Si基Bi3.25La0.75Ti3O12铁电薄膜的制备与特性研究

采用Sol-Gel工艺低温制备了Si基Bi_3.25La_0.75Ti₃O₁₂铁电薄膜.研究了退火温度对薄膜微观结构、介电特性与铁电性能的影响.500℃退火处理的Bi_3.25La_0.75Ti₃O₁₂薄膜未能充分晶化，晶粒细小且有非晶团聚，介电与铁电性能均较差.高于550℃退火处理的Bi_3.25La_{0.75 关键词： 铁电薄膜 3.25}La_0.75Ti₃O₁₂')" href="#">Bi_3.25La_0.75Ti₃O₁₂ Sol-Gel工艺     

掺铒Si/Al2O3多层结构中结晶形态对1.54 μm发光的影响

利用脉冲激光沉积的方法制备掺铒 Si/Al₂O₃多层结构薄膜,获得了由纳米结构的Si作为感光剂增强的Er³⁺在1.54 μm高效发光.利用拉曼散射、高分辨透射电镜和光致发光测量研究了在不同退火温度下（600—1000 ℃）纳米结构Si层的结晶形态变化,及对Er³⁺在1.54 μm的发光的影响特征.研究发现最佳发光是在退火温度600—700 ℃.在这个条件下纳米Si的尺寸和密度,Si和Er的作用距离以及Er^{3+ 关键词： 铒 纳米硅 能量转移 氧化铝}     

磁控共溅射法制备的Zn2GeO4多晶薄膜结构及其光致发光研究

用射频磁控共溅射方法在不同温度的单晶硅基片上生长薄膜,然后在800℃真空环境下对薄膜进行退火处理,成功获得了结晶状态良好的Zn₂GeO₄多晶薄膜.利用X射线衍射(XRD),X射线光电子能谱(XPS)和原子力显微镜(AFM)对薄膜进行了结构、成分和形貌分析,研究了基片温度对三者的影响. 结果显示,当基片温度升高到400℃以上时,薄膜中的Zn₂GeO₄晶粒在(220)方向上显示出了明显的择优取向. 当基片温度在500—600℃范围内,有利于GeO₂结晶相的形成. XPS显示薄膜中存在着Zn₂GeO₄,GeO₂,GeO,ZnO四种化合态. 同时,随着基片温度的升高,晶粒尺寸增大且薄膜表面趋于平整. 薄膜的光致发光在绿光带存在中心波长为530和550nm两个峰,应该归因于主体材料Zn₂GeO₄中两个不同的Ge²⁺的发光中心. 关键词： 射频磁控溅射 2GeO₄')" href="#">Zn₂GeO₄ 荧光体     

共溅射和离子注入制备的SiO2(Eu)薄膜中Eu3+到Eu2+的转变

采用共溅射方法和Eu离子注入热生长的SiO₂方法得到SiO₂(Eu)薄膜,Eu离子的浓度为4%和0.5%.对样品X射线吸收近边结构(XANES)的研究和分析表明,在高温氮气中发生了Eu³⁺向Eu²⁺的转变.SiO₂(Eu)薄膜高温氮气退火下蓝光的发射证明了这一结论 关键词： 2(Eu)薄膜')" href="#">SiO₂(Eu)薄膜 XANES     

退火气压对Bi3.25La0.75Ti3O12铁电薄膜的微观结构和铁电性能的影响

采用sol-gel法在Pt/TiO₂/SiO₂/p-Si(100)衬底上制备了Bi_3.25La_0.75Ti₃O₁₂(BLT)铁电薄膜,研究了在750 ℃时不同退火气压(p_{O2:10^-4—3 atm)对薄膜微观结构和电学性能的影响.XRD和拉曼光谱结果表明在10^-4和3 atm氧气压下退火 关键词： 3.25}La_0.75Ti₃O₁₂')" href="#">Bi_3.25La_0.75Ti₃O₁₂ 铁电性能 sol-gel法 正交化度     

