微乳液法制备Pt-S2O82-/ZrO2-Al2O3型固体超强酸催化剂及其异构化性能

采用微乳液法负载Pt制备了Pt-S2O82-/ZrO2-Al2O3(Pt-SZA-M)固体超强酸催化剂, 以正戊烷异构化反应为探针, 对比了微乳液法和浸渍法负载Pt制备的催化剂(Pt-SZA)的异构化性能, 并采用XRD, FTIR, BET, TG-DTA, TPR和TEM对催化剂进行了表征. 结果表明, 与Pt-SZA催化剂相比, Pt-SZA-M催化剂中Pt粒子的粒径更小(4.5 nm)且尺寸更均一; Pt-SZA-M催化剂的比表面积(109.6 m2/g)比Pt-SZA催化剂(95.0 m2/g)增加了15.4%. Pt-SZA-M催化剂的初始还原温度比Pt-SZA催化剂降低了10~20℃, 表明微乳液法负载Pt可以提高催化剂的氧化活性, 提高氢分子在催化剂上的吸附解离能力. 异构化活性实验结果表明, 与Pt-SZA催化剂相比, Pt-SZA-M催化剂的低温活性得到明显改善, 在反应压力为2.0 MPa、 氢烃摩尔比为4: 1、 质量空速为1.0 h-1的条件下, Pt-SZA-M催化剂在反应温度为230℃时活性达到60.8%, 在100 h内异戊烷的收率可稳定在58.0%左右, 选择性在95.0%以上.     

Ce0.67Zr0.33O2对CH4燃烧催化剂Fe2O3/Al2O3的改性作用

固定n(Ce)/n(Zr)比为0.67/0.33,用共沉淀法制得一系列CeO2-ZrO2-Al2O3固溶体.采用这些固溶体作载体,以Fe2O3为活性组分,用浸渍法制备了一系列催化剂.BET结果显示,将适量Ce0.67Zr0.33O2引入到Al2O3载体中有助于催化剂保持较高的比表面积.TPR结果显示,载体中引入适量的Ce0.67Zr0.33O2可以改善催化剂的氧化还原性能.XRD结果表明,Fe2O3在CeO2-ZrO2-Al2O3载体上呈现出良好的分散状况,老化前后催化剂的晶相结构基本无明显变化.特别是当载体中m(Ce0.67Zr0.33O2)∶m(Al2O3)的值为1∶2时,Fe2O3/CeO2-ZrO2-Al2O3催化剂在甲烷催化燃烧中显示出最佳的催化性能和抗高温老化性能.     

ZrxCe1－xO2催化剂催化湿式氧化乙酸的活性研究

采用共沉淀法制备了Zr_xCe_1－xO₂催化剂, 利用BET, XRD和XPS对其进行了表征, 并研究了催化剂催化湿式氧化乙酸的活性. 结果表明: Zr和Ce摩尔比为1∶9的催化剂催化湿式氧化乙酸时具有最好的活性, 当乙酸溶液的初始化学需氧量(COD)为5000 mg/L, 反应温度为230 ℃, 压力为5 MPa时, 120 min后, COD的去除率为76% . 催化剂具有良好的活性是因为在CeO₂中加入Zr能够增大催化剂的比表面积和表面缺陷氧的含量, 并最终加快了HO₂•自由基的产生, 从而提高了催化剂的活性.     

ZrxCe1－xO2催化剂催化湿式氧化乙酸的活性研究

采用共沉淀法制备了Zr_xCe_1－xO₂催化剂, 利用BET, XRD和XPS对其进行了表征, 并研究了催化剂催化湿式氧化乙酸的活性. 结果表明: Zr和Ce摩尔比为1∶9的催化剂催化湿式氧化乙酸时具有最好的活性, 当乙酸溶液的初始化学需氧量(COD)为5000 mg/L, 反应温度为230 ℃, 压力为5 MPa时, 120 min后, COD的去除率为76% . 催化剂具有良好的活性是因为在CeO₂中加入Zr能够增大催化剂的比表面积和表面缺陷氧的含量, 并最终加快了HO₂•自由基的产生, 从而提高了催化剂的活性.     

