纳米固体超强酸SO42-/Fe2O3的制备及其催化合成乙酸乙酯

将Fe₂O₃纳米粉体经一定浓度的H₂SO₄浸泡活化后制成纳米固体超强酸SO₄^2-/Fe₂O₃,将其用于催化合成乙酸乙酯以考察其活性。利用均匀设计分析了超强酸制备过程及酯化反应过程中各因素的影响,研究结果表明较好的制备条件是:H₂SO₄浓度:2.5mol·L^-1;浸泡时间:1h;活化温度:167℃;活化时间:1h,此时获得的固体超强酸SO₄^2-/Fe₂O₃的粒径小于50nm。当催化剂用量为冰乙酸质量的5%,n(乙醇)∶n(冰乙酸)为3∶1,反应3.5h后乙酸的转化率高于80%。该催化剂经H₂SO₄溶液浸泡、活化再生后可重新使用,推断出其酸强度H₀<-14.5。     

纳米Fe3O4及Ni2+掺杂Fe3O4的制备、表征及吸附Pb(Ⅱ)的特性

采用一种改进的共沉淀法制备了纳米磁铁矿(Fe₃O₄)及Ni²⁺掺杂磁铁矿(Ni_xFe_3-xO₄,x=0.1,0.3,0.6),用X-射线衍射(XRD)、扫描电镜(SEM)、氮气物理性吸附、酸碱滴定等手段对产物进行了表征,用平衡吸附法研究了4种样品对Pb(Ⅱ)离子的吸附容量及吸附模型。结果表明,Fe₃O₄和3种Ni_xFe_3-xO₄均为近似球形的单相晶质纳米颗粒;与Fe₃O₄比较,Ni_xFe_3-xO₄的颗粒尺寸变小、表面电荷零点和pH＝5.0时的表面正电荷量降低;样品的孔体积、比表面积和表面分形度以及表面羟基含量都随产物中Ni²⁺掺杂量的增加而升高。4种样品对Pb(Ⅱ)的等温吸附数据均适合用Langmuir模型拟合(R₂=0.9942~0.9858),其相关系数的大小表现为:Fe₃O₄>Ni_0.1Fe_2.9O₄>Ni_0.3Fe_2.7O₄=Ni_0.6Fe_2.4O₄;Freundlich模型对样品等温吸附Pb(Ⅱ)的实验数据拟合度较低(R²=0.9813~0.9477),4种样品的Freundlich相关系数的大小关系与Langmuir相关系数相反。初始pH=5.0时,Fe₃O₄,Ni_0.1Fe_2.9O₄,Ni_0.3Fe_2.7O₄和Ni_0.6Fe_2.4O₄对Pb(Ⅱ)的最大吸附容量分别为6.02,6.68,7.29和8.34mg·g^-1。可见,Ni_xFe_3-xO₄(尤其是Ni²⁺掺杂量较高的产物)对水环境中重金属Pb(Ⅱ)的去除能力明显高于Fe₃O₄。     

