以Fe2P2O7为前驱体制备LiFePO4及其电化学性能

以磷铁废渣（Fe_1.5P）和温室效应气体CO₂为原料,以磷酸为补充磷源合成磷酸铁锂（LiFePO₄）的前驱体Fe₂P₂O₇,并研究了其合成过程对LiFePO₄正极材料储能性能的影响。采用SEM观察了LiFePO₄的表面形貌,采用XRD分析了LiFePO₄和Fe₂P₂O₇的晶体结构。进一步对该方法进行优化,发现Fe_1.5P与磷酸混合物（n_Fe1.5P：n_H3PO4=1：1）在800℃热处理6 h合成的Fe₂P₂O₇对应的LiFePO₄/C电化学性能最好,在0.1C,0.2C,0.5C和1C倍率下的容量分别可达130,126,117和108 mAh·g^-1。该方法具有成本低廉,减少碳排放和环境友好等特点,为LiFePO₄正极材料的生产提出了一种新的工艺。     

纳米固体超强酸SO42-/Fe2O3的制备及其催化合成乙酸乙酯

将Fe₂O₃纳米粉体经一定浓度的H₂SO₄浸泡活化后制成纳米固体超强酸SO₄^2-/Fe₂O₃,将其用于催化合成乙酸乙酯以考察其活性。利用均匀设计分析了超强酸制备过程及酯化反应过程中各因素的影响,研究结果表明较好的制备条件是:H₂SO₄浓度:2.5mol·L^-1;浸泡时间:1h;活化温度:167℃;活化时间:1h,此时获得的固体超强酸SO₄^2-/Fe₂O₃的粒径小于50nm。当催化剂用量为冰乙酸质量的5%,n(乙醇)∶n(冰乙酸)为3∶1,反应3.5h后乙酸的转化率高于80%。该催化剂经H₂SO₄溶液浸泡、活化再生后可重新使用,推断出其酸强度H₀<-14.5。     

g-C3N4/CaTi2O5复合材料制备及其光催化性能

利用类石墨氮化碳（g-C₃N₄）和亚稳相钙钛氧化物（CaTi₂O₅）固相法制备C₃N₄/CaTi₂O₅复合材料。利用X射线衍射（XRD）、金相显微镜、扫描电子显微镜（SEM）及附带能谱分析仪（EDS）和N₂吸附-脱附对样品的显微结构和比表面积进行检测分析,并用紫外-可见吸收光度计（UV-Vis）测试了样品的光吸收性能,研究C₃N₄与CaTi₂O₅物质的量之比（n_C3N4/nCaTi₂O₅）对C₃N₄/CaTi₂O₅复合样品的物相结构和微观形貌的影响,同时考察C₃N₄/CaTi₂O₅复合样品在可见光照射下光催化降解罗丹明染料效果。实验结果表明：相比纯C₃N₄和CaTi₂O₅样品,C₃N₄/CaTi₂O₅复合样品在可见光下具有较高的光催化性能,随着n_C3N4/nCaTi₂O₅增加,样品的光催化降解率随之增加而后降低,当n_C3N4/nCaTi₂O₅=1：1时,样品的光催化降解率达到最大值99.5%,并且循环重复利用5次后,样品的光催化剂降解率仍几乎保持不变。复合样品光催化性能提高主要归因于复合能级结构有效地抑制了电子和空穴复合所致。     

MOF-1和Tb@MOF-1荧光探针的设计、合成及对痕量Cr2O72-、S2O82-离子的识别

采用5-（（4-吡啶基）甲氧基）-异烟酸（H₂PLIA）、1,3,5-三（1-咪唑基）-苯（TIB）合成了金属有机骨架[Cd （PLIA）（TIB）]_n （MOF-1）。MOF-1是具有理想一维孔道的二维结构化合物,其一维孔道由柔性三角形PLIA^2-配体和刚性三角形TIB配体间隔形成。利用MOF-1易掺杂的优势,采用后修饰合成策略制备了Tb@MOF-1。对MOF-1和Tb@MOF-1进行了基本表征及荧光探针性能研究。2种探针材料具有相同的结构。MOF-1和Tb@MOF-1分别对水溶液中的Cr₂O₇^2-和S₂O₈^2-离子具有较强荧光识别能力,均有响应时间快,稳定性、选择性、灵敏度高的特点。研究了MOF-1和Tb@MOF-1对Cr₂O₇^2-和S₂O₈^2-的荧光识别机理,其不同可能与Tb³⁺离子掺杂有关。     

