Scanning tunneling microscopy/spectroscopy on multi-layered cuprate superconductor Ba2Ca5Cu6O12 (O1−x Fx)2

Scanning tunneling microscopy/spectroscopy (STM/STS) measurements on multi-layered cuprate superconductor Ba₂Ca₅Cu₆O₁₂ (O_1−x F_x)₂ are carried out. STM topographies show randomly distributed bright spot structures with a typical spot size of 0.8 nm. These bright spots are occupied about 28% per one unit cell of c-plane, which is comparable to the regular amount of apical oxygen of 20% obtained from element analysis. Tunneling spectra simultaneously show both the small and the large gap structures. These gap sizes at 4.9 K are about Δ 15 meV and 90 meV, respectively. The small gap structure disappears at the temperature close to T_C, while the large gap persists up to 200 K. Therefore, these features correspond to the superconducting gap and pseudogap, respectively. These facts give evidence for some ordered state with large energy scale even in the superconducting state. For the superconducting gap, the ratio of 2Δ/K_BT_C = 4.9 is obtained with T_C = 70 K, which is determined from temperature dependence of the tunneling spectra.     

Co:LaMgAl11O19 saturable absorber Q-switch for a 1.319 μm Nd:YAG laser

Passively Q-switched output of a flashlamp-pumped 1.319 μm Nd:YAG laser is realized by using Co²⁺:LaMgAl₁₁O₁₉ (Co:LMA) as saturable absorber. When initial transmission of the saturable absorber T₀ is 78%, a Q-switched output pulse with pulse width (FWHM) 44.8 ns and pulse energy 17.4 mJ is obtained, corresponding to 19.3% of the free-running energy under the equal pumping energy of 45.4 J. The experimental results show that the higher T₀ will result in a lower pumping threshold of the laser, but lower T₀ can make the laser generate pulses with higher single-pulse energy, narrower pulse width, and accordingly higher peak power.     

Improving microwave dielectric properties of La2.98/3Sr0.01(Mg0.5Sn0.5)O3 ceramics with CuO additive

The microwave dielectric properties of CuO-doped La_2.98/3Sr_0.01(Mg_0.5Sn_0.5)O₃ ceramics were investigated with a view to their application in microwave devices. CuO-doped La_2.98/3Sr_0.01(Mg_0.5Sn_0.5)O₃ ceramics were prepared by the conventional solid-state method. The X-ray diffraction patterns of CuO-doped La_2.98/3Sr_0.01(Mg_0.5Sn_0.5)O₃ ceramics exhibited no significant variation of phase with sintering temperature. By adding 0.75 wt.% CuO, a dielectric constant of 20.07, a quality factor (Q × f) of 63,000 GHz, and a temperature coefficient of resonant frequency τ_f (−77.0 ppm/°C) were obtained when La_2.98/3Sr_0.01(Mg_0.5Sn_0.5)O₃ ceramics were sintered at 1500 °C for 4 h.     

Microstructures and microwave dielectric properties of La1-xBx(Mg0.5Sn0.5)O3 ceramics

The microwave dielectric properties of La_1-xB_x(Mg_0.5Sn_0.5)O₃ ceramics were examined with a view to their exploitation for mobile communication. The La_1-xB_x(Mg_0.5Sn_0.5)O₃ ceramics were prepared by the conventional solid-state method with various sintering temperatures. The X-ray diffraction patterns of the La_0.995B_0.005(Mg_0.5Sn_0.5)O₃ ceramics revealed no significant variation of phase with sintering temperatures. A maximum apparent density of 6.58 g/cm³, a dielectric constant (ε_r) of 19.8, a quality factor (Q × f) of 41,800 GHz, and a temperature coefficient of resonant frequency (τ_f) of −86 ppm/°C were obtained for La_0.995B_0.005(Mg_0.5Sn_0.5)O₃ ceramics that were sintered at 1500 °C for 4 h.     

