Effect of P2O5 addition on the structural and spectroscopic properties of sodium aluminosilicate glass

The structural and spectroscopic properties of Na₂O-Al₂O₃-SiO₂-xP₂O₅ glasses（x = 0 to 7 mol%） are investigated.Both Raman and IR spectra reveal that discrete phosphate species([PO₄]^-3,[PO3O_1/2]^-2) with low polymerization degree can be formed in the silicate glass.These phosphate structures scavenge non-bridging oxygen ions and cations from the silicate network,resulting in an increase of the glass transition temperature.According to the Judd-Ofelt intensity parameters（Ω₂,Ω₄,Ω₆） of Er³⁺.the asymmetry of local environment around Er³⁺ becomes higher,and the bond covalency between Er³⁺ and O^2-decreases after P2O5 is introduced.In the emission spectra,photo-luminescence intensity increases with increasing P₂O₅ concentration and the spectra are inhornogeneously broadened,revealing that the ligand electric field around Er³⁺ is dramatically changed,and the glass matrix becomes disordered.     

Spectroscopic properties in Er³⁺/Yb³⁺ Co-doped fluorophosphate glass

Using the technique of high-temperature melting, a new Er 3+ /Yb 3+ co-doped fluorophosphate glass was prepared. The absorption and fluorescence spectra were investigated in depth. The effect of Er 3+ and Yb 3+ concentration on the spectroscopic properties of the glass sample was also discussed. According to the Judd–Ofelt theory, the oscillator strength was computed. The lifetime of 4 I 13/2 level (τ m ) of Er 3+ ions was 8.23 ms, and the full width at half maximum of the dominating emission peak was 68 nm at 1.53 μm. The large stimulated emission cross section of the Er 3+ was calculated by the McCumber theory. The spectroscopic properties of Er 3+ ion were compared with those in different glasses. The full width at half maximum and σ e are larger than those of other glass hosts, indicating this studied glass may be a potentially useful candidate for high-gain erbium-doped fiber amplifier.     

Blue upconversion luminescence in Tm3+/Yb3+ co-doped new oxyfluoride tellurite glass

The thermal stability, Raman spectrum and upconversion properties of Tm3+/Yb3+ co-doped new oxyfluoride tellurite glass are investigated. The results show that Tm3+/Yb3+ co-doped oxyfluoride tellurite glass possesses good thermal stability, lower phonon energy, and intense upconversion blue luminescence. Under 980-nm laser diode (LD) excitation, the intense blue (475 nm) emission and weak red (649 nm) emission corresponding to the 1G4 → 3H6 and 1G4 → 3F4 transitions of Tm3+ ions respectively,were simultaneously observed at room temperature. The possible upconversion mechanisms are evaluated.The intense blue upconversion luminescence of Tm3+/Yb3+ co-doped oxyfluoride tellurite glass can be used as potential host material for the development of blue upconversion optical devices.     

Spectroscopic properties in Er3＋/yb3＋ Co-doped fluorophosphate glass

Using the technique of high-temperature melting, a new Er3＋/Yb3＋ co-doped fluorophosphate glass was prepared. The absorption and fluorescence spectra were investigated in depth. The effect of Er3＋ and Yb3＋ concentration on the spectroscopic properties of the glass sample was also discussed. According to the Judd Ofelt theory, the oscillator strength was computed. The lifetime of 4113/2 level （t-m） of Er3＋ ions was 8.23 ms, and the full width at half maximum of the dominating emission peak was 68 nm at 1.53 μm. The large stimulated emission cross section of the Er3＋ was calculated by the McCumher theory. The spectroscopic properties of Er3＋ ion were compared with those in different glasses. The full width at half maximum and σe are larger than those of other glass hosts, indicating this studied glass may be a potentially useful candidate for high-gain erbium-doped fiber amplifier.     

Growth and spectroscopic characteristics of Nd-doped PbWO4 crystal

Nd-doped PbWO4 crystals are grown by using the modified Bridgman method.The spectroscopic properties of the crystals are investigated.The changes of the absorption band at 350 nm are discussed for samples annealed at 740℃ and 1040℃.The radiative lifetime of the 4 F 3/2 level is calculated by using the Judd-Ofelt theory according to the absorption spectrum of 0.5 at.% Nd-doped PbWO 4 crystal.The spontaneous Raman scattering properties of the crystals are analysed.     

