Metathesis of Butylene-2 and Ethylene to Propylene over 3.0Mo/(Hβ+ γ-Al203) Catalysts with Different γ-Al203 Contents

A series of 3. 0Mo/(Hβ γ-Al2O3) samples with γ-Al2O3 contents in the range of 0-100% (mass fraction) was studied by means of XRD, NH3-TPD, TPR and BET determinations for characterizing their structures. The Hβ zeolite structure in the 3. 0Mo/Hβ sample can be effectively stabilized by adding some γ-Al2O3to Hβ zeolite. γ-Al2O3 mainly favors the formation of polymolybdate or multilayered Mo oxide, while Hβmainly forms the Al2(MoO4)3 species, as evaluated by the TPR technique. When used as the catalyst for the metathesis of butylene-2 and ethylene to propylene, there exists a close correlation between the specific surface area and stability of the catalyst. The specific surface area of the catalyst shows the maximum when (Hβ γ-Al2O3) contains 30%γ-Al2O3, which is in agreement with that of the time needed for the reaction stablization. In the case of maximum surface area, the rate of coke deposition is the minimum.     

Catalytic Combustion of Methane over MnOx／ZrO2-Al2O3 Catalysts

MnOx/Al2O3 and MnOx/ZrO2-Al2O3 catalysts were prepared by incipient wetness impregnation of Mn(CH3COO)2 on the corresponding supports, followed by the characterization using X-ray diffraction (XRD). temperature programmed reduction (TPR) and BET surface area techniques. The result shows the BET surface area of ZrO2-Al2O3 is lower than that of Al2O3 due to the loading of ZrO2.However tile resulted MnOx/ZrO2-Al2O3 catalyst exhibits higher activity for methane combustion than MnOx/Al2O3, because the addition of ZrO2 onto Al2O3 is beneficial for the dispersion of Mn species and the improvement of the lattice oxygen activity in MnOx. subsequently the activation of methane during combustion. The optimum loading of Zr in MnOx/ZrO2-Al2O3 is in the range of 5%-10% correlated with the calcination temperatures of catalyst supports.     

CH_4 reforming with CO_2 for syngas production over La_2O_3 promoted Ni catalysts supported on mesoporous nanostructured γ-Al_2O_3

Nanostructured γ-Al2O3 with high surface area and mesoporous structure was synthesized by sol-gel method and employed as catalyst support for nickel catalysts in methane reforming with carbon dioxide. The prepared samples were characterized by XRD, N2adsorption-desorption,TPR, TPO, TPH, NH3-TPD and SEM techniques. The BET analysis showed a high surface area of 204 m2 g-1and a narrow pore-size distribution centered at a diameter of 5.5 nm for catalyst support. The BET results revealed that addition of lanthanum oxide to aluminum oxide decreased the specific surface area. In addition, TPR results showed that addition of lanthanum oxide increased the reducibility of nickel catalyst. The catalytic evaluation results showed an increase in methane conversion with increasing lanthanum oxide to 3 mol% and further increase in lanthanum content decreased the catalytic activity. TPO analysis revealed that the coke deposition decreased with increasing lanthanum oxide to 3 mol%. SEM and TPH analyses confirmed the formation of whisker type carbon over the spent catalysts. Addition of steam and O2 to dry reforming feed increased the methane conversion and led to carbon free operation in combined processes.     

CH4 reforming with CO2 for syngas production over La2O3 promoted Ni catalysts supported on mesoporous nanostructured γ-A12O3

Nanostructured -y-A12O3 with high surface area and mesoporous structure was synthesized by sol-gel method and employed as catalyst support for nickel catalysts in methane reforming with carbon dioxide. The prepared samples were characterized by XRD, N2 adsorption-desorption, TPR, TPO, TPH, NH3-TPD and SEM techniques. The BET analysis showed a high surface area of 204 m2.g-1 and a narrow pore-size distribution centered at a diameter of 5.5 nm for catalyst support. The BET results revealed that addition of lanthanum oxide to aluminum oxide decreased the specific surface area. In addition, TPR results showed that addition of lanthanum oxide increased the reducibility of nickel catalyst. The catalytic evaluation results showed an increase in methane conversion with increasing lanthanum oxide to 3 mol% and further increase in lanthanum content decreased the catalytic activity. TPO analysis revealed that the coke deposition decreased with increasing lanthanum oxide to 3 mol%. SEM and TPH analyses confirmed the formation of whisker type carbon over the spent catalysts. Addition of steam and Oxide to drv reformin feed increased the methane conversion and led to carbon free ooeration in combined orocesses.     

