Catalytic methanol decomposition to carbon monoxide and hydrogen over Pd/CeO2-ZrO2-La2O3 with different Ce/Zr molar ratios

The catalytic behaviors of Pd (1.4 wt%) catalysts supported on CeO₂-ZrO₂-La₂O₃ mixed oxides with different Ce/Zr molar ratios were investigated for methanol decomposition. Nitrogen adsorption-desorption (BET), X-ray photoelectron spectroscopy (XPS), H₂ temperature-programmed reduction (H₂-TPR), X-ray diffraction (XRD) and Pd dispersion analysis were used for their characterization. Pd/Ce_0.76Zr_0.18 La_0.06O_1.97 catalyst showed the highest BET surface area, best Pd dispersion capability and strongest metal-support interaction. Moreover, XPS showed that there was lattice defect oxygen or mobile oxygen. According to the result of O 1s measurements the lattice defect oxygen or mobile oxygen helped to maintain Pd in a partly oxidized state and increased the activity for methanol decomposition. The Pd/Ce_0.76Zr_0.18La_0.06O_1.97 catalyst exhibited the best activity. A 100% conversion of methanol was achieved at around 260 °C, which was about 20-40 °C lower than other catalysts     

铈和镧改性γ-Al2O3担载Pd催化剂的结构效应

分别以镧-铈、铈-镧顺序浸渍和镧铈共浸渍的方式在γ-Al2O3载体上引入助剂La2O3和CeO2，然后担载Pd制备了一系列催化剂.以甲醇分解为探针反应，采用XRD、EXAFS和XPS对催化剂的体相和表面结构进行表征，用BET法测定比表面积，并进行了吸附态CO的FTIR研究.结果表明,La2O3容易进入CeO2的晶格中，促进了CeO2在γ-Al2O3上的分散.但不同的La2O3、CeO2加入方式对活性组分Pd在改性载体上的分散度、优势暴露面及其与CeO2之间的相互作用产生不同的影响.关联甲醇分解性能测试结果说明,Pd在载体上的高度分散以及Pd和CeO2之间通过界面产生的强相互作用是催化剂具有高活性的关键.     

CexZr1-xO2/Co/C-N催化CO2加氢性能研究

将不同比例的铈锆前驱体负载到ZIF-67,氮气气氛焙烧制备CexZr1-xO2/Co/C-N催化剂,对催化剂进行了XRD,H2-TPR、XPS表征,并在固定床反应器评价其CO2加氢制甲醇性能。XRD结果表明,在铈中加入适量锆形成铈锆固溶体,铈锆固溶体与钴物种较强的相互作用力可以阻止表明金属Co的氧化。但过量加入的锆又会削弱这一作用力,部分金属Co被氧化为Co3O4。H2-TPR结果表明适量的锆的加入改善催化剂的还原性能,催化剂还原温度降低。XPS证实了25%Ce0.67Zr0.33O2/Co/C-N催化剂中含有更多的氧空穴及氮含量,氧空穴和碱性氮都有利于CO2的解离吸附。优化后的25%Ce0.67Zr0.33O2/Co/C-N 催化剂在225 oC,2 MPa,GHSV = 6 L/gcat/h反应条件下取得最高甲醇时空收率,为3.0 mmol/gcat/h。     

Influence of CeO2 and La2O3 on properties of palladium catalysts used for emission control of natural gas vehicles

Pd/YZ-Al2O3 (Y and Zr modified Al2O3, and hereafter, labelled as Al) catalysts with 4 wt% additive CeO2 and/or La2O3 were prepared and characterized by X-ray photoelectron spectroscopy (XPS), NO-temperature programmed desorption (NO-TPD), N2-adsorption/desorption (Brunauer-Emmet-Teller BET method), X-ray diffraction (XRD) and CO-chemisorption. Catalytic activities for CH4, CO and NO conversion were tested in a gas mixture simulated the emissions from natural gas vehicles (NGVs) operated under stoichiometric conditions. The results indicated that all catalysts exhibited excellent catalytic performances for CH4 and CO oxidation and the promoting effect of CeO2 or La2O3 was significant for NO conversion. XPS results showed that the electron density around Pd was increased by CeO2 and/or La2O3, the binding energy of Pd 3d decreased as the order: Pd/Al>Pd/Ce/Al>Pd/La/Al>Pd/CeLa/Al. The electron-rich Pd showed Rh-like catalytic properties which exhibited good activity for the reduction of NO. NO-TPD results showed that the addition of CeO2 and/or La2O3 increased NO adsorption on surface, and promoted the conversion of NO.     