Preparation and characterization of amine-functionalized SiO2/TiO2 films for formaldehyde degradation

This paper investigated the gaseous formaldehyde degradation by the amine-functionalized SiO₂/TiO₂ photocatalytic films for improving indoor air quality. The films were synthesized via the co-condensation reaction of methyltrimethoxysilane (MTMOS) and 3-aminopropyltrimethoxysilane (APTMS). The physicochemical properties of prepared photocatalysts were characterized with N₂ adsorption/desorption isotherms measurement, X-ray diffraction (XRD) and Fourier Transform Infrared spectroscopy (FT/IR). The effect of amine-functional groups and the ratio of MTMOS/APTMS precursors on the formaldehyde adsorption and photocatalytic degradation were investigated. The results showed that the formaldehyde adsorption and photocatalytic degradation of the APTMS-functionalized SiO₂/TiO₂ film was higher than that of SiO₂/TiO₂ film due to the surface adsorption on amine sites and the relatively high of the specific surface area of the APTMS-functionalized SiO₂/TiO₂ film (15 times higher than SiO₂/TiO₂). The enhancement of the formaldehyde degradation of the film can be attributed to the synergetic effect of adsorption and subsequent photocatalytic decomposition. The repeatability of photocatalytic film was also tested and the degradation efficiency was 91.0% of initial efficiency after seven cycles.     

Anomalous upper critical field in ternary iron-silicide superconductor Lu2Fe3Si5

We report the upper critical field H_c2 in a ternary iron-silicide superconductor Lu₂Fe₃Si₅ with T_c  6 K obtained by the resistivity measurements. We find that H_c2 increases linearly with decreasing temperature down to T_c/3, and H_c2(T = 0) exceeds the orbital depairing field described by the Werthamer–Helfand–Hohenberg theory. We also find that the anisotropy of H_c2 is nearly independent of temperature and the angular dependence of H_c2 is well-described by the anisotropic Ginzburg–Landau model. These results strongly indicate the presence of two distinct superconducting gaps in Lu₂Fe₃Si₅ although the behavior is slightly different from that of the typical two-gap superconductor MgB₂.     

立方(Ba0.5Sr0.5)TiO3高压诱导带隙变化的第一性原理研究

采用基于密度泛函理论(DFT)的第一性原理计算研究了 (Ba_0.5Sr_0.5)TiO₃ (BST) 晶体在高压下的电子结构及能带变化行为. 研究结果发现,随着压强的增加,BST能带间隙先增加,在压强为55 GPa时达到最大值,然后减小,这些有趣的结果将有助于开发与设计新的BST铁电器件. 进一步地,通过电子态密度和密度分布图的研究分析可知:在低压区域(055 GPa),则是出现的离域现象占主导(电子的离域作用超过键态的作用),从而使带隙减小. 关键词： 钛酸锶钡 第一性原理 高压 能带间隙     

Structure and properties of the one-dimensional cobalt oxide CaCo2O4

We have studied crystal structure and transport properties of the quasi one-dimensional cobalt oxide CaCo₂O₄. The CaCo₂O₄ phase crystallizes in calcium-ferrite type structure, which consists of a corner- and edge-shared CoO₆ octahedron network including one-dimensional double chains. Large thermoelectric power (S  150 μV/K at 390 K) with metallic temperature dependence of S, moderate resistivity (ρ  2.9 × 10⁻¹ Ω cm at 390 K) with carrier localization at low temperature, and normal thermal conductivity (κ  6.3 W/Km at 390 K) were observed. The phonon mean-free path was calculated from the observed data, as a function of temperature. The long phonon mean-free path (l  24 Å at 300 K) implies that the thermal conductivity could be suppressed by impurity scattering of phonons with partial element substitution.     

