高硅无铝Mo-Beta沸石的合成与结构表征

用水热晶化法合成了无铝Mo-Beta沸石,讨论了合成条件对无铝Mo-Beta沸石晶化的影响,通过化学分析、XRD、IR、DTA/TGA、TEM、NMR、ICP和UV-Vis紫外漫反射光谱测定了样品的n(SiO₂)/n(MoO₃)比,并对其结构进行了表征,结果表明,所合成的Mo-Beta沸石晶粒均匀,Mo存在于沸石骨架中,由于Mo的掺入,引起Beta沸石红外光谱、差热分析曲线及晶胞参数, ²⁹SiMASNMR谱等发生变化。     

一种新型共生沸石(T-L)的合成与表征

在Na₂O-K₂O-Al₂O₃-SiO₂-H₂O体系中水热合成了一种新型的共生沸石, 它由L型沸石生长在T型沸石的一端而形成, 称之为T-L型沸石. 通过XRD, SEM, TEM, EDX, IR等手段对其进行了初步的表征. SEM相片表明这种沸石具有特殊的铆钉状外形; 在TEM相片上可以清楚地看到L型沸石的大孔道, 此孔道与L型沸石的表面垂直. 通过EDX的数据计算发现共生沸石的两相有不同的骨架硅铝比: T型沸石部分Si/Al＝3.71, L型沸石部分Si/Al＝3.41. 在该样品中B酸大于L酸.     

ERB-1分子筛的合成与表征

 分别以白炭黑、硼酸和氢氧化钠为硅源、硼源和碱源,以六亚甲基亚胺为模板剂,系统地研究了硅硼比、碱量、模板剂用量和水量对合成ERB-1分子筛的影响,并采用N2物理吸附、吸附NH3的程序升温脱附、热重和差热分析、 X射线衍射和傅里叶变换红外光谱等手段对样品的表面性质、酸性和热稳定性进行了表征. 结果表明,合成ERB-1分子筛较好的原料组成为 n(SiO2)/n(B2O3)=0.6～2, n(H2O)/n(SiO2)=40, n(NaOH)/n(SiO2)=0.1～0.2和n(HMI)/n(SiO2)=0.8～1; ERB-1分子筛上的酸中心以弱酸为主,且酸强度较低; ERB-1的结构在800 ℃以下保持稳定.     

Forming and Gathering of SnO2 Nanoparticles on External Surface of High Silica TON, MFI and FAU Type Zeolites

Tin dioxide （SnO2） nano-particles were prepared on high silica TON, MFI and FAU type zeolites by impregnation of SnC12 solution and subsequent calcination at 873 K. XRD and SAED were used to characterize the crystalline phase, and TEM was used to characterize the morphology, the particle size and the agglomerative state of the formed nano-materials. The nano-particles, which possess 8 nm, 10-80 nm and 6 nm in size, were found to form on the outer surface of TON, MFI and FAU zeolites, respectively. SnO2 microcapsules and SnOz netlike nanostructure were obtained by decomposition of SnO2-TON and SnO2-MFI in 40% hydrofluoric acid at room temperature. Compared with the nano-particles formed on NaY zeolite, the special morphology and the agglomerative state of SnO2 nanostructures on TON and MFI type zeolites with one and two dimension channel system indicate that the heterogeneous framework, surface structure and property perform important function for forming and growing SnO2 nanostructure on the outer surface of the zeolites.     

