Ce0.67Zr0.33O2对CH4燃烧催化剂Fe2O3/Al2O3的改性作用

固定n(Ce)/n(Zr)比为0.67/0.33, 用共沉淀法制得一系列CeO2-ZrO2-Al2O3固溶体. 采用这些固溶体作载体, 以Fe2O3为活性组分, 用浸渍法制备了一系列催化剂. BET结果显示, 将适量Ce0.67Zr0.33O2引入到Al2O3载体中有助于催化剂保持较高的比表面积. TPR结果显示, 载体中引入适量的Ce0.67Zr0.33O2可以改善催化剂的氧化还原性能. XRD结果表明, Fe2O3在CeO2-ZrO2-Al2O3载体上呈现出良好的分散状况, 老化前后催化剂的晶相结构基本无明显变化. 特别是当载体中m(Ce0.67Zr0.33O2)∶m(Al2O3)的值为1∶2时, Fe2O3/CeO2-ZrO2-Al2O3催化剂在甲烷催化燃烧中显示出最佳的催化性能和抗高温老化性能.     

Ce0.67Zr0.33O2对CH4燃烧催化剂Fe2O3/Al2O3的改性作用

固定n（Ce）／n（Zr）比为0．67／0．33,用共沉淀法制得一系列CeO2-ZrO2-Al2O3固溶体,采用这些固溶体作载体,以Fe2O3为活性组分,用浸渍法制备了一系列催化剂,BET结果显示,将适量Ce0.67Zr0．33O2引入到Al2O3载体中有助于催化剂保持较高的比表面积,TPR结果显示,载体中引入适量的Ce0．67Zr0.33O2可以改善催化剂的氧化还原性能,XRD结果表明,Fe2O3在CeO2-ZrO2-Al2O3载体上呈现出良好的分散状况,老化前后催化剂的晶相结构基本无明显变化,特别是当载体中m（Ce0.67Zr0.33O2）：m（Al2O3）的值为1：2时,Fe2O3／CeO2-ZrO2-Al2O3催化剂在甲烷催化燃烧中显示出最佳的催化性能和抗高温老化性能。     

Pt/Ce0.6Zr0.4O2催化剂在水煤气变换反应中的电导研究

采用浸渍法制备了不同载体(Ce0.6Zr0.4O2,CeO2和ZrO2)负载的Pt基水煤气变换反应(WGSR)催化剂, 并对其进行了活性评价. 利用X射线衍射(XRD), 程序升温还原(TPR)和原位电导等技术对样品进行了表征. 结果表明, Ce0.6Zr0.4O2固溶体具有比CeO2更高的氧转移能力, 因此促进了Pt/Ce0.6Zr0.4O2催化剂的WGSR活性.     

纳米CeO2基固溶体催化柴油机碳颗粒物燃烧性能

采用柠檬酸溶胶鄄凝胶法制备CeO2基固溶体催化剂(Ce0.7Zr0.3O2-δ、Ce0.7Pr0.3O2-δ和Ce0.7Gd0.3O2-δ), 并考察了固溶体和三种常用载体(TiO2、SiO2和Al2O3)及其负载KNO3后的催化碳黑燃烧活性. 结果表明, CeO2基固溶体催化剂具有很高的催化燃烧活性, 其活性接近TiO2、SiO2和Al2O3负载30%KNO3催化剂的活性. 因为纳米CeO2基固溶体的形成, 提高了催化剂的抗烧结能力, 使氧更活泼, 从而提高氧化还原性能, 有利于碳颗粒燃烧. 由于CeO2基固溶体本身的高活性, 因此KNO3的添加不能明显提高CeO2基固溶体催化剂(尤其是Ce0.7Zr0.3O2-δ和Ce0.7Pr0.3O2-δ)的催化燃烧活性, 但KNO3能显著提高TiO2, SiO2和Al2O3的催化燃烧活性.     

