SUBSTITUENT CHEMICAL SHIFT (SCS) AND THE SEQUENCE STRUCTURE OF ETHYLENE-VINYL ALCOHOL COPOLYMERS

Three ethylene-vinyl alcohol copolymers were studied by means of the substituent chemical shift (SCS) method. The SCS parameters of hydroxy (-OH) in two different solvents were obtained: in deuterium oxide/phenol (20/80 W/W ) the parameters are S_1 = 42.77±0.08ppm, S_2 = 7.15±0.06 ppm, S_3 (s)= -4.08±0.02ppm, S_3 (t) =-3.09±0.20ppm,S_4 = 0.48±0.03ppm, S_5 = 0.26±0.05ppm. In o-dichloro-benzen-d_4 S_1(s)=44.79±0.61ppm, S_2=7.40±0.00ppm, S_3(s)=-4.51±0.17ppm, S_3(t)=-3.13 ±0.00 ppm, S_4 =0.63±0.04ppm, S_5=0.36±0.00ppm.Simultaneously the ~(13)CNMR spectra of EVA copolymers were assigned by using the SCS parameters obtained.     

1,4-丁炔二醇与4,4′-二乙炔联苯共聚物的合成及表征研究

本文用(Ph_3P)_2PdCl_2为催化剂,合成了1,4-丁炔二醇(BD)与4,4-二乙炔联苯(DEBP)共聚物。对用不同比例的两种单体得到的共聚物测定了比重(d_4~(25)、溶胀度(θ_D)、最良溶剂及相邻两交联点之间的平均分子量(M_c)。实验表明,在两种单体摩尔比中,DEBP用量越多,共聚物中泡状微孔越多,颜色越淡,溶胀度和比重越小,交联度越大;DEBP/BD(摩尔比)大于1/5时,共聚物的最良溶剂为苯,溶度参数为9.15卡~(0.5)·cm~(-1.5),是1/10时,其最良溶剂为乙醇,溶度参数是12.7卡~0.5·cm~(-1.5)。对共聚物还做了红外光谱表征。     

辐照三嵌段聚苯乙烯-丁二烯-4-乙烯基吡啶共聚物离子交换膜性能的研究——Ⅱ.共聚物膜的基本性能及分离实验

本文研究了以辐照聚苯乙烯-丁二烯-4-乙烯基吡啶嵌段共聚物为膜基体所制成的嵌镶离子交换膜的基本性能.研究表明所制备的嵌镶膜在两端浓度分别为0.1及0.001 mol/L KCl 中的水渗析系数及电解质渗析系数分别是2.40×10~(-5)mol/cm~2·min及2.10×10~(-8)mol/cm~2·s.用所制备的嵌镶离子交换膜测试了牛血清白蛋白(M=67,000)与KCl混合溶液,蔗糖(M=343)与KCl混合溶液的膜分离效果.实验表明对上述两种非电解质均不能通过膜、而电解质KCl则可以.上述两种混合溶液中KCl渗透系数分别为J_(KCl)(牛血清白蛋白)=1.08×10~(-8)mol/cm~2·s及J_(KCl)(蔗糖)=1.10×10~(-8)mol/cm~2·s.     

4-甲基丙烯酸-2,2,6,6-四甲基哌啶醇酯自由基共聚合的研究——Ⅲ.共聚物组成与竞聚率的测定

本文以苯为溶剂,在60±0.1℃下测定了MTMP(4-甲基丙烯酸-2,2,6,6-四甲基哌啶醇酯,M_1)与St(苯乙烯,M_2)、MVK(甲基乙烯酮,M_2)、VAc(醋酸乙烯酯,M_2)、AN(丙烯腈,M_2)的共聚物组成曲线与竞聚率(MTMP-St:r_1=0.30±0.05、r_2=0.63±0.05;MTMP-MVK:r_1=0.53±0.05、r_2=0.41±0.05;MTMP-VAc:r_1=14±0.5、r_2=0.02±0.01;MTMP-AN:r_1=13.7±0.5、r_2=0.20±0.05)。确定了MTMP的Q(0.56)和e(0.49)值。讨论了共聚物结构单元的序列分布。     

硫在疏质子介质中电化学还原机理的研究 Ⅱ.第二步氧化还原过程的研究

用电化学方法研究了硫在DMSO溶剂中的第二步氧化还原过程,该过程在扫速大于200mV/s时表现为简单的电子转移过程;扫速小于200mV/s时转化为ECE机理,发现了S_8~(4-),S_3~(2-),S_4~(2-)的氧化峰,峰电位分别为-1.50,-0.96,-0,60(相对于银参比电极)。对S_8~(2-)/S_8~(4-)电对测定了标准电极电位和标准速率常数,分别是-1.547±0.002V(相对于银参比电极)和3.3×10~(-3)cm/s。     

