Effects of spacer layers on magnetic properties and exchange couplings of Nd-Fe-B/Nd-Ce-Fe-B multilayer films

The influences of the spacer-layer Ta on the structures and magnetic properties of Nd Fe B/Nd Ce Fe B multilayer films are investigated via DC sputtering under an Ar pressure of 1.2 Pa. An obvious(00l) texture of the hard phase is observed in each of the films, which indicates that the main phase of the film does not significantly change with Ta spacer-layer thickness. As a result, both the remanence and the saturation magnetization of the magnet first increase and then decrease,and the maximum values of 4πM_r and H_(cj) are 10.4 k Gs(1 Gs = 10_(-4)T) and 15.0 kOe(1 Oe = 79.5775 A·m_(-1)) for the film with a 2-nm-thick Ta spacer-layer, respectively, where the crystalline structures are columnar shape particles. The measured relationship between irreversible portion D(H) =-?M_(irr)/2 M_r and H indicates that the nucleation field of the film decreases with spacer layer thickness increasing, owing to slightly disordered grains near the interface between different magnetic layers.     

钽掺杂二氧化钛薄膜的光电性能研究

采用脉冲激光沉积法 (PLD), 以石英玻璃为衬底制备了钽掺杂TiO₂薄膜并研究了薄膜样品的光电性质. 沉积氧气分气压从0.3 Pa变化到0.7 Pa时薄膜样品的帯隙变化范围是3.26 eV到3.49 eV. 通过测量电阻率随温度的变化关系确定了薄膜内部的主要导电机理. 在150 K到210 K温度范围内, 热激发导电机理是主要的导电机理; 而在10 K到150 K范围内; 电导率随温度的变化复合Mott的多级变程跳跃模型 (VRH); 在210 K到300 K范围内, 电阻率和exp(b/T)^1/2呈正比关系. 关键词： 2')" href="#">Ta掺杂TiO₂ 脉冲激光沉积法 薄膜 导电机理     

High critical current density YBa2Cu3O7−δ tapes prepared by the surface-oxidation epitaxy method

YBa₂Cu₃O_7−δ (YBCO) films with high critical current density (J_c) were successfully fabricated on nickel tapes buffered with epitaxial NiO. NiO was prepared on the textured nickel tape by the surface-oxidation epitaxy (SOE) method. We have reported so far a critical temperature (T_c) of 87 K and J_c=4–6×10⁴ A/cm² (77 K, 0 T) for the YBCO films on NiO/Ni tapes. To enhance the superconducting properties of the YBCO films on the SOE-grown NiO, depositions of thin oxide cap layers such as YSZ, CeO₂, and MgO on NiO were investigated. These oxide cap layers were epitaxially grown on NiO and provided the template for the epitaxial growth of YBCO films. Substantially improved data of T_c=88 K and J_c=3×10⁵ A/cm² (77 K, 0 T) and 1×10⁴ A/cm² (77 K, Hc, 4 T) were obtained for YBCO film on NiO, by using a MgO cap layer with a thickness of 50 nm. The method described in this paper is a simple way to produce long YBCO tape conductors with high-J_c values.     

强磁场下Sm-Fe薄膜不同晶态组织演化及磁性能调控

针对Sm-Fe薄膜的不同晶态组织演化和磁性能调控问题,采用分子束气相沉积方法制备Sm-Fe薄膜时,通过改变Sm含量、膜厚和强磁场来调节薄膜的晶态和磁性能.结果表明,Sm含量可以调节Sm-Fe薄膜的晶态组织演化,而晶态组织的演化和强磁场对磁性能有显著影响.Sm-Fe薄膜在Sm原子比为5.8%时是体心立方晶态组织,在Sm含量为33.0%时为非晶态组织,而膜厚和强磁场不会影响薄膜的晶态组织.非晶态薄膜的表面粗糙度和表面颗粒尺寸都比晶态薄膜的小,施加6 T强磁场会使表面颗粒尺寸增大,而表面粗糙度降低.非晶态薄膜的饱和磁化强度M_s比晶态薄膜的M_s(1466 emu/cm~3,1 emu/cm~3=4π×10-10T)低约47.6%,施加6 T强磁场使非晶态和晶态薄膜的M_s均降低约50%.Sm-Fe薄膜的矫顽力H_c在6—130 Oe(1 Oe=103/(4π)A/m)之间,其中,非晶态薄膜的H_c比晶态薄膜的H_c大.施加6 T强磁场使晶态薄膜的H_c增大,而使非晶态薄膜的H_c减小,最高可以减少95%.结果表明含量和强磁场可以用于调控Sm-Fe薄膜的晶态和磁性能.     

