对一种低温易烧结的Yb:Y_2-2xLa_2xO₃激光透明陶瓷的光谱性能进行了初步研究，Yb:Y_2-2xLa_2xO₃激光透明陶瓷具有宽的吸收带和大的吸收截面，在最强的吸收峰977nm处吸收截面达4.0×10^-20cm²；其荧光发射寿命为1.1ms，发射截面在1033nm处为1.0×10^-20cm²，在1077nm处为0.7×10^-20cm².Yb:Y_2-2xLa_2xO₃陶瓷的各项光学性能指标接近或达到单晶的指标. 关键词： 氧化镧钇 激光陶瓷 低温烧结 光谱性能     

Cr3+:Al2O3透明多晶陶瓷光谱特性分析

对透光性良好的Cr³⁺:Al₂O₃透明多晶陶瓷的光谱性能 进行了研究，其吸收光谱中吸收峰与单晶红宝石相一致，按吸收光谱和Tanabe-Sugano能级 图，算出其晶场强度参数D_q及Racah参数B分别为1792cm^-1， 689cm ^-1，D_q/B=2.6，陶瓷中Cr³⁺离子所处格位的晶体场强 比单晶弱一些，但Cr³⁺:Al₂O₃透明陶瓷仍属于强场晶 体材料；当Cr³⁺掺杂浓度到达0.8wt%时，陶瓷的发射谱仍保持较好的R线发射 ；随Cr³⁺掺杂浓度的增大，激发峰位发生“红移”.在Cr³⁺:Al₂O₃透明多晶陶瓷的荧光谱上，发现一个波长为670nm的发射峰，经激发 谱确认为Cr³⁺的发射峰. 关键词： 氧化铝 透明陶瓷 离子格位 光谱性质     

Yb:Y2O3透明陶瓷的光学性能研究

介绍了一种基于纳米粉末真空烧结技术的新型固体激光材料——Yb：Y₂O₃多晶陶瓷的制备工艺、物理化学特性、能级结构和光谱特性，并与Yb：YAG单晶进行了对比.采用紧凑型有源镜激光器(CAMIL)的抽运方式，验证了Yb：Y₂O₃透明陶瓷的激光输出性能.在35W的最大抽运功率下，得到波长1078 nm，功率10.5 W 的连续激光输出，斜率效率达到37.5%.实验中还观察到激光输出波长随抽运功率增加而红移以及随输出耦合镜变化而漂移的现象.Yb：Y₂O₃多晶陶瓷是一种理想的激光材料，不仅具有与Yb：YAG单晶同样优秀的物理化学性能和光谱特性，而且其热导率和发射带宽约为Yb：YAG单晶的两倍，非常适合于高亮度激光器和超短脉冲激光器领域的发展应用. 关键词： 2O₃陶瓷')" href="#">Yb:Y₂O₃陶瓷 陶瓷激光器 透明陶瓷     

Cr4+在Al2O3多晶体中的光谱性能研究

采用传统无压烧结工艺制备Cr:Al₂O₃透明多晶陶瓷.测定了其退火前后的吸收光谱和荧光光谱，发现在Al₂O₃六配位的八面体结构中，Cr⁴⁺的荧光发射也处在1100—1600nm波段的红外区间，荧光发射峰位于1223nm附近，类似Cr⁴⁺在四面体中的发光行为.同时由于氧化铝晶格常数较小，晶体场强较强，使Cr⁴⁺:Al₂O_{3< 关键词： 4+')" href="#">Cr⁴⁺ 2}O₃透明陶瓷')" href="#">Cr:Al₂O₃透明陶瓷 光谱性质 八面体     

Er,Yb：(LaLu)2O3透明陶瓷制备及上转换发光性能

采用柠檬酸燃烧法制备Er,Yb：（LaLu）₂O₃陶瓷粉体,用X射线衍射对其进行了物相鉴定,研究表明1 000℃时已经得到纯相的（LaLu）₂O₃。采用冷等静压-真空烧结法制备了Er,Yb：（LaLu）₂O₃和Er：（LaLu）₂O₃陶瓷,对陶瓷的结构和光谱性能进行了详细的研究,研究发现掺杂5% Yb³⁺和10% La³⁺样品的上转换发光强度与未掺Yb³⁺、La³⁺样品相比明显增大,根据上转换光谱显示较强发射峰位于564 nm和661 nm处,对应Er³⁺的⁴S_3/2（²H_11/2）→⁴I_15/2能级跃迁和⁴F_9/2→⁴I_15/2能级跃迁,并讨论了Er³⁺-Yb³⁺的能量传递过程及其上转换发光机制。     