Structure, ferroelectric and piezoelectric properties of (Bi1−x−yNa0.925−x−yLi0.075)0.5BaxSryTiO3 lead-free piezoelectric ceramics

Lead-free multi-component ceramics (Bi_1−x−yNa_{0.925−x−y}Li_0.075)_0.5Ba_xSr_yTiO₃ have been prepared by an ordinary sintering technique and their structure and electrical properties have been studied. All the ceramics can be well-sintered at 1100 °C. X-ray diffraction patterns shows that Li⁺, Ba²⁺ and Sr²⁺ diffuse into the Bi_0.5Na_0.5TiO₃ lattices to form a new solid solution with a pure perovskite structure, and a morphotropic phase boundary (MPB) is formed at 0.04 < x < 0.08. As compared to pure Bi_0.5Na_0.5TiO₃ ceramic, the coercive field E_C of the ceramics decreases greatly and the remanent polarization P_r of the ceramics increases significantly after the formation of the multi-component solid solution. Due to the MPB, lower E_C and higher P_r, the piezoelectricity of the ceramics is greatly improved. For the ceramics with the compositions near the MPB (x = 0.04–0.08 and y = 0.02–0.04), piezoelectric coefficient d₃₃ = 133–193 pC/N and planar electromechanical coupling factor k_P = 16.2–32.1%. The depolarization temperature T_d reaches a minimum value near the MPB. The temperature dependences of the ferroelectric and dielectric properties suggest that the ceramics may contain both the polar and non-polar regions at temperatures near/above T_d.     

Effect of the synthesis route on the structural properties and shape of the indium oxide (In2O3) nano-particles

Nano-crystalline indium oxide (In₂O₃) particles have been synthesized by sol–gel and hydro-thermal techniques. A simple hydro-alcoholic solution consisting indium nitrate hydrate and citric acid (in sol–gel method) and 1, 4-butandiol (in hydro-thermal method) have been utilized. The structural properties of indium oxide nano-powders annealed at 450 °C (for both methods) have been characterized by the X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), and specific surface area (SSA) analysis. Structural analysis of the samples shows cubic phase in sol–gel and cubic-hexagonal phase mixture in hydro-thermally prepared particles. The nano-particles prepared by sol–gel method have nearly spherical shape, whereas hydro-thermally-made ones display wire- and needle-like shape in addition to the spherical shape. The obtained In₂O₃ nano-particles surface areas were 23.2 and 55.3 in sol–gel and hydro-thermal methods, respectively. The optical direct band gap of In₂O₃ nano-particles were determined to be 4.32 and 4.24 eV for sol–gel and hydro-thermal methods, respectively. These values exhibit 0.5 eV blue shift from that the bulk In₂O₃ (3.75 eV), which is related to the particle size reduction and approaching the quantum confinement limit of nano-particles.     

Conversion of egg shell membrane to inorganic porous CexZr1−xO2 fibrous network

The binary system CeO₂–ZrO₂ is thermally stable and has superior reduction–oxidation properties. It has been commonly used in the three-way catalytic converters for automobiles. In this work, an inorganic biomorphic porous Ce_xZr_1−xO₂ fibrous network was successfully synthesized by using the egg shell membrane (ESM) as templates, and its morphology was a perfect replica of the original ESM. The synthesis involved a simple infiltration and calcination process. A fresh ESM was peeled from a chicken egg shell. It was soaked in a Ce(NO₃)₃ and Zr(NO₃)₄ mixture before it was calcined at 700 °C in ambient environment. The fibers in the biomorphic network had diameter ranged from 1 to 4 μm, and they were composed of Ce_xZr_1−xO₂ nanocrystallites having an average grain size of 10 nm.     

Structure and reaction pathways of methyl lactate on Pd(1 1 1)

The adsorption and reaction of methyl lactate (CH₃CH(OH)COOCH₃) is studied in ultrahigh vacuum on a Pd(1 1 1) surface using temperature-programmed desorption (TPD) and reflection–absorption infrared spectroscopy (RAIRS). Methyl lactate reacts at relatively low temperatures (220 K) by O–H bond scission. This intermediate can either react with hydrogen to reform methyl lactate at 280–300 K or undergo β-hydride elimination to form flat-lying methyl pyruvate. This decomposes to form acetyl and methoxy carbonyl species as found previously following methyl pyruvate adsorption on Pd(1 1 1). These species predominantly react to form carbon monoxide, methane and hydrogen.     

