Fe-Al-P-O催化剂的制备及其对丙烯环氧化反应的催化性能

 采用溶胶-凝胶法制备了Fe-Al-P-O催化剂,用N2物理吸附、透射电镜、红外光谱、 X射线衍射、程序升温脱附和微反技术研究了催化剂的物化性质和催化性能. 结果表明, Fe-Al-P-O催化剂平均粒径为20～40 nm, 比表面积为87 m2/g. 催化剂表面由Lewis酸位Fe3+和Al3+及Lewis碱位 P=O 构成. Fe-Al-P-O催化剂催化丙烯在临氧条件下选择氧化的产物主要是丙烯醛; 在临氢和氧条件下,选择氧化产物则以环氧丙烷为主. 适当条件下,丙烯转化率可达9.6%, 环氧丙烷的选择性大于63%. 在原料气中引入水蒸气可以降低副产物丙烯醛的产率.     

改性Ag/α-Al_2O_3催化丙烯气相环氧化反应

制备了以分子氧为氧化剂,对丙烯气相环氧化具有较好催化性能的改性负载银催化剂,并利用氧气程序升温脱附(O2-TPD)技术研究了氧在其表面上的脱附行为.实验结果表明:Ag/α-Al2O3催化剂只能使丙烯完全氧化成二氧化碳和水;当该催化剂用K2O改性后,可获得少量的环氧丙烷;Y2O3改性的Ag/α-Al2O3催化剂,可获得极少量的丙醛和丙酮;将0.1%(w)Y2O3添加到Ag-K2O/α-Al2O3后,可以显著提高催化剂的丙烯环氧化性能.在0.1MPa、245℃、20%C3H6/8%O2/72%N2和气体空速2000h-1的反应条件下,通过20%(w)Ag-0.1%Y2O3-0.1%K2O/α-Al2O3催化剂时,丙烯转化率为4.0%,环氧丙烷的选择性为46.8%.O2-TPD研究表明,少量的Y2O3、K2O或Y2O3-K2O作为助剂添加到20%Ag/α-Al2O3催化剂中时,减少了高温区与丙烯完全氧化有关的吸附氧物种的量,低温区余下的吸附氧物种量不变,有利于丙烯环氧化反应,提高了环氧丙烷的选择性.     

硫化CoMo催化剂上H2同时还原NO和SO2的研究I．H2还原NO反应

研究了Al2O3担载的硫化CoMo催化剂上NO被H2还原的规律，并考察了不同Mo含量的CoMo/Al2O3催化剂、单一的Mo／Al2O3和Co/Al2O3催化剂，以及原料气中H2／NO比对反应活性和选择性的影响。结果表明，硫化的5．1％C-15．2％Mo/Al2O3催化剂具有最高的催化活性和选择性，在200℃以下时反应产物为N2O，在350℃以上时则完全转化为N2．进一步增加Mo含量引起在350－450℃间N2选择性轻微下降，提高原料气中的H2含量可明显提高反应活性和N2选择性，但当n（H2）／n（NO）＞3后反应性能不再变化。催化剂具有较高的稳定性，反应产物中始终未观察到有H2S或SO2产生，即反应未引起催化剂中的晶格S流失。这说明H2的存在抑制了NO对硫化物表面的氧化所导致的催化剂失活。     

Fe-Al-P-O催化1,2-二氯丙烷与水环氧化制环氧丙烷反应机理

 采用溶胶-凝胶法制备了非晶态Fe-Al-P-O催化剂,并用IR,XRD,TEM,N2吸附及微反等技术对其组成、结构特性以及催化性能进行了表征和评价,通过IR和TPD-MS等技术着重研究了其化学吸附性能,探讨了表面催化反应的机理. 结果表明,Fe-Al-P-O催化剂是FePO4和AlPO4均匀混合形成的非晶态混合物,能够促进1,2-二氯丙烷和水反应高选择性地生成环氧丙烷,其Lewis酸位的Fe3+和Lewis碱位P=O的O2-是催化剂表面的主要活性位,能使水进行解离吸附并形成Fe-O-和P-OH 键. 1,2-二氯丙烷通过Cl-与P-OH键中的H+作用形成桥式吸附态是反应进行的关键.     