N,N-二甲酰基-α-氨基苯乙酮与芳醛的羟醛缩合反应及3-羟基-2-甲酰氨基-1,3-二苯基-1-丙酮的晶体结构

研究了N,N-二甲酰基-α氨基苯乙酮与芳醛的羟醛缩合反应,得到5种控醛缩合产物,并用X-射线单晶衍射法测定了3-羟基-2-甲酰氨基-1,3-二苯-1-丙酮的晶体和分子结构.晶体的空间群为P1;晶体学数据:a=10.802(2)A,b=11.088(2)A,c=14.395(3)A,α=68.20(1)°,β=69.19(1)°,γ=64.35(1)°;V=1403.7(0.5)(?);D_c=1.27 g/cm~(-3).Z=4.F(000)=567.92(e).μ(MoKa)=0.83cm~(-1)。     

(2-甲基丙烯酰氧乙基)三甲基氯化铵-丙烯酰胺反相微乳液共聚合研究

采用SPAN-OP复合乳化剂和K_2S_2O_8-Na_2SO_3氧化还原引发剂,进行(2-甲基丙烯酰氧乙基)三甲基氯化铵-丙烯酰胺的反相微乳液共聚合。测得单体的竞聚率r_(DM·MC)=1.11±0.16,r_(AM)=0.53±0.08。在单体总浓度为20—40％(wt),引发剂浓度为0.01—0.05％,乳化剂浓度为10—18％,聚合温度为299K的条件下,得到共聚反应动力学方程:R_p=k[M]~(1.07)[I]~(0.52)[E]~(0.90),文中对上述结果做了解释。     

水合5-(4-羟基苯酚)四氮唑的溶剂热合成及其晶体结构

以4-羟基苯氰为原料,用溶剂热法合成了水合5-(4-羟基苯酚)四氮唑晶体[(C7H6N4O)·1.5H2O,1],其结构经1H NMR,IR,元素分析及X-单晶衍射表征.1属单斜晶系,C2/c空间群,晶胞参数:a=1.487 2(3) nm,b=0.992 3(2) nm,c=1.304 8(2) nm,β=113.724(3)°,V=1.762 8(5) nm3,Dc=1.365 g*cm-3,F(000)=760,Z=8,μ(MoKα)=0.104 mm-1,R1=0.050 5,wR2=0.117 6.1中存在强烈的分子间氢键和π-π堆积作用.     

1,4-丁炔二醇与4,4′-二乙炔联苯共聚物的合成及表征研究

 本文用(Ph₃P)₂PdCl₂为催化剂,合成了1,4-丁炔二醇(BD)与4,4-二乙炔联苯(DEBP)共聚物。对用不同比例的两种单体得到的共聚物测定了比重(d₄²⁵、溶胀度(θ_D)、最良溶剂及相邻两交联点之间的平均分子量(M_c)。实验表明,在两种单体摩尔比中,DEBP用量越多,共聚物中泡状微孔越多,颜色越淡,溶胀度和比重越小,交联度越大;DEBP/BD(摩尔比)大于1/5时,共聚物的最良溶剂为苯,溶度参数为9.15卡^0.5·cm^-1.5,是1/10时,其最良溶剂为乙醇,溶度参数是12.7卡^0.5·cm^-1.5。对共聚物还做了红外光谱表征。     

四氟乙烯-乙烯溶液沉淀聚合

本文编制了一个简易计算机程序,测定了氟氯烷溶液沉淀聚合体系中四氟乙烯-乙烯共聚竞聚率:40℃:γC_2H_4=0.156±0.001,γC_2F_4=0.022±0.01670℃:γC_2H_4=0.197±0.001,γC_2F_4=0.055±0.020在此聚合体系中,聚合温度和共聚物组成比对链的规整性都有明显影响。当乙烯在45～55mol%范围内时,共聚物的IR随组成比而变化,利用此规律可简便地测定共聚物的组成比。     

水溶剂中反-2,3-环氧-1-苯基-3-(2′-硝基-5′-氯苯基)-1-丙酮的合成及产物的晶体结构

用 2-硝基-5-氯苯甲醛、氯代苯乙酮和氢氧化钠以三乙基苄基氯化铵作催化剂在水溶剂中反应可合成反-2,3-环氧-1-苯基-3-(2′-硝基-5′-氯苯基)-1-丙酮(C15H10ClNO4)。产物的结构通过单晶 X-射线衍射法确定,其晶体属于单斜晶系。空间群 P21/c, a = 9.942(1), b = 15.774(3), c =8.756(1) ?, β = 96.39(1)°, Mr = 303.69, Z = 4,V = 1364.6(3) ?3, Dc = 1.478 g/cm3, μ(MoKα) =0.295 mm–1, F(000) = 624, 最终的偏离因子为 R = 0.0336, wR = 0.0745。X-衍射分析表明, 该产物为反式异构体。     

