VOx / Titanate复合材料纳米棒的水热合成及其电化学性能研究

Vanadium oxide/titanate composites nanorods (VO_x/ Titanate-CNRs) were synthesized in high yield by using titanate nanotubes as templates and V₂O₅·nH₂O sol as the precursors under hydrothermal conditions (200 ℃, 48 h). Samples were characterized with X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and energy dispersive analysis by X-ray (EDAX). X-ray diffraction structure determination showed that this new phase had the composition of V₃O₇·H₂O and crystallized with orthorhombic symmetry. SEM and TEM tests showed that the samples were uniform straight rods with the diameter range from around 100 to 300 nm and the length over 10 μm. The chemical compositions of the samples were determined with EDXA. The electrochemical tests of samples (titanates nanotubes, V₂O₅ and VO_x/ Titanate-CNRs) prove that VO_x/ Titanate-CNRs exhibit a better electrochemical performance.     

不同形态的α-Fe2O3纳米粉体的水热合成、表征及其磁性研究

Four different hematite (α-Fe₂O₃) nanopowders with various morphologies have been synthesized in the presence of surfactant (HPC) via hydrothermal route at 180 ℃, using four kinds of iron salts, Fe₂(SO₄)₃, FeC₂O₄, FeSO₄ and (NH₄)₃Fe(C₂O₄)₃, as precursor materials. The products were characterized by means of X-ray diffraction (XRD), transmission electron micrograph (TEM), Fourier transform infrared spectroscopy (FTIR) and magnetization measurements. The hysteresis measurements show that the products exhibit weak ferromagnetic property at room temperature. It is concluded that the different precursor materials and the presence of the surfactant are important factors that exert significant effects on the morphologies and magnetic properties of the products.     

La2O2S∶Mn2+荧光粉的微波合成及其荧光特性

Using La₂(SO₄)3 and the active carbon powder as reactants, La₂O₂S∶Mn²⁺ red phosphor was synthesized by microwave radiation method. The phosphor was characterized by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), laser-diffraction size analyzer and fluorospectrophotometer. The XRD analysis showed that the phosphor was pure phase La₂O₂S. The phosphor of La₂O₂S∶Mn²⁺ showed hexagonal crystal structure with diverse shapes, such as spherical and rod, with average particle size of 10.22 μm. The emission and excitation spectra of the phosphor were determined by fluorospectrophotometer and the results showed that the excitation spectrum of the phosphor under 600 nm emission wavelength was excitation bands between 250 nm and 350 nm with a peak value of 303 nm. Then ,when exicited under UV 303 nm, the phosphor showed broad band emission of 550~700 nm with a peak at 607 nm. In addition, the optimal effects were obtained for the phosphor preparation when the concentration of the activator Mn²⁺ was x_Mn=0.01, the ratio of C and O (n_C / n_O) in the reactants was 0.6∶1, and the time of reaction was about 1 h. La₂O₂S∶Mn²⁺ has strong absorption of UV spectrum and can emit bright red light.     

MgFe2O4纳米粉体的水热合成及其表征(英)

MgFe₂O₄ nanoparticles were hydrothermally synthesized at 150 ℃ using iron nitrate [Fe(NO₃)₃·9H₂O], magnesium nitrate [Mg(NO₃)₂·6H₂O] and sodium hydroxide (NaOH) as starting materials by carefully controlling the reaction conditions. The influences of several factors such as presence or absence of Na⁺, molar ratio of Fe³⁺ / Mg²⁺, concentration of mental ions, temperature and reaction time on resultant products were investigated in the hydrothermal process. The sample was characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM), and its magnetic properties were measured using vibrating sample magnetometer (VSM).     

球形α-Fe2O3纳米粉体的超声水解法合成与表征

Hematite (α-Fe₂O₃) nanopowder was synthesized from 0.1 mol·L^-1 FeCl₃ solution by sonochemical hydrolysis method, and characterized by X-ray diffraction (XRD), transmission electron micrograph (TEM), Fourier transform infrared (FTIR), Fourier transform Raman (FT-Raman) and X-ray photoelectron spectroscopy (XPS). The results showed that the spherical, well-dispersed α-Fe₂O₃ nanopowder was obtained with the average size of 20 nm. The possible mechanism for the formation of α-Fe₂O₃ nanoparticals was also discussed.     

