Al2O3忆阻器中氧空位对阻值转换性能的影响研究

忆阻器能够在外加电压下实现高阻态与低阻态的转换,在存储器件及仿神经网络计算等方面有着重要的应用。本文通过在Si衬底上制备得到Pt-Al2O3-Pt的金属-绝缘层-金属结构的忆阻器器件,研究了氧空位对阻值转换性能的影响。利用原子层沉积技术工艺控制生长不同氧空位浓度的Al2O3薄膜,测量并比较其Ⅰ—Ⅴ循环曲线,发现仅有在氧空位浓度较高情况下忆阻器才能够实现在高阻态和低阻态之间的转换。本文实验结果表明氧空位对于实现阻值转换性能有着重要的影响,对生长制备忆阻器器件有着重要意义。     

硅和锗纳米线的原子排布和电荷分布的密度泛函紧束缚方法研究

低维硅锗材料是制备纳米电子器件的重要候选材料，是研发高效率、低能耗和超高速新一代纳米电子器件的基础材料之一，有着潜在的应用价值。采用密度泛函紧束缚方法分别对厚度相同、宽度在0.272 nm~0.554 nm之间的硅纳米线和宽度在0.283 nm~0.567 nm之间的锗纳米线的原子排布和电荷分布进行了计算研究。硅、锗纳米线宽度的改变使原子排布，纳米线的原子间键长和键角发生明显改变。纳米线表层结构的改变对各层内的电荷分布产生重要影响。纳米线中各原子的电荷转移量与该原子在表层内的位置相关。纳米线的尺寸和表层内原子排列结构对体系的稳定性产生重要影响。     

中空介孔SiO2纳米球的制备、改性及其对Al3+荧光识别研究

中空介孔SiO2由于中空多孔的结构而常用作功能材料的基底.将中空介孔SiO2进行官能团修饰,并应用为荧光传感材料是中空介孔SiO2一个重要的研究领域.本论文采用聚丙烯酸(PAA)为中空模板,聚醚F127为造孔剂,正硅酸乙酯(TEOS)为硅源,氨水为催化剂在乙醇体系中制备了中空介孔SiO2纳米球.系统研究了搅拌速度和聚醚F127引入量对中空介孔SiO2纳米球形貌及比表面积的影响.通过透射电镜、N2-等温吸附脱附曲线等表征说明该合成方法具有很好的普适性,通过调节F127的引入可以实现对比表面积的有效控制.通过氨基化、席夫碱反应进行荧光修饰,进一步研究表明荧光修饰后的中空介孔SiO2纳米球在水溶液中能够实现对Al3+的有效检测,检测限为1.19×10 -7M.     

Cu2O/TiO2-Bi2WO6三元复合催化剂的制备及光催化性能研究

采用水热法制备花状Bi2 WO6,并利用超声分散法制备了Cu2 O/TiO2-Bi2 WO6复合光催化剂,通过FESEM、XRD、XPS、FI-IR、UV-vis DRS和PL对光催化剂进行了分析和表征.表征结果证明:花状Bi2 WO6表面负载着碎片状的TiO2和立方体Cu2 O形成Cu2 O/TiO2-Bi2 WO6复合光催化剂;以短链脂肪酸(SCFAs)为牺牲剂,考察复合光催化剂的光催化产生氢气和烷烃的性能.实验结果表明:Cu2 O/TiO2-Bi2 WO6复合光催化剂以乙酸为牺牲剂,主要产氢气和甲烷,降解率高达91.82;;以丙酸为牺牲剂,产物主要是乙烷和丁烷,降解率高达90.70;;以丁酸为牺牲剂,除了氢气,甲烷,乙烷,丙烷,丁烷外,气体产物还含有一定量的戊烷,其降解率高达91.50;.结合反应液中间产物的成分进行检测,由此推断出光催化反应的可能机理.     

Surface passivation in n-type silicon and its application in silicon drift detector

Based on the surface passivation of n-type silicon in a silicon drift detector(SDD), we propose a new passivation structure of SiO2/Al2O3/SiO2 passivation stacks. Since the SiO2 formed by the nitric-acid-oxidation-of-silicon(NAOS)method has good compactness and simple process, the first layer film is formed by the NAOS method. The Al2O3 film is also introduced into the passivation stacks owing to exceptional advantages such as good interface characteristic and simple process. In addition, for requirements of thickness and deposition temperature, the third layer of the SiO2 film is deposited by plasma enhanced chemical vapor deposition(PECVD). The deposition of the SiO2 film by PECVD is a low-temperature process and has a high deposition rate, which causes little damage to the device and makes the SiO2 film very suitable for serving as the third passivation layer. The passivation approach of stacks can saturate dangling bonds at the interface between stacks and the silicon substrate, and provide positive charge to optimize the field passivation of the n-type substrate.The passivation method ultimately achieves a good combination of chemical and field passivations. Experimental results show that with the passivation structure of SiO2/Al2O3/SiO2, the final minority carrier lifetime reaches 5223 μs at injection of 5×10¹⁵ cm^-3. When it is applied to the passivation of SDD, the leakage current is reduced to the order of nA.     

扩宽OMA-Ⅵ同时谱宽的新方法

OMA－Ⅵ存在同时谱宽窄的缺点，本文用一种新方法大幅度地扩宽了它的同时谱宽，且不降低其系统分辨率，应用效果甚佳。     

YBa2Cu1-xCox(Cu1-yZny)2Oz体系的Co,Zn共同掺杂效应

本文报道通过对YBa₂Cu_1-xCo_x(Cu_1-yZn_y)₂O_z(0≤x,y≤0.1)体系晶体结构、氧含量、正常态电阻-温度关系、Hall效应以及超导临界温度等的综合测量,发现随着Co和Zn含量的增加,体系经历了从正交结构的超导金属向四方结构的非超导半导体的转变,超导临界温度T_c和载流子浓度n_h均迅速下降,Co 关键词：