乙醛酸化学镀铜的电化学研究

以乙醛酸作还原剂,Na2EDTA.2H2O为络合剂,亚铁氰化钾和2,2'-联吡啶为添加剂组成化学镀铜液体系,应用线性扫描伏安法研究分析了络合剂、添加剂对该镀铜体系电化学性能的影响.结果表明,络合剂Na2EDTA对乙醛酸的氧化和铜的还原有阻碍作用.亚铁氰化钾和过量(20 mg/L)的2,2'-联吡啶对乙醛酸的氧化起较明显的抑制作用.     

2,2′-联吡啶和亚铁氰化钾对乙醛酸化学镀铜的影响

以乙醛酸作还原剂、Na2EDTA为络合剂、2,2′-联吡啶和亚铁氰化钾作为添加剂组成化学镀铜体系,研究了两种添加剂对化学镀铜速率、镀层表面形貌、组成和结构的影响.结果表明:添加适量的2,2′-联吡啶和亚铁氰化钾,不仅提高了镀液的稳定性,而且使沉积速率增加1倍.这两种添加剂的同时使用,使镀层颜色变亮,形貌发生变化.所得镀层是多晶铜,没有发现夹杂Cu2O.     

2,2''''-联吡啶和亚铁氰化钾对乙醛酸化学镀铜的影响

以乙醛酸作还原剂、Na2EDTA为络合剂、2,2'-联吡啶和亚铁氰化钾作为添加剂组成化学镀铜体系,研究了两种添加剂对化学镀铜速率、镀层表面形貌、组成和结构的影响.结果表明:添加适量的2,2'-联吡啶和亚铁氰化钾,不仅提高了镀液的稳定性,而且使沉积速率增加1倍.这两种添加剂的同时使用,使镀层颜色变亮,形貌发生变化.所得镀层是多晶铜,没有发现夹杂Cu20.     

2,2′-联吡啶在化学镀铜中的作用研究

研究了以次磷酸钠作还原剂的化学镀铜体系,添加剂2,2′-联吡啶对化学镀铜沉积速率、次磷酸钠阳极氧化和铜离子阴极还原、以及镀层形貌、结构和组分存在状态的影响.结果表明,2,2′-联吡啶对化学沉积起阻化作用.电化学线性伏安扫描实验显示,镀液中加入2,2′-联吡啶,次磷酸钠的氧化峰电势有所负移,但峰电流减小;铜离子的还原峰电势负移,但峰电流逐渐增大.扫描电子显微镜(SEM)、能量色散谱(EDS)、X射线衍射(XRD)及X射线光电子能谱(XPS)等实验分别表明,添加剂使镀层致密和光亮、镍含量降低;镀层为Cu-Ni合金,呈面心立方结构,无明显晶面择优取向现象;镀层中铜和镍以金属态存在,磷的质量含量小于0.05%.     

Zn~(2 )-HEDP-CO_3~(2-)体系镀锌机理的研究(Ⅰ)——放电混合配体络离子的组成和第二配体CO_3~(2-)的作用

本文采用化学分析、红外光谱和电导滴定等方法研究了镀锌液中络离子的组成,得出镀液中存在的是[Zn(HL)(CO_3)_2]~(6-)型混合配体络离子。此外,还研究了第二配体CO_3~2-对镀液电化学性能的影响。结果表明,CO_3~(2-)对于镀液的稳定、锌阳极的溶解以及镀液的阴极极化、分散能力和深镀能力的改善都起了重要作用,是镀液中不可缺少的主要络合剂之一。利用从镀液中分离出的固体络合物进行电镀,效果和镀液类似,从而推断镀液中放电的络离子即镀液中主要存在的络离子[Zn(HL)(CO_3)_2]~(6-)。     