Mn-Fe/Al2O3催化剂的低温脱硝性能研究

以Al_2O_3为载体,Fe、Mn为活性组分,采用浸渍法制备了Mn-Fe/Al_2O_3催化剂,研究了Mn-Fe/Al_2O_3催化剂的低温脱硝性能.实验结果表明,Fe负载量为7%时,7Fe/Al_2O_3催化剂显示出较佳的低温脱硝性能;添加Mn能明显改变7Fe/Al_2O_3催化剂低温脱硝性能,其中当Mn/Fe质量比为11∶7时,11Mn7Fe/Al_2O_3催化剂获得最佳低温脱硝效率.对催化剂的表征结果表明,比表面积和孔径的大小不是决定催化剂性能高低的主要因素;Mn O2和Fe2O3在x Mn7Fe/Al_2O_3催化剂中具有较强的相互作用,影响活性组分微观晶体结构,改善活性组分分散程度,从而提高了催化剂的低温脱硝性能;Fe的添加使催化剂表面酸性位点数目增加,从而提高7Fe/Al_2O_3催化剂的低温脱硝效率.添加Mn不仅增多了11Mn7Fe/Al_2O_3催化剂表面酸性位点数目增加,而且使催化剂表面出现新的中强性酸位点,使其低温脱硝效率进一步提高;经过详细分析,结果表明表面吸附氧Oβ、Mn4+和Fe3+的含量较高是11Mn7Fe/Al_2O_3催化剂脱硝活性较高的主要原因.     

CeO2改性Ag-V2O5/TiO2催化剂的甲基吡啶氧化脱甲基性能

以锐钛矿TiO_2为载体,考察了CeO_2改性对Ag-CeO_2-V_2O_5/TiO_2催化3-甲基吡啶氧化脱甲基性能的影响,并优化了催化剂组成与制备条件.结果表明:Ce掺杂改性不仅能够与V物种作用形成Ce VO_4,而且促进V_2O_5分散,改善活性组分的氧化还原性能,从而提高3-甲基吡啶脱甲基转化率与选择性,改善Ag-V_2O_5/TiO_2催化性能.适宜的催化剂组成为V_2O_5负载量15%,Ce/V的摩尔比0.33,Ag质量分数1.0%.过高的焙烧温度将导致TiO_2载体向金红石型转变,Ag-CeO_2-V_2O_5/TiO_2适宜制备条件为450℃焙烧4 h.     

纳米Ce 1-x ZrxO2催化剂上乙醇催化氧化发光研究

研究了纳米Ce 1-x ZrxO2上乙醇催化氧化发光特性, 重点考察了反应温度和催化剂组成［n(Ce)/n(Zr)］对发光强度的影响. 在相近的反应条件下研究了纳米Ce 1-x ZrxO2上乙醇催化氧化反应的活性、 选择性和可能的催化发光机理. 结果表明， 催化发光强度与催化反应中生成CH3CHO的产率有很好的顺变关系.     

Pt/γ-Al2O3/CexZr1-xO2催化剂低温催化燃烧去除饮食油烟

以CexZr1-xO2固溶体做载体,制备了系列Pt/γ-Al2O3/CexZr1-xO2催化剂(x=1,0.75,0.5,0.25,0).应用Brunauer-Emmet-Teller(BET)比表面积分析、X射线衍射(XRD)和H2程序升温还原(H2-TPR)等手段对催化剂进行相关表征,并系统研究了催化剂在饮食油烟催化燃烧中的催化活性.BET结果表叫催化剂的比表面积随Ce/Zr摩尔比的减小而减小.XRD结果表明贵金属Pt很好地分散在氧化铝和CexZr1-xO2固溶体上.H2-TPR结果发现催化剂Pt/γ-Al2O3/Ce0.5Zr0.5O2的还原峰面积最大且氧离子的流动性最好.催化活性研究结果表明Pt负载在CexZr1-xO2固溶体上有利于油烟的催化燃烧,降低了反应温度.随着CexZr1-xO2固溶体中Ce/Zr摩尔比的变化,催化剂的活性顺序为Pt/γ-Al2O3/Ce0.5Zr0.5O2＞Pt/γ-Al2O3/Ce0.25Zr0.75O2＞Pt/γ-Al2O3/Ce0.75Zr0.25O2＞Pt/γ-Al2O3/CeO2＞Pt/γ-Al2O3/ZrO2.     

