纳米Ce1-xLaxO2-δ的微波引诱燃烧合成及其性能表征

Nanometer Ce_1-xLa_xO_2-δ solid solutions were synthesized by microwave-induced combustion process us-ing cerium nitrate hexahydrate， lanthanum nitrate hexahydrate and urea as raw materials. The process took only six minutes to obtain La₂O₃-doped CeO₂ nanopowders. The nanopowders were characterized by XRD， Laser Raman spectrum ， UV-Vis spectroscopy，field-emission scanning electron micrograph(FE-SEM)and TEM. The results revealed that the grain size of Ce_1-xLa_xO_2-δ varied from 20 to 40 nm calculated by Scherer formula through the plane of (111)， that oxygen vacancy was produced in the crystal lattices and the concentration of oxygen vacancy was increased with La doping， therefore the covalence of Ce-O bond was strenthened， which results in more intensive UV-C(200～280 nm)absorption. It can be seen from SEM that the porous appearance was obtained. Grain size is no more than 40nm observed from TEM.     

CexPr1-xO2-δ复合氧化物的XRD和Raman表征

A series of Ce_xPr_1-xO_2-δ mixed oxides were synthesized by sol-gel method and characterized by Raman and XRD techniques. When x value was changed from 1.0 to 0.5, only a cubic phase CeO₂ was observed. The samples were very well crystallized on decreasing x from 0.50 to 0.99. For Ce_xPr_1-xO_2-δ samples 465 cm^-1 and 1 150 cm^-1 Raman peaks are attributed to the Raman active F_2g mode of CeO₂. The broad peak at about 570 cm^-1 in the region of 0.3 ≤x≤ 0.99 can be linked to lattice defects resulting in oxygen vacancies. The new band at about 195 cm^-1 may be attributed to the asymmetric vibration caused by the formation of oxygen vacancies. Calcination temperatures had great effect on the peak intensity for CeO₂ but less effect on Ce_0.8Pr_0.2O_2-δ in Raman spectra. It might be due to the transformation of the colors for the mixed oxides, the insertion of Pr atom into the ceria lattice could enhance the sintering resistance and thermal stability of the mixed oxides.     

SrCe0.95Er0.05O3-α固体电解质的导电性

SrCe_0.95Er_0.05O_3-α ceramic of a single orthorhombic phase of perovskite-type SrCeO₃ was prepared by high-temperature solid state reaction. Using the ceramic as solid electrolyte and porous platinum as electrodes, the measurements of conductivities and ionic transport numbers on SrCe_0.95Er_0.05O_3-α ceramic were performed by using electrochemical methods in the temperature range of 600～1 000 ℃ in wet hydrogen, dry air and wet air, respectively. The results indicate that the sample is a pure protonic conductor with a maximal conductivity of 0.01 S·cm^-1 in wet hydrogen, a mixed conductor of oxide-ion and hole in dry air, and a mixed conductor of proton, oxide-ion and hole in wet air.     

纳米尖晶石LixMn2O4的制备与电化学性能表征

Nano-spinel Li_xMn₂O₄(0.6 ≤x≤ 1.0) was synthesized by two steps of coprecipitation and calcination. The influences of calcination temperature, time and Li/Mn ratio on the crystal structure and the particle size of Li_xMn₂O₄ were investigated. It was shown that the higher the calcination temperature, the more complete the crystal structure, and the larger the particle size. Moreover, the influence of calcination time on the crystal structure was insignificant when it was more than 3h at 700℃. With the increase of x in Li_xMn₂O₄ in the range of 0.6～1.0, the d111 and lattice parameter a increased first and then decreased. The electrochemical properties of nano-spinel LiMn₂O₄ using as cathode material of lithium-ion battery were studied. The low discharge capacity might be due to the irreversible capacity loss brought by the large surface area and lattice vacancies of the nano-spinel.     

