机械磨抛对CdZnTe薄膜阻变特性的影响

采用磁控溅射法在ITO玻璃上制备了CdZnTe薄膜,探究机械磨抛对CdZnTe薄膜阻变特性的影响。通过对XRD图谱、Raman光谱、AFM显微照片等实验结果分析阐明了机械磨抛影响CdZnTe薄膜阻变特性的物理机制。研究结果表明,磁控溅射制备的薄膜为闪锌矿结构,F43m空间群。机械磨抛提高了CdZnTe薄膜的结晶质量;CdZnTe薄膜粗糙度(Ra)由磨抛前的3.42 nm下降至磨抛后的1.73 nm;磨抛后CdZnTe薄膜透过率和162 cm^-1处的类CdTe声子峰振动峰增强;CdZnTe薄膜的阻变开关比由磨抛前的1.2增加到磨抛后的4.9。机械磨抛提高CdZnTe薄膜质量及阻变特性的原因可能是CdZnTe薄膜在磨抛过程中发生了再结晶。     

SnSxSe2-x单晶纳米片的可控制备与表征

锡二硫族化合物可以通过改变硫和硒的含量来连续调控三元合金材料的带隙、载流子浓度等物理化学性质,在电子和光电子器件应用上具有巨大的潜力。本文采用化学气相沉积(CVD)技术可控地制备了不同元素组分的SnS_xSe_2-x(x=0,0.2,0.5,0.8,1.0,1.2,1.5,1.8,2.0)单晶纳米片。采用扫描电子显微镜(SEM)、原子力显微镜(AFM)、能量色散X射线光谱(EDS)、透射电子显微镜(TEM)以及拉曼光谱等手段对SnS_xSe_2-x纳米片进行了综合表征。结果表明本方法成功实现了元素百分比可调的SnS_xSe_2-x单晶纳米片的可控制备。重点研究了依赖于元素百分比的SnS_xSe_2-x的拉曼特征谱,实验结果与基于密度泛函理论(DFT)的第一性原理计算得到的SnS_xSe_2-x的拉曼仿真谱高度吻合,理论计算结果较好地诠释了实验拉曼光谱发生变化的原因。本研究提供了一种元素百分比可调的三元SnS_xSe_2-x单晶纳米片的可控制备方法,同时对锡二硫族化合物的明确、无损识别提供了方案。     

Chelating Metal Ions in a Metal-Organic Framework for Constructing a Biomimetic Catalyst Through Post-modification

Crystal engineering, as a burgeoning technology, has been widely used to construct metalloporphyrins biomimetic catalysts. Herein, a bimetallic metal-organic framework (MOF) was constructed by 4-(4-carboxyphenyl)-1,2,4-triazole ligand, Co²⁺ and Zr⁴⁺ metal ions by solvothermal reaction(named PFC-88). A N,N-chelation site was found between the two adjacent ligands in PFC-88, consequently a porphyrin-like structure was obtained through chelating Fe³⁺ in this site by post-modification, named PFC-88-Fe. The result of a single crystal X-ray technology verified that Fe ions were successfully metalated in the N,N-chelation site of PFC-88, which is assisted by the X-ray absorption near-edge structure(XANES) spectra. An o-phenylenediamine oxidation reaction was applied to assessing the catalytic activity of PFC-88-Fe, in which the absorbance increases of phenazine-2,3-diamine at λ=418 nm were recorded by absorption spectroscopy in kinetic mode, exhibiting the application potential as a biomimetic catalyst.     

Rapid qualitative profiling and quantitative analysis of Juglandis Mandshuricae Cortex and seven flavonoids by ultra-high performance liquid chromatography–quadrupole/orbitrap high-resolution mass spectrometry

Juglandis Mandshuricae Cortex is the bark of Juglans mandshurica Maxim., which has been used as a folk medicine plant in China and India. In this study, an ultra-high performance liquid chromatography–quadrupole/orbitrap high-resolution mass spectrometry method was developed to clarify and quantify the chemical profiling of Juglandis Mandshuricae Cortex rapidly. A total of 113 compounds were characterized. Among them, seven flavonoids were simultaneously quantified in 15 min, including myricetin, myricetrin, taxifolin, kaempferol, quercetin, quercitrin, and naringenin. The method was validated for accuracy, precision, and the limits of detection and quantification. All calibration curves showed a good linear relationship (r > 0.9990) within test ranges. The intra- and inter-day relative standard deviations were less than 2.16%. Accuracy validation showed that the recovery was between 95.6 and 101.3% with relative standard deviation values below 2.85%. The validated method was successfully applied to determine the contents of seven flavones in Juglandis Mandshuricae Cortex from seven sources and the contents of these places were calculated respectively. This method provides a theoretical basis for further developing the medicinal value of Juglandis Mandshuricae Cortex.     