添加剂对化学沉积速率的影响

基于化学镀Ni-W-P和Ni-P体系中,添加剂LaCl3、乳酸、Fe2(SO4)3、硫脲和2,2’-联吡啶的浓度对沉积速率的影响表现出较为一致的变化规律,即随添加剂浓度的增加,出现最大沉积速率的实验事实,建立了一种吸附模型并导出添加剂加速化学沉积的公式.根据该公式和实验结果进行曲线拟合,得到相当吻合的结果.由拟合结果可得到一些参数值,如吸附平衡常数等.添加剂在基体上的吸附平衡常数(K1)大于已吸附了还原剂的表面上的吸附平衡常数(K2). K1值大表明添加剂在基体表面吸附能力更强. LaCl3、硫脲和2,2’-联吡啶的K1、K2值远大于乳酸、Fe2(SO4)3的K1、K2值,这表明LaCl3、硫脲和2,2’-联吡啶的吸附能力远强于乳酸、Fe2(SO4)3的, 因此,LaCl3、硫脲和2,2’-联吡啶所引起的沉积速率峰值的浓度远小于乳酸、Fe2(SO4)3的.     

化学沉积镍-铁-磷合金和它的伏安行为(英文)

在以次亚磷酸钠为还原剂 ,硼酸为缓冲剂和柠檬酸钠为络合剂的碱性介质中 ,研究了镍_铁_磷合金化学沉积条件 (pH值 ,温度及 [Fe2 + ]/([Ni2 + ]+[Fe2 + ])物质的量比 )对沉积速率和镀层组成的影响 ;并由此建立镀液稳定的最佳沉积工艺 .实验表明 ,镀液中硫酸亚铁对沉积镍_铁_磷合金有阻碍作用 (降低了化学沉积速率 ) ,造成镀层中铁含量不高 (小于 2 0 % ) ,使用循环伏安技术研究了镍_铁_磷合金的电沉积机理 .结果发现铁对次亚磷酸钠的氧化不起催化作用 ,提高镀液温度和pH值有增加沉积速率之效     

Fe-Ni-S软磁薄膜的电沉积

酸性镀液中以硼酸为缓冲剂、柠檬酸三钠为配合剂,在紫铜箔上电沉积得到非晶Fe-Ni-S合金薄膜。 采用扫描电子显微镜和能谱分析技术(EDS)研究了镀液组成和沉积条件对镀层表面形貌和组成的影响。 结果表明,在镀液中加入2 g/L C7H5O3NS（糖精）和0.4 g/L 1,4-丁炔二醇可获得表面平整无裂缝和较小内应力的合金镀层;电流密度和镀液pH值对镀层组成影响较小,但施镀温度对镀层组成影响较大。 获得了理想的镀液组成和沉积条件,所得Fe73Ni9.5S17.5薄膜的X射线衍射表明其为非晶结构,在室温下具有较高的饱和磁化强度(Ms约为876.25 kA/m)和较低的矫顽力(Hc约为4.96 kA/m),具有良好的软磁性能。 循环伏安曲线和阴极极化曲线均表明,镀液中CS(NH2)2会促进Fe-Ni-S共沉积。     

5,5′-二甲基乙内酰脲体系电沉积金(英文)

开发了以5,5′-二甲基乙内酰脲(DMH)为配位剂的无氰电镀金工艺。利用扫描电镜(SEM)和线性扫描伏安曲线对电镀时间和添加剂(由丁炔二醇、糖精和十二烷基硫酸钠组成)对镀金层表面、断面形貌和镀液性能的影响进行了测试,结果表明随着电镀时间的延长镀金层表面形貌几乎没有发生变化,光亮剂的加入增大了阴极极化同时使镀金层结晶变得细致均匀,在由HAuCl4,DMH,K3PO4和KH2PO4组成的基础镀液中金的沉积速度可达0.3μm.min-1,镀液中添加剂的加入没有影响金的沉积速度。利用X射线衍射技术(XRD)和X射线光电子能谱技术(XPS)对镀金层性能进行了测试,结果表明镀金层沿着(111)晶面择优生长并且由纯金组成。利用循化伏安曲线和旋转圆盘电极对Au(Ⅲ)在镀液中的电化学还原机制进行了研究,结果表明当研究电极为玻碳电极(GCE),镀液温度为45℃时,镀液中金的电沉积过程是受扩散控制的不可逆的过程。同时利用循环伏安曲线对镀金液的稳定性进行了分析。     

