Electrical characteristics and low-temperature sintering of BiFeO3-modified Pb(Zr,Ti)O3–Pb(Fe2/3W1/3)O3–Pb(Mn1/3Nb2/3)O3 ceramics with ZnO addition

Effects of ZnO addition on electrical properties and low-temperature sintering of BiFeO₃-modified Pb(Zr,Ti)O₃–Pb(Fe_2/3W_1/3)O₃–Pb(Mn_1/3Nb_2/3)O₃ were investigated. The investigations revealed that the sintering temperature can be decreased to 950 °C, and the favorable properties were obtained with 0.10 wt% ZnO added ceramics. The electrical properties were as follows: d₃₃ = 313 pC/N, K_p = 0.56, tan δ = 0.0053, ε_r = 1407 and T_c = 295 °C, which showed that this system was a promising material for the multilayer devices application.     

Effects of Li2CO3 on the sintering behavior and piezoelectric properties of Bi2O3-excess (Bi0.5Na0.5)0.94Ba0.06TiO3 ceramics

(Bi_0.5Na_0.5)_0.94Ba_0.06TiO₃ ceramics doped with Li₂CO₃ and Bi₂O₃ as sintering aids were manufactured, and their micro structural, dielectric and piezoelectric properties were investigated. All specimens could be well sintered at a low-temperature of 1080 °C. The bulk density of the specimens doped with a small amount of Li₂CO₃ was enhanced. The dielectric and piezoelectric properties of ceramics were investigated with different amounts of Li₂CO₃ substitutions. High electrical properties of d₃₃ = 167 pC/N, k_p = 0.34, P_r = 40 μC/cm² and E_c = 38 kV/cm were obtained from the specimen containing 0.1 mol% of Li₂CO₃ sintered at 1080 °C.     

Effects of nano-carbon doping and sintering temperature on microstructure and properties of MgB2

We fabricated nano-carbon (NC) doped MgB₂ bulks using an in situ process in order to improve the critical current density (J_c) under a high magnetic field and evaluated the correlated effects of the doped carbon content and sintering temperature on the phase formation, microstructure and critical properties. MgB_2−xC_x bulks with x = 0 and 0.05 were fabricated by pressing the powder into pellets and sintering at 800 °C, 900 °C, or 1000 °C for 30 min.We observed that NC was an effective dopant for MgB₂ and that part of it was incorporated into the MgB₂ while the other part remained (undoped), which reduced the grain size. The actual C content was estimated to be 68–90% of the nominal content. The NC doped samples exhibited lower T_c values and better J_c(B) behavior than the undoped samples. The doped sample sintered at 900 °C showed the highest J_c value due to its high doping level, small amount of second phase, and fine grains. On the other hand, the J_c was decreased at a sintering temperature of 1000 °C as a result of the formation of MgB₄ phase.     

Effects of sintering temperature and Bi2O3 content on microstructure and magnetic properties of LiZn ferrites

The effects of sintering temperature and Bi₂O₃ content on the microstructure and magnetic properties of lithium–zinc (LiZn) ferrites prepared by a conventional ceramic method were investigated. The results show that the densification behavior and grain growth rate were greatly improved by the addition of Bi₂O₃, because a liquid phase sintering occurred during the sintering process at high temperature due to the low-melting point of Bi₂O₃ (825 °C). X-ray diffraction (XRD) patterns of the slightly doped samples did not reveal the appearance of any phase other than spinel LiZn ferrite. However, the secondary phase of perovskite BiFeO₃ was detected for Bi₂O₃ content of more than 0.25 wt%. The studies further show that Bi oxide was present at grain boundary, and promoted the grain growth as reaction center at lower temperature. A high saturation magnetization, squareness ratio, minimum ferromagnetic resonance linewidth and low coercive force were obtained for the sample with 1.00 wt% Bi₂O additive at lower sintering temperature (1100 °C).     

