烧结温度对Cao.9(NaCe)0.05Bi2Nb2O9无铅压电陶瓷性能的影响

采用传统固相反应法制备了Ca0.9(NaCe)0.05Bi2 Nb2 O9铋层状无铅压电陶瓷.采用XRD、SEM、EDS及相关电学性能测试系统表征了样品的晶体结构、断面形貌、元素组成以及介电、压电、铁电等性能,探究不同烧结温度对于陶瓷性能的影响.结果表明:当烧结温度为1150℃时,样品的晶体结构单一均匀,呈现片层状结构,致密性较好,压电常数高达17 pC/N,介电损耗仅为0.42;,居里温度为908℃,并且具有很好的温度稳定性,说明固相反应法制备的Ca0.9(NaCe)0.05Bi2Nb2O9压电陶瓷最佳烧结温度为1150℃.     

水热法合成K0.5Bi0.5TiO3纳米陶瓷粉体

K_0.5Bi_0.5TiO₃(KBT)nanocrystalline particles were hydrothermally synthesized from Bi(NO₃)₃·5H₂O, TiO₂ and KOH. The crystal phase, chemical composition and microstructure were characterized by XRD, XRF, Raman scattering spectroscopy and TEM. The results indicated that the products were pure perovskite structured K_0.5Bi_0.5TiO₃ with chemical stoichiometry and perovskite structure. The TEM observation revealed that the particles possessed a feature of cubic shape and a nano-scale of about 40 nm. The KBT ceramics sintered at 1 040 ℃ from hydrothermal powders show higher density and better electric properties than that prepared by a solid-state reaction method.     

微合金化对Sn-9Zn合金湿润性、氧化性和凝固性能的影响

低熔点合金Sn-9Zn在无铅焊料中引人注目。然而，它与铜焊接的湿润性却很低，因此，它的应用受到很大限制。在合金中添加1％的稀土(如La和Ce，稀土Y，纯P，Al，Mg及Ti元素)对Sn-9Zn合金与铜焊接时影响其润湿性、氧化性和凝固性有待检验。本文实验表明，添加Al和Ti对湿润性有害，添加Mg，Y元素有稍好的改善，而添加稀土和P却有明显的改善，其氧化性也随添加稀土而增加，而添加P影响不大，凝固的Sn-9Zn合金表面粗糙，而Sn-37Pb却很光滑。     

锆钛酸钡钙压电陶瓷的晶粒尺寸效应研究进展

锆钛酸钡钙无铅压电陶瓷具有可与锆钛酸铅媲美的压电性能,受到国内外广泛关注.晶粒尺寸是影响锆钛酸钡钙陶瓷电性能的重要因素,其晶粒尺寸效应已成为研究的热点.为此,综述了粉体制备方法、烧结方法、烧结温度和保温时间对锆钛酸钡钙陶瓷的晶粒尺寸及其电性能的影响,并提出了研究中亟待解决的问题.     

新型BT-BMT-xBNT无铅高储能密度陶瓷研究

本文采用传统固相反应法,成功制备了新型无铅弛豫铁电陶瓷(1-x)[0.9BaTiO₃-0.1Bi(Mg_0.25Ta_0.5)O₃]-xBi_0.5Na_0.5TiO₃。结果表明,较高居里温度的Bi_0.5Na_0.5TiO₃的引入,使得材料体系中建立了更多的以Bi—O耦合为主的极性纳米区域,弥补了因Bi(Mg_0.25Ta_0.5)O₃的加入导致的宏观极化强度的减少,提高了材料的饱和极化强度,实现了较高储能密度的同时具有更好的温度稳定性。在245 kV/cm电场强度下,x=0.2样品的储能密度约为4.01 J/cm³,储能效率约为84.86%,同时该组分在20~170 ℃储能密度的变化率小于5%,储能效率的变化率小于6%,表现出优异的温度稳定性。     

Effects of Li Substitution and Sintering Temperature on Properties of Bi0.5（Na,K）0.5TiO3 Lead-Free Piezoelectric Ceramics

Bi0.5 （Na0.72K0.28- x Lix ）0.5 TiO3 （BNKLT- 100x） lead-free piezoelectric ceramics are synthesized by conventional solid state sintering techniques. The dielectric and piezoelectric properties of the BNKLT-100x ceramics as a function of Li content are systematically investigated. It is found that not only Li content but also the sintering temperature has a strong effect on the piezoelectric properties of BNKLT. The piezoelectric constant d33 Of BNKLT varies from 120 to 252pC/N in the Li content range from 0.03 to 0.16. In the sintering temperature range from 1080 to 1130℃, the d33 value of BNKLT-6 changes from 200pC/N to 252pC/N. The BNKLT-6 sample sintered at 1100℃ has the highest piezoelectric constant d33 of 252pC/N, with the electromechanical coupling factors kp of 0.32 and kt of 0.44.     