含空穴传输基团三联吡啶(2,2′:6′,2″-terpyridine)衍生物铕配合物的合成及发光性能研究

以2,2′∶6′,2″-三联吡啶(L1)为基础,通过引入不同的空穴传输基团合成了4′-咔唑基-2,2′∶6′,2″-三联吡啶(L2),4′-二苯基胺基-2,2′∶6′,2″-三联吡啶(L3),4′-二(4-叔丁基苯基)胺基-2,2′∶6′,2″-三联吡啶(L4),4′-(N-苯基-1-萘基)胺基-2,2′∶6′,2″-三联吡啶(L5),4′-(N-苯基-2-萘基)胺基-2,2′∶6′,2″-三联吡啶(L6)5个N,N,N-三齿中性配体,然后以三氟乙酰噻吩丙酮(HTTA)作为第一配体合成了6种铕配合物。在369~373 nm激发条件下,配合物都表现出铕离子5D0-7FJ(J=0,1,2,3,4)的特征发射。引入不同的空穴传输基团后,在铕离子的周围形成了"光吸收天线"(light-harvesting antenna),不仅扩大了配合物吸收光能的范围、增强了配合物的吸收强度,而且提高了配合物的光致发光性能。其中含有咔唑基团的配合物具有最强的发光强度和最长的激发态寿命。     

基于柔性1，4-苯二硫乙酸和刚性的2，2′-联吡啶配体构筑的钴配合物的合成、晶体结构及电化学性质

水热法合成了2个基于柔性的1,4-苯二硫乙酸(H2L)和刚性的2,2′-联吡啶(2,2′-bipy)配体的Co(Ⅱ)配合物:{[CoL(2,2′-bipy)(H2O)].0.40H2O}n(1)和[CoL(2,2′-bipy)(H2O)2]n(2),并通过元素分析,红外光谱,热重和X-射线单晶衍射实验对其结构进行了表征。分析表明,两个配合物都是通过氢键连接一维链形成的二维层面结构。对配合物的电化学性质进行了研究,表明两个配合物有相似的电化学行为。     

Pyrylium salts in the synthesis of redoxites

Redoxites poly(2,6-diphenyl-4-vinylpyran), poly(2,6-diphenyl-4-vinylpyrylium perchlorate), poly-(2,6-diphenyl-4-vinylpyridine) and poly(2,2′,6,6′-tetraphenyl-γ,γ′-dipyridine) were obtained based on pyrylium salts. Poly(2,2′,6,6′-tetraphenyl-γ,γ′-dipyridine) was transformed into the polyene to improve its film-forming and conducting properties. Electrochemical properties of polyviologen and conductive properties of the obtained polymers were studied.     

Experimental study of kinematic focusing. Comparison of electroinjection and sequential injection determination of copper

The recently predicted phenomenon of kinematic focusing was studied experimentally using copper ions and EDTA as reactants. Kinematic focusing occurs, in electroinjection analysis, when the detected reaction product moves at the same rate as the reagent present in excess. Thus, reaction product accumulates without dispersion at the front of the excess reagent. Cu-EDTA(2-) complex was observed at 254 nm to form an exceptionally sharp peak as the front of the EDTA zone passed by the detector. The concentrating effect of kinematic focusing was quantified by electroinjection of premixed Cu-EDTA(2-). Sensitivity was compared to that of sequential injection analysis using a 1 cm optical pathlength. Sensitivity was highest in the electroinjection mode, in spite of its 120 mum capillary pathlength, due to kinematic focusing.     