Cross metathesis of butene-2 and ethene to propene overMo/MCM-22-Al_2O_3 catalysts with different Al_2O_3 contents

A series of 3.0Mo/MCM-22-Al2O3 catalysts with γ-Al2O3 contents in the range of 0-100 wt%were prepared and applied in the metathesis reaction of ethene and butene-2.Addition of γ-Al2O3 did not affect the structure of MCM-22 zeolite as evidenced by XRD and N2 adsorption measurements.It was deduced from TPR experiments that γ-Al2O3 phase favored the formation of polymolybdate or multilayered Mo oxide,while more Al2(MoO4)3 species were generated over MCM-22 zeolites.Alumina content in the support was directly related to the metathesis activity of ethene and butene-2 to propene.Mo species with higher valence(Mo6+or Mo5+)contributed more to the excellent performance of catalyst than metallic Mo.The best catalyst activity and stability was obtained over 3.0Mo/(MCM-22-30%Al2O3)under the reaction condition of 1.0 MPa and 125℃ using N2 as the pretreatment gas.     

硫化态三组元NiMoP/γ-Al2O3催化剂的TPR表征及噻吩HDS活性的研究

A series of sulfided tertiary NiMoP/γ-Al2O3 catalysts with different contents of MoO3 were prepared by using molybdophosphoric acid of Keggin structure(H3PMo12O40) and nickel nitrate as origins of active phase components of molybdenum, phosphorus and nickel, and characterized by TPR technique, with their HDS activity being investigated with thiophene as a model substrate. For the sulfided Mo-0 catalyst containing no nickel as promoter, the only hydrogen sulfide evolution peak Ⅰ　is observed at 462 K and attributed to the hydrogenation of the so-called edge sulfur atoms chemisorbed on coordinatively unsaturated(cus) Mox+ sites on the MoS2 phase(MoS2 slab). With the introduction of nickel into the active phase of the sulfided Mo-0 catalyst and with the increase of the molybdenum loading, a new hydrogen sulfide evolution peak Ⅱ gradually develops at the low temperature side of the peak Ⅰ, at the same time accompanied by both the increase of the area ratio of the peak Ⅱ to the peak Ⅰ and the shift of the hydrogen sulfide evolution maximum rate to lower temperatures, which may imply the existence of two kinds of active centers related to molybdenum and nickel respectively and the synergic action between the two centers above. It should be noted that for the sulfided NiMoP/γ-Al2O3 catalysts, the thiophene HDS rate and the quantity of hydrogen sulfide evolved during TPR process increase monotonously with the atomic ratio of molybdenum to nickel in the form of ［n(Ni)+n(Mo)］/n(Ni). On the basis of the results here, the conclusion may be reached that the two kinds of vacancies can be formed on the edge of Ni-Mo-S slab due to the loss of S during TPR process and vacancies or sites related to the H2S evolution peak II should be regarded as the mainly active reaction centers of thiophene HDS.     

Study of CO2 Hydrogenation to Methanol over Cu-V/γ-Al2O3 Catalyst

The effect of vanadium addition to CU/γ-Al2O3 catalyst used in the hydrogenation of CO2 to produce methanol was studied. It was found that the catalytic performance of the Cu-based catalyst improved after V addition. The influence of reaction temperature, space velocity and the molar ratio of H2 to CO2 on the performance of 12%Cu-6%V/γ-Al2O3 catalyst were also studied. The results indicated that the best conditions for reaction were as follows: 240℃, 3600 h-1 and a molar ratio of H2 to CO2 of 3:1. The results of XRD and TPR characterization demonstrated that the addition of V enhanced the dispersion of the supported CuO species, which resulted in the enhanced catalytic performance of CU-V/γ-Al2O3 binary catalyst.     

