Magnetic properties and magnetocaloric effects in Tb6Co1.67Si3 compound

Magnetic properties and magnetocaloric effects of Tb₆Co_1.67Si₃ have been investigated by magnetization measurement. This compound is of a hexagonal Ce$_{6}$Ni$_{2}$Si$_{3}$-type structure with a saturation magnetization of 187\,emu/g at 5\,K and a reversible second-order magnetic transition at Curie temperature $T_{\rm C} = 186$\,K. A magnetic entropy change $\Delta S = 7$\,J\,$\cdot$\,kg$^{-1}$\,$\cdot$\,K$^{-1}$ is observed for a magnetic field change from 0 to 5\,T. A large value of refrigerant capacity (RC) is found to be 330\,J/kg for fields ranging from 0 to 5\,T. The large RC, the reversible magnetization around $T_{\rm C}$ and the easy fabrication make the Tb₆Co_1.67Si₃ compound a suitable candidate for magnetic refrigerants in a corresponding temperature range.     

Magnetic properties and magnetic entropy changes of La1-xPrxFe11.5Si1.5 compounds with 0≤x≤ 0.5

Magnetic properties and magnetic entropy changes in LaFe$_{11.5}$Si$_{1.5}$ have been investigated by partially substituting Pr by La. It is found that La$_{1 - x}$Pr$_{x}$Fe$_{11.5}$Si$_{1.5}$ compounds remain cubic NaZn$_{13}$-type structures even when the Pr content is increased to 0.5, i.e. $x = 0.5$. Substitution of Pr for La leads to a reduction in both the crystal constant and the Curie temperature. A stepwise magnetic behaviour in the isothermal magnetization curves is observed, indicating that the characteristic of the itinerant electron metamagnetic (IEM) transition above $T_{\rm C}$ becomes more prominent with the Pr content increasing. As a result, the magnetic entropy change is remarkably enhanced from 23.0 to 29.4\,J/kg$\cdot$K as the field changes from 0 to 5\,T, with the value of $x$ increasing from 0 to 0.5. It is more attractive that the magnetic entropy changes for all samples are shaped into high plateaus in a wide range of temperature, which is highly favourable for Ericsson-type magnetic refrigeration.     

Dy2 AlFe13 Mn3 化合物的本征磁致伸缩

通过X-射线衍射及磁测量手段研究了Dy2AlFe13Mn3化合物的结构及磁性质。研究结果表明Dy2AlFe13Mn3化合物具有六角相的Th2Ni17型结构。通过X-射线热膨胀测定法发现Dy2AlFe13Mn3化合物在245到344K的温度范围内存在负热膨胀现象，其平均热膨胀系数为α＝-1.1×10-4K-1K-1。在105到360K的温度范围内，通过比较磁性状态下的晶胞参数和由高温顺磁状态外延得到的低温顺磁状态下的晶胞参数间的差别计算了Dy2AlFe13Mn3化合物的本征磁致伸缩。结果表明Dy2AlFe13Mn3化合物的本征体磁致伸缩ωS在105到245K的温度范围内随着温度的升高而增大，由105K时的7.0×10-3 增加到245K时的9.1×10-3。随着温度的进一步升高，ωS反而减小。沿c轴方向的本征线磁致伸缩λc随着温度的升高而减小。基面内的本征线磁致伸缩λa在105到270K的温度范围内随着温度的升高而增大，从105K时的0.8×10-3增大到270K时的3.4×10-3，然后随着温度的进一步升高而减小。     

Magnetic properties and magnetocaloric effect in RE55Co30Al10Si5 (RE = Er and Tm) amorphous ribbons