Al3+掺杂对Li2FeSiO4结构和电化学性能影响的研究

以CH₃COOLi·2H₂O、C₆H₈O₇·H₂O、FeC₆H₅O₇·5H₂O、Al₂(SO₄)₃·18H₂O和C₈H₂₀O₄Si为起始原料,采用水热辅助溶胶凝胶法及二次煅烧合成了Li₂Fe_1-xAl_xSiO₄/C(x=0.00、0.01、0.03、0.05)正极材料。用IR、XRD、FE-SEM、EDS等方法对材料的晶体结构进行了表征,用ZetaPAL粒度分析仪测量了其粒径分布范围,用SQUID(超导量子干涉仪)测定了样品的磁性,用恒流充/放电对其电化学性能进行了测试。结果表明：n_乙酸锂∶n_柠檬酸=4∶1、掺Al³⁺量为3%,80 ℃回流24 h,350 ℃恒温煅烧5 h,700 ℃恒温13 h,所得试样颗粒集中分布在150 nm左右且未出现团聚。在0.1C(16 mA·g^-1)、0.2C、0.5C下的首次放电比容量为127 mAh·g^-1、103.6 mAh·g^-1和91 mAh·g^-1,15次循环后无明显衰减,具有很好的循环稳定性。     

纳米Fe3O4及Ni2 掺杂Fe3O4的制备、表征及吸附Pb(Ⅱ)的特性

采用一种改进的共沉淀法制备了纳米磁铁矿(Fe₃O₄)及Ni²⁺掺杂磁铁矿(Ni_xFe_3-xO₄,x=0.1,0.3,0.6),用X-射线衍射(XRD)、扫描电镜(SEM)、氮气物理性吸附、酸碱滴定等手段对产物进行了表征,用平衡吸附法研究了4种样品对Pb(Ⅱ)离子的吸附容量及吸附模型。结果表明,Fe₃O₄和3种Ni_xFe_3-xO₄均为近似球形的单相晶质纳米颗粒;与Fe₃O₄比较,Ni_xFe_3-xO₄的颗粒尺寸变小、表面电荷零点和pH＝5.0时的表面正电荷量降低;样品的孔体积、比表面积和表面分形度以及表面羟基含量都随产物中Ni²⁺掺杂量的增加而升高。4种样品对Pb(Ⅱ)的等温吸附数据均适合用Langmuir模型拟合(R²=0.9942~0.9858),其相关系数的大小表现为：Fe₃O₄>Ni_0.1Fe_2.9O₄>Ni_0.3Fe_2.7O₄=Ni_0.6Fe_2.4O₄;Freundlich模型对样品等温吸附Pb(Ⅱ)的实验数据拟合度较低(R²=0.981 3~0.947 7),4种样品的Freundlich相关系数的大小关系与Langmuir相关系数相反。初始pH=5.0时,Fe₃O₄,Ni_0.1Fe_2.9O₄,Ni_0.3Fe_2.7O₄和Ni_0.6Fe_2.4O₄对Pb(Ⅱ)的最大吸附容量分别为6.02,6.68,7.29和8.34 mg·g^-1。可见,Ni_xFe_3-xO₄(尤其是Ni²⁺掺杂量较高的产物)对水环境中重金属Pb(Ⅱ)的去除能力明显高于Fe₃O₄。     

纳米Fe3O4及Ni2+掺杂Fe3O4的制备、表征及吸附Pb(Ⅱ)的特性

采用一种改进的共沉淀法制备了纳米磁铁矿(Fe₃O₄)及Ni²⁺掺杂磁铁矿(Ni_xFe_3-xO₄,x=0.1,0.3,0.6),用X-射线衍射(XRD)、扫描电镜(SEM)、氮气物理性吸附、酸碱滴定等手段对产物进行了表征,用平衡吸附法研究了4种样品对Pb(Ⅱ)离子的吸附容量及吸附模型。结果表明,Fe₃O₄和3种Ni_xFe_3-xO₄均为近似球形的单相晶质纳米颗粒;与Fe₃O₄比较,Ni_xFe_3-xO₄的颗粒尺寸变小、表面电荷零点和pH＝5.0时的表面正电荷量降低;样品的孔体积、比表面积和表面分形度以及表面羟基含量都随产物中Ni²⁺掺杂量的增加而升高。4种样品对Pb(Ⅱ)的等温吸附数据均适合用Langmuir模型拟合(R₂=0.9942~0.9858),其相关系数的大小表现为:Fe₃O₄>Ni_0.1Fe_2.9O₄>Ni_0.3Fe_2.7O₄=Ni_0.6Fe_2.4O₄;Freundlich模型对样品等温吸附Pb(Ⅱ)的实验数据拟合度较低(R²=0.9813~0.9477),4种样品的Freundlich相关系数的大小关系与Langmuir相关系数相反。初始pH=5.0时,Fe₃O₄,Ni_0.1Fe_2.9O₄,Ni_0.3Fe_2.7O₄和Ni_0.6Fe_2.4O₄对Pb(Ⅱ)的最大吸附容量分别为6.02,6.68,7.29和8.34mg·g^-1。可见,Ni_xFe_3-xO₄(尤其是Ni²⁺掺杂量较高的产物)对水环境中重金属Pb(Ⅱ)的去除能力明显高于Fe₃O₄。     

