Er3+及Er3+/Yb3+掺杂ZrO2-Al2O3的制备及发光性质

采用共沉淀法制备了纳米晶ZrO₂-Al₂O₃∶Er³⁺发光粉体.所制备的粉体室温下具有Er3+离子特征荧光发射,主发射在绿光,其中位于547 nm、560 nm的绿光最强,并得出稀土离子与基质之间有能量传递.对不同煅烧温度下的样品研究表明:因不同温度下所制得的样品晶相不同.研究了纳米晶ZrO2-Al2O3∶Er3+及ZrO₂-Al₂O₃∶Er³⁺/Yb³⁺的上转换发光,并分析了上转换的跃迁机制.发现ZrO₂-Al₂O₃∶Er³⁺的绿光为双光子过程,而ZrO₂-Al₂O₃∶Er³⁺、Yb³⁺的上转换光谱中,红光和绿光也为双光子过程,而极弱的蓝光为三光子过程.讨论了Er³⁺的浓度猝灭现象.最适宜掺杂浓度的原子分数为2%（Er³⁺/Zr⁴⁺）.     

Nd掺杂对Bi4Ti3O12铁电薄膜的微结构和铁电性能的影响

利用溶胶-凝胶法在Pt/Ti/SiO₂/Si(100)衬底上制备了Nd掺杂Bi₄Ti₃O₁₂(Bi_4-xNd_xTi₃O₁₂, x=0.00,0.30,0.45,0.75,0.85,1.00,1.50)铁电薄膜样品.研究了Nd掺杂对Bi₄Ti₃O₁₂薄膜的微结构和铁电性能的影响.研究结果表明:Nd掺杂未改变Bi₄Ti₃O₁₂薄膜的基本晶体结构.在掺杂量x<0.45时,Nd³⁺只取代类钙钛矿层中的A位Bi³⁺.当x=0.45时,样品剩余极化强度达最大值,在270kV·cm^-1的电场下为32.7μC·cm^-2.掺杂量进一步增加时,结构无序度开始明显增大,Nd³⁺开始进入(Bi₂O₂)²⁺层,削弱其绝缘层和空间电荷库的作用,导致材料剩余极化逐渐下降.当掺杂量x达到1.50时,掺杂离子最终破坏(Bi₂O₂)²⁺层的结构,材料发生铁电-顺电相变.     

焙烧温度对SiO2负载的Co3O4纳米粒子表面氧缺陷浓度和CO氧化催化性能的影响

以传统的浸渍法,在不同焙烧温度下制备了用于CO氧化反应的Co₃O₄/SiO₂催化剂．通过激光拉曼光谱(Raman)、X射线光电子能谱(XPS)、X射线衍射(XRD)、程序升温还原(TPR)和X射线吸收精细结构谱(XAFS)表征了该系列催化剂的结构．在所有的催化剂中,XRD和Raman光谱都只检测到了Co₃O₄晶相的存在．与Co₃O₄体相相比,XPS结果表明在200 oC焙烧的(Co₃O₄(200)/SiO₂)催化剂中Co₃O₄表面上存在着过量的Co²⁺．与XPS的结果一致,TPR结果表明Co₃O₄(200)/SiO₂催化剂中Co₃O₄表面上存在氧缺陷, 并且XAFS结果也表明Co₃O₄(200)/SiO₂催化剂中Co₃O₄具有更多的Co²⁺．提高焙烧温度使得过量的Co²⁺进一步氧化为Co³⁺,同时降低了表面氧缺陷浓度,从而得到计量比的Co₃O₄4/SiO₂催化剂．在所有的负载催化剂中Co₃O₄(200)/SiO₂催化剂表现出了最好的CO氧化催化性能,表明过量Co²⁺和表面氧缺陷的存在能够促进Co₃O₄催化CO氧化反应的活性.     