富氧条件下Cu/Al2O3催化剂上C3H6选择性还原NO的研究

以Cu/Al2O3为催化剂,对富氧条件下C3H6为还原剂选择性催化还原NO反应进行了研究.活性评价结果表明,与高活性的Ag/Al2O3催化剂相比,Cu/Al2O3催化剂选择性还原NO的活性较低,NO的最高转化率仅为40%.在所考察的温度范围(473～723K)内,红外谱图中不存在有机含氮化合物(R—ONO和R—NO2)的特征振动吸收峰.作为反应中间体—NCO的前驱体,有机含氮化合物在Cu/Al2O3催化剂表面难以生成是造成催化剂选择性还原NO活性低的直接原因.在Cu/Al2O3催化剂上,NO2吸附能够优先发生,并以NO3-物种的形式覆盖在大部分催化剂表面.动态原位红外光谱实验发现,这种NO3-表面物种与C3H6的反应性较差,使生成有机含氮化合物的关键反应难以发生,但此时的催化剂表面有利于C3H6和O2的完全氧化反应,这是导致Cu/Al2O3催化剂选择性较低的根本原因.     

Pt/γ-Al2O3/CexZr1-xO2催化剂低温催化燃烧去除饮食油烟

以CexZr1-xO2固溶体做载体, 制备了系列Pt/γ-Al2O3/CexZr1-xO2催化剂(x=1, 0.75, 0.5, 0.25, 0). 应用Brunauer-Emmet-Teller (BET)比表面积分析、X射线衍射(XRD)和H2程序升温还原(H2-TPR)等手段对催化剂进行相关表征, 并系统研究了催化剂在饮食油烟催化燃烧中的催化活性. BET结果表明催化剂的比表面积随Ce/Zr摩尔比的减小而减小. XRD结果表明贵金属Pt很好地分散在氧化铝和CexZr1-xO2固溶体上. H2-TPR结果发现催化剂Pt/γ-Al2O3/Ce0.5Zr0.5O2的还原峰面积最大且氧离子的流动性最好. 催化活性研究结果表明Pt负载在CexZr1-xO2固溶体上有利于油烟的催化燃烧, 降低了反应温度. 随着CexZr1-xO2固溶体中Ce/Zr摩尔比的变化, 催化剂的活性顺序为Pt/γ-Al2O3/Ce0.5Zr0.5O2>Pt/γ-Al2O3/Ce0.25Zr0.75O2>Pt/γ-Al2O3/Ce0.75Zr0.25O2>Pt/γ-Al2O3/CeO2>Pt/γ-Al2O3/ZrO2.     

二氧化钛纳米粒子的合成及其催化降解酞酸酯类化合物的研究

采用四氯化钛控制水解合成了不同形貌的金红石型二氧化钛,考察了聚乙二醇-1000(PEG-1000)对产物形貌的影响,并用XRD,TEM和UV-Vis等手段对样品进行了表征.不同条件下的实验结果表明,不加PEG-1000时梭形二氧化钛随体系中酸度的增加和四氯化钛初始浓度的降低而团聚的倾向减缓,加入PEG-1000后,所得二氧化钛纳米粒子的粒径随PEG含量的增加而变小.对酞酸酯类(PEs)环境污染物的降解实验结果表明,通过此法合成的纳米级二氧化钛具有较高的催化活性.降解程度及降解产物用GC-MS进行检测.最后推导出PEs可能的降解过程.     

锐钛矿型纳米TiO2介孔粉体表面织构的研究

以硫酸钛和尿素为原料,聚乙二醇-1000为空间构造剂,104℃下经尿素水解均匀沉淀法研制颗粒分散均匀、粒径可控的高热稳定性锐钛矿型纳米TiO2介孔粉体,并对其晶相、颗粒大小、比表面积、形貌和孔道结构进行了表征.结果表明,未经任何热处理的TiO2粉体即为锐钛型晶相,颗粒为均匀分散的类球型颗粒,且颗粒间形成直通型的介孔孔道,其孔径在10～30nm之间.控制焙烧温度可以达到控制颗粒大小及形貌的目的,经850℃焙烧5h的样品仍保持锐钛矿型晶相,未出现向金红石型晶相转变的迹象.     