钙改性的Pd/CeO2-ZrO2-Al2O3催化剂催化甲醇裂解反应

采用共沉淀法制备了未改性的和Ca掺杂的CeO2-ZrO2-Al2O3样品,进一步用浸渍法制备了Pd/CeO2-ZrO2-Al2O3(Pd/CZA)和Pd/CeO2-ZrO2-Al2O3-CaO (Pd/CZACa)催化剂.运用X射线衍射、N2吸附-脱附、储氧量测定、CO化学吸附、NH3程序升温脱附、CO2程序升温脱附、...     

MnOx/Al2O3/Ce0.45Zr0.45M0.10Oy （M = Mn, Y, La） catalysts used for ethanol catalytic combustion

MnOx/Al2O3/Ce0.45Zr0.45M0.10Oy (M = Mn,Y,La) catalysts were prepared by impregnation method and characterized by BET,TPR and XRD analyses.The catalytic activities toward ethanol combustion were investigated in a microreactor.The results demonstrated that the catalytic activity of MnOx/Al2O3/Ce0.50Zr0.50O2 monolithic catalyst could be improved by doping Mn,Y and La into Ce0.50Zr0.50O2.When doping Y into Ce0.50Zr0.50O2,the catalyst MnOx/Al2O3/Ce0.45Zr0.45Y0.10O1.95 showed the highest activity.The 100% conversion temperature of ethanol was 230 ℃.Furthermore,once the conversion of ethanol started,the complete conversion was quickly achieved.The doping of Mn,Y and La led to better activity for ethanol combustion and lower temperature reduction peaks in TPR profiles.The doping of Mn resulted in enhanced oxygen storage capacity (OSC),larger area of the reduction peaks,and excellent reactivity,and the doping of Y resulted in the lowest reduction temperature and the best activity.     

Pd-Cu/ZrO2催化CO2加氢制甲醇的性能

采用溶胶-凝胶法制备了n(Cu):n(Zr)=1:1、1:2、1:4和1:8的Cu/ZrO₂催化剂。 实验结果表明,当n(Cu):n(Zr)=1:4时,催化剂表现出较高的CO₂转化率(8.0%)和甲醇选择性(59.5%),为了增加CO₂的转化率,提高甲醇选择性,在n(Cu):n(Zr)=1:4的催化剂中添加质量分数1%的Pd,采用浸渍法制备了Pd-Cu/ZrO₂催化剂。 在250 ℃、2 MPa、12000 mL/(g·h)和V(H₂):V(CO₂)=3:1的反应条件下,CO₂转化率和CH₃OH收率相比Cu/ZrO₂催化剂(n(Cu):n(Zr)=1:4)分别提高了40.0%和80.9%。 通过X射线衍射仪(XRD)、傅里叶变换红外光谱仪(FT-IR)、N₂吸附-脱附(BET)、X射线光电子能谱仪(XPS)和程序升温还原化学吸附仪(H₂-TPR)等仪器表征证明Pd的添加提高了催化剂的分散性和比表面积。 催化剂中Pd和Cu之间强相互作用,使Cu2p轨道结合能向低处偏移,还原温度的降低,说明Pd-Cu/ZrO₂催化剂还原能力增强,使得CO₂加氢活性提高。     