乙苯工艺技术开发及工业应用进展

乙苯是重要的基本有机化工原料,主要用于生产苯乙烯,进而作为合成橡胶和塑料等高分子材料的单体.乙苯的生产主要采用苯和乙烯的烷基化工艺.传统的AlCl3法由于存在设备腐蚀和环境污染等问题己逐步被环境友好的分子筛烷基化法取代.分子筛烷基化法分为气相法和液相法.气相烷基化催化剂为ZSM-5分子筛,例如Mobil-Badger气相烷基化工艺;液相烷基化催化剂有Y,Beta和MCM-22分子筛,例如Lummus/UOP的EBOne工艺和Mobil-Raythen的EBMax工艺.近年来,随着经济的发展,全球范围内乙苯需求量逐年增加,产能也逐渐扩大.尤其在中国大陆,目前乙苯产能居世界首位,其乙苯工艺技术的开发也最为活跃.经过20多年的发展,苯烷基化制乙苯工艺取得了长足发展.中国科学院大连化学物理研究所在成功合成ZSM-5/ZSM-11分子筛的基础上,与中国石化、中国石油联合开发了苯与干气气相烷基化制乙苯工艺;中国石化上海石油化工研究院则以ZSM-5分子筛为基础,开发了适应原料多样性的苯气相烷基化制乙苯催化剂和工艺技术,可以采用石油苯、焦化苯、纯乙烯、乙醇和稀乙烯为原料;石油化工科学研究院则开发了基于Beta分子筛的苯与乙烯液相烷基化催化剂及液相循环烷基化工艺.以上催化剂及工艺技术均己工业化应用.此外,实现催化烷基化与分离同时进行的催化蒸馏工艺以及乙烷脱氢再与苯烷基化的两段法制乙苯工艺的研究也取得了一定进展.在苯烷基化制乙苯工艺中,气相法操作温度高,苯与乙烯进料摩尔比高,因而能耗高,同时二甲苯含量高,产品纯度低.液相烷基化工艺则具有温度低和苯/烯比低的特点,其能耗控制及产品质量均优于气相法工艺.但是,液相反应中的扩散阻力大,孔道为10元环的ZSM-5分子筛失活迅速,因而选用了具有12元环孔道的Y,Beta和具有表面12元环碗状半超笼的MCM-22分子筛为催化剂.然而,液相法工艺的苯与乙烯进料摩尔比仍然远高于理论化学计量比,其产品中含有一定比例的多乙基苯(主要是二乙苯),需采用烷基转移过程将多乙基苯与苯反应生成乙苯.进一步降低苯/烯比、提高单乙苯选择性是未来乙苯工艺开发的努力方向.研究表明,介孔分子筛及纳米片状分子筛在苯烷基化反应中具有优于常规分子筛的催化表现,即更高的乙烯转化率和乙苯选择性.其原因在于,扩散是影响苯烷基化反应性能的关键因素,扩散性能的改善使得产物从活性位解吸后更容易扩散出去,进而空出活性位并进一步催化新的底物.同时,单烷基化产物与新的烷基化试剂进一步发生烷基化的几率降低,提高了单烷基化产物的选择性.因而,采用扩散性能更好的催化剂催化苯烷基化反应前景看好,关键问题在于如何简单并廉价地获取该类材料.另外,虽然分子筛催化苯烷基化是一个环境友好的工艺过程,但是在分子筛催化剂制备过程中会产生环境污染.同时,失活催化剂的处理也是需要考虑的问题.开发分子筛的绿色合成技术,减轻甚至消除环境污染是一个值得努力的方向;开发失活催化剂的综合利用技术,如采用失活催化剂为原料用于分子筛的合成,可以作为环境保护的有效手段.     

Y型沸石的铝化及其性能研究

用(NH_4)_3AlF_6溶液对Y型沸石进行铝化,得到了不同硅铝比的铝化Y型沸石。XRD实验表明Al原子进入Y型沸石骨架,晶胞常数α_0增大,而且晶胞常数α_0的增大与铝化程度有一定的关系。铝化Y型沸石的吸附量略有降低。IR研究表明,骨架振动,表面羟基谱峰变化不明显。在铝化Y型沸石上存在B酸和L酸,其主要是B酸中心。     

