CO氧化反应中H2O对MOx和Au/MOx催化性能的影响

过渡金属氧化物［1,2］及负载型贵金属催化剂［3～13］是催化氧化消除CO的有效催化剂,一直是研究的热点. 虽然对MOx和Au/MOx上CO的氧化性能研究得较多,但大多是在无水条件下进行的;涉及催化剂抗水性能的报道较少［3,9,10］,且仅限于对催化剂活性的研究. Haruta等［3］对Au/Fe2O3,Au/Co3O4和Au/TiO 2等体系开展了一些工作, 认为水对CO氧化活性有促进作用. 本文重点考察了水对MOx(M=Al,Ca,Co,Cr,Cu,Fe,La,Mn,Ni和Zn)催化剂上CO氧化活性的影响,以及水对Au/MOx 催化剂活性及稳定性的影响.     

Effects of preparation conditions of Au/FeOx/Al203 catalysts prepared by a modified two-step method on the stability for CO oxidation

Composite oxide FeO x /Al 2 O 3 -supported gold catalysts were prepared by a modified two-step method. The effects of preparation conditions on the initial catalytic activity and long-time stability were studied for CO oxidation. XRD, XPS and in situ FTIR were employed to investigate the state of FeO x and the species on the catalyst surface. The results showed that Au/FeO x /Al 2 O 3 catalysts prepared by this method exhibited high activity and high stability in a wide pH value range. Calcination pretreatment was proved to be beneficial to improving the activity and stability. The beneficial effects of FeO x acting as a structural promoter could be ascribed to the ability to supply active oxygen species. As the precursor of FeO x , Fe(NO 3 ) 3 is superior to FeCl 3 for obtaining higher stability.     

Catalytic Combustion of Methane over CO1-xMgxO/Al2O3/FeCrAl Monolithic Catalysts

A series of CoxMgxO/Al2O3/FeCrAl catalysts （x=0-1） were prepared. The structures of the catalysts were characterized using XRD, SEM, and TPR analyses. The catalytic activity of the catalysts for methane combustion was evaluated in a continuous flow microreactor. The results indicated that the active washcoats adhered well on the FeCrAl foils. The phases in the catalysts were Co--xMgxO solid solutions, α-Al2O3, and γ-Al2O3. The surface particle size of the catalysts varied with variations in the molar ratios of Co to Mg. The Co component of the Co1_xMgxO/Al2O3/FeCrAl catalysts played an important role in the catalytic activity for methane combustion. In the Co1-xMgxO/AluO3/FeCrAl series catalyst （x=0.2-0.8）, the catalytic activity in terms of x was in the order of 0.5〉0.2〉0.8 under the experimental conditions. The presence of Mg in these catalysts could promote the thermal stability to a large extent. There were strong interactions between the Co1-xMgxO oxides and the AluO3/FeCrAl supports.     

制备方法对La改性的Ni/γAl2O3催化甲烷部分氧化的研究

采用共沉淀法和浸渍法制备La改性的Ni/γAl2O3催化剂，并用于催化甲烷部分氧化反应。共沉淀法制备的催化剂表现出较高的活性和稳定性。空速为80000h－1、800℃时甲烷的转化率接近100％，H2的选择性达99.8％，且在稳定性实验中保持15h活性变化不大。实验采用BET、TPR和XRD说明共沉淀法制备的镍基氧化铝催化剂中，La的加入提高了催化剂的比表面积，有效的抑制了大颗粒NiAl2O4的形成，降低了催化剂活性组分的还原温度，对POM显示出很高的催化活性。     

Kinetics of hydrogen production of methanol reformation using Cu/ZnO/Al2O3 catalyst

The catalytic performance of methanol reformation using Cu/ZnO/Al2O3 was investigated at low temperature. The operation conditions, such as composition of Cu, Zn, and Al, temperature, molar ratio of H2O/CH3OH, weight hourly space velocity, catalyst weight, and kind and flow rate of carrier gas (helium and air), were evaluated to obtain the optimum reaction condition. The catalysts were prepared by oxalic coprecipitation, coprecipitation, and polyol method. The weight composition of Cu, Zn, and Al prepared by oxalic coprecipitation was 15:15:5 by high-throughput screening of combinatorial chemistry method, which was the best Cu/ZnO/Al2O3 catalyst. The prepared catalysts showed high activity and selectivity towards hydrogen formation. The methanol conversion, production rate, and volumetric percentage of hydrogen using this best catalyst were larger than 95%, 0.65 mol/h x g and 59%, respectively, and the CO volumetric percentage was smaller than 0.22% when the reaction temperature was 240 degrees C. The size and dispersity of copper, and the activity and turnover frequency of the catalyst were calculated as well.     