助剂对Ni/SiO_2催化剂微观结构及二硝基甲苯催化加氢性能的影响

采用等体积浸渍法制备了负载型Ni/SiO2催化剂,研究了Ce、Zr、La、Co和Fe助剂对催化剂微观结构及其催化二硝基甲苯(DNT,C6H3CH3(NO2)2)加氢制备甲苯二胺(TDA,C6H3CH3(NH2)2)性能的影响。通过XRD,BET,H2-TPD、H2-TPR和XPS技术对催化剂进行了表征。结果表明,助剂的引入促进了Ni物种在载体表面的分散,减小了Ni晶粒的尺寸,使得NiO晶粒更易还原。添加La、Fe和Zr助剂增加了有效的Ni活性中心数,有利于催化活性的提高,其中,添加La助剂制备的催化剂催化性能最优,DNT转化率和TDA选择性分别为98.1%和99.1%。但Co和Ce助剂的加入降低了化学氢吸附量,使得有效的Ni活性中心数降低,降低了催化剂的催化活性。     

助剂对Ni/SiO2催化剂微观结构及二硝基甲苯催化加氢性能的影响

采用等体积浸渍法制备了负载型Ni/SiO₂催化剂,研究了Ce、Zr、La、Co和Fe助剂对催化剂微观结构及其催化二硝基甲苯（DNT,C₆H₃CH₃（NO₂）₂）加氢制备甲苯二胺（TDA,C₆H₃CH₃（NH₂）₂）性能的影响。通过XRD,BET,H₂-TPD、H₂-TPR和XPS技术对催化剂进行了表征。结果表明,助剂的引入促进了Ni物种在载体表面的分散,减小了Ni晶粒的尺寸,使得NiO晶粒更易还原。添加La、Fe和Zr助剂增加了有效的Ni活性中心数,有利于催化活性的提高,其中,添加La助剂制备的催化剂催化性能最优,DNT转化率和TDA选择性分别为98.1%和99.1%。但Co和Ce助剂的加入降低了化学氢吸附量,使得有效的Ni活性中心数降低,降低了催化剂的催化活性。     

Ce0.35Zr0.55La0.10O1.95对低贵金属Pt-Rh型三效催化剂性能的影响

采用共沉淀技术制备了Ce0.35Zr0.55La0.10O1.95固溶体, 其织构和结构性能以及氧化还原性能分别采用BET、XRD和程序升温(TP)技术进行了表征. 制备了低贵金属Pt-Rh型三效催化剂, 考察了Ce0.35Zr0.55La0.10O1.95对催化剂性能的影响. XRD和BET的结果表明, 经600 ℃焙烧5 h后, Ce0.35Zr0.55La0.10O1.95具有与Ce0.50Zr0.50O2相似的立方结构和高的比表面积；经1000 ℃焙烧5 h后, 仍能保持稳定的立方结构和47.25 m2•g−1的比表面积, 表现出优越的织构性能和高的热稳定性. H2-TPR和O2-TPO的结果表明, Ce0.35Zr0.55La0.10O1.95具有比Ce0.50Zr0.50O2更好的氧化还原性能. 和含Ce0.50Zr0.50O2的催化剂相比, 含Ce0.35Zr0.55La0.10O1.95的催化剂具有较宽的工作窗口, 优越的低温起燃性能, 较强的水气变换能力；催化剂经1000 ℃高温水热老化5 h后, 仍具有良好的催化活性, 表现出了优异的抗老化性能.     

甲醇在CeO2担载Pd催化剂上分解机理的研究

采用原位红外(in-situFTIR)技术对甲醇在CeO₂和Pd/CeO₂催化剂上的吸附和反应进行了研究,提出一个新的甲醇分解反应机理模型.甲醇在CeO₂上容易吸附并结合其晶格氧生成甲酸盐物种,而甲醇分解的产物氢被Pd活化后,溢流到CeO₂上促进了甲酸盐物种的分解.Cl^-的存在加强了Pd/CeO₂催化剂与氢的相互作用,Pd和CeO₂通过对氢和氧物种的作用对甲醇分解反应的过程表现出协同效应.     