Al掺杂的尖晶石型LiMn2O4的结构和电子性质

采用基于密度泛函理论的第一性原理方法, 在广义梯度近似(GGA)和GGA+U方法下对尖晶石型LiMn₂O₄及其Al掺杂 的尖晶石型LiAl_0.125Mn_1.875O₄晶体的结构和电子性质进行了计算. 结果表明: 采用GGA方法得到尖晶石型LiMn₂O₄是立方晶系结构, 其中的Mn离子为+3.5价, 无法解释它的Jahn-Teller 畸变. 给出的LiMn₂O₄能带结构特征也与实验结果不符. 而采用GGA+U方法得到在低温下的LiMn₂O₄和其掺杂 体系LiAl_0.125Mn_1.875O₄的晶体都是正交结构, 与实验一致. 也能明确地确定Mn的两种价态Mn³⁺/Mn⁴⁺的分布并且能够说明Mn³⁺O₆的z方向有明显的Jahn-Teller 畸变, 而Mn⁴⁺O₆则没有畸变. LiMn₂O₄的能带结构与实验比较也能够符合. 采用GGA+U方法对Al掺杂体系的LiAl_0.125Mn_1.875O₄的研究表明, 用Al替换一个Mn不会明显地改变晶体的电子性质, 但可以有效地消除Al³⁺O₆ 八面体的Jahn-Teller畸变, 从而改善正极材料LiMn₂O₄的性能, 这与电化学实验的观察结果相一致.     

Sr2CeO4电荷迁移发光的光谱结构规律研究

利用高温固相反应法分别合成了不同物相形成机理的Sr₂CeO₄，Sr ₂CeO₄∶Ca ²⁺和Sr₂CeO₄∶Ba²⁺样品，并对其光谱特性进行 了研究.结果发现，对于由SrO和CeO₂直接反应生成的Sr₂CeO₄(Ⅰ)，激发主峰位于256nm 左右；而对于SrCeO₃和SrO反应生成的Sr₂CeO₄(Ⅱ)，激发主峰位于279nm左右.在Sr₂CeO₄(Ⅰ)中掺入Ca²⁺，其激发光谱随着Ca²⁺离子浓度的增加逐渐接近于Sr₂CeO_{4(Ⅱ)的激发光谱.激发主峰带应属于CeO6八面体终端Ce⁴⁺—O^2-键的电荷迁移 带.对于激发光谱中340nm左右的弱激发峰，其峰值波长不受形成机理及Ca²⁺掺杂的影响，只是其强度 随着 激发主峰的红移而增加，它可能属于CeO6八面体平面上Ce⁴⁺—O2-键的电荷 迁移带.形成机理及Ca²⁺掺杂对发射光谱没有影响.Ca²⁺在Sr 2CeO 4(Ⅱ)与Ba²⁺在Sr2CeO4(Ⅰ)和(Ⅱ)中均难 于替代Sr²⁺的位置.}     

针状纳米MnxNi0.5-xZn0.5Fe2O4的共沉淀法制备及表征

通过在碱液中共沉淀Mn²⁺、Ni²⁺和Fe²⁺后制备了棒状的前躯体,前躯体于不同温度煅烧后制得了Mn_xNi_0:5-xZn_0:5Fe₂O₄棒状体. 利用X射线衍射仪和透射电镜对棒状体的物相、形貌及粒径进行了表征,并利用振动样品磁强计对磁性能进行研究. 结果表明长径比大于15的棒状,随着x值的增加,Mn_xNi_0:5-xZn_0:5Fe₂O₄样品的直径增加,长度下降,长径比变小,当x=0.5时其直径在50 nm左右而长径比减小到7～8. 随着x值的增加,样品的矫顽力先增加后减少,x值达到0.4时样品的矫顽力再次增加,当煅烧温度为600 oC,x=0.5时样品的矫顽力最大为134.3 Oe. 饱和磁化强度随着x值的增加先增加后减少,当煅烧温度为800 oC和x=0.2时达到最大为68.5 Oe.     

Gd2O3:Eu3+纳米晶的燃烧合成及光致发光性质

采用柠檬酸作燃烧剂用燃烧合成法制备了Gd₂O₃:Eu³⁺纳米晶.用X射线衍射仪(XRD)、高分辨透射电子显微镜(HRTEM)和荧光分光光度计等对Gd₂O₃:Eu³⁺纳米晶的结构、形貌和发光性能进行了分析.结果表明：不同柠檬酸与稀土离子配比(C/M)制备的样品经800℃ 退火1 h后，均得到了纯立方相的Gd₂O₃:Eu³⁺纳米晶，晶粒尺寸约为30 nm，尺寸分布较窄，其中以C/M=1.0时制备的纳米晶结晶性最好，发光强度最大.Gd₂O₃:Eu³⁺纳米晶主发射峰位置均在612 nm处 (⁵D₀→⁷F₂跃迁)，激发光谱中电荷迁移态发生红移，观察到Gd³⁺向Eu³⁺的有效能量传递.对柠檬酸与稀土离子配比(C/M)对结晶度、发光性质等的影响也进行了分析和讨论.     

