Structure and dielectric studies of nano-composite Fe2O3: BaTiO3 prepared by sol-gel method

Nano-structure pure barium titanate (BaTiO₃) and that was doped with iron oxide (Fe₂O₃), have been prepared by sol-gel method, using barium acetate (Ba(Ac)₂) and titanium butoxide (Ti(C₄H₉O)₄), as precursors. The as-grown prepared samples by sol-gel technique were found to be amorphous, which crystallized to the tetragonal phase after synthesized at 750 °C in air for 1 h as detected from the XRD patterns. The XRD data were confirmed by transmission electron microscope (TEM). The dielectric properties namely; dielectric constant (ε′) and loss tangent (tan δ) in the frequency range between 42 Hz and 1 MHz, at range of temperature 25-250 °C were investigated. The temperature dependence of ε′ and tan δ for the undoped and doped materials, at 1 kHz, was also investigated. As a result, tan δ increased rapidly with decreasing temperature below 125 °C (Curie temperature) while above this temperature, tan δ shows temperature independent. As a result, below and above Curie temperature, ferroelectric phase and paraelectric phase of BaTiO₃ can be obtained, respectively.