Carbon nanotubes decorated α-Al2O3 containing cobalt nanoparticles for Fischer-Tropsch reaction

A new hierarchical composite consisted of multi-walled carbon nanotubes (CNTs) layer anchored on macroscopic α-Al2O3 host matrix was synthesized and used as support for Fischer-Tropsch synthesis (FTS). The composite constituted by a thin shell of a homogeneous, highly entangled and structure-opened carbon nanotubes network and it exhibited a relatively high and fully accessible specific surface area of 76 m 2 g-1 , compared with that of 5 m 2 g-1 of the original α-Al2O3 support. The metal-support interaction between carbon nanotubes surface and cobalt precursor and high effective surface area led to a relatively high dispersion of cobalt nanoparticles. This hierarchically supported cobalt catalyst exhibited a high FTS activity along with an extremely high selectivity towards liquid hydrocarbons compared with the cobalt-based catalyst supported on pristine α-Al2O3 or on CNTs carriers. This improvement can attribute to the high accessibility of composite surface area comparing with the macroscopic host structure alone or to the bulk CNTs where the nanoscopic dimension induced a dense packing with low mass transfer which favoured the problem of reactants competitive diffusion towards the cobalt active site. In addition, intrinsic thermal conductivity of decorated CNTs could help the heat dissipating throughout the catalyst body, thus avoiding the formation of local hot spots which appeared in high CO conversion under pure syngas feed in FTS reaction. Cobalt supported on CNTs decorated α-Al2O3 catalyst also exhibited satisfied high stability during more than 200 h on stream under relatively severe conditions compared with other catalysts reported in the literature. Finally, the macroscopic shape of such composite easily rendered its usage as catalyst support in a fixed-bed configuration without facing problems of transport and pressure drop as encountered with the bulk CNTs.     

Pd/Hβ-zeolite catalysts for catalytic combustion of toluene: Effect of SiO2/Al2O3 ratio

The effect of pure and high silica Hβ zeolites on the catalytic performance of toluene combustion over Pd/H/3 catalyst was evaluated.Pure and high silica β zeolites were prepared by direct synthesis procedures,then 0.1 wt% of palladium was impregnated on different Hβ zeolites via incipient wetness technique using palladium nitrate as the Pd source.The Pd/Hβ catalysts were characterized by XRD,N2 adsorption/desorption,H2O adsorption,NH3-TPD,H2-TPR and XPS techniques.With increasing the SIO2/Al2O3 ratio of β zeolite,the activity of the Pd/Hβ catalysts for toluene combustion increased clearly and the pure silica β zeolite supported Pd catalyst showed the best catalytic activity.The superior catalytic performance of Pd/β catalyst prepared from pure silica β zeolite was attributed to its high hydrophobicity and the preserving ability for PdO active species.     

Gas Phase Selective Catalytic Oxidation of Toluene to Benzaldehyde on V2O5-Ag2O／η-Al2O3 Catalyst

Gas phase selective catalytic oxidation of toluene to benzaldehyde was studied on V2O5-Ag2O/η-Al2O3 catalyst prepared by impregnation. The catalyst was characterized by XRD, XPS, TEM,and FT-IR. The catalytic results showed that toluene conversion and selectivity for benzaldehyde on catalyst sample No.4 (V/(V Ag)=0.68) was higher than other catalysts with different V/Ag ratios. This was attributed to the higher surface area, larger pore volume and pore diameter of the catalyst sample No.4 than the other catalysts. The XRD patterns recorded from the catalyst before and after the oxidation reaction revealed that the new phases were developed, and this suggested that silver had entered the vanadium lattice. XPS results showed that the vanadium on the surface of No.4 and No.5 sample was more than that in the bulk, thus forming a vanadium rich layer on the surface. It was noted that when the catalyst was doped by potassium promoter, the toluene conversion and selectivity for benzalde hydewere higher than those on the undoped catalyst. This was attributed to the disordered structure of V2O5 lattice of the K-doped catalyst and a better interfacial contact between the particles.     

Pd/Hβ-zeolite catalysts for catalytic combustion of toluene:Effect of SiO_2/Al_2O_3 ratio

The effect of pure and high silica Hβ zeolites on the catalytic performance of toluene combustion over Pd/Hβ catalyst was evaluated.Pure and high silica β zeolites were prepared by direct synthesis procedures,then 0.1 wt% of palladium was impregnated on different Hβ zeolites via in-cipient wetness technique using palladium nitrate as the Pd source.The Pd/Hβ catalysts were characterized by XRD,N2 adsorption/desorption,H2O adsorption,NH3-TPD,H2-TPR and XPS techniques.With increasing the SiO2/Al2O3 ratio of β zeolite,the activity of the Pd/Hβ catalysts for toluene combustion increased clearly and the pure silica β zeolite supported Pd catalyst showed the best catalytic activity.The superior catalytic performance of Pd/β catalyst prepared from pure silica β zeolite was attributed to its high hydrophobicity and the preserving ability for PdO active species.     

