凝胶法制备条件对载体硅胶孔结构的影响

以水玻璃、硫酸为原料采用凝胶法制备了烯烃环氧化催化剂载体硅胶,为探讨制备条件对硅胶孔结构的影响,采用物理吸附仪对不同条件下制备的硅胶进行了表征,结果表明:溶胶pH值、老化温度和老化时间、氨水pH值对硅胶孔结构影响显著,当溶胶pH值为1.5,在80℃下用pH 10.5的氨水浸泡老化凝胶2 h,所得硅胶的比表面积在300 m2.g-1左右,孔径和孔容分别在9.71 nm和0.92 cm3.g-1以上,以此硅胶为载体制得的非均相催化剂Ti/SiO2对于氯丙烯和环己基过氧化氢的环氧化反应具有明显的催化活性。     

制备方法对CuO—Ce0．7Zr0．3O2催化剂的氧缺位和CO氧化活性的影响

采用溶胶-凝胶法和溶胶-凝胶 浸渍法两种方法制备了CuO-Ce0.7Zr0.3O2催化剂,并对催化剂进行了XRD、Raman等表征,考察了催化剂的CO氧化性能.研究结果表明,溶胶-凝胶法制备的CuO-Ce0.7Zr0.3O2催化剂的CO氧化活性明显高于溶胶-凝胶 浸渍法制备的CuO/Ce0.7Zr0.3O2催化剂,CuO-Ce0.7Zr0.3O2催化剂容易形成氧缺位和表面高分散CuO的颗粒较大,从而提高催化活性.     

过渡金属-铈基复合氧化物的制备与碳烟燃烧催化性能

采用溶胶凝胶法制备了不同过渡金属TM(Fe,Co,Ni,Mn)-Ce复合氧化物,并经800℃水热处理20 h后得到老化样品。利用XRD,BET对样品结构进行了表征,并采用CO-TPR和TPO分别考察了样品的还原性能和碳烟催化燃烧活性。结果表明,复合氧化物通过过渡金属和铈离子的变价和协同作用,有效地提高了催化剂的碳烟燃烧催化活性。在催化剂-碳烟松散接触条件和含NO+O2气氛下,由于催化剂表面氧的活化和硝酸盐分解释放的NO2,Co-Ce和Mn-Ce具有良好的碳烟燃烧活性。催化剂-碳烟紧密接触和含O2气氛中的活性则与催化剂的比表面积成正比关系,并受活性氧释放能力的影响。     

铁铈氧化物SCR脱硝催化剂的制备及性能

采用浸渍法制备了CeO₂-Fe₂O₃/TiO₂催化剂,研究了CeO₂负载量对其选择催化还原NO性能的影响,并将其中效果最好的催化剂按照同样组分配比采用溶胶凝胶法制备进行比较。采用BET、XRD、SEM和XPS等手段对催化剂进行表征。实验结果表明,采用浸渍法制备的负载10%CeO₂、3%Fe₂O₃的催化剂脱硝效率最优,最高可达96.65%。采用溶胶凝胶法制备催化剂效率更优,最高为99.36%。结果表明,浸渍法和溶胶凝胶法制备的10%-3%CeO₂-Fe₂O₃/TiO₂催化剂均具有较大的比表面积、活性成分分散度好、储氧能力强等优点。     

NiO-La_2O_3-Al_2O_3气凝胶催化剂的制备

采用改进的溶胶 -凝胶法和超临界干燥技术制备出超细三元 Ni O- L a2 O3 - Al2 O3 气凝胶催化剂 .通过 BET、TEM、XRD、DTA、IR等物性表征 ,考察了煅烧温度和组成等对气凝胶催化剂制备的影响 .结果表明 ,此种方法制备的多元气凝胶催化剂不仅保留了氧化铝和 Ni O- Al2 O3 气凝胶的主要特征 ,而且 ,氧化镧的加入使气凝胶更易晶化 ,热稳定性更好和吸附能力更强 .这种改进的溶胶 -凝胶法和超临界干燥技术操作简单有效 ,适合要求组分之间相互作用强、分布均匀、结构热稳定性好的多组元负载催化剂的制备 .     