纳米Fe3O4及Ni2 掺杂Fe3O4的制备、表征及吸附Pb(Ⅱ)的特性

采用一种改进的共沉淀法制备了纳米磁铁矿(Fe₃O₄)及Ni²⁺掺杂磁铁矿(Ni_xFe_3-xO₄,x=0.1,0.3,0.6),用X-射线衍射(XRD)、扫描电镜(SEM)、氮气物理性吸附、酸碱滴定等手段对产物进行了表征,用平衡吸附法研究了4种样品对Pb(Ⅱ)离子的吸附容量及吸附模型。结果表明,Fe₃O₄和3种Ni_xFe_3-xO₄均为近似球形的单相晶质纳米颗粒;与Fe₃O₄比较,Ni_xFe_3-xO₄的颗粒尺寸变小、表面电荷零点和pH＝5.0时的表面正电荷量降低;样品的孔体积、比表面积和表面分形度以及表面羟基含量都随产物中Ni²⁺掺杂量的增加而升高。4种样品对Pb(Ⅱ)的等温吸附数据均适合用Langmuir模型拟合(R²=0.9942~0.9858),其相关系数的大小表现为：Fe₃O₄>Ni_0.1Fe_2.9O₄>Ni_0.3Fe_2.7O₄=Ni_0.6Fe_2.4O₄;Freundlich模型对样品等温吸附Pb(Ⅱ)的实验数据拟合度较低(R²=0.981 3~0.947 7),4种样品的Freundlich相关系数的大小关系与Langmuir相关系数相反。初始pH=5.0时,Fe₃O₄,Ni_0.1Fe_2.9O₄,Ni_0.3Fe_2.7O₄和Ni_0.6Fe_2.4O₄对Pb(Ⅱ)的最大吸附容量分别为6.02,6.68,7.29和8.34 mg·g^-1。可见,Ni_xFe_3-xO₄(尤其是Ni²⁺掺杂量较高的产物)对水环境中重金属Pb(Ⅱ)的去除能力明显高于Fe₃O₄。     

Fe3+掺杂三维分级纳米Bi2WO6的合成及其光催化活性增强机理

利用水热法合成了Fe³⁺掺杂的三维分级纳米Bi₂WO₆,借助X射线衍射（XRD）、场发射扫描电镜（FE-SEM）、透射电镜（HRTEM）、能谱（EDS）、紫外可见漫反射（UV-Vis-DRS）等测试手段对所得样品的相组成、形貌和谱学特征进行了表征。选择罗丹明B为模型污染物研究所得样品在可见光下的催化活性。结果表明,Fe³⁺掺杂Bi₂WO₆为新颖的分级纳米结构,且Fe³⁺掺杂能有效提高Bi₂WO₆的光催化活性,Fe³⁺掺杂量对Bi₂WO₆活性的影响显著;实验结果还表明,所得Fe³⁺掺杂Bi₂WO₆催化剂的稳定性较好,易于回收。此外,还对Fe³⁺掺杂Bi₂WO₆的光催化活性增强机理进行了研究,缺电子的Fe³⁺作为电子捕获中心有利于促进光生电子-空穴对的分离,从而提高Bi₂WO₆的光催化活性。     

以Fe2P2O7为前驱体制备LiFePO4及其电化学性能

以磷铁废渣（Fe_1.5P）和温室效应气体CO₂为原料,以磷酸为补充磷源合成磷酸铁锂（LiFePO₄）的前驱体Fe₂P₂O₇,并研究了其合成过程对LiFePO₄正极材料储能性能的影响。采用SEM观察了LiFePO₄的表面形貌,采用XRD分析了LiFePO₄和Fe₂P₂O₇的晶体结构。进一步对该方法进行优化,发现Fe_1.5P与磷酸混合物（n_Fe1.5P：n_H3PO4=1：1）在800℃热处理6 h合成的Fe₂P₂O₇对应的LiFePO₄/C电化学性能最好,在0.1C,0.2C,0.5C和1C倍率下的容量分别可达130,126,117和108 mAh·g^-1。     

Ca2+-Mg2+-Zn2+体系在水溶性聚磷酸铵溶液中螯合规律的研究

近年来,水溶性聚磷酸铵在液体肥料和复合肥料的领域受到了广泛的关注,并在发达国家中得到了大面积的推广及应用。在pH值为5.5~8.0、温度为278.15 K~323.15 K的条件下,本文采用滴定法研究Ca_²⁺-Mg_²⁺-Zn_²⁺体系在聚磷酸铵溶液中的螯合规律。实验结果表明：相同质量分数的聚磷酸铵溶液对金属离子的螯合量会随着体系中Ca_²⁺、Mg_²⁺、Zn_²⁺的摩尔浓度的变化而变化;随着温度的升高而逐渐降低;随着pH的增加而逐渐增加;随着聚合度的升高而逐渐增加。采用傅里叶红外光谱对聚磷酸铵和A₁B₃C₃体系的螯合物进行表征。     