棒状CuFe4Ox的可控合成及其异戊醇脱氢反应的催化性能

利用液相沉淀法可控合成了均匀的棒状CuFe₄O_x催化剂。通过原位X射线粉末衍射（XRD）、高分辨透射电子显微镜（TEM）及程序升温还原（TPR）等手段表征其晶相结构、形貌和还原性能。通过还原棒状CuFe₄O_x获得Cu⁰/Fe₃O₄纳米棒,原位X射线光电子能谱（XPS）用于确定Cu⁰/Fe₃O₄表面的相组成。通过液相沉淀法制备棒状CuFe₄O_x,在120℃保持3 h后加入Na₂CO₃溶液至pH等于9时所得棒状形貌最为规整。以异戊醇脱氢反应作为探针反应,比较了Cu⁰/Fe₃O₄纳米棒和Cu⁰/Fe₃O₄纳米颗粒的催化反应性能,发现Cu⁰/Fe₃O₄纳米棒比Cu⁰/Fe₃O₄纳米粒子具有更好的活性和稳定性,表明棒状Fe₃O₄担载的Cu纳米粒子具有更好的结构稳定性。     

棒状CuFe4Ox的可控合成及其异戊醇脱氢反应的催化性能

利用液相沉淀法可控合成了均匀的棒状CuFe₄O_x催化剂。通过原位X射线粉末衍射（XRD）、高分辨透射电子显微镜（TEM）及程序升温还原（TPR）等手段表征其晶相结构、形貌和还原性能。通过还原棒状CuFe₄O_x获得Cu⁰/Fe₃O₄ 纳米棒,原位X射线光电子能谱（XPS）用于确定Cu⁰/Fe₃O₄ 表面的相组成。通过液相沉淀法制备棒状CuFe₄O_x,在120℃保持3 h后加入Na₂CO₃溶液至pH等于9时所得棒状形貌最为规整。以异戊醇脱氢反应作为探针反应,比较了Cu⁰/Fe₃O₄ 纳米棒和Cu⁰/Fe₃O₄ 纳米颗粒的催化反应性能,发现Cu⁰/Fe₃O₄ 纳米棒比Cu⁰/Fe₃O₄ 纳米粒子具有更好的活性和稳定性,表明棒状Fe₃O₄ 担载的Cu纳米粒子具有更好的结构稳定性。     

La7O6(BO3)(PO4)2:Eu3+/Tb3+荧光材料的制备及其光致发光性能

采用优化的高温固相方法制备了稀土离子Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂系荧光材料,并对其物相行为、晶体结构、光致发光性能和热稳定性进行了详细研究。结果表明,La₇O₆（BO₃）（PO₄）₂：Eu³⁺材料在紫外光激发下能够发射出红光,发射光谱中最强发射峰位于616 nm处,为⁵D₀→⁷F₂特征能级跃迁,Eu³⁺的最优掺杂浓度为0.08,对应的CIE坐标为（0.610 2,0.382 3）;La₇O₆（BO₃）（PO₄）₂：Tb³⁺材料在紫外光激发下能够发射出绿光,发射光谱中最强发射峰位于544 nm处,对应Tb³⁺的⁵D₄→⁷F₅能级跃迁,Tb³⁺离子的最优掺杂浓度为0.15,对应的CIE坐标为（0.317 7,0.535 2）。此外,对2种材料的变温光谱分析发现Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂荧光材料均具有良好的热稳定性。     

LiCoO2梯度包覆LiNi0.96Co0.04O2电极材料的电化学性能

镍钴酸锂(LiNi0.8Co0.2O2)与目前商业用锂离子电池正极材料钴酸锂(LiCoO2)相比,具有成本低、实际比容量高和环境友好等优势。但LiNi0.8Co0.2O2的充放循环性能还有待提高,对其进行阳离子掺杂或表面修饰可以改善其电化学性能,这方面的研究已经成为热点。Fey等人[1]用溶胶凝胶法制     