Lithium ion conductive glass–ceramics with Li3Fe2(PO4)3 and YAG laser-induced local crystallization in lithium iron phosphate glasses

The glasses with the composition of 37.5Li₂O–(25 − x)Fe₂O₃–xNb₂O₅–37.5P₂O₅ (mol%) (x = 5,10,15) are prepared, and it is found that the addition of Nb₂O₅ is effective for the glass formation in the lithium iron phosphate system. The glass–ceramics consisting of Nasicon-type Li₃Fe₂(PO₄)₃ crystals with an orthorhombic structure are developed through conventional crystallization in an electric furnace, showing electrical conductivities of 3 × 10^− 6 Scm^− 1 at room temperature and the activation energies of 0.48 eV (x = 5) and 0.51 eV (x = 10) for Li⁺ ion conduction in the temperature range of 30–200 °C. A continuous wave Nd:YAG laser (wavelength: 1064 nm) with powers of 0.14–0.30 W and a scanning speed of 10 μm/s is irradiated onto the surface of the glasses, and the formation of Li₃Fe₂(PO₄)₃ crystals is confirmed from XRD analyses and micro-Raman scattering spectra. The crystallization of the precursor glasses is considered as new route for the fabrication of Li₃Fe₂(PO₄)₃ crystals being candidates for use as electrolyte materials in lithium ion secondary batteries.     

Microwave dielectric properties of (1 − x)(Mg0.95Co0.05)TiO3–x(Na0.5La0.5)TiO3 ceramic system

The microstructures and the microwave dielectric properties of the (1 − x)(Mg_0.95Co_0.05)TiO₃–x(Na_0.5La_0.5)TiO₃ ceramic system were investigated. Two-phase system was confirmed by the XRD patterns and the EDX analysis. A co-existed second phase (Mg_0.95Co_0.05)Ti₂O₅ was also detected. The microwave dielectric properties are strongly related to the density and the matrix of the specimen. A new microwave dielectric material 0.88(Mg_0.95Co_0.05)TiO₃–0.12(Na_0.5La_0.5)TiO₃, possessing an excellent combination of dielectric properties: ε_r  22.36, Q × f  110,000 GHz (at 9 GHz), τ_f  2.9 ppm/°C), is proposed as a candidate dielectric for GPS patch antennas.     

Structure, ferroelectric and piezoelectric properties of (Bi1−x−yNa0.925−x−yLi0.075)0.5BaxSryTiO3 lead-free piezoelectric ceramics

Lead-free multi-component ceramics (Bi_1−x−yNa_{0.925−x−y}Li_0.075)_0.5Ba_xSr_yTiO₃ have been prepared by an ordinary sintering technique and their structure and electrical properties have been studied. All the ceramics can be well-sintered at 1100 °C. X-ray diffraction patterns shows that Li⁺, Ba²⁺ and Sr²⁺ diffuse into the Bi_0.5Na_0.5TiO₃ lattices to form a new solid solution with a pure perovskite structure, and a morphotropic phase boundary (MPB) is formed at 0.04 < x < 0.08. As compared to pure Bi_0.5Na_0.5TiO₃ ceramic, the coercive field E_C of the ceramics decreases greatly and the remanent polarization P_r of the ceramics increases significantly after the formation of the multi-component solid solution. Due to the MPB, lower E_C and higher P_r, the piezoelectricity of the ceramics is greatly improved. For the ceramics with the compositions near the MPB (x = 0.04–0.08 and y = 0.02–0.04), piezoelectric coefficient d₃₃ = 133–193 pC/N and planar electromechanical coupling factor k_P = 16.2–32.1%. The depolarization temperature T_d reaches a minimum value near the MPB. The temperature dependences of the ferroelectric and dielectric properties suggest that the ceramics may contain both the polar and non-polar regions at temperatures near/above T_d.     

Dielectric properties of barium titanate ceramics modified by SiO2 and by BaO-SiO2

The influence of SiO₂ on the dielectric properties of barium titanate ceramics was investigated. SiO₂ had been doped solely and together with BaO into barium titanate before calcination. X-ray diffraction showed that all the ceramics were of a pure perovskite phase after sintering at 1275 °C for 2 h. For SiO₂-doping, there was about 2.5 °C increase in Curie temperature per molar percentage of doping and the leakage current was obviously increased, especially at low voltages for relatively high doping levels. While for the co-doping of SiO₂ and BaO, there was little change in Curie temperature. The point defects formed through the dopings were proposed responsible for the effects. It was suggested that SiO₂ is important to barium titanate ceramics not only for sintering but also for modifying their properties.     