Structural and electrical properties of (Na0.85K0.15)0.5Bi0.5TiO3 thin films deposited on LaNiO3 and Pt bottom electrodes

(Na_0.85K_0.15)_0.5Bi_0.5TiO₃ thin films were deposited on LaNiO₃(LNO)/SiO₂/Si(1 0 0) and Pt/Ti/SiO₂/Si(1 0 0) substrates by metal-organic decomposition, and the effects of bottom electrodes LNO and Pt on the ferroelectric, dielectric and piezoelectric properties were investigated by ferroelectric tester, impedance analyzer and scanning probe microscopy, respectively. For the thin films deposited on LNO and Pt electrodes, the remnant polarization 2P_r are about 22.6 and 8.8 μC/cm² under 375 kV/cm, the dielectric constants 238 and 579 at 10 kHz, the dielectric losses 0.06 and 0.30 at 10 kHz, the statistic d_33eff values 95 and 81 pm/V. The improved piezoelectric properties could make (Na_1−xK_x)_0.5Bi_0.5TiO₃ thin film as a promising candidate for piezoelectric thin film devices.     

The effect of Si surface nitridation on the interfacial structure and electrical properties of (La2O3)0.5(SiO2)0.5 high-k gate dielectric films

Thermal stability, interfacial structures and electrical properties of amorphous (La₂O₃)_0.5(SiO₂)_0.5 (LSO) films deposited by using pulsed laser deposition (PLD) on Si (1 0 0) and NH₃ nitrided Si (1 0 0) substrates were comparatively investigated. The LSO films keep the amorphous state up to a high annealing temperature of 900 °C. HRTEM observations and XPS analyses showed that the surface nitridation of silicon wafer using NH₃ can result in the formation of the passivation layer, which effectively suppresses the excessive growth of the interfacial layer between LSO film and silicon wafer after high-temperature annealing process. The Pt/LSO/nitrided Si capacitors annealed at high temperature exhibit smaller CET and EOT, a less flatband voltage shift, a negligible hysteresis loop, a smaller equivalent dielectric charge density, and a much lower gate leakage current density as compared with that of the Pt/LSO/Si capacitors without Si surface nitridation.     

Luminescence of Strontianite (SrCO3) from Strontian (Scotland, UK)

An historic Strontianite-type specimen from Strontian, Scotland, UK, was characterized to broaden our knowledge on luminescence properties of common carbonates. These fibrous aggregates are Strontianite (Sr_xCa_1−xCO₃) with circa 6% of CaO, interfacial water, hydrosilicate anions and substitutional divalent cations, e.g., Ca²⁺, Mn²⁺, Fe²⁺ in structural Sr²⁺ positions. The specimen was analyzed by X-ray Fluorescence Spectrometry (XRF), Environmental Scanning Electron Microscopy coupled with an Energy Dispersive X-ray Spectroscopy (ESEM-EDS) probe, Spatially-resolved Cathodoluminescence under the Scanning Electron Microscope (SEM-CL), Differential-Thermal Analyses (DTA), Thermogravimetry (TG), Thermoluminescence (TL), Radioluminescence (RL) and High Resolution Spectra Thermoluminescence (3DTL), to gain an overview of the spectral emissions, the defect linkages were modified by heating from room temperature (RT) up to 500 °C. Substitutional transition elements are probably responsible for the spectral emission bands from 500 nm to 800 nm and hydrous molecules from 300 nm to 400 nm. DTA–TG analyses performed on little chips, to preserve the fiber interfaces coherence, exhibit minor endothermic peaks attributed to outflow of water groups in fiber interfaces. Both, CL and RL curves show common spectral positions but UV–blue and red emission intensities are counterbalanced since electron irradiation reduces the UV–blue emissions while X-irradiation increases them. The TL curves show a top thermal limit at 300 °C for the 300–400 nm TL emissions which become irreversibly destroyed, whereas the longer wavelength region emits at higher temperature. The non-reversible changes observed in the 320 nm and 360 nm bands during the spectra 3DTL emission could be linked with non-bridging oxygen defects, protons and hydroxyl groups and the red emissions to the ⁴G (⁴T_1g)–⁶S Mn²⁺ ion transition. Following assignations and similar spectral CL patterns of Russian Strontianite samples, the emission-defect assignments: Dy³⁺ 480 nm; Tb³⁺ 540 nm; Dy³⁺ 580 nm and Sm³⁺ 640 nm cannot be disregarded.     