不同金属负载对Cr/Al2O3-TiO2催化剂结构及氧化NO性能的影响

采用溶胶-凝胶法和浸渍法制备Cr/Al_2O_3-TiO_2催化剂,在考察不同Cr负载量的基础上,研究不同金属负载与焙烧温度对Cr/Al_2O_3-TiO_2催化剂结构与性能影响。程序升温氧化(TPO)结果表明,当Cr负载量为10%(w/w)时具有较好的催化活性;不同金属负载Cr/Al_2O_3-TiO_2时,负载Co及在焙烧温度为550℃时催化剂具有较好的活性。通过程序升温还原(H_2-TPR)表征发现,Co的负载使催化剂的低温氧化还原能力逐渐提高,表明Co-Cr具有较好的协同催化作用。X射线光电子能谱(XPS)表征表明,Co增加了Cr~(6+)和表面吸附氧(O_β)含量,随着焙烧温度的升高(450～550℃),晶格氧不断向催化剂表面流动,表面化学吸附氧O_β比例逐渐增加,导致催化活性不断升高,说明Cr~(6+)和O_β是催化氧化NO的重要活性物种。     

Na3V2(PO4)2O2F钠离子电池正极材料的水热法制备及性能

采用水热法制备了Na_3V_2(PO_4)_2O_2F (NVPOF)钠离子电池正极材料,利用X射线衍射(XRD)、扫描电子显微镜(SEM)和恒流充放电(GCD)等方法研究了其形貌、结构与电化学性能。结果显示,纯相NVPOF形貌规则,呈长1～3μm、宽300 nm～1μm、长宽比为2～3的四棱柱形貌。NVPOF具有2对平稳的充放电平台,在0.2C和2C电流密度下,放电比容量达到124.2和70.5 m Ah·g~(-1),经100次循环后,放电比容量仍有105.8和59.6 m Ah·g~(-1),容量保持率达到85.2%和84.5%,库仑效率基本在97%以上,且低温(0℃)电化学性能也有不错的表现。经还原氧化石墨烯(r GO)包覆提高电子电导率,NVPOF@r GO在0.5C和2C的室温放电比容量高达124.4和88.4 m Ah·g~(-1),且2C倍率下循环200圈后的比容量仍有78.7 m Ah·g~(-1),容量保持率高达89%,库仑效率始终保持在99%左右,显示出优异的倍率和循环性能。     

球磨辅助高温固相法制备Li1.0Na0.2Ni0.13Co0.13Mn0.54O2正极材料及其性能

以乙酸盐(乙酸锂、乙酸钠、乙酸钴、乙酸镍、乙酸锰等)为原材料,采用球磨辅助高温固相法制备Li_(1.0)Na_(0.2)Ni_(0.13)Co_(0.13)Mn_(0.54)O_2正极材料。借助XRD、SEM等表征材料的结构和形貌,利用循环伏安、恒流充放电、交流阻抗等方法研究材料的电化学性能。结果表明,钠的掺杂导致颗粒表面光滑度降低,形成Na_(0.77)Mn O_(2.05)新相。0.05C活化过程中,掺钠样品和未掺钠样品首次放电比容量分别为258.4 m Ah·g~(-1)和215.8 m Ah·g~(-1),库伦效率分别为75.2%和72.8%;2C放电比容量分别为116.3 m Ah·g~(-1)和106.2 m Ah·g~(-1)。研究发现,掺钠可减小首次充放电过程的不可逆容量,提高容量保持率;改善倍率性能与容量恢复特性;降低SEI膜阻抗和电荷转移阻抗;掺钠后样品首次循环就可以基本完成Li_2Mn O_3组分向稳定结构的转化,而未掺杂的样品需要两次循环才能逐步完成该过程;XPS结果表明,掺钠样品中Ni~(2+)、Co~(3+)、Mn~(4+)所占比例明显提高,改善了样品的稳定性和电化学性能;循环200次后的XRD结果表明掺钠与未掺钠材料在脱嵌锂反应中的相变化过程基本一致,良好有序的层状结构遭到破坏是循环过程中容量衰减的主要原因。     