无铅四方相钙钛矿短周期超晶格压电效应机理研究

超晶格压电行为与内部正离子之间的内在联系尚缺乏相关的研究.本文基于密度泛函理论的第一性原理方法,研究了三种无铅四方相钙钛矿铁电超晶格(BaTiO_3/SrTiO_3,KNbO_3/KTaO_3和BaTiO_3/KNbO_3)中A,B位正离子对整体的极化和压电贡献.通过计算超晶格不同轴向应变条件下原子结构和Born有效电荷,获得了超晶格和各个正离子的极化值和压电系数.结果表明,在轴向压缩应变条件下(-0.15—0 A),无铅超晶格中的正离子位移D(A)和D(B)受到抑制,在拉应变时位移才显著增大,因此极化和压电行为不明显.在轴向拉伸应变作用下(0—0.15 A),无铅超晶格中各原子的极化贡献显著增大,特别是B位原子Ti,Nb和Ta的极化贡献使得总的极化强度也显著提高,并当拉应变达到一定值,超晶格才会出现明显的压电行为.无铅超晶格的极化和压电行为主要由B位正离子贡献.     

CeO2掺杂KNN-LiNbO3无铅压电陶瓷的压电与介电性能研究

采用传统固相烧结法制备了0.98K0.5Na0.5NbO3-0.02LiNbO3-xCeO2(0.98KNN-0.02LN+xCeO2)无铅压电陶瓷.研究了不同CeO2掺杂含量(x=0、0.01、0.02、0.03、0.04)对0.98KNN-0.02LN陶瓷显微结构和电学性能的影响.研究结果表明:当CeO2掺杂含量从x=0.00到x=0.01和从x=0.02到x=0.03时,样品出现了正交-四方相转变.当x=0.00和x=0.02时,样品都处于正交与四方两相共存状态.CeO2少量掺杂时Ce4+完全进入晶格,表现为"受主"掺杂的特性;而大量CeO2掺杂时,有杂相的生成,主要起到烧结助剂的作用.样品在1080℃下烧结,当掺杂含量为x=0.02时取得最佳的综合性能:d33=104pC/N,Qm=2201,kp=0.24423,εr=804.2,tanδ=8.748;.     

高温无铅BaTiO_3-(Bi_(1/2)Na_(1/2))TiO_3正温度系数电阻陶瓷阻抗和介电谱分析

采用固相反应法制备了Y2O3施主掺杂的92 mol%BaTiO3-8 mol%(Bi1/2Na1/2)TiO3(BBNT8)高温无铅正温度系数电阻(positive temperature coe?cient resistivity,PTCR)陶瓷.利用透射电镜观察材料的显微结构,发现陶瓷的显微结构主要包括晶粒和晶界两部分,观察不到明显的壳层结构.进一步利用交流阻抗谱研究了陶瓷的宏观电学性能,发现陶瓷的总电阻是晶粒和晶界两部分的贡献,而晶粒电阻很小,在居里温度以上变化不大,材料的PTCR效应主要是晶界部分的贡献.当温度高于居里温度时,随着温度的升高,晶界介电常数逐渐减小,导致势垒增加,晶界电阻增大,从而产生正温度系数效应.最后,通过测试材料的介电频谱特性,研究计算了陶瓷的室温电阻率.     

(Ba0.85Ca0.15)(Ti1-xZrx)O3无铅压电陶瓷的性能研究

采用固相法制备了(Ba0.85Ca0.15)(Ti1-xZrx)O3(BCTZ)无铅压电陶瓷,研究Zr含量(x=0～0.15)对BCTZ陶瓷微观结构和电性能的影响。结果表明:所有样品均具有纯的钙钛矿结构;随Zr含量的增加,室温下样品逐渐由四方相向三方相转变,在0.05相似文献