Effect of Ca doping on the superconducting properties of GdBaSrCu3O7−δ bulk samples

Gd_1−xCa_xBaSrCu₃O_7−δ samples (0  x  0.1) were prepared via solid-state reaction. Four-point probes method was used for resistance versus temperature measurements. Results show decrease in T_c by increasing x content. This variation is assumed to be irrelevant to the different phases or impurity effects since X-ray patterns show all samples are tetragonal single-phase. Ca doping decreases the oxygen content and lattice parameters of the samples. It is suggested that Ca prevents the dislocation of oxygen, and then disrupts the hole concentration of the system and antiferromagnetic correlation at CuO₂ planes. Subsequently, destroys the superconductivity of the samples.     

Neutron polarization analysis on the multiferroic TbMn2O5

Polycrystalline TbMn₂O₅ was prepared by the standard solid-state reaction method and characterized by powder X-ray diffraction and magnetization to assure it is of single phase. Heat capacity measurements on the compound reveal an antiferromagnetic phase transition at 45 K. A broad peak below 6 K in the heat capacity measurements corresponds to the crossover transition of Tb³⁺ ordering. To confirm these magnetic orderings, neutron powder diffractions on TbMn₂O₅ with XYZ neutron polarization analysis were performed at the diffuse neutron scattering (DNS) spectrometer, FRJ-II, by using neutron wavelength of 4.8 Å in the temperature range of 1.8–250 K. Magnetic scattering was separated from nuclear coherent and spin incoherent scattering contributions. Long-range ordered magnetic peaks were observed below 39 K which is consistent with the heat capacity results. The drastic increasing intensities below 6 K indicate the ferromagnetic transition in Tb³⁺ orderings.     

Low-threshold operation of a 355-nm pumped nanosecond β-BaB2O4 optical parametric oscillator

We report the low-threshold operation of a nanosecond β-BaB₂O₄ optical parametric oscillator (OPO) pumped by the third harmonic of a Q-switched Nd:YAG laser. Using cylindrical focusing of the pump beam, a threshold pulse energy of 0.5 mJ is obtained at the signal wavelength of 560 nm, which is about sixteen times lower than that of a spherical focusing configuration. The importance of diffraction loss in the design of tightly focused OPOs is discussed in terms of a simple extension of the conventional OPO model.     

The electrodeposition of copper onto UHV-prepared GaAs(0 0 1) surfaces

Synchrotron surface X-ray diffraction has been used to investigate in situ the morphology and epitaxy of monolayer amounts of copper electrodeposited from aqueous electrolyte onto ultra-high vacuum prepared, smooth, Ga- or As-terminated GaAs(0 0 1) surfaces. The fcc lattice of the epitaxial Cu islands is rotated by 5° and tilted by about 9° with respect to the GaAs substrate lattice, leading to eight symmetry equivalent domains of Cu islands terminated by {1 1 1} facets.     

The Fe3O4 origin of the “Biphase” reconstruction on α-Fe2O3(0 0 0 1)

The so-called Biphase termination on α-Fe₂O₃ has been widely accepted to be a structure with a 40 Å unit supercell composed of coexisting islands of Fe_1−xO and α-Fe₂O₃. Based on thermodynamic arguments and experimental evidence, including transmission electron diffraction, imaging, magnetic and spectroscopic information, it is found that the previously proposed structure model is inaccurate. The actual Biphase structure is instead a layered structure related to the reduction of α-Fe₂O₃ to Fe₃O₄. A model for the Biphase termination is proposed which does not contain islands of Fe_1−xO but instead consists of bulk α-Fe₂O₃ and a Fe₃O₄-derived overlayer. The proposed model is consistent with all current and previously reported experimental findings.