超声波振动在Ce-Zr-La/Al2O3及负载型Pd三效催化剂制备中的应用

制备了CeO2-ZrO2-La2O3/Al2O3材料, 在制备过程中使用超声波振动对材料进行处理, 并以此材料为载体制备了单Pd三效催化剂. 对所制备的载体进行了织构性能分析(BET)和X射线衍射(XRD)表征. 对催化剂进行了NO程序升温脱附(NO-TPD)及H2程序升温还原(H2-TPR)表征, 并对催化剂进行了活性测试. BET结果表明, 900 ℃焙烧后, 超声波振动处理的载体比表面积为130 m2·g-1, 而没有进行处理的载体比表面积为117 m2·g-1. 超声波处理的CeO2-ZrO2-La2O3/Al2O3材料介孔直径为11.4 nm, 相对较大, 载体更加稳定. XRD测试结果表明, 超声波处理的载体在1150 ℃焙烧5 h后仍然只有Ce0.5Zr0.5O2一个单一物相, 而未经过超声波处理的载体此时出现相分离, 体相中有θ-Al2O3出现. 以超声波处理材料为载体的Pd催化剂新鲜和老化后NO-TPD测试结果变化很小. H2-TPR测试中, 超声波振动处理的材料制备的催化剂中活性组分和载体的还原峰温较未超声处理材料制备的催化剂稍高, 而峰面积远大于未超声处理材料制备的催化剂. 活性测试结果说明, 由超声波振动处理过的载体制备的三效催化剂对汽车尾气中的三种污染物的起燃温度更低, 有更好的活性以及温度特性.     

过渡金属掺杂亚铁锌双金属氰化物催化合成生物柴油的研究

研究了掺杂过渡金属盐(La、Ce、Zr、Mn)对亚铁锌双金属氰化物(DMC)固体酸催化剂合成生物柴油的影响,并采用XRD、FT-IR、ICP、BET等方法对其进行结构和性能表征。结果表明,1%的镧、铈、锆、锰金属盐对催化剂的活性都有提高,其中,添加1%镧的DMC催化剂活性最高,在醇油摩尔比16∶1,反应温度160 ℃,催化剂加入量2%条件下,反应7 h,脂肪酸甲酯收率达到99.3%。过渡金属盐引入对催化剂的组成没有影响,但使得催化剂更加分散,颗粒粒径更小,比表面积变大,有利于催化剂和反应物的接触,从而提高了催化剂活性。     

超声波振动在Ce-Zr-La／Al2O3及负载型Pd三效催化剂制备中的应用

制备了CeO2-ZrO2-La2O3/Al2O3材料,在制备过程中使用超声波振动对材料进行处理,并以此材料为载体制备了单Pd三效催化剂.对所制备的载体进行了织构性能分析(BET)和X射线衍射(XRD)表征.对催化剂进行了NO程序升温脱附(NO-TPD)及H2程序升温还原(H2-TPR)表征,并对催化剂进行了活性测试.BET结果表明,900 ℃焙烧后,超声波振动处理的载体比表面积为130 m2·g-1,而没有进行处理的载体比表面积为117 m2·g-1.超声波处理的CeO2-ZrO2-La2O3/Al2O3材料介孔直径为11.4 nm,相对较大,载体更加稳定.XRD测试结果表明,超声波处理的载体在1150 ℃焙烧5 h后仍然只有Ce0.5Zr0.5O2一个单一物相,而未经过超声波处理的载体此时出现相分离,体相中有θ-Al2O3出现.以超声波处理材料为载体的Pd催化剂新鲜和老化后NO-TPD测试结果变化很小.H2-TPR测试中,超声波振动处理的材料制备的催化剂中活性组分和载体的还原峰温较未超声处理材料制备的催化剂稍高,而峰面积远大于未超声处理材料制备的催化剂.活性测试结果说明,由超声波振动处理过的载体制备的三效催化剂对汽车尾气中的三种污染物的起燃温度更低,有更好的活性以及温度特性.     

Catalytic Combustion of Methane over MnOx／ZrO2-Al2O3 Catalysts

MnOx/Al2O3 and MnOx/ZrO2-Al2O3 catalysts were prepared by incipient wetness impregnation of Mn(CH3COO)2 on the corresponding supports, followed by the characterization using X-ray diffraction (XRD). temperature programmed reduction (TPR) and BET surface area techniques. The result shows the BET surface area of ZrO2-Al2O3 is lower than that of Al2O3 due to the loading of ZrO2.However tile resulted MnOx/ZrO2-Al2O3 catalyst exhibits higher activity for methane combustion than MnOx/Al2O3, because the addition of ZrO2 onto Al2O3 is beneficial for the dispersion of Mn species and the improvement of the lattice oxygen activity in MnOx. subsequently the activation of methane during combustion. The optimum loading of Zr in MnOx/ZrO2-Al2O3 is in the range of 5%-10% correlated with the calcination temperatures of catalyst supports.     