MoPO/SiO2催化剂上丙烷选择氧化制丙烯醛反应机理

 考察了丙烷以及丙烷选择氧化反应的有关中间体或其探针分子(如丙烯、烯丙醇、异丙醇和正丙醇)和产物(如丙烯醛、丙酮和丙醛)在MoPO/SiO2催化剂上的反应行为,用以探明该催化剂上丙烷选择氧化制丙烯醛反应的可能路径. 结果表明,异丙氧基是MoPO/SiO2催化剂上丙烷选择氧化制丙烯醛反应的主要中间体,异丙氧基脱β-H生成丙烯或脱α-H生成丙酮,而丙烯则经σ-氧烯丙基转化为丙烯醛.     

以N2O为氧化剂, Fe-P-O催化剂气相催化氧化苯制苯酚的研究

考察了应用N2O为氧化剂，FePO4、FePO4／SiO2、Fe0．5Al0.5PO4为催化剂气相催化氧化苯制苯酚的反应。在450℃下，FePO4催化剂上苯的转化率为2％，苯酚的选择性为85%；FePO4／SiO2(5％)催化剂上苯的转化率约为7％，苯酚的选择性为89％．Fe0．5Al0.5PO4催化剂可以使反应温度降低约100℃，350℃下反应苯的转化率为3．5％，苯酚的选择性为60％．分析表明，四面体结构的FeO4在该催化反应中具有重要的作用。     

固载化AlCl_3催化剂上α-蒎烯异构化反应

分别以SiO2和γ-Al2O3为载体采用两步气相法制备了固载化AlCl3催化剂,并首次将其用于α-蒎烯液相异构化反应.结果表明,该催化剂对α-蒎烯异构化反应具有非常高的催化活性,其中AlCl3/SiO2催化剂在40oC反应时α-蒎烯转化率和主产物(莰烯、柠檬烯和异松油烯)选择性分别为98.4%和93.7%;AlCl3/γ-Al2O3催化剂活性更高,在30oC反应时,即可获得95.5%的α-蒎烯转化率和94.4%的主产物选择性.固载化AlCl3催化剂的高活性与其强酸性有关.     

Te掺杂对MoPO/SiO2催化剂上丙烷选择氧化制丙烯醛反应的影响

 考察了Te的添加及Te含量对MoPO/SiO2催化剂催化丙烷选择氧化制丙烯醛反应性能的影响. MoPO/SiO2催化剂对丙烷选择氧化制丙烯醛反应的中间产物丙烯选择性较高,而Te的添加促进了丙烯向丙烯醛的转化. N2吸附、XRD、Raman、XPS、H2-TPR、丙烷脉冲、NH3-TPD和Py-IR等实验结果表明,催化剂添加Te后虽然比表面积有所下降,但单位比表面积上的酸量增加,催化剂低温可还原性得到改善,从而有利于丙烷的转化. Te可能有利于丙烯α-H的脱除和/或烯丙基的插氧反应.     

La2O3助剂对CH4部分氧化制氢Ni-Cu/ZrSiO催化剂的影响

用等体积浸渍法制备了ZrO2-SiO2(ZrSiO)表面复合氧化物负载的Ni-Cu双金属催化剂，并用TPR、XPS、IR、TPD及微反技术考察了稀土La2O3助剂对CH4和H2O在Ni-Cu/ZrSiO催化剂表面上的吸附及甲烷部分氧化制氢反应性能的影响。结果表明，加入La2O3助剂使催化剂表面Ni, Cu原子电子云密度增加，CH4和H2O在催化剂表面上的吸附增强；在反应温度450 ℃、进料摩尔比n-CH4∶nO2∶nH2O＝1∶0-5∶2-5以及甲烷空速SV(CH4)＝1 200 h－1的条件下，催化剂Ni-Cu-La2O3/ZrSiO上CH4转化率大于90％，生成H2的选择性高于99％，副产物CO的选择性仅为1.1％。根据实验结果，讨论了La2O3助催化剂的作用机理。     