(ZrO2)1-x(Yb2O3)x纳米晶的水热法合成及其烧结体的电性能

(ZrO₂)_1-x(Yb₂O₃)_x (x=0.07, 0.09, 0.11) nanocrystallites were hydrothermally prepared in basic media by using co-precipitated Zr(OH)₄ and Yb(OH)₃ as precursor. The nanocrystallites have small particle sizes of 5.8~7.5 nm, narrow size distribution, less agglomeration and high sinterability. The oxide-ionic conduction properties of the prepared ceramics were investigated by means of AC impedance spectroscope, oxygen concentration cell at 600~1 000 ℃. The results show that the ceramic with x=0.09 is superior to the ceramics with x=0.07 and 0.11 in oxide-ionic conduction.     

掺镍型层状LixNiyMn1-yO2正极材料的合成与电性能研究

A kind of cathode material of layered Li_xNi_yMn_1-yO₂ characterized with the O2 type has been synthesized by a simple method. Its precursor Na_xNi_yMn_1-yO₂ has been prepared from manganese dioxide， nickel hydroxide and sodium carbonate at high temperature in air and quickly cooled in cold water， then it has been exchanged by the melted LiNO₃ at 300～400℃ in air. The effects of calcine-temperature for the precursors and its compositions (the content of Na and Ni) on the electrochemical properties of the material Li_xNi_yMn_1-yO₂ have been investingated by XRD and electrochemical tests. The results show that the sample Li_0.7Ni_0.3Mn_0.7O₂， has the best electrochemical properties which shows only one charge-discharge potential stage of 2.8～3.0V and has a high specific capacity over 180mAh·g^-1 cycled between 2.0～4.20V. A significant structure transformation to the spinal-type phase has not been found in the charge-discharge cycling and the discharge specific capacity around 165mAh·g^-1 has re-mained after the 20th cyclings for the material.     

BaO-Al2O3-B2O3系密封玻璃的结构与性质

The BaO-Al₂O₃-B₂O₃ glasses manufactured for solid oxide fuel cell(SOFC) sealing were studied. The effect of different n_BaO/n_B2O3 on crystal, thermal properties, density and infrared spectra of this system has been discussed. The results show that the trends of crystallization, glass transformation temperature, dilatometric softening temperature and density increase with n_BaO/n_B2O3 values. But a typical property deviation occurs when n_BaO/n_B2O3 is 0.875, and its coefficient of thermal expansion has the maximum at this point. The changes of properties can attribute to the conversion of boron from tetrahedral coordination to trigonal, breakage of the local glass network and interaction between the network modifiers. These can be proved by infrared spectra of glasses. Thermal properties of some studied samples are suitable for the sealing of SOFC using Sm doped ceria electrolyte and operating at 400～600 ℃.     

LiNi1-xMxVO4的红外光谱和拉曼光谱研究

The vanadates of LiNi_1-xM_xVO₄(M=Fe,Co,Ni) containing VO₄ tetrahedrons were synthesized by soft chemical method through a new mild liquid route. The samples sintered at 450℃ for 3h and at 650℃ for 3h are named for LT-LiNiVO₄ and for MT-LiNi_1-xM_xVO₄ respectively. All of the products were measured by X-ray diffraction, IR and Raman spectra respectively. In comparison with IR spectra of V₂O₅ and NiO, the LT-LiNiVO₄ has a strong and broad IR absorption band of VO₄ tetrahedrons located at 600～850cm^-1 with three small splitting peaks corresponding to the asymmetry stretching vibrations of V-O bonds. The results of IR and Raman spectra for MT-LiNi_1-xM_xVO₄ show that the cations of Ni²⁺, Co²⁺, Fe²⁺ have the influences on the frequency shifts of the V-O vibrations.     