Ce0.5+xZr0.4-xLa0.1O2-Al2O3催化剂催化燃烧柴油车碳烟

采用共沉淀法制备了系列Ce_0.5+xZr_0.4-xLa_0.1O₂-Al₂O₃催化剂, 其中0≤x≤0.4且Ce_0.5+xZr_0.4-xLa_0.1O₂与Al₂O₃的质量比为1:1. 考察了该系列催化剂对柴油车排放碳烟的催化燃烧性能, 并用低温N2吸附-脱附、X射线衍射(XRD)、X射线光电子能谱(XPS)、氢气程序升温还原(H₂-TPR)和氧气程序升温脱附(O₂-TPD)等手段对催化剂进行了表征. 研究结果表明该系列催化剂均形成了具有立方萤石结构的固溶体. 当x=0.2时, Ce³⁺离子在催化剂表面有一定的富集, 此时催化剂具有最大的β氧脱附峰和最好的表面还原性能, 同时具有良好的催化碳烟氧化活性, 碳烟在该催化剂的起燃温度为360 °C, 具有较好的应用前景.     

柠檬酸盐凝胶法制备纳米CuO-ZnO-ZrO_2的工艺分析及CO_2加氢制甲醇的性能

采用柠檬酸盐凝胶法制备出纳米CuO-ZnO-ZrO_2(CZZ)催化剂,应用XPS、BET、XRD、H_2-TPR、H_2-TPD、CO_2-TPD和TG-DTA等检测手段对催化剂及前驱体的结构进行表征。研究了湿凝胶干燥时间和柠檬酸用量对催化剂结构的影响,并与燃烧法制得的催化剂进行对比,考察了不同催化剂CO_2加氢制甲醇的性能。研究表明,延长湿凝胶干燥时间可有效防止催化剂焙烧时发生喷溅,有利于催化剂中各组分的分散,提高催化剂对H_2和CO_2的吸附能力;112℃干燥48h制得的催化剂(CZZ-48h)BET比表面积为43.5m~2/g,高于燃烧法;柠檬酸用量等于化学计量比时催化剂的性能最佳,在240℃、2.6MPa、空速为3600h-1、H_2/CO_2(体积比)为3的条件下甲醇时空收率达109.4g/(kg·h);柠檬酸过量会影响催化剂组分的分散度,并造成分解残留覆盖催化剂表面活性位而不利于CO_2加氢反应。     