红色荧光粉La2Mo2O9:Eu3+,W6+的制备及发光性能

采用高温固相法合成出La₂Mo₂O₉:Eu³⁺,W⁶⁺系列红色荧光粉,其结构为立方晶系的β- La₂Mo₂O₉。在395 nm光激发下,样品La_1.40Mo₂O₉:0.60Eu³⁺发射出很强的红光,最强发射峰位于616 nm处。适量地掺杂W⁶⁺离子可以提高样品的激发和发射强度,在395 nm光激发下,La_1.40Mo_1.84O₉:0.60Eu³⁺,0.16W⁶⁺荧光粉的Eu³⁺的⁵D₀→⁷F₂跃迁发射强度最大,是样品La_1.40Mo₂O₉:0.60Eu³⁺的1.23倍。最后,将La_1.40Eu_0.60Mo_1.84O₉:0.16W⁶⁺荧光粉与~395 nm发射的InGaN芯片一起制作成红光发光二极管(LED),该LED发射出很强的红光。     

尺寸效应对Er3+掺杂纳米Y2O3的发光特性的影响

采用燃烧法制备了不同尺寸的Er³⁺掺杂Y₂O₃粉体材料,研究了尺寸效应对Er³⁺掺杂纳米Y₂O₃材料发光特性的影响.光声光谱显示,对于不同晶粒尺寸的样品,Er³⁺离子光声峰位置几乎保持不变.这表明小尺寸效应对稀土离子能级位置影响很小.对488nm激光激发下的发射谱的分析发现,随着样品颗粒尺寸的减小,4S_3/2能级和关键词： 3+离子')" href="#">Er³⁺离子 纳米 发光 能量传递     

Nd3+掺杂的氧化镧钇透明激光陶瓷的光谱性能研究

采用传统无压烧结工艺制备了Nd³⁺掺杂的Y_2-2xLa_2xO₃(x=0.08)透明陶瓷并对其光谱性能进行了研究. 结果表明：Nd³⁺:Y_1.84La_0.16O₃透明陶瓷在780—850 nm的波长范围内有较宽的吸收带. 当Nd³⁺掺杂量为1.5at%时，在820 nm和激光二极管抽运的808 nm处的吸收截面分别为σ_abs(820 nm)=1.81×10^-20 cm²，σ_abs(808 nm)=1.54×10^-20 cm². 最强的发射峰位于1078 nm处，并具有荧光寿命长、发射带宽宽、量子效率高等特点. 加入La₂O₃后，基质的光谱品质参数X_Nd由1.6减小到0.46，因此和⁴F_3/2—⁴I_11/2跃迁相对应的荧光分支比β_J,11/2增大为56.82%. Nd³⁺:Y_1.84La_0.16O₃透明陶瓷的这些性质有利于高效率的激光输出和超短锁模激光脉冲的实现. 关键词： 氧化镧钇透明陶瓷 光谱性能 3+')" href="#">Nd³⁺     

La2O3对Yb:Y2O3透明陶瓷光谱性能的影响

研究了La2O3对Yb:Y2O3透明陶瓷光谱性能的影响,添加适量La2O3以后,Yb:Y2O3透明陶瓷的吸收峰和发射峰的位置不变,但由于La3+的离子半径大于Y3+的离子半径,在Y2O3中引入La3+离子后,导致Y2O3晶格常数变大,晶场强度变弱,同时降低了Y2O3晶体的有序度,致使发射峰强度有所下降,发射截面变小.过量的La2O3(x=0.16)造成Yb3+激活离子发射强度明显下降;其荧光寿命在添加La2O3后总体增大45%-60%.     