In2O3八面体的碳还原法制备及其发光性能研究

In₂O₃ octahedrons were synthesized by carbothermal reduction using In₂O₃ nanoparticles as the source material. The as-synthesized products were characterized by X-ray powder diffraction (XRD), energy dispersive X-ray(EDX), scanning electron microscopy(SEM), transmission electron microscopy(TEM), high-resolution transmission electron microscopy (HRTEM), selected-area electron diffraction analysis(SAED) and Room-temperature photoluminescence(PL) spectroscopy. The results show that the products are single-crystalline In₂O₃ octahedrons, the length of the octahedrons is in the range of 400～3 000 nm; the PL patterns display two peaks located at 447nm and 555 nm upon excitation at 380 nm, and the other two peaks located at 444 nm and 550 nm upon excitation at 325 nm; the excitation pattern shows two peaks located at 274 nm and 371 nm, respectively. The growth mechanism of the In₂O₃ octahedrons is discussed, and the high supersaturation ratio is considered as the key factor.     

溶胶凝胶法制备Nd2O3改性钛酸钡陶瓷的研究

The technological condition for the preparation of BaTiO₃ ceramics doped with Nd₂O₃ by Sol-Gel was deter-mined through orthogonal experiment. When n_Ba(Ac)2∶n_Ti(OC4H9)4∶n_Nd2O3∶n_{CH3(CH2)2CH2OH}∶n_H2O=1.00∶1.00∶0.003∶7.30∶37.04, pH=3.5,T=25℃,the light-yellow-transparent-stable solution and thorough transparent gel was generat-ed, the transforming time of solution to gel was 25h. The crystal structure and particle size of BaTiO₃ ceramics doped with Nd₂O₃ were studied by SEM and X-ray respectively, the type of the crystal was tetragonal, the particle size was about 24.7nm. The dielectric constant (ε) and dielectric loss (tanδ) of BaTiO₃ ceramics doped with Nd₂O₃ were determined between 10⁴～10⁶Hz, and the results showed that the dielectric constant was increased obviously, the dielectric loss was decreased clear and the resistivity (ρ_V) was also decreased noticeably.     

Sr3Al2O6∶Eu2+红色发光纳米晶的新型形貌与发光性能的研究

A red luminescent Sr₃Al₂O₆∶Eu²⁺ nanocrystallites with new morphology were synthesized by sol-gel route assisted by microwave irradiation. The phosphor powders were characterized by X-ray diffraction (XRD)， scanning electron microscopy (SEM) and fluorescence spectroscopy. The results reveal that the calcination temperature of the Sr₃Al₂O₆∶Eu²⁺ phosphor crystallites greatly affects its morphology. With temperature increasing， the phosphor crystallites morphology showed primarily from nanorod-like， mixture of nanorod and flower-like to homogeneous flower-like morphology. The effects of new morphology on luminescent properties of phosphors were investigated. Uniformly dispersed flower-like Sr₃Al₂O₆∶Eu²⁺ phosphor powders showed the strongest luminescent intensity and the longest afterglow time.     

MgFe2O4-Fe2O3纳米粉体的软化学合成及电磁学特性

Nano-MgFe₂O₄-Fe₂O₃ magnetic powders were synthesized by citrate gel under microwave irradiation. The structure，particle size distribution，electromagnetic characteristics of nano-MgFe₂O₄-Fe₂O₃ were characterized by using TG-DTA, X-ray, electronic microscope, nano-size measurement and electromagnetism measurement apparatus。The results show that the product is a mixture of MgFe₂O₄ and Fe₂O₃ with average size of 44 nm, tanδ for the product is 0.265 and 0.610 at frequency of 1.0 GHz and 1.8 GHz respectively.     