Magnetostriction and spin reorientation in ferromagnetic Laves phase Pr(Ga_xFe_(1-x))_(1.9) compounds

The magnetostriction, magnetization, and spin reorientation properties in Pr(Ga_xFe_(1-x))_(1.9) alloys have been investigated by high-precision x-ray diffraction(XRD) step scanning, magnetization, and Mo¨ssbauer spectra measurements. Ga substitution reduces the magnetostriction(λ_(||)) with magnetic field H ≥ 8 kOe(1 Oe = 1.33322×10~2 Pa), but it also increases the λ|| value when H ≤ 8 kOe at 5 K. Spin-reorientations(SR) are observed in all the alloys investigated, as determined by the step scanned XRD, Mo¨ssbauer spectra, and the abnormal temperature dependence of magnetization. An increase of the spin reorientation temperature(T_(SR)) due to Ga substitution is found in the phase diagram, which is different from the decrease one in many R(T_x Fe_(1-x))_(1.9)(T = Co, Al, Mn) alloys. The present work provides a method to control the easy magnetization direction(EMD) or T_(SR) for developing an anisotropic compensation system.     

Nd-Ce-Fe-B纳米复合薄膜的磁性及交换耦合作用

采用磁控溅射技术制备了具有永磁特征的Nd-Ce-Fe-B多层纳米复合薄膜,并对其进行了退火处理.通过改变退火温度,研究其对薄膜磁性能和晶体结构的影响.结果表明,随着退火温度的提高薄膜磁性能逐渐增大,但当温度达到695℃以上时,薄膜的磁性能急剧下降.当退火温度为675℃时,薄膜的矫顽力Hci=10.1 kOe(1Oe=79.5775 A/m),垂直于薄膜表面方向的剩余磁化强度4πM_(r⊥)=5.91 kG(1 G=10~3/(4π)A/m).薄膜的X射线衍射结果表明,磁性薄膜具有较好的c轴取向.通过对薄膜磁化反转过程的研究,发现随着外加磁场的增大,M_(rev)的极小值向M_(irr)减小的方向移动,这与畴壁弯曲模型类似,表明在薄膜中存在较强烈的局部钉扎作用,而剩余磁化强度曲线表明这种钉扎作用在薄膜矫顽力机制中并不占支配作用.此外,薄膜的Henkel曲线结果表明在薄膜中存在较强的交换耦合作用,在经过685℃退火的薄膜中磁相互作用更加显著.     

Synthesis of YBa2Cu3O7−x superconducting thin films on LaAlO3 by means of PAMOCVD

High-T_c superconducting thin films have been deposited in situ by means of a plasma assisted metal-organic chemical vapour deposition (PAMOCVD) process on LaAlO₃. An EMCORE high-speed rotating disc reactor was used to deposit the films at a substrate temperature of 600°C to 800°C. The system is equipped with a (remote) 120 W microwave plasma generator. The oxidising plasma gas is N₂O and/or O₂ while Ar was used as the inert carrier gas for the different metal-organics. The influence of different process parameters (such as the temperatures of the metal-organics, substrate temperature, and plasma gas composition) on the superconductive properties and on the morphology of the films was investigated. Surface morphology and composition were studied by SEM/EDX or EPMA, and AC susceptibility measurements were used to investigate the superconductive properties (T_c and J_c). X-ray diffraction measurements indicated that single-phase YBa₂Cu₃O_7−x films were epitaxially grown with the 00l orientation perpendicular to the substrate surface. The critical temperature (T_c) of the films is about 90 K and the critical current density (J_c) is higher than 10⁶ A/cm² at 77 K and zero field.     

钙钛矿薄膜气相制备的晶粒尺寸优化及高效光伏转换

钙钛矿薄膜的气相制备是一种极具潜力的工业化生产工艺,但薄膜的质量控制目前远落后于溶液制备法.本文通过建立PbI_2薄膜向钙钛矿薄膜完全转化过程中反应时间、晶粒尺寸与温度的关系,实现了薄膜的质量优化及大面积钙钛矿薄膜的制备,将薄膜的平均晶粒粒径从0.42μm优化到0.81μm.基于空间电荷限制电流模型对缺陷密度的研究显示,钙钛矿薄膜的缺陷密度由5.90×10~(16)cm~(–3)降低到2.66×10~(16)cm~(–3).光伏器件(FTO/TiO_2/C_(60)/MAPbI_3/spiro-OMeTAD/Au结构)测试显示,面积为0.045cm~2器件的平均光电转换效率从14.00%提升到17.42%,最佳光电转换效率达到17.80%,迟滞因子减小至4.04%.同时,基于180℃制备的1cm~2器件的光电转换效率达到13.17%.     