二氧化硅负载磷钼酸铯催化苯液相硝化反应的研究

采用溶胶-凝胶法制备了二氧化硅负载磷钼酸铯催化剂,利用XRD、IR以及电位滴定等方法对催化剂进行了表征,并初步评价了催化剂的苯液相硝化反应催化性能。结果表明,溶胶-凝胶法制备的二氧化硅负载磷钼酸铯具有典型的Keggin结构,且在苯液相硝化反应中表现出优良的催化性能;催化剂用量、反应时间和温度等反应参数对催化苯液相硝化反应有明显的影响,在优化实验条件下,苯硝化转化率可达95%;催化剂可回收重复使用,多次反应后催化剂活性组分有所损失,但催化剂整体物相和结构没有发生明显变化。     

Mn/Ba/Al2O3催化剂的NOx氧化-储存和耐硫性能

采用分步等体积浸渍法制备了Mn/Ba/Al2O3催化剂, 并用XRD和TPD等方法进行表征. 考察了催化剂在不同温度下NOx氧化-储存特性和NOx脱附行为. 结果表明, Mn/Ba/Al2O3催化剂具有较高的催化NO氧化活性和较大的NOx储存容量. BaMnO3是主要的活性组分；Mn能够催化NO的氧化反应, 且具有一定的NOx储存能力; Ba是主要的储存组分, 将NOx以硝酸盐的形式储存; 硝酸盐在300～600 ℃分解, 释放出NOx. Mn/Ba/Al2O3催化剂在800 ℃老化6 h后, NO氧化活性和NOx储存能力稍有下降. 低含量的SO2对催化剂的NO氧化活性和NOx储存能力没有明显影响; 高含量的SO2使催化剂的NO氧化活性降低, NOx储存量减小, 最终导致催化剂失活.     

NiO－La2O3-Al2O3气凝胶催化剂的制备

采用改进的溶胶－凝胶法和超临界干燥技术制备出超细三元ＮｉＯ－Ｌａ２Ｏ３－Ａｌ２Ｏ３气凝胶催化剂。通过ＢＥＴ、ＴＥＭ、ＤＴＡ、ＩＲ等物性表征,考察了煅烧温度和组成等对气凝胶催化剂制备的影响。结果表明,此种方法制备的多元所凝胶催化剂不仅保留了氧化铝和ＮｉＯ－Ａｌ２Ｏ３气凝胶的主要特征,而且,氧化镧的加入使气凝胶理易晶化,热稳定性更好和吸附能力更强。这种改进的溶胶－凝胶法和超临界干燥技术操作简单有效,适     

推荐一个工科大学化学实验

推荐一个工科大学化学实验———BaTiO3 纳米粉的溶胶 凝胶法制备及其表征。该实验以钛酸四丁酯和醋酸钡为原料 ,正丁醇为溶剂 ,利用溶胶 凝胶法 ,基于DTA曲线适当的热处理条件下 ,制备BaTiO3 纳米粉 ,并进行了XRD分析 ,使学生对溶胶 凝胶法制备纳米粉和纳米粉的一般表征方法有了基本的认识和理解     

碘酸改性溶胶凝胶法制备CuO/CeO2催化剂及富氢条件下催化CO氧化

采用一种碘酸改性的柠檬酸溶胶-凝胶法制备了CuO/CeO₂催化剂, 研究其在富氢气氛中CO优先氧化反应(CO-PROX)的催化活性. 与传统柠檬酸溶胶-凝胶法制备的催化剂相比, 碘酸改性溶胶-凝胶法制备的催化剂活性更好. 程序升温还原、 X射线衍射、 透射电子显微镜和X射线光电子能谱等表征证明该催化剂粒径较小, 表面含有更多的Ce³⁺及还原性氧化铜物种, 有利于提高催化剂的催化活性.     

α-Amino acid derived enaminones and their application in the synthesis of N-protected methyl 5-substituted-4-hydroxypyrrole-3-carboxylates and other heterocycles

A new and simple synthesis of novel N-protected methyl 5-substituted-4-hydroxypyrrole-3-carboxylates, which exist in equilibrium with their 4-oxo tautomers, has been developed in two steps starting from N-protected α-amino acids. The key intermediates are enaminones, which can also be isolated, characterized, and used for the construction of other functionalized heterocycles, before they spontaneously decompose to pyrrole products. 4-Hydroxypyrroles are prone to partial aerial oxidation but can be efficiently alkylated or reduced to stable polysubstituted pyrrolidine derivatives.     

Specific intramolecular aromatic CH insertion of diazosulfonamides

The chemoselectivity in the intramolecular CH insertion of various diazosulfonamides has been experimentally studied. The results reveal that the aliphatic 1,4-, 1,5-, or 1,6-C(sp³)?H insertions of diazosulfonamides are not accessible, while the aromatic 1,5-C(sp²)?H insertion can be realized specifically by adjusting the diazo-adjacent group. In addition, the general chemoselectivities in the intramolecular CH insertions of diazosulfonyl compounds are summarized. Generally, diazosulfones undergo both aromatic 1,5-C(sp²)?H and aliphatic 1,5- and 1,6-C(sp³)?H insertions, while diazosulfonates undergo aliphatic 1,5- and 1,6-C(sp³)?H insertions. However, diazosulfonamides only undergo aromatic 1,5-C(sp²)?H insertion.     