Enhancement of upconversion luminescence of YAlO3：Er^3＋ by Gd^3＋ doping

Two series of Yb3+-doped silica glasses (YA and YAP) are fabricated using the sol-gel method, and their spectroscopic properties are investigated. The longest fluorescence lifetime of 0.96 ms is obtained in YAP2 and YAP3 glasses. The emission cross-section (σemi) and σemi ×τ of Yb3+ in the YAP1 glass are 1.00 pm2 and 0.94 pm2·ms, respectively. Co-doping with Al and P decreases the hydroxyl group content in the glasses because of the reduction in non-bridging oxygen content. The lowest OH content in the YAP3 glass is 9.6 ppm.     

Growth and spectroscopic characteristics of Nd-doped PbWO₄ crystal

Nd-doped PbWO4 crystals are grown by using the modified Bridgman method.The spectroscopic properties of the crystals are investigated.The changes of the absorption band at 350 nm are discussed for samples annealed at 740℃ and 1040℃.The radiative lifetime of the 4 F 3/2 level is calculated by using the Judd-Ofelt theory according to the absorption spectrum of 0.5 at.% Nd-doped PbWO 4 crystal.The spontaneous Raman scattering properties of the crystals are analysed.     

2-um emission performance of Tm^3＋-Ho^3＋ co-doped tellurite glasses

The emission properties of 2-um region fluorescence of Tm^3＋-Ho^3＋ co-doped tellurite glasses are investigated. Introducing F- ions to the composition of tellurite glasses plays a positive effect on the 2-#m emission. A maximum intensity of 2-um emission is achieved when 1.5-mol% Tm2O3 and 1-mol% Ho203 concentration are doped in the glasses. The emission cross section and gain coefficient of the ^5I8-^5I7 transition of Ho^3＋ are calculated. The emission cross section has a maximum of 1.29×10-20 cm^2 at 2048 nm wavelength. The results indicate that Tm＆3＋-Ho^3＋ co-doped tellurite glasses are suitable for 2-um application.     

Blue Upconversion Luminescence in Tm^3＋／Yb^3＋-Codoped Lead Chloride Tellurite Glass

The upconversion properties of Tm^3 /Yb3 -codoped lead chloride tellurite glass under 980hm excitation were investigated. The intense blue (476nm) emission and weak red (649 nm) emission corresponding to the ^1G4→4 ^3H6 and ^1G4→^3H4 transitions of Tm^3 ions, respectively, were simultaneously observed at room temperature. The dependence of upconversion intensities on excitation power and the possible upconversion mechanisms are evaluated. The intense blue upconversion luminescence of Tm^3 /Yb^3 -codoped lead chloride tellurite glass can be used as potential host material for the development of blue upconversion optical devices.     

Determination of energy constants for Yb3＋/Er3＋ transfer and upconversion codoped phosphate glass

The energy transfer and cooperation upconversion processes are investigated in Yb3＋/Er3＋ codoped phos- phate glass. Based on the measured curves of output power versus incident power, the laser and spectroscopic parameters of the glass are fitted and analyzed. We focus on the resonant energy transfer constant k from Yb3＋ to Er3＋ as well as the cooperation upconversion coefficient Cup from 4113/2 of Era＋. The fitted k and Cup can give almost the same results for different thicknesses of glass disk with the same dop- ing concentrations. The determination of these parameters is helpful for the development of Yb3＋/Er3＋ codoped laser glass.     

The effects of Er3+ ion concentration on 2.0-μm emission performance in Ho3+/Tm3+ co-doped Na5Y9F32 single crystal under 800-nm excitation