Complete Oxidation of Methane Alumina Modified with Calcium, over Palladium Supported on Lanthanum, and Cerium Ions

The activity and thermal stability of Pd/Al2O3 and Pd/（Al2O3＋MOx） （M=Ca, La, Ce） palladium catalysts in the reaction of complete oxidation of methane are presented in this study. The catalyst supports were prepared by sol-gel method and they were dried either conventionally or with supercritical carbon dioxide. Then they were impregnated with palladium nitrate solution. The catalysts with unmodified alumina had a high surface area. The activity and thermal stability of the aluminasupported catalyst was also very high. The introduction of calcium, lanthanum, or cerium oxide into alumina support caused a decrease of the surface area in the way dependent on the support precursor drying method. These modifiers decreased the activity of palladium catalysts, and they required higher temperatures for the complete oxidation of methane than unmodified Pd/Al2O3. The improvement of the palladium activity by lanthanum and cerium support modifier was observed only at low temperatures of the reaction.     

Methane reforming With CO2 to syngas over CeO2-promoted Ni/Al2O3-ZrO2 catalysts Prepared Via a direct sol-gel process

CeO2-promoted Ni/Al2O3-ZrO2 (Ni/Al2O3-ZrO2-CeO2) catalysts were prepared by a direct sol-gel process with citric acid as gelling agent. The catalysts used for the methane reforming with CO2 was studied by infrared spectroscopy (IR), thermal gravimetric analysis (TGA), microscopic analysis, X-ray diffraction (XRD) and temperature-programmed reduction (TPR). The catalytic performance for CO2 reforming of methane to synthesis gas was investigated in a continuous-flow micro-reactor under atmospheric pressure. TGA, IR, XRD and microscopic analysis show that the catalysts prepared by the direct sol-gel process consist of Ni particles with a nanostructure of around 5 nm and an amorphous-phase composite oxide support. There exists a chemical interaction between metallic Ni particles and supports, which makes metallic Ni well dispersed, highly active and stable. The addition of CeO2 effectively improves the dispersion and the stability of Ni particles of the prepared catalysts, and enhances the adsorption of CO2 on the surface of catalysts. The catalytic tests for methane reforming with CO2 to synthesis gas show that the Ni/Al2O3-ZrO2-CeO2 catalysts show excellent activity and stability compared with the Ni/Al2O3 catalyst. The excellent catalytic activity and stability of the Ni/Al2O3-ZrO2-CeO2 are attributed to the highly, uniformly and stably dispersed small metallic Ni particles, the high reducibility of the Ni oxides and the interaction between metallic Ni particles and the composite oxide supports.     

甲烷部分氧化制合成气Pt-Ni/Al~2O~3催化剂的研究

研究了Ni/Al~2O~3,Pt/Al~2O~3和一系列Pt-Ni/Al~2O~3催化剂对甲烷部分氧化制合成气的催化作用,发现Pt-Ni/Al~2O~3催化剂显示了比Ni/Al~2O~3和Pt/Al~2O~3更高的活性和稳定性。H~2-TPR,CO-TPD,CO~2-TPD,SEM,XPS和XRD等结果证明:Pt和Ni之间存在较强的相互作用,Pt和部分Ni形成固溶体合金并且Pt在催化剂表面富集。Pt和Ni之间的相互作用提高了催化剂的活性和稳定性,甲烷在Pt-Ni/Al~2O~3上的催化部分氧化具有不同于在Pt/Al~2O~3和Ni/Al~2O~3上的反应性能。     

Ni/Al2O3 catalysts for syngas methanation: Effect of Mn promoter

Ni/Al2O3 catalysts with different amounts of manganese ranging from 1 to 3 wt% as promoter were prepared by co-impregnation method. The catalysts were characterized by N2 physisorption, XRD, TPR, SEM and TEM. Their catalytic activity towards syngas methanation reaction was also investigated using a fixed-bed integral reactor. It was demonstrated that the addition of manganese to Ni/Al2O3 catalysts can increase the catalyst surface area and average pore volume, but decrease NiO crystallite size, leading to higher activity and stability. The effects of reaction temperature, pressure and weight hourly space velocity (WHSV) on carbon oxides conversion and CH4 formation rate were also studied. High carbon oxides conversion, CH4 selectivity and formation rate were achieved at the reaction temperature range of 280 300℃.     