Microstructure and photoluminescence of Er-doped SiOx films synthesized by ion beam assisted deposition

Er-doped SiO_x films were synthesized at 500℃ by ion beam assisted deposition technique and annealed at 800 and 1100℃ for 2h in the air atmosphere. The analysis by using energy dispersive x-ray spectroscopy showed that the ratio of Si to O decreased from 3 in the as-deposited films to about 1 in the annealed films. The investigation by using transmission electron microscopy and x-ray diffraction indicated that annealing induces a microstructure change from amorphous to crystalline. The grain sizes in the films were about 10 and 40nm when annealed at 800 and 1100℃, respectively. The films annealed at temperatures of 800 and 1100℃ exhibited a sharp photoluminescence (PL) at 1.533μm from the Er centres when pumped by 980nm laser. The influence of microstructure and grain size on the PL from Er-doped SiO_x films has been studied and discussed.     

Physical and electrical characteristics of a high-k Yb2O3 gate dielectric

High-k ytterbium oxide (Yb₂O₃) gate dielectrics were deposited on Si substrate by reactive sputtering. The structural features of these films after postdeposition annealing treatment were studied by X-ray diffraction and X-ray photoelectron spectroscopy. It is found that the Yb₂O₃ gate dielectrics annealed at 700 °C exhibit a larger capacitance value, a lower frequency dispersion and a smaller hysteresis voltage in C-V curves compared with other annealing temperatures. They also show negligible charge trapping under high constant voltage stress. This phenomenon is mainly attributed to the decrease in the amorphous silica thickness.     

Annealing effects on the optical and structural properties of Al2O3/SiO2 films as UV antireflection coatings on 4H-SiC substrates

Al₂O₃/SiO₂ films have been prepared by electron-beam evaporation as ultraviolet (UV) antireflection coatings on 4H-SiC substrates and annealed at different temperatures. The films were characterized by reflection spectra, ellipsometer system, atomic force microscopy (AFM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), respectively. As the annealing temperature increased, the minimum reflectance of the films moved to the shorter wavelength for the variation of refractive indices and the reduction of film thicknesses. The surface grains appeared to get larger in size and the root mean square (RMS) roughness of the annealed films increased with the annealing temperature but was less than that of the as-deposited. The Al₂O₃/SiO₂ films maintained amorphous in microstructure with the increase of the temperature. Meanwhile, the transition and diffusion in film component were found in XPS measurement. These results provided the important references for Al₂O₃/SiO₂ films annealed at reasonable temperatures and prepared as fine antireflection coatings on 4H-SiC-based UV optoelectronic devices.     

Er3+掺杂SiO2复合的Al2O3粉末结构及光致发光特性

采用溶胶-凝胶(sol-gel)工艺制备0.1 mol% Er³⁺掺杂Al₂O₃体系和SiO₂-Al₂O₃复合体系粉末. 实验结果表明：5 mol%的SiO₂复合加入Al₂O₃抑制γ→θ和θ→α相转变. 掺0.1 mol%Er³⁺:Al₂O₃体系粉末，900℃烧结，在1.47—1.63μm波段内光致发光(PL)谱为中心波长1.53 μm、半高宽56 nm的单一宽峰，1000—1200℃烧结，劈裂为多峰PL谱. 掺0.1 mol%Er³⁺:SiO₂-Al₂O₃复合体系粉末，在高达1200℃烧结，仍保持中心波长1.53 μm的单一宽峰PL谱，由于—OH更完全的脱除，PL强度较900℃烧结Al₂O₃体系，SiO₂-Al₂O₃复合体系均提高1个数量级. 关键词： 2-Al₂O₃复合体系')" href="#">SiO₂-Al₂O₃复合体系 掺铒 溶胶-凝胶工艺 光致发光     