The magnetic and magnetocaloric effects (MCE) of the amorphous $RE_{55}$Co$_{30}$Al$_{10}$Si$_{5}$ ($RE={\rm Er}$ and Tm) ribbons were systematically investigated in this paper. Compounds with $R ={\rm Er}$ and Tm undergo a second-order magnetic phase transition from ferromagnetic (FM) to paramagnetic (PM) around Curie temperature $T_{\rm C} \sim 9.3$ K and 3 K, respectively. For Er$_{55}$Co$_{30}$Al$_{10}$Si$_{5}$ compound, an obvious magnetic hysteresis and thermal hysteresis were observed at low field below 6 K, possibly due to spin-glass behavior. Under the field change of 0 T-5 T, the maximum values of magnetic entropy change ($-\Delta S_{\rm M}^{\rm max}$) reach as high as 15.6 J/kg$\cdot$K and 15.7 J/kg$\cdot$K for Er$_{55}$Co$_{30}$Al$_{10}$Si$_{5}$ and Tm$_{55}$Co$_{30}$Al$_{10}$Si$_{5}$ compounds, corresponding refrigerant capacity (RC) values are estimated as 303 J/kg and 189 J/kg, respectively. The large MCE makes amorphous $RE_{55}$Co$_{30}$Al$_{10}$Si$_{5 }$ ($RE={\rm Er}$ and Tm) alloys become very attractive magnetic refrigeration materials in the low-temperature region.     

Effect of Dy substitution on magnetic properties and magnetocaloric effects of Tb6Co1.67Si3 compounds

The magnetic and magnetocaloric properties of(Tb1-xDyx) 6 Co 1.67 Si 3(0 ≤ x ≤ 0.8) have been experimentally investigated.The compounds exhibit a Ce6Ni2Si3-type hexagonal structure and undergo a second-order magnetic transition.The Curie temperature decreases from ～ 187 K to 142 K as the content of Dy grows from 0 to 0.8.The maximal magnetic entropy change,for a field change of 0-5 T,varies between ～ 6.2 and ～ 7.4 J/kg.K,slightly decreasing when Dy is introduced.The substitution of Dy leads to a remarkable increase in refrigeration capacity(RC).A large RC value of ～ 626 J/kg is achieved for x = 0.4 under a field change of 0-5 T.     

Growth of Mn5Ge3 ultrathin film on Ge（111）

The growth of Mn5Ge3 ultrathin films with different thicknesses, prepared by solid phase epitaxy, is studied. The results of scanning tunnelling microscopy and low energy electron diffraction studies show that the film can be formed and it is terminated with a （√3 × √3） R30° surface reconstruction when the thickness of Mn exceeds 3 monolayers. The magnetic properties show that the Curie temperature is about 300 K and the T^2-dependent behaviour is observed to remain up to 220 K.     

Magnetic properties and magnetocaloric effect in NdxLa1-xFe11.5Al1.5 compounds

Effects of Nd-doping on the magnetic properties and magnetocaloric effects （MCEs） of NdxLa1-xFe11.5Al1.5 have been investigated. Substitution of Nd leads to a weakening of the antiferromagnetic （AFM） coupling and an enhancement of the ferromagnetic （FM） coupling. This in turn results in a complex magnetic behaviour for Nd0.2La0.8Fe11.5Al1.5 characterized by the occurrence of two phase transitions at ～188 K （PM AFM） and ～159 K （AFM-FM）. As a result, a table-like MCE （9 J/kg.K） is found in a wide temperature range （160-185 K） for a field change of 0-5T around the transition temperature, as evidenced by both the magnetic and calorimetric measurements. Based on the analysis of low-temperature heat capacity, it is found that the AFM-FM phase transition modifies the electron density significantly, and the major contribution to the entropy change comes from the electronic entropy change.     