均匀共沉淀法制备BaTiO3 -Nix Zn1-x Fe2 O4 核-壳粒子及其性能

以尿素为沉淀剂, 在无后续热处理的情况下, 采用均匀共沉淀法制备了BaTiO3-NixZn1-xFe2O4核-壳粒子. 采用透射电子显微镜(TEM)、 X射线衍射仪(XRD)、 能谱仪(EDS)及振动样品磁强计(VSM)对BaTiO3-NixZn1-xFe2O4核-壳粒子的形貌、 结构、 成分和磁性能进行了表征. 结果表明, 制备的核-壳结构粒子中NixZn1-xFe2O4壳层在BaTiO3颗粒的表面包覆完整. 通过控制共沉淀中NiCl2·6H2O与ZnCl2的摩尔比可以调控BaTiO3-NixZn1-xFe2O4核-壳粒子的磁性; 加入的NiCl2·6H2O与ZnCl2摩尔比为7∶3时制得的核-壳粒子具有较好的磁性能, 其饱和磁化强度和矫顽力分别为26.999 A·m2/kg和902.787 A/m.     

MnOx/Al2O3催化剂低温SCR脱硝性能

采用浸渍法制备了MnO_x/Al_2O_3低温脱硝催化剂,研究了Mn的含量对MnO_x/Al_2O_3催化剂低温烟气中NOx脱除率的影响,并通过XRD、SEM、BET、XPS、NH_3-TPD和H_2-TPR等手段对催化剂进行了表征.结果表明,当Mn含量为9%,空速为45 000 h-1时,MnO_x/Al_2O_3催化剂NO_x脱除率最高,在220℃时达79%;9MnO_x/Al_2O_3催化剂表面MnO_x氧化物分散较均匀,且稳定性及抗H_2O性能较好,但抗SO_2性能有待提高;MnO_x/Al_2O_3催化剂孔径主要分布在4~20 nm范围内,Mn含量对催化剂孔径变化影响较小;催化剂中活性组分Mn主要以Mn~(3+)和Mn~(4+)的形式存在;Mn~(4+)和Oα含量增加有利于NO_x的脱除;且添加Mn后,活性酸位点的数量增长,增强了催化剂还原能力,促进了NO_x脱除率的增加.     

CeO2改性Ag-V2O5/TiO2催化剂的甲基吡啶氧化脱甲基性能

以锐钛矿TiO_2为载体,考察了CeO_2改性对Ag-CeO_2-V_2O_5/TiO_2催化3-甲基吡啶氧化脱甲基性能的影响,并优化了催化剂组成与制备条件.结果表明:Ce掺杂改性不仅能够与V物种作用形成Ce VO_4,而且促进V_2O_5分散,改善活性组分的氧化还原性能,从而提高3-甲基吡啶脱甲基转化率与选择性,改善Ag-V_2O_5/TiO_2催化性能.适宜的催化剂组成为V_2O_5负载量15%,Ce/V的摩尔比0.33,Ag质量分数1.0%.过高的焙烧温度将导致TiO_2载体向金红石型转变,Ag-CeO_2-V_2O_5/TiO_2适宜制备条件为450℃焙烧4 h.     