Synthesis and magnetic properties of hard magnetic (CoFe2O4)-soft magnetic (Fe3O4) nano-composite ceramics by SPS technology

CoFe₂O₄/Fe₃O₄ nano-composite ceramics were synthesized by Spark Plasma Sintering. The X-ray diffraction patterns show that all samples are composed of CoFe₂O₄ and Fe₃O₄ phases when the sintering temperature is below 900 °C. It is found that the magnetic properties strongly depend on the sintering temperature. The two-step hysteresis loops for samples sintered below 500 °C are observed, but when sintering temperature reaches 500 °C, the step disappears, which indicates that the CoFe₂O₄ and Fe₃O₄ are well exchange coupled. As the sintering temperature increases from 500 to 800 °C, the results of X-ray diffractometer indicate the constriction of crystalline regions due to the ion diffusion at the interfaces of CoFe₂O₄/Fe₃O₄ phases, which have great impact on the magnetic properties.     

Dielectric and impedance measurements on (1−x)Ba(Fe1/2Ta1/2)O3-xBa(Zn1/3Ta2/3)O3 ceramics

In this work, ((1−x)Ba(Fe_1/2Ta_1/2)O₃-xBa(Zn_1/3Ta_2/3)O₃), ((1−x)BFT-xBZT) ceramics with x = 0.00–0.12 were synthesized by the solid–state reaction method. X-ray diffraction data revealed that both the powders and ceramics were of a pure-phase cubic perovskite structure. All ceramics showed large dielectric constants. For the x = 0.12 sample, a very high dielectric constant (>20,600) was observed. A lowering in the dielectric loss compared to pure BFT ceramics was observed with the BZT addition. The impedance measurements indicated that BZT has a strong effect on the bulk grain and grain boundary resistance of BFT ceramics. These results are in agreement with the measured dielectric properties. Based on dielectric and impedance results, (1−x)BFT-xBZT ceramics could be of great interest for high performance dielectric materials applications due their giant dielectric constant behavior.     

Improving microwave dielectric properties of La2.98/3Sr0.01(Mg0.5Sn0.5)O3 ceramics with CuO additive

The microwave dielectric properties of CuO-doped La_2.98/3Sr_0.01(Mg_0.5Sn_0.5)O₃ ceramics were investigated with a view to their application in microwave devices. CuO-doped La_2.98/3Sr_0.01(Mg_0.5Sn_0.5)O₃ ceramics were prepared by the conventional solid-state method. The X-ray diffraction patterns of CuO-doped La_2.98/3Sr_0.01(Mg_0.5Sn_0.5)O₃ ceramics exhibited no significant variation of phase with sintering temperature. By adding 0.75 wt.% CuO, a dielectric constant of 20.07, a quality factor (Q × f) of 63,000 GHz, and a temperature coefficient of resonant frequency τ_f (−77.0 ppm/°C) were obtained when La_2.98/3Sr_0.01(Mg_0.5Sn_0.5)O₃ ceramics were sintered at 1500 °C for 4 h.     

The effect of Si surface nitridation on the interfacial structure and electrical properties of (La2O3)0.5(SiO2)0.5 high-k gate dielectric films

Thermal stability, interfacial structures and electrical properties of amorphous (La₂O₃)_0.5(SiO₂)_0.5 (LSO) films deposited by using pulsed laser deposition (PLD) on Si (1 0 0) and NH₃ nitrided Si (1 0 0) substrates were comparatively investigated. The LSO films keep the amorphous state up to a high annealing temperature of 900 °C. HRTEM observations and XPS analyses showed that the surface nitridation of silicon wafer using NH₃ can result in the formation of the passivation layer, which effectively suppresses the excessive growth of the interfacial layer between LSO film and silicon wafer after high-temperature annealing process. The Pt/LSO/nitrided Si capacitors annealed at high temperature exhibit smaller CET and EOT, a less flatband voltage shift, a negligible hysteresis loop, a smaller equivalent dielectric charge density, and a much lower gate leakage current density as compared with that of the Pt/LSO/Si capacitors without Si surface nitridation.     