La掺杂对Bi4Ti3O12薄膜铁电性能的影响

利用Sol-Gel法在Pt/Ti/SiO₂/Si衬底上制备出Bi₄Ti₃O₁₂和Bi_3.25La_0.75Ti₃O₁₂薄膜，研究了La掺杂对Bi₄Ti₃O₁₂薄膜的晶体结构、铁电性能和疲劳特性的影响，发现La掺杂没有改变Bi₄Ti₃O₁₂薄膜的基本晶体结构，并且提高了Bi₄Ti₃O₁₂铁电薄膜的剩余极化值和抗疲劳性能，对La掺杂改善Bi₄Ti₃O₁₂铁电薄膜性能的机理进行了讨论. 关键词： 铁电性能 4Ti₃O₁₂薄膜')" href="#">Bi₄Ti₃O₁₂薄膜 3.25La_0.75Ti₃O₁₂薄膜')" href="#">Bi_3.25La_0.75Ti₃O₁₂薄膜 sol-gel法 La掺杂     

制备工艺对Zn1-xMgxO薄膜结构及光学性能的影响

采用脉冲激光沉积（PLD）方法在单晶Si（100）衬底上沿c轴方向生长单晶Zn_1-xMg_xO薄膜,通过X射线衍射（XRD）、原子力显微镜（AFM）、扫描电镜（SEM）和荧光光谱（PL）研究了膜厚、Mg含量、退火温度及氧气氛等制备工艺对Zn_1-xMg_xO薄膜的结构、形貌和光学性质的影响.实验结果表明,Mg含量x≤0.15时, Zn_{关键词： 1-x}Mg_xO薄膜')" href="#">Zn_1-xMg_xO薄膜 制备工艺 结构 光学性质     

Anodization of aluminium thin films on pSi and annihilation of strong luminescence from Al2O3

Photoluminescence (PL) of Al₂O₃ films obtained by anodization of thermally evaporated and annealed thin Al films on p⁺⁺Si in 0.3 M oxalic acid has been investigated. Thermal annealing at 200–950 °C under the dry nitrogen atmosphere was used for deactivation of luminescence centres. Luminescence from as grown films was broad and located at 425 nm. This luminescence reached to highest level after annealing at 600 °C. Maximum 10 min was required for full optical activation and prolonged annealing up to 4 h did not change the luminescence intensity. Because of deep levels, absorption band edge of as grown films was shifted to the lower energy which is 3.25 eV. Annealing above 800 °C reduced the PL intensity and this observation was correlated with the blue shift of band edge as the defects annealed out. Disappearing PL intensity and blue shift of band edge absorption after annealing at 950 °C was mainly attributed to the oxygen-related defects and partly to impurities that may be originated from oxalic acid. AFM results did not show any hexagonally ordered holes but uniformly distributed nanosized Al₂O₃ clusters that were clearly seen. XRD measurements on as grown Al₂O₃ showed only [1 1 0] direction of α phase. Debye–Scherer calculation for this line indicates that cluster size is 35.7 nm. XRD and AFM pictures suggest that nanocrystalline Al₂O₃ are embedded in amorphous Al₂O₃.     

The effect of Si surface nitridation on the interfacial structure and electrical properties of (La2O3)0.5(SiO2)0.5 high-k gate dielectric films

Thermal stability, interfacial structures and electrical properties of amorphous (La₂O₃)_0.5(SiO₂)_0.5 (LSO) films deposited by using pulsed laser deposition (PLD) on Si (1 0 0) and NH₃ nitrided Si (1 0 0) substrates were comparatively investigated. The LSO films keep the amorphous state up to a high annealing temperature of 900 °C. HRTEM observations and XPS analyses showed that the surface nitridation of silicon wafer using NH₃ can result in the formation of the passivation layer, which effectively suppresses the excessive growth of the interfacial layer between LSO film and silicon wafer after high-temperature annealing process. The Pt/LSO/nitrided Si capacitors annealed at high temperature exhibit smaller CET and EOT, a less flatband voltage shift, a negligible hysteresis loop, a smaller equivalent dielectric charge density, and a much lower gate leakage current density as compared with that of the Pt/LSO/Si capacitors without Si surface nitridation.     