Preparation and properties of magnetic alumina microspheres with a γ-Fe_2O_3/SiO_2 core and Al_2O_3 shell

Magnetic alumina composite microspheres with γ-Fe 2 O 3 core/Al 2 O 3 shell structure were prepared by the oil column method. A dense silica layer was deposited on the surface of γ-Fe 2 O 3 particles (denoted as γ-Fe 2 O 3 /SiO 2 ) with a desired thickness to protect the iron oxide core against acidic or high temperature conditions. γ-Fe 2 O 3 /SiO 2 /Al 2 O 3 particles with about 85 wt% Al 2 O 3 were obtained and showed to be suitable for practical applications as a magnetic catalyst or catalyst support due to their magnetic properties and pore structure. The products were characterized with scanning electron microscope (SEM) and transmission electron microscope (TEM), nitrogen adsorption-desorption, and vibrating sample magnetometer (VSM). The specific surface area and pore volume of the γ-Fe 2 O 3 /SiO 2 /Al 2 O 3 composite microspheres calcined at 500 ? C were 200 m 2 /g and 0.77 cm 3 /g, respectively.     

Study of The Pd-B/ γ-Al2O3 Amorphous Alloy Catalyst

The Pd-B/γ-Al2O3 amorphous alloy catalyst and Pd/γ-Al2O3 crystalline metal catalyst were prepared by KBH4 reduction and routine impregnation,respectively.Pd-B/γ-Al2O3 and Pd/γ-Al2O3 catalysts were characterized by XRD and SEM.It was found that the catalytic activity of the Pd-B/γ-Al2O3 amorphous alloy catalyst was higher than that of the Pd/γ-Al2O3 crystalline metal catalyst in the anthraquinone hydrogenation.     

Enhanced catalytic performance for direct synthesis of dimethyl ether from syngas over a La2O3 modified Cu-ZrO2/γ-Al2O3 hybrid catalyst

A series of hybrid catalysts were made by physically mixing Cu-ZrO 2 and γ-Al 2 O 3,for former it was modified with different loadings of La 2 O 3 prepared by co-precipitation method.The catalysts were characterized by BET,XRD,N 2 O-adsorption,EXAFS,H 2-TPR,NH 3-TPD techniques and evaluated in the synthesis of dimethyl ether from syngas.The results show that La 2 O 3 promoted catalysts displayed a significantly better catalytic performance compared with Cu-ZrO 2 /γ-Al 2 O 3 catalyst in CO conversion and DME selectivity,and the optimum catalytic activity was obtained when the content of La 2 O 3 was 12 wt%.The characterizations reveal that high copper dispersion,facile reducibility of copper particles and appropriate amount of acidic sites are responsible for the superior catalytic performance.     

Preparation of AgBiVMoO/γ-Al_2O_3 Catalysts for the Partial Oxidation of Propane to Acrylic Acid by the Mixed Sol Method

A novel mixed sol method was developed for the preparation of supported catalysts. Analyses by means of XRD and BET show that a 40%AgBiVMoO/γ-Al2O3 catalyst prepared by this method possessed high specific surface area and high dispersion of the active phase. As a result, high acrylic acid selectivity of 8.5% was obtained when the catalyst was used in the reaction of propane partial oxidation to acrylic acid in a fixed-bed reactor.     

Synthesis of Ni2P promoted trimetallic NiMoW/γ-Al2O3 catalysts for diesel oil hydrotreatment

The Ni2P promoted and γ-Al2O3 supported NiMoW sulfide catalyst consisting of 4 wt% Mo, 22 wt% W, 2 wt% Ni and 2.5 wt% Ni2P was synthesized by a co-impregnation method. The catalysts were characterized by N2 adsorption-desorption, X-ray diffraction (XRD), diffuse reflectance infrared Fourier transform (DRIFT) spectroscopy, NH3 temperature-programmed desorption (NH3-TPD) and transmission electron microscopy (TEM). The results showed that Ni2P, Ni, Mo and W species were highly dispersed over γ-Al2O3. The hydrodesulfurization (HDS) of dibenzothiophene (DBT) showed that the presence of Ni2P brought a strong promotional effect on the HDS activity, which was further confirmed by the HDS and hydrodenitrogenation (HDN) of diesel oil under industrial conditions. The enhancement in HDN activity and stability by Ni2P addition could be attributed more to the effect of new active sites of Ni2P than that of acidity modification. The as-prepared Ni2P-NiMoW/γ-Al2O3 catalyst showed better hydrotreating performance than NiMoW/γ-Al2O3 and commercial catalysts.     