Cu1-xAgxI(x=0.5～0.6)纳米微粒的制备与表征

In the presence of PVPK30,Cu_1-xAg_xI nanoparticles were prepared by ion exchange reaction.The product was characterized by FT-IR,XRD,TEM,EDS and SPS,respectively.It was found that the value of x is ap-proximately 0.5～0.6and the average diameter of the nanoparticles is 10～20nm.The product shows surface photovoltage property of semiconductor and the existence of Cu⁺ greatly enhances the separation efficiency of photoinduced electron-hole pairs.Meanwhile,SPS of Cu_1-xAg_xI nanoparticles with different X (Ag/I)value had been investigated. The results show that when X is 0.5～0.576, the SPS intensity of Cu_1-xAg_xI nanoparticles is highest.     

LixNi0.8-yCo0.2ZnyOp的合成及电化学性能研究

A series of single-phase Li_xNi_0.8-yCo_0.2Zn_yO_p(0.96 ≤x≤ 1.10， 0 ≤y≤ 0.05， 2 ≤p≤ 2(1+y) ) (different in the y values) were synthesized by a two-step solid state reaction method， in which LiOH·H₂O， Zn-doped spherical Ni(OH)₂ and Co₂O₃ were used as the precursors. The ICP-AES analyses proved that the Zn-doped compounds synthesized had the nonstoichiometric form. The results of the XRD， SEM identified that the uniform particles of the as-prepared materials having a good layered structure were fine， narrowly distributed and well crystallized. The electrochemical performance test was carried out and the results showed that the as-prepared Zn-doped materials had not only a high capacity， but also a better cycling stability characterization than the un-doped one. The Li_1.06Ni_0.75Co_0.22Zn_0.03O_2.03 material has an initial reversible capacity as high as 160.5mAh·g^-1; and a first discharge efficiency 89.2%， and exhibits satisfactory cyclic stability with 90% retainable capacity after 50 cycles.     

掺钇锆酸锶-TiO2复合光催化剂的制备及性能研究

SrZrO₃ particles were prepared by a co-precipitation method and Sr(Zr_1-xY_x)O_3-δ -TiO₂ composite particles were then synthesized by Sr(Zr_1-xY_x)O_3-δ and titanium dioxide. The composite particles were characterized by XRD, SEM, FTIR and TG-DTA techniques. The photocatalytic degradation of methylene blue (MB) in aqueous solution was used as a probe reaction to evaluate the photocatalytic activity of the composite particles. The effect of the preparation method for SrZrO₃, doping content of yttrium and TiO₂ amount in the composite particles on the photocatalytic activity of composite particles was also discussed. The results show that the methylene blue solution could be completely degraded by Sr(Zr_1-xY_x)O_3-δ -TiO₂ composite particles under UV-light or visible light irradiation. The photocatalytic activity of composite particles was higher than that of pure TiO₂. The fast recombination of photogenerated electrons and holes were restrained by the heterojunction formed in composite particles. The particle of SrZrO₃ prepared by co-precipitation was small, and the photocatalytic activity of composite particles prepared from this kind of SrZrO₃ was higher than that of particles prepared by solid sintering method. The best doping content of yttrium is 5%. The optimal content of TiO₂ in composite particles is 90wt%, 70wt%, respectively under UV-light and visible light irradiation, the degradation rates of MB are 98.8% and 93.5% , respectively after 50 min irradiation.     