溶胶-凝胶法Er2O3薄膜的结构和光学特性

针对稀土Er掺杂Si光源中Er离子掺杂浓度低的问题,采用溶胶-凝胶（Sol-gel）法在Si(100)和SiO2/Si(100)基片上旋涂法制备Er₂O₃光学薄膜,Er离子浓度与以前掺杂方法相比提高了2个数量级.900 ℃热处理获得单一立方结构的Er₂O₃薄膜材料.光致发光（PL）特性研究表明在654 nm波长的激光泵浦下,Er₂O₃薄膜材料获得了1.535 μm的发光峰,并具有较小的温度猝灭1/5.在SiO₂/Si(100)基体上制备的Er2O3薄膜材料的光致发光强度比Si(100)基体上制备的薄膜提高2-3倍.研究结果表明具有强光致发光特性的Er₂O₃薄膜是一种有前景的硅基光源和放大器材料.     

Influence of deposition conditions on the optical properties of erbium-doped yttrium oxide films grown by aerosol-UV assisted MOCVD

Erbium-doped Y₂O₃ films were prepared by aerosol-UV assisted metal-organic chemical vapour deposition (MOCVD) at 410 °C. The effects of humidity of carrier gas and UV-assistance on their structure and optical properties were investigated on the as-deposited and thermal annealed films using infrared spectroscopy, X-ray diffraction and transmission electron microscopy. It was found that the as-deposited Er:Y₂O₃ films crystallise in the Y₂O₃ cubic structure and present a very low organic contamination when the deposition takes place under high air humidity and, even better, with UV-assistance. After annealing, two different structural phases are observed corresponding to the cubic and the monoclinic structures of Y₂O₃. The Er³⁺ luminescence analysed in the visible and IR regions, shows the classical green transitions. The best optical properties were obtained with as-deposited and annealed Er:Y₂O₃ films grown under high air humidity with UV-assistance. Under such deposition conditions, ⁴I_13/2 lifetimes was found to be 3.07 and 6.1 ms for films annealed at 800 and 1000 °C, respectively, and up-conversion phenomena were underlined. This indicates that the deposition conditions, in particular air humidity, play an important role in the luminescent properties even after annealing.     

SrBi2Ta2O9/Bi4Ti3O12复合铁电薄膜的制备与特性研究

采用溶胶凝胶工艺在p-Si衬底上制备了SrBi₂Ta₂O₉/Bi₄Ti₃O₁₂复合铁电薄膜. 研究了SrBi₂Ta₂O₉/Bi₄Ti₃O₁₂复合薄膜的微观结构与生长行为、铁电性能和疲劳特性. 研究表明: Si衬底Bi₄Ti< 关键词： 2Ta₂O₉')" href="#">SrBi₂Ta₂O₉ 4Ti₃O₁₂')" href="#">Bi₄Ti₃O₁₂ 复合铁电薄膜 溶胶凝胶工艺     