以Fe2P2O7为前驱体制备LiFePO4及其电化学性能

以磷铁废渣（Fe_1.5P）和温室效应气体CO₂为原料,以磷酸为补充磷源合成磷酸铁锂（LiFePO₄）的前驱体Fe₂P₂O₇,并研究了其合成过程对LiFePO₄正极材料储能性能的影响。采用SEM观察了LiFePO₄的表面形貌,采用XRD分析了LiFePO₄和Fe₂P₂O₇的晶体结构。进一步对该方法进行优化,发现Fe_1.5P与磷酸混合物（n_Fe1.5P：n_H3PO4=1：1）在800℃热处理6 h合成的Fe₂P₂O₇对应的LiFePO₄/C电化学性能最好,在0.1C,0.2C,0.5C和1C倍率下的容量分别可达130,126,117和108 mAh·g^-1。该方法具有成本低廉,减少碳排放和环境友好等特点,为LiFePO₄正极材料的生产提出了一种新的工艺。     

La7O6(BO3)(PO4)2:Eu3+/Tb3+荧光材料的制备及其光致发光性能

采用优化的高温固相方法制备了稀土离子Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂系荧光材料,并对其物相行为、晶体结构、光致发光性能和热稳定性进行了详细研究。结果表明,La₇O₆（BO₃）（PO₄）₂：Eu³⁺材料在紫外光激发下能够发射出红光,发射光谱中最强发射峰位于616 nm处,为⁵D₀→⁷F₂特征能级跃迁,Eu³⁺的最优掺杂浓度为0.08,对应的CIE坐标为（0.610 2,0.382 3）;La₇O₆（BO₃）（PO₄）₂：Tb³⁺材料在紫外光激发下能够发射出绿光,发射光谱中最强发射峰位于544 nm处,对应Tb³⁺的⁵D₄→⁷F₅能级跃迁,Tb³⁺离子的最优掺杂浓度为0.15,对应的CIE坐标为（0.317 7,0.535 2）。此外,对2种材料的变温光谱分析发现Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂荧光材料均具有良好的热稳定性。     

Fe2O3/Al2O3二元气凝胶合成高质量单壁纳米碳管

通过溶胶和超临界干燥方法制得了Fe₂O₃/Al₂O₃二元气凝胶，其比表面积和孔隙体积分别为246 m²·g^-1和1.89 cm³·g^-1，并具有较宽的孔径分布。以Fe₂O₃/Al₂O₃二元气凝胶作催化剂，通过甲烷催化裂解成功地合成了高质量的单壁纳米碳管。利用FESEM、TEM和HRTEM、Raman光谱等分析手段研究了反应温度对单壁纳米碳管生长的影响。结果表明在900 ℃时合成单壁纳米碳管的质量较高，并且合成的炭产物为毡状，该炭产物主要为高质量的单壁纳米碳管。     

SrAl2O4：Eu2+，Dy3+的助熔剂法制备及其发光特性

以B₂O₃为助熔剂，在1 350 ℃、还原性气氛下成功制备了SrAl₂O₄单相粉末样品。用同样的方法制备了系列单相Sr_1-x-yAl₂O₄：Eu²⁺_x，Dy³⁺_y·nB₂O₃(0.005≤x≤0.07， 0.01≤y≤0.05，0.05≤n≤0.25)样品并表征了其长余辉发光特性。结果表明，最佳的Eu²⁺含量为0.02。辅助激活离子Dy³⁺在Sr_0.98Al₂O₄：Eu²⁺_0.02中的掺杂在一定范围内可以显著提高亮度和余辉时间，最佳Dy³⁺含量为0.03。研究不同B₂O₃含量对Sr_0.95Al₂O₄：Eu²⁺_0.02，Dy³⁺_0.03发光性能的影响，结果说明最佳的B₂O₃含量为n=0.1，余辉肉眼可见(≥0.32 mcd·m^-2)时间达4 000 min。利用正电子湮灭技术和热释光技术，研究和讨论了B₂O₃对Sr_0.95Al₂O₄：Eu²⁺_0.02，Dy³⁺_0.03的发光和余辉性能的影响，结果表明B₂O₃的添加有助于Dy³⁺在晶格中形成深度合适、有益于余辉的空位缺陷。     