纳米Mn-Zn铁氧体的制备和研究

Nanosize manganese zinc ferrites were fabricated by hydrothermal precipitation route using Fe₂(SO₄)₃, ZnSO₄·7H₂O, MnSO₄·H₂O as material, then some calcinated at 500 ℃ and studied by XRD, TEM, IR and VSM. The results showed that the products were spinel crystal structure and uniformly sized nanoparticles (15～25 nm) with little aggregation. The analysis of IR showed that the superficial water can be eliminated, but that was embedded in crystal lattice can not be removed by calcinating. The effect Zn content x on the lattice (a) of nanosize Mn_1-xZn_xFe₂O₄ was also discussed. The lattice of nanosize Mn_1-xZn_xFe₂O₄ decreases with x increasing; and its value deviated the standard lattice (a₀) of normal size manganese zinc ferrites. A lot of water was absorbed during the hydrothermal process owing to the large surface of nanosize particles. The change of magnetic properties of Mn_xZn_1-xFe₂O₄ with x increasing was studied: nanosize Mn_xZn_1-xFe₂O₄ particles synthesized by us exhibited peculiar magnetic properties curve with Zn content (x) increasing, Superparamagnetic behaviors of the synthesized ZnFe₂O₄ samples were confirmed by magnetic characterization, which can be explained by the difference between the distribution of the metal ions (Mn²⁺, Zn²⁺ and Fe³⁺) among the tetrahedral (A) and the octahedral (B) sites of nanosize ferrite and that of bulk ferrite.     

ZrWO4F2的前驱物法合成和表征

Zirconium tungsten oxyfluoride, ZrWO₄F₂, was firstly synthesized with the precursor route. The composition of the compound was determined by combining the results of ICP and XPS. The indexed powder X-ray diffraction pattern of this compound indicates that it is a pure phase, orthorhombic crystal system, space group D₂²=P2₁22 and a=15.32(2)?,b=13.877(7)?,c=8.42(2)?.Combining the results of the DTA-TGA curves from room temperature to 700℃ and XRD patterns in different temperatures the mechanism was revealed during the solid precursor (1) been heated to 700℃. The zirconium tungsten oxyfluoride was considered to be a metastable com-pound. The ascertaining of annealing time and temperature is the key of handling.     

电镀烧结法制备Ti/SnO2-Sb2O4电极的研究

The Ti/SnO₂-Sb₂O₄ electrode has been prepared by the electroplate-sinter method. The effect of SbCl₃ adding amount and sintering temperature on its electrode lifetime and oxygen evolution potential were investigated by means of EDX, SEM and XRD analysis. The results indicated that the electrode appeared the best performance when the SbCl₃ adding amounts was 0.2g and the sintering temperature was 550℃. In optimized conditions Ti substrate was entirely covered by SnO₂-Sb₂O₄ and the combinations among them were tight. Due to the use of electroplate method, the electrical conductivity, the oxygen evolution potential and the electrode lifetime were increased, so the elec-tro-catalytic activity and the electrochemical stability of the prepared electrode were found to be superior.     

新型阴极材料Ba0.5Sr0.5Co0.8Fe0.2O3-σ制备与性能研究

Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3-σ(BSCF), a new cathode material for solid oxide fuel cell (SOFC), was synthesized by polyacrylicacid (PAA) method. The lattice structures of samples calcined at different temperatures were characte-rized by XRD. Shrinkage, porosity and pore size of the porous BSCF as a function of sintering temperature were investigated. It was found that the cubic perovskite structure could be formed after calcination at 800 ℃ for 2 h, but not well crystallized as seen from some unknown phases, and the pure cubic perovskite structure was formed after calcination at 1 150 ℃ for 2 h. The particle size of BSCF was less than 1～2 μm. The shrinkage of the porous BSCF increased with sintering temperature, but the opposite was true for the porosity. After sintering at 1 100 ℃ for 4 h, the porous BSCF was still in an appropriate structure, with porosity of 29% and electrical conductivity above 400 S·cm^-1.     

ZrxTixAl1-2xO2的制备及其在三效催化剂上的应用

Zr_0.5Ti_0.5O₂(ZT) and Zr_0.25Ti_0.25Al_0.5O₂(ZTA) mixed oxides were prepared by co-precipitation method and characterized by low temperature adsorption-desorption， XRD and NH₃-TPD. The activity of Pt/Zr_0.5Ti_0.5O₂ and Pt/ Zr_0.5Ti_0.5Al_0.5O₂ catalysts was evaluated using the simulated gases. The results show that ZTA samples exhibit higher specific surface area， larger pore volume and proper surface acidic amount and acidity in comparison with ZT. The results of the catalytic test indicate that Pt/ZT and Pt/ZTA catalysts exhibit excellent low-temperature catalytic activity and lower light-off temperatures of hydrocarbon， carbon monoxide and nitrogen oxides， especially better conversion for nitrogen oxides (NO_x). The addition of Al₂O₃ into ZT enhanced the anti-aging property of Pt/ ZTA catalysts due to the excellent textural， structural， surface acidity and thermal stability.     