伏安法研究五元瓜环对Cu(Ⅱ)配合物的识别性能

利用伏安法研究了五元瓜环(记为Q[5])对Cu(Ⅱ)配合物的识别性能。结果表明:在pH 5.0的Na2(H2EDTA)介质中,扫描速度为100 mV.s-1时,Q[5]-[Cu(H2EDTA)H2O]配合物的电极反应为单电子准可逆氧化还原反应。摩尔比法测出Q[5]与[Cu(H2EDTA)H2O]作用比为2∶1,稳定常数为3.59×109 L2.mol-2。在所选择的实验条件下,Cu(Ⅱ)浓度在2×10-6~1.6×10-4 mol.L-1范围内,峰电流与其浓度具有较好的线性关系,方法回收率为99.4%~100.7%。     

由5-溴间苯二甲酸和2,2’-联吡啶构筑的两个铜(Ⅱ)配合物的合成、晶体结构及磁性质（英文）

采用水热方法,在120℃温度下选用5-溴间苯二甲酸(H2BIPA)和2,2′-联吡啶(2,2′-bipy)与CuCl2·2H2O分别在NaOH与H2BIPA的物质的量之比为2∶1和3∶1时反应,得到了1个具有零维单核铜结构的配合物[Cu(BIPA)(2,2′-bipy)(H2O)2]·H2O(1)和1个一维链状配位聚合物[Cu3(μ3-BIPA)2(μ-OH)2(2,2′-bipy)2]n(2),并对其结构和磁性质进行了研究。结构分析结果表明2个配合物均属于单斜晶系,分别为P21/c和P21/n空间群。配合物1具有零维单核铜结构,而且这些单核铜单元通过O-H…O氢键作用进一步形成了二维层。而配合物2具有基于三核铜单元的一维链结构。这些一维链通过链间的π-π相互作用进一步形成了二维层。2个配合物的结构差异是由反应中NaOH与H2BIPA的物质的量之比不同造成的。研究表明,配合物2的三核铜单元中相邻铜离子间存在反铁磁相互作用。     

甲醛在脯氨酸膜修饰电极上的电催化氧化

应用电化学法和光谱电化学法研究了脯氨酸膜修饰电极的制备 ,用循环伏安法探讨了该膜的电化学性质及其对甲醛的催化氧化 .该电极催化稳定性良好 ,在NaOH溶液中 ,掺杂Ni (Ⅱ )后的脯氨酸膜修饰电极对甲醛和乙醇的氧化均有一定的催化活性 ,但对甲醛的催化活性更佳     

4′-(二茂铁基)-2,2′∶6′,2″-三联吡啶钴(Ⅱ)配合物混合价态的电荷转移

设计合成了4′-(二茂铁基)-2,2′∶6′,2″-三联吡啶钴(Ⅱ)配合物1以及参比配合物4′-(4-甲苯基)-2,2′∶6′,2″-三联吡啶钴(Ⅱ)配合物2和2,2′∶6′,2″-三联吡啶钴(Ⅱ)配合物3,配合物1中二茂铁基给电子基团的引入使其在可见光区的吸收明显增强,并在部分氧化时呈现混合价态的电荷转移(MVCT)吸收.     

Direct Electrochemical Synthesis and Crystal Structure of a New Mononuclear Copper(Ⅱ) Complex: [(bipy)_2Cu(PhCOO)]ClO_4·(benzil) (benzil = 1,2-Diphenyl-ethane-1,2-dione)

A new mononuclear copper(Ⅱ) complex [(bipy)2Cu(PhCOO)]ClO4·(benzil) (bipy = 2,2′-bipyridine, benzil = 1,2-diphenyl-ethane-1,2-dione) was synthesized by direct electrochemical oxidation of Cu electrode in an acetonitrile solution with benzoic acid, 2,2′-bipyridine and benzoin. As soon as the current flowed in the cell, benzoin was oxidized to benzil quickly. The crystal structure was determined by X-ray diffraction. It belongs to monoclinic system, space group P21/c with a = 14.860(2), b = 20.784(3), c = 11.9150(17) , β = 101.401(3)°, V = 3607.3(9) 3, Z = 4, Mr = 806.69, Dc = 1.485 g/cm3, F(000) = 1660, μ = 0.742 mm-1, R = 0.0788 and wR = 0.1519 for 6254 observed reflections (I > 2σ(I)). The complex contains a mononuclear [(bipy)2Cu(PhCOO)]+ cation, a solvate benzil molecule and a ClO4- anion which locates around the cation outside acting as the counter ion. The Cu(Ⅱ) ion is coordinated by two 2,2′-bipyridines and one benzoato ligand to form a distorted square-pyramid.