水热条件下Y型沸石的转晶行为

系统研究了以KOH为结构导向剂,Y型沸石（HY和NaY）在水热条件下转晶为MER型沸石的行为.MER型沸石是硅铝比（Si/Al）在2~3之间且具有四种尺寸8元环孔道（3.1Å×3.5Å,2.7Å×3.6Å,3.4Å×5.1Å,3.3Å×3.3Å）的硅铝沸石分子筛,在小分子催化以及分离方面具有重要的潜在应用.传统水热法合成高结晶度MER型沸石需要7~10 d,将Y型沸石置于KOH的溶液中,经水热处理可在2 d内生成高结晶度的MER型沸石,而水热处理具有等价摩尔组成的无定形硅铝凝胶则得不到高结晶度MER型沸石的纯相.HY沸石可在100和150℃发生转晶,而NaY则只能在150℃发生转晶.KOH/SiO₂比和H₂O/SiO₂比对Y型沸石的转晶行为有重大的影响,只有在最优KOH/SiO₂比和H₂O/SiO₂比条件下才能生成高结晶度的MER型沸石.该转晶合成法显著缩短了MER型沸石的合成周期,对缩短其它有重大工业应用价值的沸石分子筛的合成周期有重要的借鉴意义.     

高效ZSM-5-L二元复合分子筛的合成及正戊烷芳构化性能

通过优化水热陈化条件制备纳米L沸石,再采用水热合成结合原位二次晶化法,合成具有微-介复合孔结构的高效ZSM-5-L二元复合分子筛.考察了体系pH、二次晶化温度等因素对ZSM-5-L复合分子筛合成的影响,采用X射线衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)和傅里叶变换红外光谱(FTIR)等技术对复合分子筛进行表征,确定了最佳复合条件:pH=10.5~11.5,晶化温度170℃,晶化时间24 h.ZSM-5-L复合分子筛具有不同于ZSM-5沸石、L沸石及两者机械混合物的物性特征,且具有微-介复合孔结构.以正戊烷催化转化为探针反应,评价了ZSM-5-L复合分子筛轻烃芳构化反应性能.在相同反应条件下,ZSM-5-L复合分子筛具有优于2种单分子筛及二者机械混合物的正戊烷芳构化催化性能.     

Fabrication of Zeolite A Rods with Irregular Macropores by Self-assembly of Zeolite A Microcrystals Using Microwave-assisted Hydrothermal Synthesis

Zeolite A rods by self-assembly of zeolite A microcrystal were successfully synthesized by microwave-assisted hydrotherrnal synthesis. The average size of zeolite crystals consisting of self-assembling materials was about 300 nm and the length of zeolite rods was in the range of 15--30μm.     

纳米分子筛ZSM-5的热稳定性研究

Nanosized ZSM 5 zeolite was synthesized by hydrothermal method and characterized by XRD and TEM techniques. The specific heat of the nanosized ZSM 5 zeolite was measured in the temperature range from 79 to 370 K, and its enhancement in specific heat was observed as compared with the corresponding microsized zeolite, indicating that the nanosized ZSM 5 zeolite possesses higher surface activity. The thermostability of the samples was determined by differential scanning calorimetric (DSC) and thermogravimetric (TG) techniques. The DSC results showed that, for the nanosized ZSM 5, a broad exothermic peak is observed from 1?300 K; for the microsized ZSM 5, the corresponding exothermic peak begins at 1?400 K, and a distinct phase transition can be observed at 1?620 K. The TG results showed that, for the nanozised ZSM 5, the maximum mass loss ratio is 6 9%, and two mass loss stages can be observed in the temperature ranges of 298～663 K and 923～ 1?273 K, respectively; for the microsized ZSM 5, the maximum mass loss ratio is 6 5% and it is more stable than the nanosized ZSM 5.     

NiMo/Al_2O_3 catalyst containing nano-sized zeolite Y for deep hydrodesulfurization and hydrodenitrogenation of diesel

Two mixed-matrix NiMo/Al2O3 catalysts containing nano-and micro-sized zeolite Y have been prepared to explore the size effect of zeolite Y particle on the hydrodesulfurization(HDS)and hydrodenitrogenation(HDN)activities of fluid catalytic cracking(FCC)diesel.They were characterized by SEM,BET,XRD,H2-TPR,NH3-TPD and HRTEM.The results show that the catalyst containing nano-sized zeolite Y possesses larger average pore diameter,higher pore volume,weaker and lesser acid sites,more easily reducible metal phases,shorter MoS2 slabs and more slab layers than the catalyst containing micro-sized zeolite Y.The catalysts were also evaluated with a high-pressure fixed-bed reactor using real FCC diesel as feed.The results display that the catalyst containing nano-sized zeolite Y bears higher HDS and HDN activities and exhibits higher relative rate constant for the removal of total sulfur or nitrogen than the one containing micro-sized zeolite.     