钴掺杂镍酸锂的密度泛函计算及电化学性能

LiNiO₂ and LiNi_0.5Co_0.5O₂ cathodes for lithium-ion batteries were synthesized with co-precipitation method and their electrochemical property was characterized by Galvanostatic cycling. Meanwhile, plane-wave pseudopotential method base on density functional theory was used to calculate average cell voltage and the electronic structure of LiNiO₂ and LiNi_0.5Co_0.5O₂. The experimental and computational results showed that the average voltage of the cell decreased as Li-ion intercalated to the host cathode (discharge); The potential of Li_xNi_0.5Co_0.5O₂ was higher than that of Li_xNiO₂ (when 0.25≤x≤0.5). The calculations also indicated that the distortion of the NiO₆ octahedron in Li_xNiO₂ was decreased by Co-doped. During the Li-ion intercalates to the host cathode, the micro-structures of NiO₆ and CoO₆ in the Li_xNi_0.5Co_0.5O₂ were mutually stabilized, the Jahn-Teller effect was weakened and the electrochemical properties of the materials were enhanced.     

Ba0.95Ce0.9Y0.1O3-α固体电解质的氧离子导电性

Ba_0.95Ce_0.9Y_0.1O_3-α solid electrolyte was prepared by high temperature solid state reaction. The electrochemical oxygen permeation (oxygen pumping) rates and oxide ion transport number in this electrolyte were detected in the temperature of 600～1000℃ . It was found that this electrolyte exhibited the oxide ion conduction with the oxide ion transport number of 0.3～0.5.     

γ-Fe2O3纳米粉的低热固相制备及其电磁损耗特性(英)

The Fe(OH)₃ precursor was prepared by solid -state reaction with Fe(NO₃)₃·9H₂O, NaOH and dispersed poly-ethylene glycol at low heating temperature(25 ℃). Synthesis of iron oxide (γ-Fe₂O₃) nanoparticle was achieved by thermal decomposition of Fe(OH)₃·xH₂O precursor. The nanoparticle was characterized by TG-DTA, X-ray diffra-ction, TEM etc. The results showed that the nanoparticle was composed of γ-Fe₂O₃ and was a better absorber for electromagnetic wave within the low frequency band.     

阴极材料LaFe0.8-xCuxNi0.2O3的合成和烧结性能

LaFe_0.8-xCu_xNi_0.2O₃ (x=0.0~0.2) (LFCN), a new cathode material of solid oxide fuel cell (SOFC), was synthesized by Co-precipitation method using sodium bicarbonate. The lattice structures of samples with different x contents were characterized by XRD. Porosity and density of the porous LaFe_0.8-xCu_xNi_0.2O₃ (x=0.0~0.1) as a function of sintering temperature were investigated. It was found that the orthorhombic structure could be formed after calcination at 900 ℃ for 4 h. The particle size of LFCN was about 350 nm. The density of the porous LFCN increased with sintering temperature, but the opposite was true for the porosity. On the other hand, at the same sintering temperature, the porosity of LaFe_0.8-xCu_xNi_0.2O₃ (x=0.0~0.1) decreased with increasing x contents. It is indicated that the dopant of Cu on LaFe_0.8Ni_0.2O₃ can facilitate the sintering of the materials. After sintering at 1 100 ℃ for 4 h, the porous LaFe_0.7Cu_0.1Ni_0.2O₃ was still with appropriate structure, and its porosity was 29%.