丙烯、氧气和环氧丙烷在Cu-NaC1／SiO2催化剂上吸附的红外光谱研究

用红外光谱法研究了丙烯、丙烯／氧气混合气以及环氧丙烷(PO)在Cu-Nacl／SiO2催化剂上的吸附，结果表明，丙烯在载体和催化剂上的吸附是完全可逆的，丙烯和氧气在催化剂上共吸附后生成了丙烯醛，未观察到环氧丙烷(PO)生成，PO在载体和未还原催化剂上的吸附行为表明，PO与载体的硅羟基有强相互作用，PO发生开环反应生成开环物种，而PO在还原态催化剂上的吸附行为较复杂，可能生成了酮类化合物。     

Direct gas-phase epoxidation of propylene to propylene oxide using air as oxidant on supported gold catalyst

Gold catalysts supported on SiO2, TiO2, TiO2-SiO2, and ZrO2-SiO2 supports were prepared by impregnating each support with a basic solution of tetrachloroauric acid. X-ray diffraction （XRD）, transmission electron microscopy （TEM）, and X-ray photoelectron spectroscopy （XPS） techniques were used to characterize their structure and surface composition. The results indicated that the size of gold particles could be controlled to below 10 nm by this method of preparation. Washing gold catalysts with water could markedly enhance the dispersion of metallic gold particles on the surface, but it could not completely remove the chloride ions left on the surface. The catalytic performance of direct vapor-phase epoxidation of propylene using air as an oxidant over these catalysts was evaluated at atmospheric pressure. The selectivity to propylene oxide （PO） was found to vary with reaction time on the stream. At the reaction conditions of atmosphere pressure, temperature 325 ℃, feed gas ratio V（C3H6）/V（O2）= 1/2, and GHSV =6000h^-1, 17.9% PO selectivity with 0.9% propylene conversion were obtained at initial 10 min for Au/SiO2 catalyst. After reacting 60 min only 8.9% PO selectivity were detected, but the propylene conversion rises to 1.4% and the main product is transferred to acrolein （72% selectivity）. Washing Au/TiO2-SiO2 and Aa/ZrO2-SiO2 samples with magnesium citrate solution could markedly enhance the activity and PO selectivity because smaller gold particles were obtained.     

非晶态Fe0.5Al0.5PO4表面上激光促进甲烷直接氧化合成甲醇的研究

用溶胶—凝胶法合成了非晶态Fe0.5Al0.5PO4。用XRD和TPR表征了其结构和晶格氧的活性;用IR和TPD表征了CH4在其表面上的吸附行为;用LSSR方法考察了CH4直接氧化合成CH3OH的反应规律。结果表明,Fe0.5Al0.5PO4具有非晶态的结构,FePO4和AlPO4的微区被均匀地相互隔离,导致固体本身不具有长程有序性。非晶态的Fe0.5Al0.5PO4与晶态的Fe0.5Al0.5PO4相比,其晶格氧的活性大且活性氧的含量高。CH4以分子态吸附于固体表面P=O键上,非晶态Fe0.5Al0.5PO4表面上CH4的吸附强度和吸附量都较晶态Fe0.5Al0.5PO4上大。用1073 cm-1的激光激发固体表面P=O键,在100℃以上CH4的直接氧化反应顺利进行,CH3OH保持高选择性。在相同的反应条件下,非晶态Fe0.5Al0.5PO4能更有效地促进反应的进行,表明在激发相同表面化学键的情况下,固体表面材料的其它性质如粒度、比表面积和晶格氧的活性对反应也有一定程度的影响。     