H_2O/TiCl_4/Py体系引发苯乙烯正离子聚合

研究了在少量吡啶(Py)存在下由水(H2O)四氯化钛(TiCl4)体系引发苯乙烯于二氯甲烷正己烷中进行碳正离子聚合,分别考察[Py]、[H2O]和[TiCl4]对聚合速率、产物分子量与分子量分布的影响.实验结果表明,少量亲核试剂吡啶(Py)对聚合反应起着重要作用,可有效地降低聚合速率和使分子量分布变窄;随着[H2O]和[Py]降低或[TiCl4]增加,聚合产物的分子量增加,而分子量分布指数(Mw Mn)基本维持在1.8左右;随着[Py]增加,聚合速率降低;随着[H2O]和[TiCl4]增加,聚合速率提高.聚合速率对单体浓度呈一级动力学关系,对Py、H2O和TiCl4的反应级数分别为-0.72、0.72和1.86.聚合速率对TiCl4浓度呈接近二级动力学关系,这可能与体系中TiCl4主要以二聚体形式存在有关.聚合转化率和产物分子量均随着反应时间延长而逐渐增大,PS的数均分子量与转化率呈线性增加关系.     

制备具有光催化活性的金红石相纳米氧化钛粉体

以TiCl4为原料，通过控制盐浓度和水解温度可以在温和条件下制备出晶粒尺 寸为6nm的金红石相氧化钛粉体，比表面积为175m^2/g。测定了粉体的X衍射、红外 和拉曼光谱。TEM照片显示粉体呈放射状颗粒，其粒径尺寸在200－400nm。苯酚的 光催化降解实验表明它比具有相同比表面积的锐钛矿粉体有更高的光催化活性。其 较大的团聚颗粒尺寸有利于光催化反应后的分离。     

Molecular selective photocatalysis by TiO2/nanoporous silica core/shell particulates

The coating of TiO(2) particles (P25) by a nanoporous silica layer was conducted to impart molecular recognitive photocatalytic ability. TiO(2)/nanoporous silica core/shell particles with varied pore diameters of the shell were synthesized by the reaction of P25 with an aqueous mixture of tetraethoxysilane and alkyltrimethylammonium chloride with varied alkyl chain lengths, followed by calcination. The TEM and nitrogen adsorption/desorption isotherms of the products showed that a nanoporous silica shell with a thickness of ca. 2nm and controlled pore diameter (1.2, 1.6, and 2.7 nm) was deposited on the titania particle when surfactants with different alkyl chain lengths (C12, C16 and C22) were used. The water vapor adsorption/desorption isotherms of the core/shell particles revealed that a larger amount of water adsorbed on the core/shell particles when the pore diameter is larger. The (29)Si MAS NMR spectra of the core/shell particles showed that the amount of surface silanol groups was independent of the water vapor adsorption capacity of the products. The possible molecular recognitive photocatalysis on the products was investigated under UV irradiation using two kinds of aqueous mixtures containing different organic compounds with varied sizes and functional groups: a 4-butylphenol, 4-hexylphenol, and 4-nonylphenol mixture and a 2-nitrophenol, 2-nitro-4-phenylphenol, and 4-nitro-2,6-diphenylphenol mixture. It was found that the core/shell particles exhibited selective adsorption-driven molecular recognitive photocatalytic decomposition of 4-nonylphenol and 2-nitrophenol in the two mixtures.     

Photodegradation of rhodamine B in aqueous solution via SiO2@TiO2 nano-spheres

Titania coated silica spheres (SiO₂@TiO₂) prepared by heterocoagulation of silica and titania nano-particles were investigated as catalyst in the photodegradation of rhodamine B (RB) in aqueous solution. The silica spheres were prepared by the well-known Stöber method and titania sol by a hydrolysis–condensation reaction in acidic media. The uncoated and coated particles were characterized by zeta potential measurements, acoustic attenuation spectroscopy and scanning electron microscopy. The degradation of the dye was induced by illuminating the coated spheres in aqueous solution with artificial solar light. The spectral distribution of the applied light corresponds to the sunlight spectrum on the earth's surface. Rhodamine B was used as model dye and decomposed completely to colourless end products after illumination. The decrease in concentration of rhodamine B was monitored by UV–vis spectroscopy and the total organic carbon (TOC) was determined in order to verify the degradation mechanism described elsewhere.     