Reforming of CH4 with CO2 over Co/Mγ-Al oxide catalyst

A series of Co/Mg–Al oxide samples,CoMgAl-x(x=(Mg+Co)/Al molar ratio of 1–5),were prepared by the self-combustion method followed by H2reduction.The catalytic performance and stability of the samples were studied in dry reforming of CH4.XRD and H2-TPR characterization results showed that the reduced CoMgAl-x samples mainly consisted of solid solution and spinel phases with cobalt particles.The spinel phases contained Co3O4 and Con Mg1-n Al2O4(0≦n≦1)varying with the(Mg+Co)/Al ratio.The effect of (Mg+Co)/Al molar ratio on the catalytic behavior was investigated in detail and CoMgAl-3 exhibited the highest catalytic activity and stability among the catalysts studied.     

CeO2纳米层对多层载体x-CeO2/3DOM Al2O3负载纳米Au催化剂催化柴油炭烟燃烧活性的影响

与汽油车相比,柴油车具有CO2排放低、寿命长和经济性好等优点,所以近年来受到广泛关注并被大量使用.但是,柴油车在使用过程中会产生大量炭烟颗粒物(PM),对大气环境和人类健康造成很大威胁.因此,开展这方面的基础研究具有重要的科学意义及环境保护意义.催化柴油炭烟燃烧反应是一个气-固-固多相深度氧化反应,由于PM的粒径远大于传统催化剂,导致PM不能进入催化剂孔道内部,造成催化剂活性比表面积利用率较低.设计并制备大孔径的三维有序大孔结构(3DOM)的催化剂,能够减小反应扩散阻力,增加催化剂与炭烟颗粒物的有效接触,加快反应进行.另外,可以通过在3DOM氧化物表面担载其它活性组分,提高催化剂的氧化还原性能,进而提高其活性.CeO2有很好的储放氧性能,在柴油车尾气净化催化剂中较为常见,但是单一的CeO2热稳定性较差,高温下容易烧结,使得比表面积减小,并且失去储氧能力,造成催化剂失活.文献中较常见的解决办法是在CeO2中掺杂其它阳离子,如Zr4+,Pr3+,Al3+,La3+及Y3+等离子,以提高CeO2的抗高温烧结能力.此外,研究报道的催化剂对催化柴油炭烟颗粒物燃烧的峰值温度已经远低于炭烟颗粒物的自燃温度,但是对颗粒物的起燃温度仍普遍较高.我们前期研究结果表明,担载纳米Au颗粒催化剂能够显著降低炭烟燃烧的起燃温度.本文采用胶体晶体模板法制备了3DOM Al2O3载体,利用微孔膜-氨沉淀法担载不同量的活性组分CeO2,制备出一种负载型x-CeO2/3DOM Al2O3催化剂,它既可减少稀土元素用量,降低成本,又因为Al2O3的机械强度较高,还能保证催化剂的机械强度足够好.为了进一步降低催化剂催化炭烟燃烧的起燃温度,利用还原沉积法在多层载体x-CeO2/3DOM Al2O3上负载纳米Au催化剂,制备出不同厚度的CeO2纳米层负载Au催化剂(Au/x-CeO2/3DOM Al2O3).利用X射线衍射、扫描电镜、透射电镜、H2程序升温还原和O2程序升温脱附等方法研究了催化剂的结构及物化性质与催化剂活性之间的关系,提出了消除PM反应的可能机理.结果表明,Al3+离子能够部分进入到CeO2中,形成Al-Ce固溶体.由于Al离子半径小于Ce离子,Al3+掺杂后能引起CeO2晶格发生畸变,产生大量缺陷,形成大量氧空位,促进晶格氧的移动,从而使催化剂具有更大的储放氧能力.在Au/x-CeO2/3DOM Al2O3催化剂中,CeO2担载量过高时,氧化铈纳米层较厚,活性组分容易烧结,不利于催化剂活性提高;而CeO2担载量过低,则CeO2纳米层较稀薄,催化剂的氧化还原性能受限,催化剂活性也不高.因此,CeO2的担载量应适当.此外,Au和CeO2之间的强相互作用能够增加Au纳米颗粒表面活性氧物种的数量,从而促进柴油炭烟燃烧反应.活性测试结果表明,担载纳米Au颗粒后,催化剂催化柴油炭烟燃烧的起燃温度均明显降低,在所制备的系列催化剂中Au/20％CeO2/3DOM Al2O3催化剂展示了最高的催化活性,T10,T50和T90分别为267,372和426 oC.     