以磷化铁为添加剂沿(111)面生长磷掺杂金刚石大单晶

掺杂是调控金刚石性能的一种重要手段。本文采用温度梯度法,在5.6 GPa、1 312 ℃的条件下,选用Fe₃P作为磷源进行磷掺杂金刚石大单晶的合成。金刚石样品的显微光学照片表明,随着Fe₃P添加比例的增加,金刚石晶体的颜色逐渐变深,包裹体数量逐渐增加,晶形由板状转变为塔状直至骸晶。金刚石晶形的变化表明Fe₃P的添加使生长金刚石的V形区向右偏移,这是Fe₃P改变触媒特性的缘故。红外光谱分析表明,Fe₃P的添加使金刚石晶体中氮含量上升,这说明磷的进入诱使氮原子更容易进入金刚石晶格中。激光拉曼光谱测试表明,随着Fe₃P添加比例的增加,所合成的掺磷金刚石的拉曼峰位变化不大,其半峰全宽(FWHM)值变大,这说明磷的进入使得金刚石晶格畸变增加。XPS测试结果显示,随着Fe₃P添加比例的增加,金刚石晶体中磷相对碳的原子百分含量也会增加,这意味着添加Fe₃P所合成的金刚石晶体中有磷存在。     

自掺杂SnO2微球的水热合成及其可见光催化性能

本研究采用水热法,以柠檬酸为螯合剂,通过控制n(Sn⁴⁺)/n(Sn²⁺)的数值,合成了由具有丰富氧空位的SnO₂纳米晶体组装成的微球。通过X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、傅里叶红外光谱(FT-IR)、X射线光电子能谱(XPS)及UV-Vis漫反射光谱对SnO₂纳米微球进行表征分析,结果表明:在酸性水热条件和柠檬酸的螯合作用下,二氧化锡纳米晶体聚集形成微球;在Sn⁴⁺/Sn²⁺摩尔比例为3:7时,其微球尺寸最小,整体分散性较好;同时适量二价锡离子的掺杂使得该样品氧空位浓度达到最佳,氧空位的存在将使得样品光吸收范围拓展至可见光,因而该样品显示出较强的可见光催化效率,在8 min内完全降解甲基橙。     

微区X射线荧光成像技术在岩心分析中的应用

微区X射线荧光（Micro-XRF）分析技术是通过微小的X射线光束照射样品，对样品进行原位成分观测的无损分析手段之一，具有灵敏度高、速度快和准确性高的特点。采用微区X射线荧光光谱仪（M6 JETSTREAM）对安徽铜陵冬瓜山铜矿床四段岩心样品进行面扫描，分析不同矿层共17种元素区域分布特征、空间分布规律及组合关系等，结果表明：（1）Cu和Fe两种成矿元素高值空间分布区域基本不重叠，S与Fe分布范围高度重叠，关系密切，微量元素Ni，Bi，Pb，Zn，Si，Na与Cu密切相关，而Ti，Al，K与Fe具有弱相关性；（2）垂向上，Fe元素含量随深度增加逐步增大，而Cu元素含量呈降低趋势，其他元素也随深度呈下降趋势；（3）元素分布受石炭纪中期海底喷流沉积成矿作用和岩浆热液成矿作用叠加改造作用明显；（4）该钻孔矿石矿物以磁黄铁矿、黄铜矿和黄铁矿为主，垂向上组合规律明显，脉石矿物以石英、石榴子石和透辉石为主。该技术通过分析元素空间分布规律、相关性以及矿物组合和分配关系等可对元素富集和运移以及对矿床的成矿机制、成因模式等地质环境和地质过程提供新认识和新证据。结合矿床地球化学特征的分布模式，微量元素可作为寻找主矿种的指示元素，为深部找矿提供依据。此外，该技术能作为预分析技术快速筛选出感兴趣的信息和位置，为后期各种更高精度的微区分析提供不同尺度、不同层次的元素分布信息。