Low temperature fired Ni-Cu-Zn ferrite with Bi4Ti3O12

The Ni-Cu-Zn ferrites with different contents of Bi₄Ti₃O₁₂ ceramics (1-8 wt%) as sintering additives were prepared by the usual ceramic technology and sintered at 900 °C to adapt to the low temperature co-fired ceramic (LTCC) technology. The magnetic and dielectric properties of the ferrite can be effectively improved with the effect of an appropriate amount of Bi₄Ti₃O₁₂. For all samples, the ferrite sintered with 2 wt% Bi₄Ti₃O₁₂ has relatively high density (98.8%) and permeability, while the ferrite with 8 wt% Bi₄Ti₃O₁₂ has relatively good dielectric properties in a wide frequency range. The influences of Bi₄Ti₃O₁₂ addition on microstructure, magnetic and dielectric properties of the ferrite have been discussed.     

Structure and dielectric studies of nano-composite Fe2O3: BaTiO3 prepared by sol-gel method

Nano-structure pure barium titanate (BaTiO₃) and that was doped with iron oxide (Fe₂O₃), have been prepared by sol-gel method, using barium acetate (Ba(Ac)₂) and titanium butoxide (Ti(C₄H₉O)₄), as precursors. The as-grown prepared samples by sol-gel technique were found to be amorphous, which crystallized to the tetragonal phase after synthesized at 750 °C in air for 1 h as detected from the XRD patterns. The XRD data were confirmed by transmission electron microscope (TEM). The dielectric properties namely; dielectric constant (ε′) and loss tangent (tan δ) in the frequency range between 42 Hz and 1 MHz, at range of temperature 25-250 °C were investigated. The temperature dependence of ε′ and tan δ for the undoped and doped materials, at 1 kHz, was also investigated. As a result, tan δ increased rapidly with decreasing temperature below 125 °C (Curie temperature) while above this temperature, tan δ shows temperature independent. As a result, below and above Curie temperature, ferroelectric phase and paraelectric phase of BaTiO₃ can be obtained, respectively.     

(Ba, Ca)(Ti, Zr)O3-BiFeO3 lead-free piezoelectric ceramics

Effects of BiFeO₃ (BFO) content on the microstructure and electrical properties of Ba_0.85Ca_0.15Ti_0.90Zr_0.10O₃ (BCTZ) ceramics prepared by normal sintering in air were investigated. A stable solid solution is formed between BCTZ and BFO. The grain size gradually becomes smaller, and the ceramics become denser with increasing the BFO content. The Curie temperature, dielectric constant, and dielectric loss of BCTZ ceramics decrease simultaneously with the introduction of BFO. Moreover, the remanent polarization reaches a maximum at x = 0.2 mol%, and the coercive field continuously increases with increasing the BFO content due to the introduction of BFO with a higher coercive field. Improved piezoelectric properties (d₃₃ ∼ 405 pC/N and k_p ∼ 0.44) are demonstrated for the BCTZ ceramic with x = 0.2 mol%.     

Synthesis, phase and microstructure characteristics of Pb(Zr0.52Ti0.48)O3–(Bi3.25La0.75)Ti3O12 ceramics

Ceramics with formula (1 − x)Pb(Zr_0.52Ti_0.48)O₃–x(Bi_3.25La_0.75)Ti₃O₁₂ (when x = 0, 0.1, 0.3, 0.5, 0.7, 0.9 and 1.0) were prepared by a solid-state mixed-oxide method and sintered at temperatures between 950 °C and 1250 °C. It was found that the optimum sintering temperature was 1150 °C at which all the samples had densities at least 95% of theoretical values. Phase analysis using X-ray diffraction indicated the existence of BLT- as well as PZT-based solid solutions with corresponding lattice distortion. Scanning electron micrographs of ceramic surfaces showed a plate-like structure in BLT-rich phase while the typical grain structure was observed for PZT-rich phase. The grain sizes of both pure BLT and PZT ceramics were found to decrease as the relative amount of the other phase increased. This study suggested that tailoring of properties of this PZT–BLT system was possible especially on the BLT-rich side due to its large solubility limit.     