费-托合成Co/ZrO2-Al2O3催化剂反应性能的研究

以ZrOCl2·6H2O和AlCl3为原料，采用共沉淀方法制得一系列不同ZrO2质量分数的ZrO2-Al2O3混合氧化物载体；并以该混合氧化物为载体，采用初湿浸渍法制得钴质量分数为12％的Co/ZrO2-Al2O3催化剂。XRD、NH3-TPD、TPR和原位IR等表征结果表明，随着混合载体中ZrO2质量分数的增加，载体比表面积先增加后减少，混合载体的平均孔径则小于单一氧化物ZrO2和Al2O3的平均孔径。ZrO2和Al2O3载体混合后会导致氧化物的比表面积和酸性增大并且有新的物相生成。当混合氧化物用作载体时，能够抑制载体表面金属钴的分散，改变催化剂的还原行为，降低催化剂对CO物种的吸附能力。CO加氢反应表明，与单一金属氧化物相比，钴负载ZrO2-Al2O3混合氧化物催化剂的加氢活性和重质烃选择性有所降低。     

超细CuO/ZnO/TiO2-SiO2的表征和CO2加氢合成甲醇性能研究

用溶胶-凝胶法制备了铜、锌质量分数不同的超细Cu/ZnO/TiO2-SiO2催化剂。通过BET、TPR、XRD及FT-IR等方法对催化剂前驱体CuO/ZnO/TiO2-SiO2的物化性能进行表征。用固定床连续流动微反装置，考察催化剂CO2加氢合成甲醇的催化性能。研究结果表明，溶胶-凝胶法制备的CuO/ZnO/TiO2-SiO2催化剂比表面较大（240 m2/g～590 m2/g），孔径分布单一，晶相组成为CuO。随着铜、锌质量分数的增大，催化剂的比表面积减小，最可几孔径增大; CuO微晶结晶度增大,同时微晶尺寸逐渐增大至20 nm。催化剂具有较高的反应活性和选择性，当氧化铜、氧化锌质量分数各为25%时，在260 ℃，2 500 h－1，CO2∶H2=1∶3（mol比），2.0 MPa的反应条件下，甲醇时空收率为0.126g/(h·g)。     

TiO2负载Co2+、Cu2+催化剂的制备及其对甲酚催化氧化性能

用浸渍法制备了一系列以TiO2为载体的负载型催化剂,利用XRD和IR分析测试技术研究了负载Co2+与Cu2+后催化剂的表面结构,催化剂用于对甲酚氧化制备对羟基苯甲醛的反应中。 结果表明,n(Co2+)∶n(Cu2+)=1∶0.5时,催化剂的催化效果最佳。 在反应优化条件下,对甲酚的转化率可达100%,对羟基苯甲醛的选择性达95.2%。     

Effect of barium on reducibility and activity for cobalt-based Fischer-Tropsch synthesis catalysts

Barium modified Co/Al2O3 catalysts were prepared by incipient wetness impregnation. The catalysts were characterized by XRD, TPD and DRIFTS. The catalytic activity for Fischer-Tropsch synthesis was measured in a continuously stirred tank reactor. It was found that small amounts of BaO (≤ 2 wt%) improved the cobalt reducibility, which led to more cobalt active sites on the catalyst surface, and then resulted in higher CO conversion and C5+ selectivity. However, for the catalysts with high BaO loadings negative effects on the catalytic activity and selectivity for high hydrocarbons were observed because of low cobalt reducibility.     

X-ray absorption spectroscopy of Mn/Co/TiO2 Fischer-Tropsch catalysts: relationships between preparation method, molecular structure, and catalyst performance