Doping of Ceria-Zirconia Solid Solution with Rare-earth Elements

The increasingly restrictive regulations on car exhaust emissions will necessitate the development of a new generation of three way catalysts (TWC) with better performance1. Ceria (CeO2) is the main component of the current TWC: its key role is to compensate the fluctuations in the exhaust stream composition, therefore, allowing to expand the air/fuel(A/F) operating window of catalytic converters2. This property is related to its oxygen storage capacity (OSC), associated to the redox couple Ce4+/Ce3+. However, CeO2 alone is easy to sinter to lost OSC at high temperature3.Ceria-zirconia (CexZr1-xO2) solid solutions by incorporation of Zr4+ in the CeO2 lattice have enhanced OSC and greater thermal stability, which are becoming the key materials for the new generation of TWC4. OSC of ceria-zirconia solid solutions can be further improved by the addition of M3+ dopants5. Besides Ce, other rare-earth elements such as Pr and Tb can vary their oxidation state. Pr and Tb are particularly suitable for making solid solutions with cerium because the known structure of PrO2 and TbO2 is of the cubic fluorite type, and the ionic radii of Pr4+ and Tb4+ are close to that of Ce4+6.In this paper, Ce0.6Zr0.3M0.1O2 (M=Y, La, Pr, Tb) were prepared by co-precipitation technique and characterized by a series of methods. Meanwhile, palladium-only TWCs were prepared by slurry coating and their catalytic activity was evaluated under the condition of simulated exhaust in the lab.XRD and FT-Raman spectra results show Ce0.6Zr0.3M0.1O2 have cubic fluorite structure which keep unchanging at high temperature. The different dopant ion radii brought different effect on the cell parameter of Ce0.6Zr0.3M0.1O2. The X-ray photoelectron spectroscopy (XPS) results show that the binding energy of Ce3d, Zr3d and O1s for Ce0.6Zr0.3M0.1O2 rose compared with that for Ce0.6Zr0.4O2, indicating dopant elements changed chemistry environment of solid solutions which was available to improve redox performance From TPR results, doping La can not change redox performance of solid solution, but doping Y decreased reduction temperature. Doping Pr and Tb notably improved redox performance of solid solutions due to appearance of low-temperature reduction peak in TPR profile which come from mobility of bulk oxygen.Compared with Pd/Ce0.6Zr0.4O2, doping Y and La unchanged A/F characteristic of TWCs, but doping Pr and Tb widen A/ F operating window and make HC, CO and NO have higher conversion.The light-off temperature of Pd/Ce0.6Zr0.3La0.1O2 was corresponded to that of Pd/Ce0.6Zr0.4O2.However, the light-off temperatures of Pd/Ce0.6Zr0.3M0.1O2 (M=Y, Pr, Tb) were lower than that of Pd/Ce0.6Zr0.4O2, which kept much lower after high temperature treatments. Among Pd/Ce0.6Zr0.3M0.1O2 (M=Y, La, Pr, Tb), Pd/Ce0.6Zr0.3Tb0.1O2 showed wider A/F operating window,higher conversion, lower light-off temperature and better high-temperature resistance     

焙烧温度对柴油车氧化催化剂Pt-Pd-（x）ZrO2/Ce0.3Zr0.7O2-Al2O3性能的影响

制备了氧化铝、铈锆固溶体复合氧化物负载铂、钯的双金属催化剂Pt-Pd/ Ce0.3Zr0.7O2-Al2O3,并添加3% ZrO2助剂改性,用于柴油车尾气中CO、HC和NO的催化氧化,其中贵金属负载量仅为0.68 wt%。考察了制备过程中焙烧温度对催化剂性能的影响。催化剂活性评价结果表明,与未添加ZrO2的催化剂比较。添加ZrO2明显提高了催化剂的低温氧化活性,而且焙烧温度对催化剂的氧化性能有较大影响。焙烧温度为800 ?C时,CO和C3H6的起燃温度最低,分别为168、189 ?C,焙烧温度为700 ?C时,NO转化为NO2的转化率最高,最大转化率为36%,具有较好的热稳定性。通过XRD、N2吸附-脱附、CO化学吸附、XPS、H2-TPR等表征手段考察了催化剂物理化学性质随焙烧温度的变化情况,并分析了与催化剂活性之间的关系,得到贵金属分散度、表面化学吸附氧含量、催化剂的还原性质对氧化性能有重要影响,发挥协同作用。进而可以通过优化焙烧温度提升柴油车氧化催化剂性能,对提高工业应用柴油车尾气后处理系统的净化效率有重要意义。     

Low-temperature CO oxidation over CuO-CeO2/SiO2 catalysts：Effect of CeO2 content and carrier porosity

The effects of CeO2 contents and silica carder porosity with their pore diameters ranging from 5.2 nm to 12.5 nm of CuO-CeO2/SiO2 catalysts in CO oxidation were investigated. The catalysts were characterized by N2 adsorption/desorption at low temperature, X-ray diffraction (XRD), temperature-programmed reduction by H2 (H2-TPR), oxygen temperature programmed desorption (O2-TPD) and X-ray photoelectron spectroscopy (XPS). The results suggested that, the ceria content and the porosity of SiO2 carder possessed great impacts on the structures and catalytic performances of CuO-CeO2/SiO2 catalysts. When appropriate content of CeO2(Ce content ≤8 wt%) was added, the catalytic activity was greatly enhanced. In the catalyst supported on silica carrier with larger pore diameter, higher dispersion of CuO was observed, better agglomeration-resistant capacity was displayed and more lattice oxygen could be found, thus the CuO-CeO2 supported on Si-1 showed higher catalytic activity for low-temperature CO oxidation.