钛硅分子筛中铝杂质对其性能的影响

 以四丙基溴化铵为模板剂,以硅溶胶为硅源,采用水热合成法制备了不同铝杂质含量的钛硅分子筛,并系统考察了铝杂质对钛硅分子筛性能的影响．结果表明,原料中的铝杂质可促进钛硅分子筛晶化,但同时也引入了酸性中心;在丙烯环氧化反应中,铝杂质形成的酸性中心会催化环氧丙烷与溶剂的副反应;加入少量碱性添加物可抑制铝杂质的酸催化作用,提高环氧丙烷的选择性,但过量碱性添加物会使钛硅分子筛失活．     

Effect of water on the ionothermal synthesis of molecular sieves

AlPO4-11 and AlPO4-5 molecular sieves are ionothermally prepared without addition of water by using anhydrous starting materials, such as NH4H2PO4, pseudoboehmite (AlOOH), and NH4F. The synthesis appears to be an autocatalytic process. Water has a remarkable effect on the synthesis process. Addition of reagent quantities of water (H2O/Al = 1, molar ratio) can enhance the crystallization kinetics greatly.     

Au／TS-1@Mesosilica双功能催化材料的制备及其催化丙烯直接环氧化性能

设计制备了一种新型微孔介孔复合核壳结构钛硅分子筛TS-1@Mesosilica（TS-l@Ms）,核为MFI结构钛硅分子筛TS-1,壳层为以非离子表面活性剂P123为模板剂组装形成的介孔氧化硅．壳层氧化硅具有三维蠕虫状孔道结构,有利于微孔和介孔部分的连通及反应物和产物的扩散．通过沉积沉淀法将金纳米粒子负载在壳层介孔孔道,和TS-1中的钛活性中心协同,形成适合于C3H6和H2、O2直接气相环氧化制备环氧丙烷（PO）的双功能催化材料．实验结果表明,Au／TS-1@MS在空速8000mLg-h、温度473K条件下连续反应132h,活性和选择性没有明显下降,丙烯转化率保持在3．7％左右,PO选择性87％以上．     

Modification of Cr/SiO2 for the dehydrogenation of propane to propylene in carbon dioxide

Summary Dehydrogenation of propane to propylene in carbon dioxide was investigated over promoted Cr/SiO2. The results showed that the catalysts were effective for the reaction and CO2 in the feed promoted the catalytic activity. XRD, TPR and microcalorimetric adsorption techniques were used to study the structure and surface acidity of the catalysts. It was found that the surface acidity decreased with the increase of K in the Cr/SiO2 and led to the increase of selectivity toward propylene. A propane conversion of 31% with 91% selectivity to propylene over the 5%Cr-0.4%K/SiO2 catalyst was observed at 923 K with CO2 /C3H8 molar ratio of 3.6.     

Fe1/2Al1/2PO4催化1,2-二氯丙烷脱氯氧化制备环氧丙烷

Fe1/2Al1/2PO4催化1;2-二氯丙烷脱氯氧化制备环氧丙烷     

Fe-P-O超细非晶态催化剂的制备与表征

共沉淀法;乙烷化学吸附;Fe-P-O超细非晶态催化剂的制备与表征     

弱酸性多级孔MFI沸石上甲醇转化制丙烯（英文）

使用葡萄糖辅助模板合成了H-[B,Al]-ZSM-5沸石并用于催化甲醇转化制丙烯。优越的丙烯选择性和活性持久性关联于有利于丙烯生成的高的弱酸/强酸比例以及有利于改善反应物扩散的防止快速积炭的高的介孔率。较多的位于MFI沸石直/正弦孔道的骨架铝增加了产物丙烯/乙烯比归因于促进的丙烯生成。低的酸密度有助于高的丙烯/乙烯比。B/Al比为2且（Al₂+B₂）/Si比为0.01的HZ5-G-2B样品用于甲醇制丙烯反应,在原料CH₃OH/H₂O（1∶1.2）重时空速为1.8 h^-1、480°C反应条件下,丙烯选择性为51.6%, C_2-4⁼烯烃选择性为83.7%,甲醇完全转化。丙烯/乙烯比为2。催化活性保持580 h稳定。