Influence of magnetic field sweep rate on the hysteresis loops of Ni0.8Fe0.2/Fe0.5Mn0.5 exchange bias bilayer

The influence of the magnetic field sweep rate on the hysteresis loops of exchange bias Ni0.8Fe0.2/Fe0.5Mn0.5 bilayers has been investigated with a vibrating sample magnetometer. It was found that the sweep rate of 13.6 kA/4πms is high enough to bring about obvious changes in the hysteresis loops of the exchange bias bilayer. High sweep rate in the magnetization reversal stage enlarges the coercivity of the sample, while high sweep rate in the saturation state reduces the coercivity. The above phenomena were attributed to magnetic viscosity in the ferromagnetic layer enhanced by the interface exchange interaction and domain magnetization reversals assisted by thermal fluctuation in the antiferromagnetic layer respectively.     

Electron spin resonance study of the Ba-doping manganite Nd0.5Sr0.5MnO3

We have performed magnetization measurements and electron spin resonance （ESR） on polycrystalline manganites of Nd0.5Sr0.5-xBaxMnO3 （x = 0.1）. Phase separation and phase transitions are observed from the susceptibility and the ESR spectra data. Between 260 K （～ Tc） and 185 K （～ TN）, the system coexists of the paramagnetic phase and the ferromagnetic （FM） phase. Between 185 K and 140 K, the system coexists of the FM phase and the antiferromagnetic （AFM） phase. These results indicate that the system has a very complex magnetic state due to the origin of the instability stemming from manganite Nd0.5Sr0.4Ba0.1MnO3 by partially substituting the larger Ba^2＋ ions for the smaller Sr^2＋ ions.     

Microwave properties and surface topography of softmagnetic films with high resistivity

A single layer of CoFeB and a multilayer of CoFeB--MgO films are prepared by means of DC/RF magnetron sputter deposition. The excellent microwave properties and high electrical resistivity are simultaneously achieved in the discontinuous multilayer structure of [Co₄₄Fe₄₄B₁₂(0.7nm)/MgO(0.4nm)]_{40} film. This film has a high permeability ({μ \prime }) (larger than 100 below 2.1GHz), a high magnetic loss (μ') (larger than 100 in a range from 1.5 to 3.3GHz), a resistivity of 3.3× 10^*     

Effect of R substitution on magnetic properties and magnetocaloric effects of La1-xRxFe11.5Si1.5 compounds with R=Ce, Pr and Nd

<正>Magnetic properties and magnetocaloric effects of La_1-xR_xFe₁₁₀₅ Si₉105)（R=Pr,（0≤x≤0.5）;R = Ce and Nd, （0≤x≤0.3）） compounds are investigated.Partially replacing La with R = Ce,Pr and Nd in La_1-xR_xFe_11.5Si_1.5 leads to a reduction in Curie temperature due to the lattice contraction.The substitution of R for La causes an enhancement in field-induced itinerant electron metamagnetic transition,which leads to a remarkable increase in magnetic entropy change△S_m and also in hysteresis loss.However,a high effective refrigerant capacity RC_eff is still maintained in La_1-xR_xFe_11.5Si_1.5.In the present samples,a large△S_m and a high RC_eff have been achieved simultaneously.     

Synthesis and characterization of Ca2Sn1-xCexO4 with blue luminescence originating from Ce^4＋ charge transfer transition

Ce^4＋-doped Ca2SnO4 with a one-dimensional structure, which emits bright blue light, is prepared by using a solid-state reaction method. The x-ray diffraction results show that the Ce^4＋ ions doped in Ca2SnO4 occupy the Sn^4＋ sites. The excitation and emission spectra of Ca2Sn1-xCexO4 appear to have broad bands with peaks at - 268nm and -442nm, respectively. A long excited-state lifetime （-83μs） for the emission from Ca2Sn1-xCexO4 suggests that the luminescence originates from a ligand-to-metal Ce^4＋ charge transfer （CT）. The luminescent properties of Ca2Snl_xCexO4 have been compared with those of Sr2CeO4, which is the only material reported so far to show Ce^4＋ CT luminescence. More interestingly, it is observed that the emission intensity of Ca2Sn1-xCexO4 with a small doping concentration （x - 0.03） is comparable to that of Sr2CeO4 in which the concentration of active centre is 100%.     