TiCl_4共引发异丁烯正离子聚合合成反应活性聚异丁烯

由H2O/TiCl4/甲醇或乙醚体系引发异丁烯在二氯甲烷与己烷混合溶剂中进行正离子聚合,探讨甲醇用量、聚合时间等因素对正离子聚合以及产物分子量、分子量分布和末端基结构的影响,并在此基础上探讨TiCl4共引发混合C4馏分中异丁烯选择性正离子聚合以制备活性聚异丁烯的可行性.结果表明,含氧试剂对聚合反应起到明显的调节作用,可适当稳定碳正离子活性中心,降低链增长速率,降低聚合产物的分子量(Mn=1600~4600),使分子量分布明显变窄(Mw/Mn=1.35~2.05),并可调节大分子链末端基结构及其含量.降低聚合体系中微量单体浓度以及适当延长聚合反应时间,均有利于提高聚异丁烯大分子链末端α-双键结构含量.通过TiCl4共引发异丁烯正离子聚合制备出末端α-双键含量可以达到70%以上的低分子量高反应活性聚异丁烯.此外,该引发体系还可引发混合C4馏分原料中异丁烯进行高选择性正离子聚合,得到Mn=2000、Mw/Mn=2.59、端基α-双键含量为38.9%的聚异丁烯.     

Synthesis of Submicron-Sized Titania-Coated Silica Particles with a Sol-Gel Method and Their Application to Colloidal Photonic Crystals

A previously proposed method for preparing monodispersed titania particles was extended to preparation of titania-coated silica spherical particles. The core silica particles with an average size of 264 nm were prepared with Stöber method. The titania-coating was performed in ethanol/acetonitrile solvent in the presence of silica particles by a sol-gel method with the use of titanium tetraisopropoxide (TTIP) and methylamine (MA) catalyst. Average size of the silica-titania particles decreased from 457 to 292 nm with an increase in concentration of silica particles. Coefficient of variation for the particle size was less than 5%. Colloidal crystals could be fabricated with a dip-coating technique and a sedimentation process, respectively. Measurements of reflectance revealed peaks based on the Bragg diffraction. Those peaks red-shifted with an increase in titania shell thickness because of a high refractive index of titania. Annealing at high temperature transformed crystal structure of titania shell from amorphous to anatase (500°C) and rutile (1000°C), which led to red-shift of reflection peak because of an increase in refractive index of titania due to the crystallization.     

纳米TiO2 的制备及其光催化降解性能

采用低温水解沉淀法以TiCl4为原料制备了纳米TiO2,其结构经TEM和XRD表征。研究了太阳光激发下纳米TiO2对甲基橙的光催化降解性能,结果显示：纳米TiO2的分散性越好,粒径越小,光催化降解能力越强;以锐钛矿为主的复合纳米TiO2晶体比纯锐钛矿晶相具有更优异的光催化活性。     

HES/TiCl_4体系引发异丁烯可控正离子聚合

由六官能团引发剂环氧化角鲨烯(HES)与TiCl4组成引发体系,引发异丁烯(IB)在CH2Cl2/n-Hex(40/60,V/V)混合溶剂中进行正离子聚合,分别探讨了HES和2,6-二甲基吡啶(DMP)用量对IB正离子聚合转化率、产物分子量及其分布的影响.结果表明HES和微量水均可与TiCl4发生络合,并分别形成碳正离子和质子两种引发活性中心,导致聚合产物GPC谱图呈明显双峰分布.增加引发剂HES用量([HES]=2.64mmol/L),可以减少聚合体系中微量水的不可控引发,提高HES引发效率;在聚合体系中引入少量DMP时,可明显地减少微量水的不可控引发和提高HES的引发效率,使得即使在较低HES用量下([HES]=0.084mmol/L),也可达到主要由HES引发IB正离子聚合,制备出官能叔氯末端的六臂星形支化遥爪聚异丁烯,GPC谱图呈现单峰分子量分布,分布指数为1.5左右.