Cu/SO42-/La2O3-ZrO2-Al2O3催化剂的制备及其对C3H6选择还原NO的催化性能

以Al₂O₃为基质，添加ZrO₂和La₂O₃，制成La₂O₃-ZrO₂-Al₂O₃复合载体，然后采用SO₄^2-进行改性，再负载上Cu²⁺，制备了铜基SO₄^2-改性的复合载体催化剂(Cu/SO₄^2-/La₂O₃-ZrO₂-Al₂O₃)。考察了它在富氧条件下对丙烯选择还原NO的催化性能，并借助XRD、SEM、TG、Py-IR、NH₃-TPD、FTIR和TPR等方法研究了Cu/SO₄^2-/La₂O₃-ZrO₂-Al₂O₃的结构和性能的关系。结果表明，ZrO₂的加入主要有利于提高催化剂的低温活性；La₂O₃的加入则主要有利于提高催化剂的热稳定性和还原性能；SO₄^2-能够与Zr形成螯合双配位结构，大幅度促使催化剂表面酸量增加并且酸性增强；因此，有效地提高了Cu/SO₄^2-/La₂O₃-ZrO₂-Al₂O₃在富氧条件下对丙烯选择还原NO的催化活性和水热稳定性。在无水条件下，Cu/SO₄^2-/La₂O₃-ZrO₂-Al₂O₃能使NO的最大转化率高达84.3%，即使在275 ℃ 10%水蒸气存在的情况下，仍能使NO的转化率高达81.2%。     

Eu3+掺杂SiO2-B2O3-NaF玻璃的制备及发光性质

The Eu-doped SiO₂-B₂O₃-NaF glass was prepared by sol-gel process, using tetraethoxy Silicane, boric acid and sodium fluoride as starting materials, 0.10 mol·L^-1 EuCl₃ solution as the dopant. The luminescent properties of Eu³⁺ doped SiO₂-B₂O₃-NaF phosphors were investigated. The phosphors showed prominent luminescence in pink, the strong emission of Eu³⁺ comes from electronic transition of ⁵D₀- ⁷F₁（591 nm）and ⁵D₀- ⁷F₂（615 nm）,which derived from two transition modes of magnetic-dipole and electric-dipole .The peak intensity of 591nm in SiO₂-B₂O₃-NaF matrix is much stronger than it in the other matrixes, it means that SiO₂-B₂O₃-NaF has sensitization on the transition of ⁵D₀- ⁷F₁ (Eu³⁺). If there are broad bonds in the range of 275～380 nm in the excitation spectrum of Eu³⁺ -doped SiO₂-B₂O₃-NaF glass, the emission peak intensity should be intensified. It is because the electron migration CT band of O^2--Eu³⁺. For all Eu³⁺ concentrations used, the investigation found that when the mass of fraction got to 29.19×10^-3, the luminescence intensity reached the summit. And there is a phenomenon of concentration quenching. Investigation with the same concentration of Eu³⁺ at different annealed temperature, we found that the sample annealed at 400 ℃, the luminescence intensity achieved its maximum value, and Eu³⁺ in this matrix had a phenomenon of temperature quenching. The structural characterization of these luminescent materials was carried by used XRD and TEM. The result showed that the phosphor was in amorphous phase.     