Na₅Y₉F₃₂ single crystals doped with ~0.8-mol% Ho³⁺,~1-mol% Tm³⁺,and various Er³⁺ ion concentrations were prepared by a modified Bridgman method.The effects of Er³⁺ion concentration on 2.0-μm emission excited by an800-nm laser diode were investigated with the help of their spectroscopic properties.The intensity of 2.0-μm emission reached to maximum when the Er³⁺ ion concentration was ~1 mol%.The energy transfer mechanisms between Er³⁺,Ho³⁺,and Tm³⁺ ions were identified from the change of the absorption spectra,the emission spectra,and the measured decay curves.The maximum 2.0-μm emission cross section of the Er³⁺/Ho³⁺/Tm³⁺tri-doped Na₅Y₉F₃₂ single crystal reached 5.26 × 10^-21 cm².The gain cross section spectra were calculated according to the absorption and emission cross section spectra.The cross section for ~2.0-μm emission became a positive gain once the inversion level of population was reached 30%.The energy transfer efficiency was further increased by 11.81% through the incorporation of Er³⁺ ion into Ho³⁺/Tm³⁺ system estimated from the measured lifetimes of Ho³⁺/Tm³⁺-and Er³⁺/Ho³⁺/Tm³⁺-doped Na₅Y₉F₃₂single crystals.The present results illustrated that the Er³⁺/Ho³⁺/Tm³⁺tri-doped Na₅Y₉F₃₂ single crystals can be used as promising candidate for 2.0-μm laser.     

Experimental investigation of photolunlinescence spectra of Yb~(3+) sensitized Er~(3+)-doped glass samples in series

Fabrication technology of the Yb3+:Er3+ co-doped glass samples is introduced. Photolummescence (PL) characteristics of a single sample were experimentally investigated. The PL peak intensities of two samples in series were measured and discussed. The results show that the PL peak intensities of two samples in series depend on pump manners and arrangement of the samples. The better amplification ability can be obtained by two samples in series doped with low-concentration ytterbium instead of a single sample doped with high-concentration ytterbium.     

Effect of lithium-potassium mixed alkali on spectroscopic properties of Er^3＋-doped aluminophosphate glasses

Er^3＋-doped lithium-potassium mixed alkali aluminophosphate glasses belonging to the oxide system xK2O-（15-x）Li2O-4B2O3-11Al2O3-5BaO-65P2O5 are obtained in a semi-continuous melting quenching process. Spectroscopic properties of Er^3＋-doped glass matrix have been analysed by fitting the experimental data with the standard Judd-Ofelt theory. It is observed that Judd-Ofelt intensity parameters Ωt（t = 2, 4 and 6） of Er^3＋ change when the second alkali is introduced into glass matrix. The variation of line strength Sed[^4I13/2,^4I15/2] follows the same trend as that of the/26 parameter. The effect of mixed alkali on the spectroscopic properties of the aluminophosphate glasses, such as absorption cross-section, stimulated emission cross-section, spontaneous emission probability, branching ratio and the radiative lifetime, has also been investigated in this paper.     

Er^3＋ and Yb^3＋ Codoped Phosphate Laser Glass for High Power Flashlamp Pumping

A novel yb^3＋-Er^3＋ codoped phosphate glass for high power flashlamp pumping and high repetition rate laser at 1.54μm, designated EAT5-2, is developed. The weight-loss rate of is 1.3 × 10^-5 gcm^-2h^-1 in boiling water, which is comparable to Kigre＇s QX-Er glass. Some spectroscopic parameters are analysed by Judd-Ofelt theory and McCumber theory. The emission cross section is calculated to be 0.73 × 10^-20 cm^2. The thermo-mechanical properties of EAT5-2 are modified after an ion-exchange chemical strengthening process in a KNO3/NaNO3 molten salt bath. The thresholds for optical damage from the flashlamp pumping are tested on glass rods. A repetition rate of 15 Hz is achieved for chemically strengthened glass. The laser experimental results at 1.54 μm from flashlamp pumping are also reported.     

Empowering perovskite PbTiO3 nanoparticles with enhanced up-conversion luminescence and thermal sensitivity by introducing Er3+ dopant

Up-convertion(UC)perovskite Er³⁺-doped Pb TiO3(Er-PTO)nanoparticles with green and red emissions were synthesized via the hydrothermal method.The UC properties were manipulated by adjusting the concentration of Er³⁺ ions dopant.The green emission intensity was decreased as the doping concentration increased from 1% to 4%(mole fraction),whereas the red emission intensity was increased.The influences of Er³⁺ ions on the temperature-sensing performance were further investigated.The results demonstrated that Er-PTO nanoparticles with doping 1% Er³⁺ ions possessed a sensitivity of3.1×10^-3 K^-1 at 475 K,presenting a high potential in optical heating devices.     