Cross metathesis of butene-2 and ethene to propene over Mo/MCM-22-Al2O3 catalysts with different Al2O3 contents

A series of 3.0Mo/MCM-22-Al2O3 catalysts with γ-Al2O3 contents in the range of 0-100 wt% were prepared and applied in the metathesis reaction of ethene and butene-2. Addition of γ-Al2O3 did not affect the structure of MCM-22 zeolite as evidenced by XRD and N2 adsorption measurements. It was deduced from TPR experiments that γ-Al2O3 phase favored the formation of polymolybdate or multilayered Mo oxide, while more Al2(MoO4)3 species were generated over MCM-22 zeolites. Alumina content in the support was directly related to the metathesis activity of ethene and butene-2 to propene. Mo species with higher valence (Mo⁶⁺or Mo⁵⁺) contributed more to the excellent performance of catalyst than metallic Mo. The best catalyst activity and stability was obtained over 3.0Mo/(MCM-22-30%Al2O3) under the reaction condition of 1.0 MPa and 125 ℃ using N2 as the pretreatment gas.     

Syngas production by combined carbon dioxide reforming and partial oxidation of methane over Ni/α-Al2O3 catalysts

Ni/α-Al2O3 catalysts were found to be active in the temperature range 600~900 ℃ for both CO2 reforming and partial oxidation of methane. The effects of Ni loading, reaction temperature and feed gas ratio for the combination of CO2 reforming and partial oxidation of CH4 over Ni/α-Al2O3 were investigated. Catalysts of xwt%Ni/α-Al2O3 (x = 2.5, 5, 8 and 12) were prepared by wet impregnating the calcined support with a solution of nickel nitrate. XRD patterns and activity tests have verified that the 5wt%Ni/α-Al2O3 was the most active catalyst, as compared with the other prepared catalyst samples. An increase of the Ni loading to more than 5 wt% led to a reduction in the Ni dispersion. In addition, by combining the endothermic carbon dioxide reforming reaction with the exothermic partial oxidation reaction, the loss of catalyst activity with time on stream was reduced with the amount of oxygen added to the feed.     

Environment-friendly synthesis of N-phenylpiperidine from aniline and 1,5-pentanediol over γ-Al2O3 catalyst

An efficient environment-friendly synthesis of N-phenylpiperidine was developed from aniline and 1,5-pentanediol over γ-Al2O3 catalyst under atmospheric pressure. The conversion of 1,5-pentanediol reached 97% and the selectivity for N-phenylpiperidine attained 94%. The structure of the catalyst was characterized by NH3-TPD and BET. The influences of calcination temperature of the catalyst and reaction temperature on activity and selectivity of the catalyst were investigated.     

Methanation of carbon dioxide on Ni/ZrO2-Al2O3 catalysts:Effects of ZrO2 promoter and preparation method of novel ZrO2-Al2O3 carrier

The novel nickel-based catalysts with a nickel content of 12 wt% were prepared with the zirconia-alumina composite as the supports. The new carriers, ZrO2 improved alumina, were synthesized by three methods, i.e., impregnation-precipitation, co-precipitation, and impregnation method. The catalytic properties of these catalysts were investigated in the methanation of carbon dioxide, and the samples were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscope (XPS), temperature-programmed reduction (TPR) and temperature-programmed desorption (TPD) techniques. The new catalysts showed higher catalytic activity and better stability than Ni/γ-Al2O3. Furthermore, as a support for new nickel catalyst, the ZrO2-Al2O3 composite prepared by the impregnation-precipitation method was more efficient than the other supports in the methanation of carbon dioxide. The highly dispersed zirconium oxide on the surface of γ-Al2O3 inhibited the formation of nickel aluminate-like phase, which was responsible for the better dispersion of Ni species and easier reduction of NiO species, leading to the enhanced catalytic performance of corresponding catalyst.