Ho3+/Yb3+共掺ZnO-Al2O3-GeO2-SiO2玻璃陶瓷的制备和上转换发光性质

综合ZnO-Al₂O₃-SiO₂系和锗酸盐玻璃陶瓷的优点,采用熔融-晶化法首次制备了Ho³⁺/Yb³⁺共掺以ZnAl₂O₄为主晶相的ZnO-Al₂O₃-GeO₂-SiO₂系玻璃陶瓷。因[GeO₄]四面体和[SiO₄]四面体都是玻璃网络形成体,讨论了GeO₂取代SiO₂对玻璃陶瓷样品硬度及发光性能的影响,最终确定GeO₂的取代量为10.55%（w/w）时,玻璃陶瓷综合性能最佳。在980 nm泵浦光的激发下,发现强的绿色（546 nm）和弱的红色（650 nm）上转换发光,并研究了不同Ho³⁺/Yb³⁺掺杂比对样品上转换发光的影响,最终结果表明当Ho³⁺/Yb³⁺掺杂比为1：11（n/n）时样品荧光强度最强,在绿色上转换发光材料方面具有潜在的应用。     

低温凝胶燃烧法合成Y2O3∶Er3+，Yb3+纳米晶上转换发光材料

分别以柠檬酸和甘氨酸为燃烧剂,采用低温凝胶燃烧法合成了Er³⁺、Yb³⁺共掺Y₂O₃纳米晶粉体。通过TG-DSC、XRD、SEM等分析手段对两种燃烧剂所对应的反应过程及纳米晶粉体的物理性能进行了分析,结果表明甘氨酸法具有更高的反应效率、更好的粉体分散性及粒径均匀性。在980 nm激光二极管(LD)激发下,对甘氨酸法所得样品的上转换发光性能分析表明,绿光和红光发射谱带分别来自于Er³⁺的⁴S_3/2/ ²H_11/2→ ⁴I_15/2和⁴F_9/2→ ⁴I_15/2跃迁。此外,对Er³⁺和Yb³⁺掺杂浓度、粉体煅烧温度对纳米晶样品上转换发光性能的影响进行了讨论。     

Fe3O4@SiO2@mTiO2介孔多功能纳米复合颗粒的制备及载药能力

以溶剂热法制备氨基功能化的Fe₃O₄纳米颗粒为磁核,结合溶胶-凝胶法和模板法在其表面先后包覆上致密的SiO₂层和介孔TiO₂层,制备了磁性-发光-微波热转换性-介孔结构为一体的多功能核-壳结构纳米复合颗粒,并对其结构、性能及载药能力进行了研究。XRD分析表明:Fe₃O₄表面包覆上了无定形结构的SiO₂和TiO₂。TEM照片表明:所得的纳米复合颗粒具有明显的核壳结构和完美的球形,构成核的Fe₃O₄颗粒的尺寸在40~50 nm之间,Fe₃O₄@SiO₂@mTiO₂核壳结构纳米复合颗粒的尺寸为60~70 nm,壳层厚度约10 nm,并可观察到壳层中清晰的孔状结构。磁性、荧光光谱和微波热转换特性分析表明:该复合颗粒同时具有良好的发光性、磁性和微波热转换特性。N₂气吸附及药物负载率分析表明,该复合颗粒具有较高的比表面积(640 m²·g^-1)和介孔结构(孔径约2.8 nm)并且具有较高的药物负载率。     

CaSb2O6:Bi3+,Eu3+荧光粉的制备和发光性质

采用共沉淀法及1 200 ℃后续煅烧4 h,成功制备了CaSb₂O₆:Bi³⁺,Eu³⁺荧光粉,并对其结构及发光性能进行了研究。所制备荧光粉颗粒为六边形类圆饼状,平均尺寸在100~600 nm之间。对CaSb₂O₆:Bi³⁺,Eu³⁺发光的机理分析表明,Bi³⁺对Eu³⁺的发光存在高效的敏化与能量传递。当Bi³⁺和Eu³⁺的掺杂浓度分别为0.5%和8%,Eu³⁺位于580 nm(⁵D₀→⁷F₀ )处的荧光发射显著增强,Bi³⁺,Eu³⁺共掺样品的荧光强度是CaSb₂O₆:Eu³⁺的10倍左右。调节Bi³⁺/Eu³⁺离子掺杂比,色坐标呈现了从蓝、白光到红光的变化,表明该荧光粉可分别作为蓝或红色荧光粉使用,甚至可实现从蓝、白光到红光的自由调控,这为白光LED荧光粉的发展提供了参考。     