Ti1－xCrxO2±δ体系的相关系、晶体结构和磁性能研究

采用溶胶凝胶法制备了Ti_1-xCr_xO_2±δ体系系列样品.利用扫描电子显微镜(SEM)，X射线光电子能谱(XPS)，粉末X射线衍射分析(XRD)方法研究了Ti_1-xCr_xO_2±δ系列样品的颗粒尺寸、形貌、组分化学态、相关系和固溶区范围；并利用超导量子干涉磁强计对样品的磁性能进行了研究.采用Rietveld结构精修的方法研究了Cr的不同掺杂量对TiO₂晶体结构的影响，研究表明，1000℃烧结的样品的固溶区范围是x=0—0.03，为金红石单相；随着Cr掺杂量的增加，金红石相晶胞参数规律性地减小；当x>0.03，为金红石相和CrO₂相两相共存.综合XRD和磁性测量结果，500℃烧结的样品的固溶区范围是x=0—0.02，为锐钛矿单相；随着Cr掺杂量的增加，锐钛矿相晶胞参数规律性地减小；当x≥0.04，为锐钛矿相和绿铬矿相(Cr₂O₃)两相共存.XPS实验结果表明，500℃和1000℃退火的样品中Cr都是以Cr⁺³和Cr⁺⁶两种化学态存在，1000℃烧结的样品中可能有更多的Cr³⁺转化为Cr⁶⁺.根据M-H和M-T曲线的测试结果发现，本文500℃烧结的Ti_1-xCr_xO_2±δ体系样品当x=0—0.02时，为室温铁磁性.当x≥0.04时，由铁磁相和顺磁相所组成，在低温下有较强的铁磁性；室温下主要是顺磁相，铁磁相只占据很小的体积分数. 关键词： 1-xCr_xO_2±δ体系')" href="#">Ti_1-xCr_xO_2±δ体系 相关系 固溶区 磁性能     

Amorphous Er2O3 films for antireflection coatings

This paper reports that stoichiometric, amorphous, and uniform Er2O3 films are deposited on Si(001) substrates by a radio frequency magnetron sputtering technique. Ellipsometry measurements show that the refractive index of the Er2O3 films is very close to that of a single layer antireflection coating for a solar cell with an air surrounding medium during its working wavelength. For the 90-nm-thick film, the reflectance has a minimum lower than 3% at the wavelength of 600 nm and the weighted average reflectances (400-1000 nm) is 11.6%. The obtained characteristics indicate that Er2O3 films could be a promising candidate for antireflection coatings in solar cells.     

Highly efficient photoluminescence of Er2SiO5 films grown by reactive magnetron sputtering method

E₂SiO₅ thin films were fabricated on Si substrate by reactive magnetron sputtering method with subsequent annealing treatment. The morphology properties of as-deposited films have been studied by scanning electron microscope. The fraction of erbium is estimated to be 23.5 at% based on Rutherford backscattering measurement in as-deposited Er-Si-O film. X-ray diffraction measurement revealed that Er₂SiO₅ crystalline structure was formed as sample treated at 1100 °C for 1 h in O₂ atmosphere. Through proper thermal treatment, the 1.53 μm Er³⁺-related emission intensity can be enhanced by a factor of 50 with respect to the sample annealed at 800 °C. Analysis of pump-power dependence of Er³⁺ PL intensity indicated that the upconversion phenomenon could be neglected even under a high photon flux of 10²¹(photons/cm²/sec). Temperature-dependent photoluminescence (PL) of Er₂SiO₅ was studied and showed a weak thermal quenching factor of 2. Highly efficienct photoluminescence of Er₂SiO₅ films has been demonstrated with Er³⁺ concentration of 10²²/cm³, and it opens a promising way towards future Si-based light source for Si photonics.     

退火氧压对YBa2Cu3O7-x薄膜中的激光感生热电电压效应的影响

测量了在不同氧压下退火生长的YBa₂Cu₃O_7-x(YBCO)薄膜中的激光感生热电电压(LITV)信号,发现随退火氧压的增大可使LITV信号的峰值有2—4倍的增强,并且变化趋势与薄膜热电势的各向异性随氧含量的变化规律相同.波长在473—808nm范围内的连续激光辐照,在5000Pa的氧压下退火生长的YBCO薄膜中探测到的LITV信号最大;而紫外脉冲激光辐照时,LITV信号的最大值出现在退火氧压为10⁵Pa 关键词： 2Cu₃O_7-x薄膜')" href="#">YBa₂Cu₃O_7-x薄膜 激光感生热电电压 各向异性的Seebeck系数 氧含量