Ce3+掺杂SiO2-Al2O3-Gd2O3玻璃的闪烁性能

通常, Ce离子掺杂的低密度玻璃有较高的发光效率, 而高密度的Ce离子掺杂玻璃其发光效率很低. 为了解释这一现象, 采用高温熔融法获得了SiO₂-Al₂O₃-Gd₂O₃三元系统的玻璃形成区, 并在还原气氛下制备了Ce³⁺掺杂SiO₂-Al₂O₃-Gd₂O₃以及SiO₂-Al₂O₃-Gd₂O₃-Ln₂O₃ (Ln=Y, La, Lu)闪烁玻璃, 研究了其光谱和闪烁性能. 测试结果显示: 随着Gd₂O₃含量增加, 玻璃紫外截止波长发生红移, 荧光强度降低, 衰减时间缩短; 加入Lu₂O₃, La₂O₃, Y₂O₃后, 紫外截止波长发生红移, 荧光强度降低, 衰减时间变短; 当Gd₂O₃超过10% mol时, X射线荧光积分光产额从相当于锗酸铋 晶体的61%降低到13%. 荧光强度降低、衰减时间缩短的原因是随着玻璃的紫外截止波长红移玻璃的能带宽度变窄, 使得Ce³⁺离子的d电子轨道开始接近玻璃的导带, Ce³⁺离子受辐射后跃迁到d电子轨道的电子会通过导带与玻璃中的空穴复合, 产生电荷迁移猝灭效应.     

Spectral and laser properties of Yb and Ho co-doped（YLa）2O3 transparent ceramic

Highly transparent Yb,Ho doped(YLa)2O3 ceramic was fabricated by conventional ceramic processing with nanopowders.The absorption and emission spectra of the ceramic was investigated.The energy transfer mechanism between Yb3+ and Ho3+ was also discussed.The strong emission band around 2 μm indicated that the Yb-Ho:(Y 0.90 La 0.10)2O3 transparent ceramic is a promising gain medium for the generation of 2 μm laser emissions.The laser operation of Yb-Ho co-doped(YLa)2O3 ceramic at 2.1 μm is first reported.     

Y2O3-Eu2O3-SnO2三元系固相线下相关系及其发光性质研究

采用固态反应法及改良固态反应法合成了一系列Y₂O₃-Eu₂O₃-SnO₂体系中的试样，利用X射线粉末衍射法测定了Y₂O₃-Eu₂O₃-SnO₂三元系固相线下的相关系.结果表明，Y₂O₃-Eu₂O₃二元系 关键词： 2O₃-Eu₂O₃-SnO₂三元系')" href="#">Y₂O₃-Eu₂O₃-SnO₂三元系 烧绿石型结构 激发光谱 发射光谱     

Investigation of up-conversion luminescence properties of RE/Yb co-doped Y2O3 transparent ceramic (RE=Er, Ho, Pr, and Tm)

RE/Yb co-doped Y₂O₃ transparent ceramics (RE=Er, Ho, Pr, Tm) were fabricated and characterized from the point of up-conversion luminescence. All the samples exhibit high transparence not only in near-infrared band (NIR) band but also in visible region, which ensures the output of the up-conversion luminescence. Under 980 nm excitation, green and red emissions were observed in Er, Yb:Y₂O₃ transparent ceramic, while green emission was detected in Ho, Yb and Pr, Yb co-doped Y₂O₃ transparent ceramics. In Tm, Yb co-doped Y₂O₃ ceramic, very intense blue up-conversion luminescence was detected. The dependence of up-conversion emission intensity on the pumping power was measured for each RE/Yb co-doped Y₂O₃ transparent ceramic, and the up-conversion mechanism was discussed in detail. Meanwhile, the energy transfer efficiency was calculated.     

Comparative spectroscopic investigation of Yb3x Y3(1 ? x )Al5O12 (x = 3, 5, 10 and 15%) transparent ceramics

Transparent Yb_3x Y_{3(1 ? x} )Al₅O₁₂ (x = 3, 5, 10 and 15%) ceramics were fabricated by solid-state reaction and vacuum sintering method with a mixture of commercial Al₂O₃, Y₂O₃ and Yb₂O₃ powders. Ethanol and 0.5 wt % tetraethoxysilane were doped. Transparent fully dense samples with grain sizes of several micrometers were obtained by sintered at 1750 K. The absorption spectra, emission spectra and fluorescence life time of these transparent Yb_3x Y_{3(1 ? x} )Al₅O₁₂ ceramics at room temperature have been measured and calculated. The air annealed effects of Yb_3x Y_{3(1 ? x} )Al₅O₁₂ ceramics have been compared with un-annealed Yb:YAG transparent ceramics which shows the difference of the Yb³⁺ ions between annealed and unannealed Yb:YAG ceramics is less than 1%.     