Transparent conductive oxide thin films of CdTe-doped indium oxide prepared by pulsed-laser deposition

Transparent conducting oxide thin film CdTe-doped indium oxide (In₂O₃) has been grown by pulsed-laser deposition from a target of CdTe powder embedded in metallic indium. The electro-optical and structural properties were investigated as a function of oxygen partial pressure (PO₂) and substrate temperature (T_s). A film deposited at T_s=420 °C and PO₂=4 Pa shows the minimum resistivity 7.5×10⁻⁴ Ω cm, its optical transmission is 83% and the carrier concentration was 8.9×10²⁰ cm³. The optical band gap and the average roughness of that sample were 3.6 eV and 6.45 Å, respectively. X-ray diffraction studies indicated that the films were polycrystalline. This material is a good candidate for being used as transparent conductor in the CdTe–CdS solar cell.     

SUPERCONDUCTING PROPERTIES AND STRUCTURAL PERFECTION OF EPITAXIAL YBa2Cu3O7-x THIN FILMS

High quality epitaxial YBa₂Cu₃O_7-x thin films have been succcessfully prepared by dc magnetron sputtering deposition, on (100) and (110) aligned SrTiO₃, LaAlO₃ and yttria-stabilized zirconia (YSZ) substrates. The films showed zero resistance around 90 K and had a J_c (at 77 K, H=0) over 10⁶A/cm². It was found that superconducting properties and structures of the films were strongly dependent on oxygen pressure and substrate temperature. The epitaxial structure of the films have been studied by X-ray diffraction. Rutherford backscattering and channeling spectroscopy, X-ray double-crystal diffraction and transmission election microscopy. The experimental results demonstrated that the epitaxial YBa₂Cu₃O_7-x films had excellent superconducting properties and quite perfect structure.     

金属有机物化学气相沉积生长GaN薄膜的室温热电特性研究

采用金属有机物化学气相沉积技术生长了不同掺杂浓度的GaN薄膜, 并且通过霍尔效应测试和塞贝克效应测试, 表征了室温下GaN薄膜的载流子浓度、迁移率和塞贝克系数. 在实验测试的基础上, 计算了GaN薄膜的热电功率因子, 并且结合理论热导率确定了室温条件下GaN薄膜的热电优值(ZT). 研究结果表明: GaN薄膜的迁移率随着载流子浓度的增加而减小, 电导率随着载流子浓度的增加而增加; GaN 薄膜材料的塞贝克系数随载流子浓度的增加而降低, 其数量级在100–500 μV/K范围内; GaN薄膜材料在载流子浓度为1.60×10¹⁸ cm^-3时, 热电功率因子出现极大值4.72×10^-4 W/mK²; 由于Si杂质浓度的增加, 增强了GaN薄膜中的声子散射, 使得GaN薄膜的热导率随着载流子浓度的增加而降低. GaN薄膜的载流子浓度为1.60×10¹⁸ cm^-3时, 室温ZT达到极大值0.0025.     

新型硒化锑材料及其光伏器件研究进展

硒化锑(Sb₂Se₃)是一种二元单相化合物, 原料储量大、毒性低、价格便宜; 同时其禁带宽度合适(～1.15 eV), 吸光系数大(>10⁵ cm^-1), 长晶温度低, 非常适合制作新型低成本低毒的薄膜太阳能电池, 理论光电转换效率可达30%以上. 目前文献报道的Sb₂Se₃薄膜太阳能电池效率已达3.7%, 初步证明了Sb₂Se₃材料在薄膜太阳能电池应用方面的巨大潜力. 本文综述了近年来Sb₂Se₃太阳能电池的研究进展, 着重介绍了Sb₂Se₃的材料特性和薄膜制备及相关理论研究, 阐述了不同结构电池器件的研究进展, 并对其发展趋势进行了展望.     