Effect of Cu doping on the magnetic and electrical properties of n=2 Ruddlesden-Popper manganates

A series of polycrystalline Cu-doped n=2 Ruddlesden-Popper manganates La1.2Sr1.8CuzMn（2-x）O7 （x=0, 0.04, 0.13） were synthesized by the solid state reaction method. The effect of Cu doping on the magnetic and transport properties has been studied. It is found that Cu substitution for Mn greatly affects the magnetic and electrical properties of the parent phase La1.2Sr1.8Mn2O7. With the increase of Cu content, the system undergoes a transition from longrange ferromagnetic order to the spin glass state and further to an antiferromagnetic order. A little of Cu dopant can lead to the samples showing semiconductor or insulator behaviour in the whole observed temperature range while the parent phase has a metal-insulator transition. These samples show colossal magnetoresistance at low temperatures and the value of it decreases with increasing Cu content.     

Temperature-dependent structure and magnetization of YCrO3 compound

We have grown a YCrO$_3$ single crystal by the floating-zone method and studied its temperature-dependent crystalline structure and magnetization by x-ray powder diffraction and PPMS DynaCool measurements. All diffraction patterns were well indexed by an orthorhombic structure with space group of $Pbnm$ (No. 62). From 36 K to 300 K, no structural phase transition occurs in the pulverized YCrO$_3$ single crystal. The antiferromagnetic phase transition temperature was determined as $T_\textrm{N} = 141.58(5)$ K by the magnetization versus temperature measurements. We found weak ferromagnetic behavior in the magnetic hysteresis loops below $T_\textrm{N}$. Especially, we demonstrated that the antiferromagnetism and weak ferromagnetism appear simultaneously upon cooling. The lattice parameters ($a$, $b$, $c$, and $V$) deviate downward from the Grüneisen law, displaying an anisotropic magnetostriction effect. We extracted temperature variation of the local distortion parameter $\varDelta$. Compared to the $\varDelta$ value of Cr ions, Y, O1, and O2 ions show one order of magnitude larger $\varDelta$ values indicative of much stronger local lattice distortions. Moreover, the calculated bond valence states of Y and O2 ions have obvious subduction charges.     

Spontaneous magnetization and resistivity jumps in bilayered manganite （La0.8Eu0.2）4/3Sr5/3Mn2O7 single crystals

Owing to the inhomogeneous state resulting from the doping of a small number of Eu ions into Laa/3Sr5/3Mn2O7, from the resulting single crystal （La0.8Eu0.2）a/3Sr5/3Mn2O7 we have observed the magnetization jump, the resistivity jump, as well as the relaxation phenomena. For （Lao.sEuo.2）a/3Sr5/3Mn2O7, it has a very delicate ground state due to the interplays among spin, charge, orbital, lattice degrees of freedom. Consequently, the magnetization state is sensitive to temperature, magnetic field, as well as time. Meanwhile, the evolution of the magnetization with time shows a spontaneous jump when both the temperature and the magnetic field are constant. Similar step-like behaviours are also observed in resistivity. All these results suggest that Eu doping can greatly modulate the physical properties of Laa/3Sr5/3Mn2O7 and cause such interesting behaviours.     

Temperature-frequency dependence and mechanism of dielectric properties for γ-Y2Si2O7

This paper reports that single-phase γ-Y2Si2O7 is prepared via a sufficient blending and cold-pressed sintering technique from Y2O3 powder and SiO2 nanopowder. It studies the dielectric properties of γ-Y2Si2O7 as a function of the temperature and frequency. The γ-Y2Si2O7 exhibits low dielectric loss and non-Debye relaxation behaviour from 25 to 1400℃ in the range of 7.3-18 GHz. The mechanism for polarization relaxation of the as-prepared γ-Y2Si2O7 differing from that of SiO 2 is explained. Such particular dielectric properties could potentially make specific attraction for extensive practical applications.     