Spectral properties of Ce3+ doped yttrium lanthanum oxide transparent ceramics

Ce3+-doped yttrium lanthanum oxide (Y0.9La0.1)2O3 transparent ceramics is fabricated with nanopowders and sintered in H2 atmosphere. The spectral properties of Ce:(Y0.9La0.1)2O3 transparent ceramics are investigated. There appear two characteristic absorption peaks of Ce3+ ions at 230 nm and 400 nm, separately. It is found that Ce3+ ions can efficiently produce emission at 384 nm from (Y0.9La0.1)2O3 transparent ceramic host, while the emission is completely quenched in Re2O3 (Re=Y, Lu, La) host materials.     

Ga2O3组分对Tm3+掺杂GeO2-Ga2O3-Li2O-BaO-La2O3玻璃的光谱性能影响

制备了Tm³⁺(8.0mol%)掺杂(77-x)GeO₂-xGa₂O₃-8Li₂O-10BaO-5La₂O₃(x=4,8,12,16)系列玻璃.系统地研究了Ga₂O₃从4mol%变化到16mol%时,玻璃的光谱性质与热学性质的变化规律.差热分析表明,随着Ga₂O₃含量的增加,锗酸盐玻璃的热稳定性增加.运用Judd-Ofelt(J_O)理论计算得到了Tm³⁺在不同Ga₂O₃含量的GeO₂-Ga₂O₃-Li₂O-BaO-La₂O₃玻璃中的J-O强度参数(Ω₂,Ω₄,Ω₆)及Tm³⁺各激发能级的自发跃迁概率、荧光分支比以及辐射寿命等光谱参量.在808nm激光二极管的激发下,测试并分析了Ga₂O₃对Tm³⁺荧光光谱特性的影响.随着Ga₂O₃从4mol%增加到16mol%,Tm³⁺在1.8μm处的荧光强度呈现先减弱后增强的特性.当Ga₂O₃含量大约在12mol%时,Tm³⁺在1.8μm处的荧光强度最弱,受激发射截面达到最小.还初步讨论了Ga₂O₃对玻璃结构与光谱参数的影响规律. 关键词： 3+掺杂锗酸盐玻璃')" href="#">Tm³⁺掺杂锗酸盐玻璃 光谱性能 Judd-Ofelt参数 热稳定性     

Dielectric properties and temperature stability of BaTiO3 co-doped La2O3 and Tm2O3

The influence of La₂O₃ and Tm₂O₃ co-doping on the dielectric properties and the temperature stability of BaTiO₃ was investigated. BaTiO₃ ceramics were prepared with the compositional formula of (Ba_1−xLa_x)(Ti_1-x/4−yTm_y)O₃. La₂O₃ and Tm₂O₃ co-doping in BaTiO₃ mainly had effects on an increase in the dielectric constant and the temperature stability, respectively. The increase of La₂O₃ concentration and the decrease of Tm₂O₃ concentration in BaTiO₃ resulted in a decrease of lattice parameter and tetragonality because La³⁺ ion substituting for Ba site is smaller than Ba²⁺ ion and Tm³⁺ ion substituting for Ti site is larger than Ti⁴⁺ ion. With the increase of La₂O₃ and the decrease of Tm₂O₃, the dielectric constant of BaTiO₃ was enhanced in spite of the reduction of tetragonality. P-E hysteresis measurements revealed that this phenomenon was based on the improvement of remanent polarization with the increase of La₂O₃ concentration. The introduction of excess Tm₂O₃ in BaTiO₃ suppressed the grain growth and BaTiO₃ ceramics showed higher temperature stability due to the stable tetragonal structure and the small grain size with the increase of Tm₂O₃ concentration.