Synthesis and properties of the double perovskites La2NiVO6, La2CoVO6, and La2CoTiO6

The double perovskites La₂CoVO₆, La₂CoTiO₆, and La₂NiVO₆, are described. Rietveld fitting of neutron and powder X-ray diffraction data show La₂NiVO₆ and La₂CoVO₆ to have a disordered arrangement of B-cations whereas La₂CoTiO₆ shows ordering of the B-cations (with ∼5% Co/Ti inversion). Curie-Weiss fits to the linear region of the 1/χ plots reveal Weiss temperatures of −107, −34.8, and 16.3 K for La₂CoVO₆, La₂CoTiO₆, and La₂NiVO₆, respectively, and magnetic transitions are observed. La₂CoTiO₆ prepared by our method differs from material prepared by lower-temperature routes. A simple antiferromagnetic spin model is consistent with the data for La₂CoTiO₆. These compounds are semiconductors with bandgaps of 0.41 (La₂CoVO₆), 1.02 (La₂CoTiO₆) and 0.45 eV (La₂NiVO₆).     

Preparation of ZrO2-TiO2-CeO2 and Its Application in the Selective Catalytic Reduction of NO with NH3

TiO₂,ZrO₂-TiO₂,andZrO₂-TiO₂-CeO₂ were prepared by co-precipitation method and characterized by X-ray diffraction (XRD), specific surface area measurements (BET), temperature programmed desorption (NH₃-TPD), oxygen storage capacity (OSC), and temperature programmed reduction (H₂-TPR). The results showed that ZrO₂-TiO₂-CeO₂ exhibited large number of surface strong acid, possessed some oxygen storage capacity, and strong redox property. The three materials were used as supports and the monolith catalysts were prepared with 1% (w) V₂O₅ and 9% (w)WO₃ for selective catalytic reduction (SCR) of NO with ammonia in the presence of excessive O₂, and the results of catalytic activity showed that the catalyst used ZrO₂-TiO₂-CeO₂ as support yielded nearly 100% NO conversion at 275 °C at a gas hourly space velocity (GHSV) of 10000 h⁻¹, and it had the best catalytic activity and showed great potential for practical application.     

WS2/CuGa2O4复合材料的制备及其气敏性

采用共沉淀法制备了CuGa₂O₄纳米材料,并利用水热法制备了一系列WS₂/CuGa₂O₄复合材料。结合X射线衍射(XRD)、扫描电子显微镜(SEM)、X射线光电子能谱(XPS)等对制备的材料进行了物相组成、表面形貌以及元素价态的分析。研究了WS₂的复合量对 CuGa₂O₄材料检测乙醇气体敏感性能的影响。实验结果表明,当 WS₂与 CuGa₂O₄质量比为 1%时,该复合材料制备的传感器在室温下对 100 μL·L^-1乙醇气体表现出 345.3 的灵敏度,响应时间和恢复时间分别为 184 和 69 s,且最低检测限为 0.1μL·L^-1。     

WS2/CuGa2O4复合材料的制备及其气敏性

采用共沉淀法制备了CuGa₂O₄纳米材料,并利用水热法制备了一系列WS₂/CuGa₂O₄复合材料。结合X射线衍射(XRD)、扫描电子显微镜(SEM)、X射线光电子能谱(XPS)等对制备的材料进行了物相组成、表面形貌以及元素价态的分析。研究了WS₂的复合量对CuGa₂O₄材料检测乙醇气体敏感性能的影响。实验结果表明,当WS₂与CuGa₂O₄质量比为1%时,该复合材料制备的传感器在室温下对100μL·L^-1乙醇气体表现出345.3的灵敏度,响应时间和恢复时间分别为184和69 s,且最低检测限为0.1μL·L^-1。     

Cr2(WO4)3和Cr2(MoO4)3的负热膨胀特性研究

用液相反应-前驱物烧结法制备了Cr₂(WO₄)₃和Cr₂(MoO₄)₃粉体。298～1 073 K的原位粉末X射线衍射数据表明Cr₂(WO₄)₃和Cr₂(MoO₄)₃的晶胞体积随温度的升高而增大, 本征线热膨胀系数分别为(1.274±0.003)×10^-6 K^-1和(1.612±0.003)×10^-6 K^-1。用热膨胀仪研究了Cr₂(WO₄)₃和Cr₂(MoO₄)₃在静态空气中298～1 073 K范围内热膨胀行为，即开始表现为正热膨胀，随后在相转变点达到最大值，最后表现为负热膨胀，其负热膨胀系数分别为(-7.033±0.014)×10^-6 K^-1和(-9.282±0.019)×10^-6 K^-1。     