钡改性的Ni/γ- Al2O3催化剂用于甲烷部分氧化的研究

800 ℃、80 000 h－1、CH4/O2/N2=14/7/79下比较了质量分数20%的Ni/γ- Al2O3和Ba改性的Ni/γ- Al2O3催化剂，用于甲烷部分氧化反应的活性和选择性。结果表明，Ba的添加提高了镍基催化剂的活性和稳定性。BET和XRD表明，Ba的加入有利于高温焙烧下抑制大颗粒的Ni Al2O4的形成，保持了高比例的活性镍组分，提高了催化剂催化活性。常压下，xCH4接近100%，sCO、sH2达到92.2%和98.1%，催化剂15 h内活性稍微下降。Ba的加入使Al2O3的晶型转化温度由800 ℃提高到900 ℃，提高了载体的稳定性。     

CuO/ZnO/Y2O3/γ-Al2O3双功能催化剂上二甲醚水蒸气重整制氢

将沉积-沉淀法制备的CuO/ZnO/Y2O3催化剂同γ-Al2O3进行机械混合, 制备了CuO/ZnO/Y2O3/γ-Al2O3双功能催化剂, 用于二甲醚水蒸气重整制氢反应, 实验结果表明其活性、稳定性等均优于常用的CuO/ZnO/Al2O3/γ-Al2O3催化剂. 结合N2吸附-脱附(BET)、N2O化学吸附(N2O chemisorption)、NH3程序升温脱附(NH3-TPD)、X射线衍射(XRD)、H2程序升温还原(H2-TPR)等表征手段研究了两种催化剂在表面酸性及微观结构上的差异, 发现CuO/ZnO/Y2O3催化剂具有相对较高的铜分散度, 铜晶粒更加细小化, 并且具有高温稳定性的Y2O3可能起到隔离铜的作用, 在一定程度上防止了铜晶粒的团聚, 从而改善了重整组分的性能, 提高了双功能催化剂的重整制氢活性及稳定性.     

BaO对Pd/Al2O3催化性能的影响

以 Pd(C2 H3O2 ) 2 为前身 ,制备了系列 Ba O- Al2 O3复合氧化物负载钯的催化剂 .用质量滴定法 ,测定了复合载体的零电荷点 (pzc) .结果表明 ,体系的 pzc随 Ba O含量的增加而增大 ,在 5 %～ 10 %之间存在一拐点 ,并与XRD所测 Ba O在 Al2 O3上的单层分散阈值相对应 .复合载体在制备中发生固相反应 ,所生成的 Ba Al2 O4可以阻止 Al2 O3的相变 ,并极大地提高载体的热稳定性 ,其中 5 % Ba O的作用最为明显 .Ba O的引入 ,增强了 Pd/Al2 O3对 CO的氧化能力 ,同时 ,提高了其热稳定性     

FeOx／ZrO2催化剂结构及CO氧化性能的研究

利用XRD、TPR及固定床微反技术,研究了添加FeOx对ZrO2载体结构稳定性和催化性能的影响。结果表明,FeOx对载体ZrO2具有良好的热稳定性,能阻止ZrO2从四方晶型向单斜晶型的转变;FeOx与载体ZrO2之间的相互作用,能促进FeOx在载体表面的分散,并提提高FeOx/ZrO2催化剂的氧化和还原性能。     

ZrxTixAl1-2xO2的制备及其在三效催化剂上的应用

Zr_0.5Ti_0.5O₂(ZT) and Zr_0.25Ti_0.25Al_0.5O₂(ZTA) mixed oxides were prepared by co-precipitation method and characterized by low temperature adsorption-desorption， XRD and NH₃-TPD. The activity of Pt/Zr_0.5Ti_0.5O₂ and Pt/ Zr_0.5Ti_0.5Al_0.5O₂ catalysts was evaluated using the simulated gases. The results show that ZTA samples exhibit higher specific surface area， larger pore volume and proper surface acidic amount and acidity in comparison with ZT. The results of the catalytic test indicate that Pt/ZT and Pt/ZTA catalysts exhibit excellent low-temperature catalytic activity and lower light-off temperatures of hydrocarbon， carbon monoxide and nitrogen oxides， especially better conversion for nitrogen oxides (NO_x). The addition of Al₂O₃ into ZT enhanced the anti-aging property of Pt/ ZTA catalysts due to the excellent textural， structural， surface acidity and thermal stability.     