The effects of the addition of manganese to a series of TiO(2)-supported cobalt Fischer-Tropsch (FT) catalysts prepared by different methods were studied by a combination of X-ray diffraction (XRD), temperature-programmed reduction (TPR), transmission electron microscopy (TEM), and in situ X-ray absorption fine structure (XAFS) spectroscopy at the Co and Mn K-edges. After calcination, the catalysts were generally composed of large Co(3)O(4) clusters in the range 15-35 nm and a MnO(2)-type phase, which existed either dispersed on the TiO(2) surface or covering the Co(3)O(4) particles. Manganese was also found to coexist with the Co(3)O(4) in the form of Co(3-x)Mn(x)O(4) solutions, as revealed by XRD and XAFS. Characterization of the catalysts after H(2) reduction at 350 degrees C by XAFS and TEM showed mostly the formation of very small Co(0) particles (around 2-6 nm), indicating that the cobalt phase tends to redisperse during the reduction process from Co(3)O(4) to Co(0). The presence of manganese was found to hamper the cobalt reducibility, with this effect being more severe when Co(3-x)Mn(x)O(4) solutions were initially present in the catalyst precursors. Moreover, the presence of manganese generally led to the formation of larger cobalt agglomerates ( approximately 8-15 nm) upon reduction, probably as a consequence of the decrease in cobalt reducibility. The XAFS results revealed that all reduced catalysts contained manganese entirely in a Mn(2+) state, and two well-distinguished compounds could be identified: (1) a highly dispersed Ti(2)MnO(4)-type phase located at the TiO(2) surface and (2) a less dispersed MnO phase being in the proximity of the cobalt particles. Furthermore, the MnO was also found to exist partially mixed with a CoO phase in the form of rock-salt Mn(1-x)Co(x)O-type solid solutions. The existence of the later solutions was further confirmed by scanning transmission electron microscopy with electron energy loss spectroscopy (STEM-EELS) for a Mn-rich sample. Finally, the cobalt active site composition in the catalysts after reduction at 300 and 350 degrees C was linked to the catalytic performances obtained under reaction conditions of 220 degrees C, 1 bar, and H(2)/CO = 2. The catalysts with larger Co(0) particles ( approximately >5 nm) and lower Co reduction extents displayed a higher intrinsic hydrogenation activity and a longer catalyst lifetime. Interestingly, the MnO and Mn(1-x)Co(x)O species effectively promoted these larger Co(0) particles by increasing the C(5+) selectivity and decreasing the CH(4) production, while they did not significantly influence the selectivity of the catalysts containing very small Co(0) particles.     

Role of Bismuth Oxide in Bi-MCo2O4（M=Co,Ni,Cu,Zn） Catalysts for Wet Air Oxidation of Acetic Acid

Two series of cobalt (Ⅲ)-containing spinel catalysts were prepared by the decomposition of the corre-sponding nitrates. The catalysts doped with bismuth oxide exhibit a higher activity in the wet air oxidation ofacetic acid than those without dopant bismuth oxide. The catalysts were investigated by XRD, TEM, ESR,UV-DRS and XPS, and the interaction between Co and Bi was studied as well. It has been found that nano-sized bismuth oxide is paved on the surface of cobalt spinel crystal and the structures of cobalt(Ⅲ)-containingspinel are still maintained. The shift of the binding energy of Bi4/7/2 is related to the catalytic activity of thesecatalysts doped with bismuth oxide.     

N_2O分解催化剂Co-Al尖晶石型复合氧化物制备参数的优化

以柠檬酸为配合剂,用溶胶-凝胶法制备了一组不同组成的Co-Al复合氧化物(CoAl_2O_4、CoCo0.5Al1.5O4、CoCoAlO_4、CoCo_(1.5)Al_(0.5)O_4、Co_3O_4),用于催化分解N_2O.用N_2物理吸附、X射线衍射(XRD)、扫描电镜(SEM)、H2程序升温还原(H2-TPR)、X射线光电子能谱(XPS)等技术对催化剂进行了结构表征,考察了复合氧化物组成、母液pH值、配合剂用量等制备参数对催化剂活性的影响.结果表明:用Al取代Co_3O_4中部分Co制备Co-Al复合氧化物,提高了催化剂的比表面积和催化活性,其中组成为CoCo_(1.5)Al_(0.5)O_4、母液pH=2、柠檬酸/金属离子(摩尔比)为1的催化剂活性较高.在CoCo_(1.5)Al_(0.5)O_4表面浸渍K2CO3溶液制得K改性催化剂,弱化了钴-氧化学键,提高了催化活性.其中0.02K/CoCo1.5Al0.5O4催化剂在有氧有水气氛400℃连续反应50h,N_2O转化率达97.1%.     