La2Zr2O7:Eu3+纳米棒的合成、表征及其荧光性能

采用传统固相法和水热法成功地制备出棒状La₂Zr₂O₇:Eu³⁺荧光粉. 利用X射线粉末衍射仪、透射电镜和荧光光谱仪等分析了产物的结构、形貌和发光特性. 结果表明红色荧光粉La₂Zr₂O₇:Eu³⁺有良好的晶相,属于立方结构,空间点群为Fd3m; 其形貌主要为纳米棒, 平均直径约47 nm, 长度为50～700 nm. 并对纳米棒的生长机理进行了探讨. 在466 nm蓝光激发下,La₂Zr₂O₇:Eu³⁺荧光粉能发射出Eu³⁺的特征红色荧光,发射主峰位于616 nm处,归属于Eu³⁺的⁵DO_→⁷F2_{超灵敏电偶极跃迁.此外,在产物的发射光谱中能够观察到⁵D}1_→⁷FJ _{(J=0, 1, 2)跃迁和⁵D}1_→⁷FJ _{(J=1, 2, 4)跃迁的劈裂峰,这说明Eu³⁺处在低对称性的晶体场格位中.}     

Mn4+掺杂对BiFeO3陶瓷微观结构和电学性能的影响研究

利用传统的固相反应法制备了BiFe_1-xMn_xO₃ (x= 0-0.20)陶瓷样品, 研究了不同Mn⁴⁺掺杂量对BiFeO₃陶瓷密度、物相结构、显微形貌、 介电性能和铁电性能的影响.实验结果表明:所制备的BiFe_1-xMn_xO₃ 陶瓷样品的钙钛矿主相均已形成,具有良好的晶体结构, 且在掺杂量x=0.05附近开始出现结构相变.随着Mn⁴⁺添加量的增加, 体系的相结构有从菱方钙钛矿向斜方转变的趋势,且样品电容率大幅度增大, 而介电损耗也略有增加;在测试频率为10⁴ Hz条件下, BiFe_0.85Mn_0.15O₃ (ε_r=1065)的 ε_r是纯BiFeO₃ (ε_r=50.6)的22倍; 掺杂后样品的铁电极化性能均有不同程度的提高,可能是由于Mn⁴⁺稳定性优于 Fe³⁺,高价位Mn⁴⁺进行B位替代改性BiFeO₃陶瓷, 能减少Bi³⁺挥发,抑制Fe³⁺价态波动,从而降低氧空位浓度,减小样品的电导和漏电流.     

Er3+/Yb3+共掺Gd3Sc2Ga3O12晶体的上转换发光

研究了提拉法生长的Er³⁺/Yb³⁺:Gd₃Sc₂Ga₃O₁₂和Er³⁺:Gd₃Sc₂Ga₃O₁₂晶体在室温下320—1700nm范围的吸收光谱和500—750nm范围内的上转换荧光谱,同时对其上转换荧光的可能发生机制、途径以及上转换过程可能对Er^{3+相似文献}   

Fe3O4/β-CD的高压电学性质研究

 高压下的电学性质测量是获得材料物理性质的有效手段。利用集成在金刚石对顶砧上的薄膜微电路,测量了高压下Fe₃O₄/β-CD（β-糊精）的电导率,并分析了电导率随压力的变化关系。在0～39.9 GPa范围内,Fe₃O₄/β-CD的电导率随压力的增加而逐渐增大,并呈半导体的特征;而在17.0 GPa处其电导率发生突变,表明样品发生了高压相变。在卸压过程中,电导率随压力的变化呈线性关系,并且卸压后样品的电导率不能回到最初的状态,推测这是一个不可逆的高压结构相变。     

Exchange coupling behavior in bimagnetic CoFe2O4/CoFe2 nanocomposite

In this work we report a study of the magnetic behavior of ferrimagnetic oxide CoFe₂O₄ and ferrimagnetic oxide/ferromagnetic metal CoFe₂O₄/CoFe₂ nanocomposite. The latter compound is a good system to study hard ferrimagnet/soft ferromagnet exchange coupled. Two steps were followed to synthesize the bimagnetic CoFe₂O₄/CoFe₂ nanocomposite: (i) first, preparation of CoFe₂O₄ nanoparticles using a simple hydrothermal method, and (ii) second, reduction reaction of cobalt ferrite nanoparticles using activated charcoal in inert atmosphere and high temperature. The phase structures, particle sizes, morphology, and magnetic properties of CoFe₂O₄ nanoparticles were investigated by X-Ray diffraction (XRD), Mossbauer spectroscopy (MS), transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM) with applied field up to 3.0 kOe at room temperature and 50 K. The mean diameter of CoFe₂O₄ particles is about 16 nm. Mossbauer spectra revealed two sites for Fe³⁺. One site is related to Fe in an octahedral coordination and the other one to the Fe³⁺ in a tetrahedral coordination, as expected for a spinel crystal structure of CoFe₂O₄. TEM measurements of nanocomposite showed the formation of a thin shell of CoFe₂ on the cobalt ferrite and indicate that the nanoparticles increase to about 100 nm. The magnetization of the nanocomposite showed a hysteresis loop that is characteristic of exchange coupled systems. A maximum energy product (BH)_max of 1.22 MGOe was achieved at room temperature for CoFe₂O₄/CoFe₂ nanocomposites, which is about 115% higher than the value obtained for CoFe₂O₄ precursor. The exchange coupling interaction and the enhancement of product (BH)_max in nanocomposite CoFe₂O₄/CoFe₂ are discussed.     