Spectroscopic properties and mechanism of Tm^3＋/Er^3＋/Yb^3＋ co-doped oxyfluorogermanate glass ceramics containing BaF2 nanocrystals

Transparent Tm^3＋/Er^3＋/yb^3＋ co-doped oxyfluorogermanate glass ceramics containing BaF2 nanocrystals are prepared. Under excitation of a 980-nm laser diode （LD）, compared with the glass before heat treatment, the Tm^3＋/Er^3＋/yb^3＋ co-doped oxyfluorogermanate glass ceramics can emit intense blue, green and red up-conversion luminescence and Stark- split peaks; X-ray diffraction （XRD） and transmission electron microscope （TEM） results show that BaF2 nanocrystals with an average diameter of 20 nm are precipitated from the glass matrix. Stark splitting of the up-conversion luminescence peaks in the glass ceramics indicates that Tm^3＋, Er^3＋ and （or） Yb^3＋ ions are incorporated into the BaF2 nanocrystals. The up-conversion luminescence intensities of Tm^3＋, Er^3＋ and the splitting degree of luminescence peaks in the glass ceramics increase significantly with the increase of heat treat temperature and heat treat time extension. In addition, the possible energy transfer process between rare earth ions and the up-conversion luminescence mechanism are also proposed.     

Properties of steady-state in Er3+-Yb3+ co-doped phosphate glass for optical waveguide laser

Transitions of laser diode (LD) pumped Er3+-Yb3+ co-doped glass laser are rather complicated. Considering energy transfer between Er3+ and Yb3+ ions, cross-relaxation, upconversion luminescence, and other transition processes, rate equations of quasi-three energy-level-system of the Er3+-Yb3+ co-doped laser are presented. The output characteristics are also calculated and analyzed in detail. The results show that Er3+-Yb3+ co-doped phosphate waveguide lasers with high slope efficiency and low threshold can be achieved.     

QUANTUM EFFICIENCY AND MULTIPHONON NONRADIATIVE TRANSITION OF Er3+ IONS IN FLUORIDE GLASS

Optical absorption, emission and excitation spectra, lifetimes of ⁴S_3/2 state and ⁴F_9/2 state from 10K to 500K, and Raman spectra were measured for Er³⁺ ions in fluoride glass. The radiative transition probabilities were calculated on the basis of Judd-Ofelt theory. The nonradiative transition probabilities and the quantum efficiencies were determined by calculating the difference between the measured lifetimes and the calculated radiative transition probabilities. The temperature dependence of nonradiative transition provavility was investigated using the Huang-Rhys theory of multiphonon relaxation , in which two kinds of phonons as well as the parameter s were taken into consideration. A fairly good agreement of the theoretical calculation with the experimental results has been obtained. The value of s is estimated and the effect of s is discussed.     

Effect of aluminum co-doping on the formation of Yb2+ in Ytterbium-doped high silica glass

Yb3+ singly doped and Yb3+/Al3+ co-doped high silica glass samples are prepared,and their luminescent properties are investigated.Al3+ is considered as a beneficial activator for Yb3+-doped glass.However,the experimental result shows that the addition of Al3+ results in the transformation from Yb3+ to Yb2+ and the improvement in the photon luminescence of Yb2+.These characteristics indicate the role of Al3+ in Yb3+-doped glass.     

Investigation on Nonradiative Decay of the Er^3＋^4I13/2 → ^4I15/2 Transition in Different Tellurite Glass Matrix

Three kinds of Er^3＋-doped tellurite glasses with different hydroxyl groups are prepared by the conventional melt-quenching method. Infrared spectra are measured to estimate the exact content of OH^- groups in samples. The maximum phonon energy in glasses are obtained by measuring the Raman scattering spectra. The strength parameters Ωt （t = 2, 4, 6） for all the samples are calculated and compared. The nonradiative decay rate of the Er^3＋ ^4I13/2 → ^4I15/2 transition are calculated for the glass samples with different phonon energy and OH^- group contents. Finally, the effect of OH^- groups on fluorescence decay rate of Er^3＋ is analysed, the constant KOH-Er of TWN, TZPL and TZL glasses are calculated to be 9.2 × 10^-19 cm^4s^-1, 5.9 × 10^-19 cm^4s^-1, and 3.5 × 10^-19 cm^4s^-1, respectively.