微孔-微孔复合分子筛的结构特征及应用

微孔-微孔复合分子筛是指两种(或多种)微孔分子筛的复合晶体,不仅具备单一分子筛的特性,而且由于复合过程中产生的结构畸变使其具有独特的孔道结构和酸性质,进而体现出优异的催化反应特性,成为当今分子筛领域的研究热点。微孔-微孔复合分子筛可分为共晶分子筛和共生分子筛两种,前者通过两种分子筛晶体的无限成分单元重排,有利于构成新的完整的晶体结构,后者则是两种分子筛共生长过程中得到的两相交错生长的复合体,产生微结构畸变和界面效应。本文对微孔-微孔复合分子筛进行归纳和分类,并系统介绍了微孔-微孔复合分子筛的研究进展,着重阐述了共晶分子筛和共生分子筛的合成与微结构特点以及在催化反应领域中的应用。     

Reconstructive and displacive transformations of tectosilicates

By using the thermally induced phase transformation initial zeolites were converted into pure carnegieite, stuffed derivative of cristobalite. The polymorphs obtained from Na-LTA are stoichiometric (NaAlSiO₄), since those obtained from Na-FAU zeolite are non-stoichiometric (Na_1-xAl_1-xSi_1+xO₄). Stoichiometric carnegieite have cubic structure, while non-stoichiometric carnegieite crystallized in cubic and orthorhombic forms. ²⁹Si MAS NMR spectra show a very large but expecting difference between stoichiometric and non-stoichiometric carnegieite. The spectrum of stoichiometric carnegieite has only one peak Si(4Al), while the spectrum of non-stoichiometric carnegieite consist few superimposed peaks assigned to Si(4Al), Si(3Al), Si(2Al), Si(1Al) and Si(0Al). DTA study indicates the occurrence of displacive phase transition of all synthesized carnegieite. The transition temperature is depending on silicon aluminum order: T _m=690°C for stoichiometric, T _m=565 and 660°C for non-stoichiometric, low-temperature and high-temperature carnegieite, respectively. This revised version was published online in July 2006 with corrections to the Cover Date.     

以两种季铵碱为模板剂合成A形体富集Beta沸石及其晶化过程

以三甲基环己基氢氧化铵和二甲基乙基环己基氢氧化铵为模板剂或结构导向剂(SDA), 采用超浓水热方法合成了A形体富集的Beta沸石, 用粉末X射线衍射(XRD)、 扫描电子显微镜(SEM)、 ²⁹Si固体魔角自旋核磁共振(²⁹Si MAS NMR)以及氮气吸附等表征手段对其进行了详细表征, 探索了最优合成条件, 研究了其晶化过程. 结果表明, 在晶化初期产物中己出现A形体过量特征, 随着晶化的进行, A形体的过量程度无显著变化.     

丁烯在纳米H-ZSM-5催化剂上的催化裂解反应

在小型固定床反应器中考察了纳米H-ZSM-5催化剂(晶粒度为20～50nm)对丁烯催化裂解制丙烯反应的催化性能,并与两种微米H-ZSM-5催化剂样品(晶粒度分别为1～2和1～6μm)进行了比较.结果表明,在相同的反应条件下,纳米H-ZSM-5和微米H-ZSM-5催化剂上的初始丁烯转化率及丙烯收率相当,但纳米H-ZSM-5催化剂在反应中的抗积碳失活性能优于微米H-ZSM-5催化剂.在进料质量空速7h-1,常压和560℃的条件下反应,当丁烯转化率和丙烯收率下降50%时,两种微米催化剂上的反应时间仅为28h左右,而纳米催化剂上的反应时间为120h左右.积碳分析结果表明,纳米催化剂上的积碳速率明显低于微米催化剂.     