纳米SrAl2O4∶Eu2+，Dy3+长余辉发光材料的制备与性能

采用水热-均匀共沉淀法制备了纳米SrAl₂O₄∶Eu²⁺,Dy³⁺长余辉发光材料。通过XRD、TEM、荧光光谱、热释光谱对其结构和性能进行分析。XRD结果表明所制备的SrAl₂O₄∶Eu²⁺,Dy³⁺纳米发光材料为单相,属单斜晶系。TEM测试表明纳米SrAl₂O₄∶Eu²⁺,Dy³⁺发光材料为规则的球状粒子,粒径为50~80 nm,且分散性良好。激发和发射光谱测试表明,样品的激发光谱是峰值在356 nm的连续宽带谱,发射光谱是峰值位于512 nm的宽带谱,与SrAl₂O₄∶Eu²⁺,Dy³⁺粗晶材料相比,激发和发射光谱都出现了“蓝移”现象。样品的热释光峰值位于358 K,适合于产生长余辉。     

棒状CuFe4Ox的可控合成及其异戊醇脱氢反应的催化性能

利用液相沉淀法可控合成了均匀的棒状CuFe₄O_x催化剂。通过原位X射线粉末衍射（XRD）、高分辨透射电子显微镜（TEM）及程序升温还原（TPR）等手段表征其晶相结构、形貌和还原性能。通过还原棒状CuFe₄O_x获得Cu⁰/Fe₃O₄纳米棒,原位X射线光电子能谱（XPS）用于确定Cu⁰/Fe₃O₄表面的相组成。通过液相沉淀法制备棒状CuFe₄O_x,在120℃保持3 h后加入Na₂CO₃溶液至pH等于9时所得棒状形貌最为规整。以异戊醇脱氢反应作为探针反应,比较了Cu⁰/Fe₃O₄纳米棒和Cu⁰/Fe₃O₄纳米颗粒的催化反应性能,发现Cu⁰/Fe₃O₄纳米棒比Cu⁰/Fe₃O₄纳米粒子具有更好的活性和稳定性,表明棒状Fe₃O₄担载的Cu纳米粒子具有更好的结构稳定性。     

复合催化剂上CO2加氢合成C2烃类

介绍了由CO₂+H₂合成C2⁺烃的几种复合催化剂体系的研究进展，比较和评价了复合催化剂体系的活性和选择性及对C2⁺烃类生成的影响。着重于复合催化剂体系对C4⁺烃的生成及产物分布的影响并简述反应机理。     

不同稀土改性SO42-/ZrO2催化剂的结构与性能表征

Solid superacid catalyst SO₄^2-/ZrO₂ was modified by different rare earth compounds and applied to the esterification of acetic acid and n-butanol. The effects of rare earth elements loading on the catalytic properties were studied and the correlation between the structure and properties was investigated by means of XRD, IR, UV, DTA and TG. The results show that the (NH₄)₂Ce(NO₃)₆ modification can enhance catalytic activity more and exhibit better stability than the other two compounds La(NO₃)₃ and Ce(NO₃)₃. Meanwhile,(NH₄)₂Ce(NO₃)₆ modification can restrain the loss of SO₄^2- efficiently. The optimum calcination temperature and molar ratio of Ce(NH)∶Zr for SO₄^2-/ZrO₂ catalyst modified by (NH₄)₂Ce(NO₃)₆ are 450 ℃ and 2, respectively.