Rh/Al_2O_3-Cr_2O_3整体式催化剂的制备和二氯甲烷催化氧化性能

以粉末Al_2O_3为载体,通过浸渍Rh(NO_3)_3制备Rh/Al_2O_3催化剂;再以Rh/Al_2O_3、粉末Cr_2O_3和铝胶经过研磨混合制得催化剂活性浆料;将催化剂活性浆料涂覆到堇青石蜂窝陶瓷载体表面,经烘干,焙烧制得不同Rh含量的Rh/Al_2O_3-Cr_2O_3系列整体式催化剂.研究了该类催化剂的二氯甲烷催化氧化性能,发现Rh负载量为0.4 g/L的Rh/Al_2O_3-Cr_2O_3催化剂活性最佳,且未生成含氯中间产物.结合催化剂的表征结果发现,Rh的添加可增加催化剂的表面酸性和氧化还原性能,二者的协同作用提高了催化剂活性;而Cr_2O_3的存在有利于CH_3Cl中间体的进一步氧化,从而提高了催化剂的选择性.     

Al含量对Pt-S2O82-/ZrO2-Al2O3型固体超强酸催化剂异构化性能的影响

通过向S₂O₈^2-/ZrO₂催化剂中同时引入适量的Pt和Al₂O₃, 制备出了具有较高催化性能和高稳定性的Pt-S₂O₈^2-/ZrO₂-Al₂O₃型固体超强酸催化剂. 以正戊烷异构化反应为探针, 考察了Al含量对催化剂的异构化性能的影响, 并采用XRD, BET, FTIR, TPR, TG-DTA, NH₃-TPD和ICP手段对催化剂进行了表征. 结果表明, Al能够延迟ZrO₂的晶化温度, 抑制硫的分解; Al能够增加催化剂的比表面积, 增强硫氧键的结合, 提高催化剂的还原性能, 增加催化剂的酸强度和酸总量. 当Al₂O₃质量分数为2.5%时, Pt-S₂O₈^2-/ZrO₂-Al₂O₃固体超强酸催化剂的催化活性最高, 正戊烷异构化收率可达60.02%, 选择性在98.2％以上.     

制备条件对Pd催化剂上C3H6选择性还原NO性能的影响

采用浸渍法和溶胶凝胶法,制备了Pd/AI2O3和Pd/AI2O3-CeO2样品,并测定了不同温度焙烧后催化剂的物相、比表面积及对丙烯选择性还原NO的活性。对于Pd/AI2O3,随着焙烧温度的提高,其NO的最大转化率逐渐下降,对应的反应温度在290－310℃左右,而溶胶凝胶法制备的样品活性略高于浸渍法制备的样品;对于Pd/AI2O3-CeO2,经600℃焙烧后,其NO的最大转化率为22％,900℃焙烧的催化剂样品上NO的最大转化率达到40％左右,对应的反应温度也逐渐下降,说明活性随焙烧温度的提高而明显提高,溶胶凝胶法和浸渍法制备的样品结果很接近,浸渍法制备了若干不同Pd负载量的Pd/AI2O3样品,活性测定的结果表明,Pd含量在0．5％左右的催化剂样品中具有最高的活性。     

KOH修饰Au/Al2O3催化剂的低温CO氧化催化反应性能

采用等体积浸渍法制备了KOH-Au/Al<,2>O<,3>系列催化剂,考察了催化剂对低温CO氧化反应的初始活性和干、湿气氛下连续反应的稳定性能,并用电感耦合等离子发射光谱、红外光谱、高分辨透射电镜、紫外漫反射光谱等技术对催化剂进行了结构表征.结果表明:与母体催化剂(Au/Al<,2>O<,3>)相比,修饰催化剂(KOH...