Electronic structure studies of the spinel CoFe2O4 by X-ray photoelectron spectroscopy

The spinel CoFe₂O₄ has been synthesized by combustion reaction technique. X-ray photoelectron spectroscopy shows that samples are near-stoichiometric, and that the specimen surface both in the powder and bulk sample is most typically represented by the formula (Co_0.4Fe_0.6)[Co_0.6Fe_1.4]O₄, where cations in parentheses occupy tetrahedral sites and those within square brackets in octahedral sites. The results demonstrate that most of the iron ions are trivalent, but some Fe²⁺ may be present in the powder sample. The Co 2p_3/2 peak in powder sample composed three peaks with relative intensity of 45%, 40% and 15%, attributes to Co²⁺ in octahedral sites, tetrahedral sites and Co³⁺ in octahedral sites. The O 1s spectrum of the bulk sample is composed of two peaks: the main lattice peak at 529.90 eV, and a component at 531.53 eV, which is believed to be intrinsic to the sample surface. However, the vanishing of the O 1s shoulder peak of the powder specimen shows significant signs of decomposition.     

Cation distribution dependence of magnetic properties of sol-gel prepared MnFe2O4 spinel ferrite nanoparticles

MnFe₂O₄ nanoparticles have been synthesized with a sol-gel method. Both differential thermal and thermo-gravimetric analyses indicate that MnFe₂O₄ nanoparticles form at 400 °C. Samples treated at 450 and 500 °C exhibit superparamagnetism at room temperature as implied from vibrating sample magnetometry. Mössbauer results indicate that as Mn²⁺ ions enter into the octahedral sites, Fe³⁺ ions transfer from octahedral to tetrahedral sites. When the calcination temperature increases from 450 to 700 °C, the occupation ratio of Fe³⁺ ions at the octahedral sites decreases from 43% to 39%. Susceptibility measurements versus magnetic field are reported for various temperatures (from 450 to 700 °C) and interpreted within the Stoner-Wohlfarth model.     

Preparation and characterization of multi-functional CoFe2O4-ZnO nanocomposites

Multi-functional magnetic, photoluminescent and photocatalytic CoFe₂O₄-ZnO nanocomposites were successfully synthesized by a collosol method. The average diameter of the prepared CoFe₂O₄-ZnO nanocomposites was 30±5 nm, and a diffusion layer was formed to link CoFe₂O₄ and ZnO. The saturation magnetization of the CoFe₂O₄-ZnO nanocomposites was 8.99 emu/g. Generation of ZnO from Zn(OH)₂ collosol was nearly complete after thermal decomposition at about 380 °C. A photoluminescence emission peak was observed at 443 nm when excitated at 350 nm. Degradation of methyl orange is performed by CoFe₂O₄-ZnO nanocomposites under ultraviolet radiation, with a degradation rate of up to 93.9%.     

类花状ZnO-CoFe2 O4 复合纳米管束的制备及其电磁波吸收特性

在90 ℃水溶液中采用两步晶体生长法制备出类花状ZnO-CoFe₂O₄复合纳米管束.ZnO纳米管束的管壁厚度大约为60 nm,管的直径大约为350 nm,CoFe₂O₄纳米颗粒连续包覆在ZnO纳米管束的表面,CoFe₂O₄纳米颗粒尺寸小于40 nm, 壳层厚度随着CoFe₂O₄在ZnO-CoFe₂O_{4 关键词： 类花状 2}O₄')" href="#">ZnO-CoFe₂O₄ 纳米管束 微波吸收剂     