CoMo/ZrO2-Al2O3催化剂的制备及其加氢脱氧性能

以ZrOCl₂·6H₂O和Al₂(SO₄)₃为原料,采用超声波共沉淀法制得一系列不同ZrO₂质量分数的ZrO₂- Al₂O₃复合氧化物载体;并以该复合氧化物为载体,采用等体积浸渍法制得Co和Mo质量分数分别为6.0%和16.0%的CoMo/ZrO₂-Al₂O₃催化剂。BET、XRD、H₂-TPR和NH₃-TPD等表征结果表明,ZrO₂-Al₂O₃复合氧化物载体具有较高的比表面积与较大的孔容、孔径,随着复合载体中ZrO₂质量分数的增加,复合载体比表面积逐渐减小。ZrO₂-Al₂O₃复合载体能高度分散活性组分,钴钼负载量接近其在载体上的单层分散阈值。相比于CoMo/Al₂O₃,CoMo/ZrO₂-Al₂O₃催化剂具有较高的还原性能和较多的表面酸性活性中心,由此导致其在苯酚加氢脱氧(HDO)反应中,具有较高的加氢脱氧活性和苯选择性。
     

用不同前驱体制备的Co/SiO2催化剂的结构及其CO2/CH4重整反应性能

 分别采用硝酸钴、醋酸钴、硫酸钴和氯化钴为前驱体制备了Co／SiO2催化剂,用XRD,TPR,SEM和H2－TPD等实验技术考察了钴盐前驱体对催化剂结构和二氧化碳重整甲烷反应性能的影响,重点考察了硝酸钴和醋酸钴的作用．结果表明,由醋酸钴制备的Co／SiO2催化剂有最佳的催化活性和稳定性,它在钴物种的存在状态、金属－载体相互作用、钴金属晶粒度及抗烧结、抗积炭能力等方面,均与由硝酸钴制备的Co／SiO2催化剂存在显著的差别．Co／SiO2催化剂的反应活性和稳定性分别与其金属分散度和抗烧结、抗积炭能力密切相关．     

乙二醇促进制备高分散的Co/SiO2催化剂及其催化乳酸乙酯转化为1,2-丙二醇的气相加氢活性

研究了利用乙二醇共浸渍方法制备高分散的二氧化硅负载钴催化剂,该催化剂有效地提高了乳酸乙酯的气相加氢反应活性。系统地考察了钴金属负载量、乙二醇与硝酸钴摩尔比、醇种类和焙烧温度等制备参数对四氧化三钴纳米粒子物性的影响。乙二醇与硝酸钴摩尔比和醇种类对二氧化硅负载的四氧化三钴纳米粒子大小有显著影响。与常规的浸渍方法相比较,共浸渍过程中的乙二醇增强了二价钴粒子和载体二氧化硅之间的相互作用力,从而引起金属钴分散度的提高以及四氧化三钴纳米粒子粒径从16 nm降到5 nm以下;金属钴的高分散与无定型硅酸钴的形成密切相关;同时显著地提高了乳酸乙酯的加氢活性,在反应条件下(2.5MPa、160 ℃和10%(w,质量分数)Co/SiO₂)乳酸乙酯的转化率从69.5%提高到98.6%,1,2-丙二醇的选择性达到98.0%。利用X射线衍射(XRD)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、N₂吸脱附实验、H₂程序升温还原(H₂-TPR)等表征手段对共浸渍制备的Co/SiO₂催化剂结构和形貌进行了表征分析。