1, 3-双(2-(2,2-二氰乙烯基)苯氧基)-2-丙醇及其银(Ⅰ)配合物的合成、晶体结构及其荧光性质

用1,3-双(2-甲酰基苯氧基)-2-丙醇和丙二腈进行反应得到1,3-双(2-(2,2-二氰乙烯基)苯氧基)-2-丙醇配体L,然后将配体与Ag Sb F6进行配位反应,得到配合物[Ag LSb F6]n·n CHCl3(1),并用元素分析,FTIR和X-射线单晶衍射进行了表征。结果表明,配体L属于单斜晶系,空间群P21/n,晶体学参数:a=0.990 2(11)nm,b=2.181(2)nm,c=1.012 2(11)nm,β=109.374(10)°,V=2.062(4)nm3,Z=4,Dc=1.277 g·cm-3,Mr=396.40,μ=0.087 mm-1,F(000)=824,R1=0.064 2,w R2=0.117 4(I>2σ(I))。配合物1属于单斜晶系,空间群P21/n,晶体学参数:a=1.270 57(11)nm,b=1.456 44(13)nm,c=1.669 85(14)nm,β=105.643(3)°,V=2.975 6(4)nm 3,Z=4,Dc=1.918 g·cm-3,Mr=859.39,μ=1.907 mm-1,F(000)=1 664,R1=0.0417,w R2=0.1 032(I>2σ(I))。在配合物1中,配体L表现为四齿配体分别与4个银(Ⅰ)离子配位,同时,每一个银(Ⅰ)离子与4个相邻配体配位形成2D层状结构。同时,研究了配体和配合物的固体荧光性质。     

双核钼铁硫簇合物[Fe(2,2’-联吡啶_3)][(S_2MoS_2FeCl_2]的合成与晶体结构

双核Mo-Fe-S原子簇配合物[Fe(2,2′-bpy)_3][S_2MoS_2FeCl_2],是(Et_4N)_2MoS_4、FeCl_2和2,2′-联吡啶在乙腈中反应得到的结晶化合物.晶体属单斜晶系,空间群P2_1/c;a=9.328(3),b=26.788(2),c=13.764(3)(?);β=95.38(3)°;V=3424.2(11)(?)~3;Z=4;D_c=1.698g/cm~3;F(000)=1752.晶体结构用直按法解出;经全矩阵最小二乘法修正,最后R=0.068,R_ω=0.071(3933个I>3(?)(I)的独立衍射).在晶体结构中配位阴离子[S_2MoS_2FeCl_2]~(2-)是排布在阳离子[Fe(2,2′-bpy)_3]~(2+)所形成的空腔中.它是以非统计分布的形式存在,从而较准确地测定了各项键参数.Mo…Fe距离为2.773(2)(?),Mo-S_b和Fe-S_b有大致相等的键长.     

辐照三嵌段聚苯乙烯-丁二烯-4-乙烯基吡啶共聚物离子交换膜性能的研究——Ⅱ.共聚物膜的基本性能及分离实验

 本文研究了以辐照聚苯乙烯-丁二烯-4-乙烯基吡啶嵌段共聚物为膜基体所制成的嵌镶离子交换膜的基本性能.研究表明所制备的嵌镶膜在两端浓度分别为0.1及0.001 mol/L KCl 中的水渗析系数及电解质渗析系数分别是2.40×10^-5mol/cm²·min及2.10×10^-8mol/cm²·s.用所制备的嵌镶离子交换膜测试了牛血清白蛋白(M=67,000)与KCl混合溶液,蔗糖(M=343)与KCl混合溶液的膜分离效果.实验表明对上述两种非电解质均不能通过膜、而电解质KCl则可以.上述两种混合溶液中KCl渗透系数分别为J_KCl(牛血清白蛋白)=1.08×10^-8mol/cm²·s及J_(KCl)(蔗糖)=1.10×10^-8mol/cm²·s.     

碱性深共晶溶剂催化醇解乙烯-醋酸乙烯共聚物研究

截至目前,工业化生产乙烯-乙烯醇共聚物(EVOH)主要通过乙烯-醋酸乙烯共聚物(EVA)的醇解反应。然而,EVOH生产过程中伴随大量废水的产生,不可避免地会引起环境问题。本文合成了一系列的碱性深共晶溶剂,并将其用于催化醇解EVA。系统研究了深共晶溶剂结构与催化性能的关系,以及醇解反应参数、EVA结构组成和氮气流辅助对醇解效率的影响。研究表明,碱性越强的深共晶溶剂,EVA的醇解效率越高。其中,1,8-二氮杂二环十一碳-7-烯/苯甲醇(DBU-BA)表现出了优异的催化活性,在极低的催化剂用量下,即可得到醇解度接近100%的EVOH产物。此外,DBU-BA可以重复使用至少5次,催化活性没有明显降低,表现出优异的可重复使用性。基于核磁共振氢谱(¹H-NMR)和傅里叶红外光谱(FTIR)分析,本文揭示了深共晶溶剂在EVA醇解体系中可能的催化机理。     