微晶硅锗薄膜作为近红外光吸收层在硅基薄膜太阳电池中的应用

采用射频等离子体增强化学气相沉积技术,制备了具有一定晶化率不同Ge含量的氢化微晶硅锗(μcSi1-xGex:H)薄膜.通过Ⅹ射线荧光谱、拉曼光谱、X射线衍射谱、傅里叶红外谱、吸收系数谱和电导率的测试,表征了μc-Si_(1-x)Ge_x:H的材料微结构随Ge含量的演变.研究表明:提高Ge含量可以增强μc-Si_(1-x)Ge_x:H薄膜的吸收系数.将其应用到硅基薄膜太阳电池的本征层中可以有效提高电池的短路电流密度(J_(sc)).特别是在电池厚度较薄或陷光不充分的情况下,长波响应的提高会更为显著.应用ZnO衬底后,在Ge含量分别为9%和27%时,μc-Si_(1-x)Ge_x:H太阳电池的转换效率均超过了7%.最后,将μc-Si_(1-x)Ge_x:H太阳电池应用在双结叠层太阳电池的底电池中,发现μc-Si_(0.73)Ge_(0.27):H底电池在厚度为800 nm时即可得到比1700 nm厚微晶硅(μc-Si:H)底电池更高的长波响应.以上结果体现μc-Si_(1-x)Ge_x:H太阳电池作为高效近红外光吸收层,在硅基薄膜太阳电池中应用的前景.     

线性微波化学气相沉积制备SiNx薄膜的微结构及光学性能研究

利用自主研发的线性微波化学气相沉积系统在不同微波功率、微波占空比、基片温度、特气比例条件下制备了SiN_x薄膜. 通过扫描电子显微镜、椭圆偏振仪等表征测量技术, 研究了不同工艺参数对SiN_x薄膜表面形貌、元素配比、折射率、沉积速度的影响, 并探讨了薄膜元素配比、折射率、沉积速度间的关系. 结果表明: 利用线性微波沉积技术, 不同工艺参数下制备的SiN_x薄膜组成元素分布均匀, 同时具有平整的表面状态; 特气比例和微波占空比是影响薄膜折射率的最主要因素, 薄膜折射率在1.92–2.33之间连续可调; 微波功率、微波占空比、沉积温度、特气比例都对SiN_x 薄膜沉积速度影响较大, 制备的SiN_x薄膜最大沉积速度为135 nm·min^-1.     

Ge20Sb15Se65薄膜的热致光学特性变化研究

采用磁控溅射法制备了Ge₂₀Sb₁₅Se₆₅薄膜, 研究热处理温度(150—400 ℃)对薄膜光学特性的影响. 通过分光光度计、X射线衍射仪、显微拉曼光谱仪对热处理前后薄膜样品 的光学特性和微观结构进行了表征, 并根据Swanepoel方法以及Tauc公式分别计算了薄膜折射率色散曲线和光学带隙等参数. 结果表明当退火温度(T_a)小于薄膜的玻璃转化温度(T_g)时,薄膜的光学带隙(E_g^opt)随着退火温度的增加由1.845 eV上升至1.932 eV, 而折射率由2.61降至2.54; 当退火温度大于薄膜的玻璃转化温度时,薄膜的光学带隙随退火温度的增加由1.932 eV降至1.822 eV, 折射率则由2.54增至2.71. 最后利用Mott和Davis提出的非晶材料由非晶到晶态的结构转变模型对结果进行了解释, 并通过薄膜XRD和Raman光谱进一步验证了结构变化是薄膜热致变化的重要原因. 关键词： 20Sb₁₅Se₆₅薄膜')" href="#">Ge₂₀Sb₁₅Se₆₅薄膜 热处理 光学带隙 折射率     

A comparison of FePt thin films with HfO2 or MnO additive

The influence of oxide additives on the magnetic and structural properties of FePt L1₀ thin films has been studied. FePt films with HfO₂ additive grown on a 5 nm MgO buffer showed a primarily random texture for both as-deposited and annealed samples. The average grain size was limited to 10 nm and the perpendicular coercivity was 1.3 kOe for a 10 nm thick FePt +20% HfO₂ film annealed at 650°C for 10 min. In direct contrast, MnO additive neither limited grain size nor L1₀ ordering in annealed FePt films. A 10 nm thick FePt+20% MnO film grown on a 5 nm MgO buffer showed a unique discontinuous microstructure composed of clusters of (0 0 1) textured L1₀ grains after being annealed at 650°C for 10 min. The average size of the grains making up these clusters was 50 nm and the perpendicular coercivity of the film exceeded 7 kOe.     