二维层状结构十钒酸盐[K(H2O)2Ni(H2O)6]2[V10O28]的合成及性质(英)

A novel heteropoly compound, containing two kinds of coordinated cations, [K(H₂O)₂Ni(H₂O)₆]₂[V₁₀O₂₈], has been synthesized through routine process and characterized by elemental analyses, IR, ⁵¹V NMR and single crystal X-ray diffraction. It crystallizes in the triclinic system, space group P1 with a=0.87382(17) nm, b=1.075 4(2) nm, c=1.111 1(2) nm, α=65.10(3)°, β=75.01(3)°, γ=70.63(3)°, V=0.884 8(3) nm³ and Z=1. The X-ray analysis reveals that the two kinds of coordinated cations are linked by three shared coordinated water molecules, and K⁺ cations coordinate with ten oxygen atoms: five of which come from V₁₀O₂₈^6- anion, the other five from water molecules. The title compound exhibits extended 2D array building up of V₁₀O₂₈^6- groups connected by ten-coordinated K⁺ cations. The hexahydrated nickel cations Ni(H₂O)₆²⁺ lie in neat apposition to three adjacent V₁₀O₂₈^6- clusters. CSD: 413271.     

低温固相反应合成Li3V2(PO4)3正极材料及其性能

利用V₂O₅·nH₂O湿凝胶，LiOH·H₂O，NH₄H₂PO₄和C等作原料，通过低温固相还原反应在550 ℃焙烧12 h制备出Li₃V₂(PO₄)₃正极材料。采用XRD，SEM和电化学测试对Li₃V₂(PO₄)₃样品性能进行研究。XRD研究表明本法所合成的Li₃V₂(PO₄)₃同传统的高温固相反应法所合成的Li₃V₂(PO₄)₃一样同属于单斜晶系结构。SEM测试表明所合成的样品平均粒径大小约为0.5 μm且粒径分布较窄。电化学测试表明以0.2 C的倍率放电时，样品的首次放电容量为130 mAh·g^-1，室温下循环30次后其比容量为124 mAh·g^-1。     

新型笼状同多钒酸盐[Ni(1,10′-phen)3]2·[V2ⅣV8ⅤO26]的水热合成和晶体结构

尽管多金属氧酸盐(POMs)的研究已有180多年的历史, 但大量的POMs结构在最近几十年才被陆续解析出来[1～4].     

一维链状配位聚合物[Cu(en)2]2[Cu(en)2·α-AsⅢ8VⅣ14O42(HPO4)]·8H2O的合成与晶体结构

通过在As-V反应体系中加入H3PO4制得了内含HPO2-4基团的[As8V14O42(HPO4)]6-笼, 并对其结构进行了表征.     

长链烷胺及手性钛的螯合物Ti[(OC2H4)3N][OCH(CH3)2]在层状V2O5中的插层行为

用一种简便快速方法合成了一系列长链有机胺插层V₂O₅化合物. 用粉末X射线衍射(XRD)、红外光谱(FT-IR)、漫反射紫外-可见光谱(DR UV-VIS)等手段对插层产品的结构进行了表征. 除了正十六胺插层V₂O₅产品外, 其它长链烷胺插层V₂O₅产品的层间距d₀₀₁与长链烷胺碳数n之间具有良好的线性关系: d₀₀₁＝0.160n_C＋0.731 nm. 正十六胺与V₂O₅反应后生成两个插层相, 一个相的层间距d₀₀₁为4.01 nm, 另一相的d₀₀₁为3.20 nm. 此外, 研究了手性钛的螯合物Ti[(OC₂H₄)₃N][OCH(CH₃)₂] (记为TEAIP)在V₂O₅层间的插层行为, 得到相应的插层产品.     

Co3O4纳米片的制备及对H2O2电还原反应的催化性能简

通过恒电势电沉积和加热处理在泡沫镍基体上制备了Co3O4纳米片. 利用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X射线衍射(XRD)、傅里叶变换红外光谱(FTIR)和X射线光电子能谱(XPS)等手段对纳米片的形貌和结构进行了表征. 采用线性伏安扫描和计时电流技术研究了Co3O4纳米片电极对H2O2的电还原性能. 结果表明,在3.0 mol/L KOH 和 0.4 mol/L H2O2溶液中,当电压为-0.4 V(vs. Ag/AgCl)时,线性伏安扫描电流密度达到-0.386 A/cm2,在1000 s 测试时间内,计时电流密度衰减很小,表明Co3O4纳米片电极对H2O2具有很高的活性和稳定性.     

