Hopf algebra _B . Geometrical aspects of these results are discussed.     

GLq(N)-covariant braided differential bialgebras

We study the possibility of defining the (braided) comultiplication for the GL _q (N)-covariant differential complexes on some quantum spaces. We discover suchdifferential bialgebras (and Hopf algebras) on the bosonic and fermionic quantum hyperplanes (with additive coproduct) and on the braided matrix algebra BM _q (N) with both multiplicative and additive coproducts. The latter case is related (forN = 2) to theq-Minkowski space andq-Poincaré algebra.     

Structural and magnetic properties of Co50Ni50 powder mixtures

In the present work, morphological, structural, thermal and magnetic properties of nanocrystalline Co₅₀Ni₅₀ alloy prepared by high energy planetary ball milling have been studied by means of scanning electron microscopy, X-ray diffraction, and differential scanning calorimetry. The coercivity and the saturation magnetization of alloyed powders were measured at room temperature by a vibration sample magnetization. Morphological observations indicated a narrow distribution in the particle and homogeneous shape form with mean average particle size around 130 μm². The results show that an allotropic Co transformation hcp→fcc occurs within the three first hours of milling and contrary to what expected, the Rietveld refinement method reveals the formation of two fcc solid solutions (SS): fcc Co(Ni) and Ni(Co) beside a small amount of the undissolved Co hcp. Thermal measurement, as a function of milling time was carried out to confirm the existence of the hcp phase and to estimate its amount. Magnetic measurement indicated that the 48 h milled powders with a steady state particles size have the highest saturation (105.3 emu/g) and the lowest coercivity (34.5 Oe).