N-Heterocyclic carbene-palladacyclic complexes: synthesis,characterization and their applications in the C-N coupling and α-arylation of ketones using aryl chlorides

N-Heterocyclic carbene-palladacyclic complexes 3 were successfully achieved in a one-pot procedure under mild conditions. The structure of 3a was unambiguously confirmed by X-ray single crystal diffraction and it was an active catalyst in the Buchwald-Hartwig amination and α-arylation of ketones even at very low catalyst loadings (0.01?mol%).     

Iodine-mediated oxidative Pictet-Spengler reaction using terminal alkyne as the 2-oxoaldehyde surrogate for the synthesis of 1-aroyl-β-carbolines and fused-nitrogen heterocycles

An efficient iodine-mediated oxidative Pictet-Spengler reaction in dimethyl sulphoxide (DMSO) using terminal alkynes as the 2-oxoaldehyde surrogate for the synthesis of aryl (9H-pyrido[3,4-b]indol-1-yl)methanones is described. The scope of the protocol includes the total synthesis of Fascaplysin, Eudistomins Y₁ and Y₂. The methodology is extended for preparing pyrrolo[1,2-a]-quinoxaline and indolo[1,5-a]quinoxaline derivatives. The utility of 1-aroyl-β-carbolines was demonstrated by performing palladium-catalyzed β-carboline directed ortho-C(sp2)-H functionalization of the phenyl ring with thiomethyl (SMe) group using DMSO as source and for accessing 4-aryl-canthin-6-ones.     

Facile synthesis of bicyclic 1-arylpyrazol-5-ones

In this Letter, we described a facile method for constructing fused bicyclic 1-arylpyrazol-5-one ring system. We employed various methylene-containing carboxylic acids as the substrates and proved that the pyrazolone ring closure requires activated methylene group in intermediate II. Accordingly, a series of structurally diversified, fused bicyclic 1-arylpyrazol-5-ones was prepared in moderate to high yields using the requisite substrates.     

Synthesis of pyrrolo[1,2-a]pyrazines and pyrazino[1,2-a]indoles by Curtius reaction in Morita-Baylis-Hillman derivatives

Synthesis of substituted pyrrolo[1,2-a]pyrazines and pyrazino[1,2-a]indoles from the Morita-Baylis-Hillman derivatives of acrylates via saponification followed by Curtius reaction is described.     

正丁胺对激光染料荧光谱影响的研究

用正丁胺作为碳源,采用射频辉光放电制备碳膜,选用激光染料R6G和聚乙二醇混合液作为蒸气源,采用单源热蒸发,在蒸发室与染料同时沉积得到混合膜,用拉曼光谱和红外光谱分析了碳膜的结构和键合方式,分析表明:碳膜中存在胺基团和氢原子.混合膜的荧光谱测量结果表明,认为正丁胺对染料荧光谱的影响是因为胺基和氢原子的存在.     

Cu0-catalysed 1,3-dipolar cycloadditions of α-amino acid derived N,N-cyclic azomethine imines to ynones

A series of 20 CuAIAC reactions between eight 4-acylamino substituted pyrazolidine-3-one-1-azomethine imines and four terminal ynones were performed using Cu⁰ as catalyst. The corresponding fluorescent cycloadducts were obtained in very high yields upon simple workup. Thus, Cu-metal turned out to be a better catalyst than Cu^I in terms of yield and ease of isolation. Availability of azomethine imines, mild reaction conditions, and simple workup enable a “click” access to libraries of densely substituted 2,3-dihydro-1H,5H-pyrazolo[1,2-a]pyrazol-1-ones. Reactivity of differently substituted dipoles was evaluated experimentally and by quantum chemical methods (DFT).     

Synthesis and antioxidative/anti-inflammatory activity of novel fullerene–polyamine conjugates

(E)-4-(Fullerenopyrrolidin-1-yl)-3-methylbut-2-enoic acid and its corresponding succinimidyl ester, readily obtained through Prato-type modification of C₆₀, were used for the selective N-acylation of polyamines. The thus obtained conjugates were evaluated for their antioxidative and anti-inflammatory activity and their cytotoxicity was determined. Members of this family of compounds showed interesting anti-lipid peroxidation, anti-lipoxygenase and anti-inflammatory activity and comparable cytocompatibility to spermidine.