Growth and characterization of superconducting Ca1-xNaxFe2As2 single crystals by NaAs-flux method

High-quality superconducting Ca$_{1-x}$Na$_x$Fe$_2$As$_2$ single crystals have been successfully grown by the NaAs-flux method, with sodium doping level $x = 0.4$-0.64. The typical sizes of these crystals are more than 10 mm in $ab$-plane and $\sim 0.1$ mm along $c$-axis in thickness. X-ray diffraction, resistance and magnetization measurements are carried out to characterize the quality of these crystals. While no signature of magnetic phase transitions is detected in the normal state, bulk superconductivity is found for these samples, with a sharp transition at $T_{\rm c}$ ranging from 19.8 K ($x = 0.4$) to 34.8 K ($x = 0.64$). The doping dependences of the $c$-axis parameter and $T_{\rm c}$ are consistent with previous reports, suggesting a possible connection between the lattice parameters and superconductivity.     

Magnetization and magnetic phase diagrams of a spin-1/2 ferrimagnetic diamond chain at low temperature

We used the Jordan–Wigner transform and the invariant eigenoperator method to study the magnetic phase diagram and the magnetization curve of the spin-1/2 alternating ferrimagnetic diamond chain in an external magnetic field at finite temperature. The magnetization versus external magnetic field curve exhibits a 1/3 magnetization plateau at absolute zero and finite temperatures, and the width of the 1/3 magnetization plateau was modulated by tuning the temperature and the exchange interactions. Three critical magnetic field intensities H_(CB), H_(CE) and H_(CS) were obtained, in which the H_(CB) and H_(CE) correspond to the appearance and disappearance of the 1/3 magnetization plateau, respectively, and the higher H_(CS) correspond to the appearance of fully polarized magnetization plateau of the system. The energies of elementary excitation ωσ,k(σ = 1, 2, 3) present the extrema of zero at the three critical magnetic fields at 0 K, i.e., [hω_(3,k)(HCB)]_(min)= 0, [hω_(2,k)(H_(CE))]_(max)= 0 and [hω _(2,k)(H_(CS))]_(min)= 0, and the magnetic phase diagram of magnetic field versus different exchange interactions at 0 K was established by the above relationships. According to the relationships between the system's magnetization curve at finite temperatures and the critical magnetic field intensities, the magnetic field-temperature phase diagram was drawn. It was observed that if the magnetic phase diagram shows a three-phase critical point, which is intersected by the ferrimagnetic phase, the ferrimagnetic plateau phase, and the Luttinger liquid phase, the disappearance of the1/3 magnetization plateau would inevitably occur. However, the 1/3 magnetization plateau would not disappear without the three-phase critical point. The appearance of the 1/3 magnetization plateau in the low temperature region is the macroscopic manifestations of quantum effect.     

Magnetocrystalline anisotropy and dynamic spin reorientation of half-doped Nd_(0.5)Pr_(0.5)FeO_3 single crystal

The single crystals of Nd_(0.5)Pr_(0.5)FeO_3 were successfully grown by optical floating zone method.Room temperature x-ray diffraction and Laue photograph declared the homogeneity and high quality of the crystal.The significant magnetic anisotropy and multiple magnetic transitions illustrate the complex magnetic structure.At high temperatures(T 66 K),it shows the typical characteristics of Γ_4(G_x,A_y,F_z) state.With the decrease of the temperature,it undergoes a first-order spin reorientation transition from Γ_4(G_x,A_y,F_z) to Γ_2(F_x,C_y,G_z) state in the temperature window of 45-66 K under an applied magnetic field of 0.01 T.As the temperature drops to ～17 K,a new magnetic interaction mechanism works,which results in a further enhancement of magnetization.The T-H phase diagram of Nd_(0.5)Pr_(0.5)FeO_3 single crystal was finally constructed.