Ni(phen)(H2O)(V2O6)的水热合成和晶体结构（英）

A novel compound Ni(phen)(H₂O)(V₂O₆) has been hydrothermally synthesized and structurally determined to be a two-dimensional compound, which contains {V₂O₆}_n^2n- chains interconnected by nickel(Ⅱ) complexes via oxygen atoms. The crystallographic data measured by single-crystal X-ray diffraction analysis are as follows: C₁₂H₁₀N₂NiO₇V₂, M_r=454.81, monoclinic, space group P2₁/c, a=0.784 6(3), b=2.103 6(8), c=0.942 3(4) nm, β=112.872(5)°, V=1.433 0(10) nm³, Z=4, D_c=2.104 Mg·m^-3, μ(Mo Kα)=2.615 mm^-1, F(000)=904, T=298(2) K, 4 480 reflections collected, 2 470 independent (R_int=0.032 2), the final R=0.058 4 and wR₂=0.145 7 for 2 303 observed reflections with I>2σ(I). CCDC: 192520.     

鼓形有机锡氧杂环羧酸簇合物[PhCH2Sn(O)(O2CC4H3S)]6·2CH2Cl2 和 [PhCH2Sn(O)(O2CC3H2NO)]6·2CH2Cl2的合成和晶体结构

利用三苄基氧化锡与2-噻吩甲酸和2-唑甲酸反应,合成了六聚体苄基锡氧2-噻吩甲酸酯(1)和六聚体苄基锡氧2-唑甲酸酯(2)鼓形簇合物.通过元素分析、红外光谱和X射线单晶衍射对其结构进行了表征.测试结果表明:化合物1属三斜晶系,空间群p1,a=1.2760(3)nm,b=1.3056(3)nm,c=1.3343(3)nm,α=105.65(3)°,β=96.27(3)°,γ=97.20(3)°,Z=1,V=2.0997(7)nm3,Dc=1.809g/cm3,μ=2.097mm-1,F(000)=1116,R=0.0651,wR=0.1292.化合物2属三斜晶系,空间群p1,a=1.2240(4)nm,b=1.3673(4)nm,c=1.3744(4)nm,α=107.760(4)°,β=98.069(5)°,γ=91.480(5)°,Z=2,V=2.1631(12)nm3,Dc=3.373g/cm3,μ=3.799mm-1,F(000)=2136,R=0.0382,wR=0.079.它们均为鼓形簇状结构,锡原子呈畸变的八面体构型.化合物1通过分子间S…S近距离作用,形成一维链状结构.     

柠檬酸对Ni2P/TiO2-Al2O3催化剂加氢脱硫性能的影响

采用溶胶-凝胶法制备了TiO2-Al2O3复合载体,以柠檬酸(CA)为络合剂采用浸渍法制备了Ni2P负载的TiO2-Al2O3复合载体催化剂,并用X射线衍射(XRD)、N2吸附比表面积测定、H2程序升温氢还原(H2-TPR)、程序升温氧化(TPO)、X射线光电子能谱(XPS)技术对催化剂的结构和性质进行了表征,考察了CA/Ni摩尔比对在Ni2P/TiO2-Al2O3催化剂上进行的二苯并噻吩(DBT)加氢脱硫(HDS)性能的影响.结果表明:适量的CA可以丰富催化剂的孔道,提高催化剂的比表面积.当n(CA)/n(Ni)=2:1时,催化剂的比表面积达到126.75m2·g-1,与不加CA时相比,提高了57.05m2·g-1.调节n(CA)/n(Ni)能够改善活性相的分布,改变活性相的种类;引入CA使Ni和P前驱体的还原温度明显降低,促进活性相Ni2P的生成,一定程度上能够抑制催化剂表面炭的形成和沉积,提高其稳定性.n(CA)/n(Ni)=2:1时,催化剂具有最好的加氢脱硫活性,在360°C,3.0MPa,氢油比为500(V/V),液时体积空速为2.0h-1的条件下,二苯并噻吩转化率为99.5%,可将模拟油中硫含量由2%(w)降低到0.01%(w).     

Subsolidus Phase Relations in the ZnO-BaO-V2O5 System

The subsolidus phase relations of the ZnO-BaO-V2O5 ternary systems were investigated by means of X-ray diffraction analysis. There are three ternary compounds, nine binary compounds and sixteen 3-phase regions found in this system. The crystal structure of the ternary compound Ba2ZnV2O8 was refined by Rietveld profile fitting method and the powder diffraction pattern is given. A new ternary compound Ba3.4Zn0.8V4O14.2 has been found by the powder diffraction pattern.