MgO(111)衬底MgB2 超薄膜的制备和性质研究

利用混合物理化学气相沉积法(HPCVD)在MgO(111)衬底上制备了干净的MgB₂超导超薄膜. 在背景气体压强, 载气氢气流量以及沉积时间一定的情况下, 改变B₂H₆的流量, 制备得到不同厚度系列的MgB₂超导薄膜样品, 并测量了其超导转变温度 T_c, 临界电流密度J_c等临界参量. 该系列超导薄膜沿c轴外延生长, 表面具有良好的连接性, 且有很高的超导转变温度T_c(0) ≈ 35-38 K和很小的剩余电阻率ρ(42 K) ≈ 1.8-20.3 μΩ·cm^-1. 随着膜厚的减小而减小, 临界温度变低, 而剩余电阻率变大. 其中20 nm的样品在零磁场, 5K时的临界电流密度J_c ≈ 2.3×10⁷ A/cm². 表明了利用HPCVD在MgO(111)衬底上制备的MgB₂超薄膜有很好的性能, 预示了其在超导电子器件中广阔的应用前景. 关键词： MgO(111)衬底 2超薄膜')" href="#">MgB₂超薄膜 混合物理化学气相沉积     

分子束外延制备的垂直易磁化MnAl薄膜结构和磁性

系统地研究了利用分子束外延方法在GaAs(001) 衬底上外延生长的MnAl_x薄膜的结构和垂直易磁化特性随组分及生长温度的依赖关系. 磁性测试表明, 可在较大组分范围内 (0.4≤x≤1.2) 获得大矫顽力的垂直易磁化MnAl_x薄膜, 然而同步辐射X射线衍射和磁性测试发现当x≤0.6时MnAl薄膜出现较多的软磁相, 当x >0.9时, MnAl薄膜晶体质量和化学有序度逐渐降低, 组分为MnAl_0.9时制备的薄膜有最好的[001]取向. 随着生长温度的增加, MnAl_0.9薄膜的有序度、垂直磁各向异性常数、矫顽力和剩磁比均增加, 350℃时制备的MnAl_0.9薄膜化学有序度高达0.9, 其磁化强度、剩磁比、矫顽力和垂直磁各向异性常数分别为265emu/cm³、93.3%、8.3kOe (1 Oe=79.5775A/m)和7.74Merg/cm³ (1 erg=10^-7J). 不含贵金属及稀土元素、良好的垂直易磁化性质、 与半导体材料结构良好的兼容性以及磁性能随不同生长条件的可调控 性使得MnAl薄膜有潜力应用于多种自旋电子学器件. 关键词： 分子束外延 大矫顽力材料 磁各向异性     

铟锡氧化物薄膜表面等离子体损耗降低的研究

本文采用直流磁控溅射方法在普通浮法玻璃基底上制备了立方多晶铁锰矿结构的铟锡氧化物(indium tin oxide, ITO)薄膜,并对其进行了结晶性、表面粗糙度、紫外-可见吸收光谱、折射率、介电常数及霍尔效应的测试.研究了溅射时基底温度的改变对于ITO薄膜的光电、表面等离子体性质的影响.随着基底温度由100?C升高至500?C,其光学带隙(3.64—3.97eV)展宽,减少了电子带间跃迁的概率,有效降低了ITO薄膜的光学损耗.与此同时,对应ITO薄膜的载流子浓度(4.1×10~(20)-—2.48×10~(21)cm~(-3))与迁移率(24.6—32.2 cm~2·V~(-1)·s~(-1))得到提高,电学损耗明显降低.     

Buffers for high temperature superconductor coatings. Low temperature growth of CeO2 films by metal–organic chemical vapor deposition and their implementation as buffers

Smooth, epitaxial cerium dioxide thin films have been grown in-situ in the 450–650°C temperature range on (001) yttria-stabilized zirconia (YSZ) substrates by metal–organic chemical vapor deposition (MOCVD) using a new fluorine-free liquid Ce precursor. As assessed by X-ray diffraction, transmission electron microscopy (TEM), and high-resolution electron microscopy (HREM), the epitaxial films exhibit a columnar microstructure with atomically abrupt film-substrate interfaces and with only minor bending of the crystal plane parallel to the substrate surface near the interface and at the column boundaries. With fixed precursor temperature and gas flow rate, the CeO₂ growth rate decreases from 10 Å/min at 450°C to 6.5 Å/min at 540°C. The root-mean-square roughness of the films also decreases from 15.5 Å at 450°C to 4.3 Å at 540°C. High-quality, epitaxial YBa₂C₃O_7−x films have been successfully deposited on these MOCVD-derived CeO₂ films grown at temperatures as low as 540°C. They exhibit T_c=86.5 K and J_c=1.08×10⁶ A/cm² at 77.4 K.