CeO2改性Ag-V2O5/TiO2催化剂的甲基吡啶氧化脱甲基性能

以锐钛矿TiO_2为载体,考察了CeO_2改性对Ag-CeO_2-V_2O_5/TiO_2催化3-甲基吡啶氧化脱甲基性能的影响,并优化了催化剂组成与制备条件.结果表明:Ce掺杂改性不仅能够与V物种作用形成Ce VO_4,而且促进V_2O_5分散,改善活性组分的氧化还原性能,从而提高3-甲基吡啶脱甲基转化率与选择性,改善Ag-V_2O_5/TiO_2催化性能.适宜的催化剂组成为V_2O_5负载量15%,Ce/V的摩尔比0.33,Ag质量分数1.0%.过高的焙烧温度将导致TiO_2载体向金红石型转变,Ag-CeO_2-V_2O_5/TiO_2适宜制备条件为450℃焙烧4 h.     

Why pressure induces an abrupt structural rearrangement in PdTe2 but not in PtTe2

High-pressure X-ray diffraction measurements were carried out for polymeric CdI₂-type compounds MTe₂ (M=Pt, Pd) to investigate if they undergo a structural phase transition under pressure as does IrTe₂. Up to 27 GPa at room temperature PtTe₂ does not undergo any structural phase transition. In contrast, however, an abrupt change in the inter-atomic distances occurs in PdTe₂ above 15.7 GPa at room temperature, and above 5 GPa at 300 °C, but the volume vs. pressure curve exhibits no discontinuity. To account for the differences between the isostructural compounds PtTe₂, PdTe₂ and IrTe₂, their electronic structures and bonding were analyzed on the basis of first principles electronic band structure calculations.     

Conversion of NO in NO/N2, NO/O2/N2, NO/C2H4/N2 and NO/C2H4/O2/N2 Systems by Dielectric Barrier Discharge Plasmas

An experimental study on the conversion of NO in the NO/N₂, NO/O₂/N₂, NO/C₂H₄/N₂ and NO/C₂H₄/O₂/N₂ systems has been carried out using dielectric barrier discharge (DBD) plasmas at atmospheric pressure. In the NO/N₂ system, NO decomposition to N₂ and O₂ is the dominating reaction; NO conversion to NO₂ is less significant. O₂ produced from NO decomposition was detected by an on-line mass spectrometer. With the increase of NO initial concentration, the concentration of O₂ produced decreases at 298 K, but slightly increases at 523 K. In the NO/O₂/N₂ system, NO is mainly oxidized to NO₂, but NO conversion becomes very low at 523 K and over 1.6% of O₂. In the NO/C₂H₄/N₂ system, NO is reduced to N₂ with about the same NO conversion as that in the NO/N₂ system but without NO₂ formation. In the NO/C₂H₄/O₂/N₂ system, the oxidation of NO to NO₂ is dramatically promoted. At 523 K, with the increase of the energy density, NO conversion increases rapidly first, and then almost stabilizes at 93–91% of NO conversion with 61–55% of NO₂ selectivity in the energy density range of 317–550 J L⁻¹. It finally decreases gradually at high energy density. A negligible amount of N₂O is formed in the above four systems. Of the four systems studied, NO conversion and NO₂ selectivity of the NO/C₂H₄/O₂/N₂ system are the highest, and NO/O₂/C₂H₄/N₂ system has the lowest electrical energy consumption per NO molecule converted.     

Transport and optical properties of heavily hole-doped semiconductors BaCu2Se2 and BaCu2Te2

Experimental and theoretical studies of the electronic and optical properties of orthorhombic BaCu₂Se₂ and BaCu₂Te₂ are reported. Experimental data include the electrical resistivity, Hall coefficient, Seebeck coefficient, thermal conductivity, and lattice constants for , and optical transmission and diffuse reflectance data at room temperature. Nominally stoichiometric, polycrystalline samples form with hole concentrations inferred from Hall measurements of 2×10¹⁸ and 5×10¹⁹ cm⁻³ near room temperature for the selenide and telluride, respectively. The corresponding mobilities are near 15 cm² V⁻¹ s⁻¹ for both materials. Optical measurements reveal a transition near 1.8 eV in BaCu₂Se₂, while no similar feature was observed for BaCu₂Te₂. First principles calculations indicate both materials are direct or nearly direct gap semiconductors with calculated gaps near 1.0 eV and 1.3 eV for the telluride and selenide, respectively, and predict weak absorption below about 2 eV. Transport properties calculated from the electronic structure are also presented.