沸石分子筛催化剂的“限域”效应

沸石分子筛催化剂因其独特的酸性、规则的孔道结构和良好的水热及化学稳定性被广泛应用于石油化工、煤化工和精细化工等重要领域.沸石分子筛活性位点的数目和分布,以及孔结构效应是沸石分子筛催化科学研究中最根本的问题,直接影响催化反应历程和反应结果.几十年来,沸石分子筛催化研究多集中在对活性位点的基本认识和合成设计,而忽视了活性位点、反应分子和沸石分子筛孔道微环境之间的相互作用.受益于先进的化学分析表征技术和化学理论计算科学的发展,沸石分子筛催化剂孔道内的微环境研究引起了越来越多研究人员的重视.通过对相关文献的分析整理,本文从沸石分子筛结构"限域"理论的发展历程,对分子扩散、吸附和催化过程的影响及其应用拓展等几个方面讨论了沸石分子筛催化剂中的"限域"效应.     

微波场中A型分子筛及分子筛膜合成的研究

Effects of aging time and alkalinity as well as cation concentration(Na⁺) on the synthesis of A type zeolite and zeolite membrane were investigated in this paper. The results showed that aging time for synthesis of A type zeolite and zeolite membrane had remarkable influence and alkalinity could accelerate the formation of zeolite but was disadvantage to zeolite membrane synthesis. Cation concentration(Na⁺) also couldn′t accelerate the synthesis of zeolite and zeolite membrane but it was probable an important factor to accelerate crystal growth .Moreover, more compact zeolite membranes could be synthesized by this method while the thickness of membrane was thinner than that of convention. Zeolites and zeolite membranes were characterized by XRD, TEM as well as IR characterization techniques.     

新型洗涤剂用沸石MAP的合成及其性能表征

在ＳｉＯ_２－Ａｌ_２Ｏ_３－Ｎａ_２Ｏ－Ｈ_２Ｏ体系中,采用加入晶种的方法水热合成出新型洗涤剂用沸石－ＭＡＰ。其硅铝比（Ｓｉ／Ａｌ）在 １．０７－１．１３之间,平均晶粒直径小于０．４μｍ,钙离子交换容量为２９０～３１３ ｍｇＣａＣＯ_３／ｇ（干沸石）,非离子表面活性剂的吸附量在 ８３～ １００ｇ ｏｉｌ／１００ｇ（沸石）之间。本文着重考察了影响合成 ＭＡＰ沸石的因素,确定了ＭＡＰ沸石会成的最佳范围,并对其物理化学性质进行了表征。     

ZSM-5/Y复合分子筛的酸性及其重油催化裂化性能

 ZSM-5/Y是本研究组合成的一种新型复合分子筛材料. 用“两次交换,两次焙烧”和磷 酸氢二铵浸渍方法对该复合分子筛材料进行了改性,采用红外光谱表征了复合分子筛的酸性,研究了磷改性对复合分子筛样品羟基区谱学性质的影响,并与相应的机械混合分子筛样品进 行了对比. 红外光谱数据表明,磷改性后复合分子筛的B酸(主要是中强酸)增加,而机械混合分子筛在各个酸强度区域的B酸量和L酸量都减少. 以新疆重油为原料考察了改性后复合分子 筛样品和机械混合分子筛样品的催化裂化性能. 与相应的机械混合分子筛催化剂相比,磷改 性复合分子筛催化剂具有较高的柴油选择性,其柴油产率增加了4.1个百分点,柴汽比增加了0.11,总轻油产率与机械混合分子筛相当. 用气体产物中的CMR(裂化机理比)和C3/C4比 值分析了复合分子筛的催化性能与其聚集体结构的关系.     

加料方式及底物浓度对Ti-MWW催化剂上环己酮氨肟化反应的影响

 研究了加料方式和底物浓度对钛硅分子筛Ti-MWW催化环己酮液相氨肟化反应的影响. 结果表明,加料方式对 Ti-MWW 催化环己酮氨肟化过程有重要影响,过氧化氢的浓度对反应过程也有一定的影响. 在过氧化氢缓慢加入反应体系的情况下,环己酮转化率和环己酮肟选择性都高于99%, 而且该反应过程以水作溶剂,对环境友好.