A facile synthesis of monodisperse CoFe2O4/SiO2 nanoparticles

Aminated-CoFe₂O₄/SiO₂ magnetic nanoparticles (NPs) were prepared from primary silica particles using modified StÖber method. By optimizing the preparation conditions, monodisperse CoFe₂O₄/SiO₂ NPs with high amino groups’ density were obtained, which is necessary for enzyme immobilization. TEM confirm that the sample is a core/shell structure. These aminated-CoFe₂O₄/SiO₂ NPs have narrow size distributions with a mean size of about 60 nm. Moreover, the aminated-CoFe₂O₄/SiO₂ NPs can be easily dispersed in aqueous medium. The experimental results also show that the NPs have superparamagnetism, indicating that the aminated-CoFe₂O₄/SiO₂ NPs can be used as an effective carrier for the enzyme immobilization.     

Structure and photoluminescence properties of Er3+-doped TiO2-SiO2 powders prepared by sol-gel method

Er 3+-doped TiO 2-SiO 2 powders are prepared by the sol-gel method,and they are characterized by high resolution transmission electron microscopy (HR-TEM),X-ray diffraction (XRD) spectra,and Raman spectra of the samples.It is shown that the TiO 2 nanocrystals are surrounded by an SiO 2 glass matrix.The photoluminescence (PL) spectra are recorded at room temperature.A strong green luminescence and less intense red emission are observed in the samples when they are excited at 325 nm.The intensity of the emission,which is related to the defect states,is strongest at the annealing temperature of 800 C.The PL intensity of Er 3+ ions increases with increasing Ti/Si ratio due to energy transfer between nano-TiO 2 particles and Er 3+ ions.     

Optical properties of (ZnO)0.5(P2O5)0.5 glasses doped with Gd2O3:Eu nanoparticles and Eu2O3

Binary (ZnO)_0.5(P₂O₅)_0.5 glasses doped with Eu₂O₃ and nanoparticles of Gd₂O₃:Eu were prepared by conventional melt-quench method and their luminescence properties were compared. Undoped (ZnO)_0.5(P₂O₅)_0.5 glass is characterized by a luminescent defect centre (similar to L-centre present in Na₂O-SiO₂ glasses) with emission around 324 nm and having an excited state lifetime of 18 ns. Such defect centres can transfer the energy to Eu³⁺ ions leading to improved Eu³⁺ luminescence from such glasses. Based on the decay curves corresponding to the ⁵D₀ level of Eu³⁺ ions in both Gd₂O₃:Eu nanoparticles incorporated as well as Eu₂O₃ incorporated glasses, a significant clustering of Eu³⁺ ions taking place with the latter sample is confirmed. From the lifetime studies of the excited state of L-centre emission from (ZnO)_0.5(P₂O₅)_0.5 glass doped with Gd₂O₃:Eu nanoparticles, it is established that there exists weak energy transfer from L-centres to Eu³⁺ ions. Poor energy transfer from the defect centres to Eu³⁺ ions in Gd₂O₃:Eu nanoparticles doped (ZnO)_0.5(P₂O₅)_0.5 glass has been attributed to effective shielding of Eu³⁺ ions from the luminescence centre by Gd-O-P type of linkages, leading to an increased distance between luminescent centre and Eu³⁺ ions.     

Emission features of Ho ion in Nb2O5, Ta2O5 and La2O3 mixed Li2O-ZrO2-SiO2 glasses

Li₂O-ZrO₂-SiO₂: Ho³⁺ glasses mixed with three interesting d-block elemental oxides, viz., Nb₂O₅, Ta₂O₅ and La₂O₃, were prepared. Optical absorption and photoluminescence spectra of these glasses have been recorded at room temperature. The luminescence spectra of Nb₂O₅ and Ta₂O₅ mixed Li₂O-ZrO₂-SiO₂ glasses (free of Ho³⁺ ions) have also exhibited broad emission band in the blue region. This band is attributed to radiative recombination of self-trapped excitons (STEs) localized on substitutionally positioned octahedral Ta⁵⁺ and Nb⁵⁺ ions in the glass network. The Judd-Ofelt theory was successfully applied to characterize Ho³⁺ spectra of all the three glasses. From this theory various radiative properties, like transition probability A, branching ratio β_r and the radiative lifetime τ_r, for ⁵S₂ emission levels in the spectra of these glasses have been evaluated. The radiative lifetime for ⁵S₂ level of Ho³⁺ ions has also been measured and quantum efficiencies were estimated. Among the three glasses studied the La₂O₃ mixed glass exhibited the highest quantum efficiency. The reasons for such higher value have been discussed based on the relationship between the structural modifications taking place around the Ho³⁺ ions.