Novel nanostructures of β-Ga2O3 synthesized by thermal evaporation

In this study, we report the novel β-Ga₂O₃ nanostructures synthesized by the thermal evaporation of Ga droplet in the presence of Au catalysts at 900 °C. The morphology and structure of the products were analyzed by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffraction (XRD). The single-crystalline β-Ga₂O₃ nanosheets have lateral dimensions up to several tens of microns. Large arrays of column-like layered crystal β-Ga₂O₃ structures that consisted of many nanosheets were formed on the Au-coated silicon substrate under the suitable vapor concentration. These novel β-Ga₂O₃ nanostructures are expected to have potential application in functional nanodevices.     

Preparation and properties of composite ceramic coating containing Al2O3–ZrO2–Y2O3 on AZ91D magnesium alloy by plasma electrolytic oxidation

A composite ceramic coating containing Al₂O₃–ZrO₂–Y₂O₃ was successfully prepared on AZ91D magnesium alloy by plasma electrolytic oxidation (PEO) technique in an alkaline aluminate electrolyte. The morphology, elemental and phase composition, corrosion behavior and thermal stability of the uncoated and coated samples were studied by environmental scanning electron microscopy (ESEM), energy dispersive X-ray spectrometer (EDS), X-ray diffractometer (XRD), electrochemical corrosion test, high temperature oxidation test and thermal shock test. The results showed that the composite ceramic coating was composed of Al₂O₃, c-ZrO₂, t-ZrO₂, Y₂O₃ and some magnesium compounds, such as MgO, MgF₂ and MgAl₂O₄. After PEO treatment, the corrosion potential of AZ91D alloy was increased and the corrosion current density was significantly reduced. Besides, the coated magnesium alloys also showed excellent high temperature oxidation resistance and thermal shock resistance at 500 °C environment.     

Synthesis and magnetic properties of single-crystalline BaFe12O19 nanoparticles

Rod-like and platelet-like nanoparticles of simple-crystalline barium hexaferrite (BaFe₁₂O₁₉) have been synthesized by the molten salt method. Both particle size and morphology change with the reaction temperature and time. The easy magnetization direction (0 0 l) of the BaFe₁₂O₁₉ nanoparticles has been observed directly by performing X-ray diffraction on powders aligned at 0.5 T magnetic field. The magnetic properties of the BaFe₁₂O₁₉ magnet were investigated with various sintering temperatures. The maximum values of saturation magnetization (σ_s=65.8 emu/g), remanent magnetization (σ_r=56 emu/g) and coercivity field (H_ic=5251 Oe) of the aligned samples occurred at the sintering temperatures of 1100 °C. These results indicate that BaFe₁₂O₁₉ nanoparticles synthesized by the molten salt method should enable detailed investigation of the size-dependent evolution of magnetism, microwave absorption, and realization of a nanodevice of magnetic media.     

CaCu3Ti4O12陶瓷的微观结构和电学性能

利用传统的固相反应工艺，在不同的烧结温度下制备了一系列的CaCu₃Ti₄O₁₂陶瓷样品，考察了其微观结构以及介电和复阻抗方面的电学性质.研究发现这些样品在微观结构方面可分为三种类型，高介电性与微观结构有着密切的关联性.室温下，样品的低频介电常数随陶瓷晶粒尺寸的增大而提高.随着测试温度的升高，不同微观结构类型的样品呈现出不同的电学性质的变化，但其中也存在着一些相同的特征.高温下，介电频谱呈现出一个低频介电响应和两个类Debye型弛豫色散，复阻抗谱呈现出三个Cole-Cole半圆弧.将实验上观测到的电学性质的起因归于陶瓷多晶微结构中的晶畴、晶界和晶粒内的缺陷. 关键词： 3Ti₄O₁₂')" href="#">CaCu₃Ti₄O₁₂ 微观结构 电学性质