完全交替结构乙烯-丙烯共聚物的制备与表征

对顺-1,4含量为100%的高顺式聚异戊二烯(HCPI)进行加氢反应,得到了序列结构高度规整的乙烯-丙烯交替共聚物(alt-EP).所用的HCPI有适当的分子量(Mn=41×104)和极窄的分子量分布(Mw/Mn=1.02).HCPI的加氢反应以环烷酸镍和三异丁基铝为催化剂,在60℃和4.0MPa氢压的条件下反应3h,加氢产物的加氢度为100%.GPC测试结果显示所得乙烯-丙烯交替共聚物保持了窄分布的特点,表明HCPI加氢后未发生交联和降解反应;NMR,FTIR和广角X射线衍射测试结果表明此乙烯-丙烯交替共聚物具有高度规整的序列结构,为完全交替结构的乙烯-丙烯共聚物.并通过TGA和DSC对乙烯-丙烯交替共聚物的热性能进行了表征.     

4-(H酸偶氮)-1-苯基-3-甲基吡唑啉酮与钍的显色反应及其应用

研究了新试剂4-(H酸偶氮)-1-苯基-3-甲基吡唑啉酮(HAPMP)与钍的显色反应.在pH=5.0的HAc-NaAc缓冲介质中,阳离子表面活性剂CFMAB存在下,HAPMP与Th(Ⅳ)反应生成2:1红色络合物,λ_(mas)=55nm,ε=2.24×10~5 L·mol~(-1)·cm~(-1).钍(Ⅳ)含量在0～640μg/L内符合比定律,方法用于合金中钍的测定,结果令人满意.     

9,9-二(4-羟基苯基)呫吨、1,4-二(4-氟苯甲酰基)苯和双酚A三元共聚物聚醚醚酮酮的合成与表征

通过亲核取代反应,将9,9-二(4-羟基苯基)呫吨(BHPX)、1,4-二(4-氟苯甲酰基)苯和双酚A(BPA)进行三元共缩聚反应,合成了几种主链含二甲基甲烷和呫吨结构的聚醚醚酮酮无规共聚物(PEEKK-X/PEEKK-A),并以FTIR、DSC、TG、WAXD等对其结构和性能进行了表征.结果表明,共聚物的玻璃化转变温度(Tg)为185～218℃,均为无定形结构,其数均分子量为39500～41600,多分散性指数为1.94～2.05.在氮气、空气气氛中,在430℃之前不分解,5%的热失重温度(Td5)分别为490～511℃、480～505℃,在氮气中700℃时的残炭率均在40%以上;在常温下易溶于非质子极性溶剂(如NMP和DMAc)以及极性较弱的溶剂(如THF和CHCl3)中.共聚物均可通过溶液浇铸成膜,所得到的薄膜韧性好,透明且耐折,其拉伸强度为58～75MPa,杨氏膜量为1.95～2.70GPa,断裂伸长率为8%～13%.当双酚单体BHPX和BPA摩尔比为60/40～50/50时,所得到的PEEKK-X/PEEKK-A共聚物更有潜在的应用前景.     

2-(5-溴-2-吡啶偶氮)-5-二乙氨基酚-BrO_3~--SCN-三元离子缔合物测定微量BrO_3~-的研究

本文研究了5-Br-PADAP在酸性介质中质子化,与BrO_3~-和SCN~-形成三元离子缔合物的最佳条件,其表观摩尔吸光系数ε_(540)=4.3×10~4L·mol~(-1)·cm~(-1),缔合物组成比为:5-Br-PADAP:BrO_(3-)SCN~-=1:1·1。提供了测定微量BrO_(3-)的新方法,可应用于化学试剂中微量BrO~(3-)的测定。此外,本文还探讨了反应机理。     

EVAc共聚物的序列结构和它的~(13)C NMR谱的关系

本文以EVAc共聚物为例,阐述了EV共聚物序列结构的符号表示与Bovey关系(Ⅰ)的一致性。在此基础上,选择了EV共聚物序列结构的Sung表示并赋予它以化学位移的意义,在二元组和三元组序列水平上分析了EV共聚物的13种序列结构与Sung表示,与取代基参数,与其~(13)C NMR谱13个谱峰之间的一一对应关系。其主要内容由Sung表示与取代基参数之间的α～S_1,β～S_2,γ～S_3,δ～S_4,δ~+～0ppm对应关系表征,从而构架了由EV共聚物的~(13)C NMR谱通向其序列结构的桥梁,建立起研究EV共聚物序列结构的普适方法。