在CeO2-ZrO2中加入La2O3对改善单Pd三效催化剂性能的作用

浸渍法制备了CeO₂-ZrO₂-La₂O₃复合氧化物，用XRD、热分析（TG-DTA，DSC）、BET表面积、H₂-TPR等对合成样品进行表征，研究了La₂O₃的加入对CeO₂-ZrO₂和单钯Pd/CeO₂-ZrO₂/γ-Al₂O₃/蜂窝陶瓷催化剂性能和热稳定性的影响。结果表明，在CeO₂-ZrO₂-La₂O₃中，La的存在能促进CeO₂-ZrO₂固溶体的还原，提高贮氧能力；在Pd/CeO₂-ZrO₂/γ-Al₂O₃中加入La有利于提高催化剂的耐热稳定性，阻止γ-Al₂O₃在高温下的晶相转变，进一步稳定Al₂O₃的结构，保持其高的表面积。在贵金属Pd的负载量为1 g·L^-1的条件下，测定了Pd/CeO₂-ZrO₂-La₂O₃/γ-Al₂O₃/蜂窝陶瓷催化剂对CO、C₃H₈和NOx的三效催化净化活性。结果表明，在Pd/CeO₂-ZrO₂/Al₂O₃/蜂窝陶瓷催化剂中加入La₂O₃后，能明显地改善催化剂的低温活性和三效催化性能，经1 000 ℃老化10 h后，CO、C₃H₈和NO_x净化的起燃温度（T₅₀）分别为330 ℃、350 ℃和380 ℃。     

Ni2+在γ-Al2O3上的分散状态及负载型Ni/γ-Al2O3催化剂的α-蒎烯加氢活性

用X-射线衍射(XRD)、紫外-可见漫散射光谱(UV-Vis DRS)、程序升温还原(TPR)、CO化学吸附和微反测试等方法研究了Ni²⁺在γ-Al₂O₃上的分散状态和负载型Ni/γ-Al₂O₃催化剂的α-蒎烯加氢催化活性。结果表明，当Ni²⁺负载量远低于其在γ-Al₂O₃载体表面分散容量时，Ni²⁺优先嵌入载体表面四面体空位，随着Ni²⁺负载量的增加，嵌入载体表面八面体空位Ni²⁺的比例增大。由于八面体Ni²⁺易被还原为金属态Ni⁰，NiO/γ-Al₂O₃样品的还原度随Ni²⁺负载量的增加而大幅度地增加，经氢还原所得Ni/γ-Al₂O₃催化剂的CO吸附量和α-蒎烯加氢催化活性大幅度增加。对La₂O₃助剂的作用进行了研究，结果表明分散在γ-Al₂O₃上的La³⁺物种可阻止Ni²⁺嵌入γ-Al₂O₃表面四面体空位，增大了八面体Ni²⁺物种所占比例，提高了催化剂的还原度，故Ni-La₂O₃/γ-Al₂O₃催化剂催化活性高于Ni/γ-Al₂O₃催化剂。     

H2SO4处理的Nb2O5/γ -Al2O3催化剂表面酸性与催化性能研究

用Hammett指示剂法、红外光谱（IR）、示差扫描量热-热重法（DSC-TG）和微型催化反应装置等研究了H₂SO₄处理的负载型Nb₂O₅/γ-Al₂O₃催化剂表面酸性和催化异丁烯（IB）与异丁醛（IBA）反应生成2，5-二甲基-2，4-己二烯（DMHD）的催化性能。结果表明随所用H₂SO₄浓度增加，Nb₂O₅/γ-Al₂O₃催化剂表面酸性增强，B酸量增加，L酸量先增加后下降。经H₂SO₄处理的Nb₂O₅/γ-Al₂O₃催化剂的催化活性明显增加，但当H₂SO₄浓度超过0.05 mol·L^-1时催化活性又急剧下降，这可能是因为在H₂SO₄处理的催化剂表面形成的强酸中心上，产物分子进一步转化为积炭且封闭催化剂活性表面，导致催化活性下降。     

纳米固体超强酸SO42-/Fe2O3的制备及其催化合成乙酸乙酯

将Fe₂O₃纳米粉体经一定浓度的H₂SO₄浸泡活化后制成纳米固体超强酸SO₄^2-/Fe₂O₃,将其用于催化合成乙酸乙酯以考察其活性。利用均匀设计分析了超强酸制备过程及酯化反应过程中各因素的影响,研究结果表明较好的制备条件是:H₂SO₄浓度:2.5mol·L^-1;浸泡时间:1h;活化温度:167℃;活化时间:1h,此时获得的固体超强酸SO₄^2-/Fe₂O₃的粒径小于50nm。当催化剂用量为冰乙酸质量的5%,n(乙醇)∶n(冰乙酸)为3∶1,反应3.5h后乙酸的转化率高于80%。该催化剂经H₂SO₄溶液浸泡、活化再生后可重新使用,推断出其酸强度H₀<-14.5。     

Pt/ZrO2-Al2O3催化剂催化氧化C3H6和CO性能

采用共沉淀法合成了ZrO₂与Al₂O₃的不同质量比的ZrO₂-Al₂O₃复合氧化物,并以此为载体通过等体积浸渍法制备了1.5% Pt/ZrO₂-Al₂O₃（w/w）催化剂。以C₃H₆和CO为反应物的催化性能评价显示,在系列催化剂中以Pt/Zr（0.4）-Al₂O₃催化剂催化氧化活性最为优异,其C₃H₆和CO的起燃温度（T₅₀）小于125℃,完全转化温度（T₉₀）小于150℃。采用XRD、低温N₂吸附、H2-TPR、CO脉冲吸附等分析表征技术探索了催化剂物相结构、比表面积、颗粒尺寸等对催化活性的影响规律。结果发现,ZrO₂-Al₂O₃复合氧化物具有Al₂O₃材料的介孔织构和大比表面积特性,且产生了Al_xZr_1-xO_y固溶体新物相。适当的ZrO₂与Al₂O₃的质量比,是改善Pt与ZrO₂-Al₂O₃的相互作用强度,促进贵金属Pt的分散,提升Pt/ZrO₂-Al₂O₃催化剂的低温氧化活性的关键。     

Pt/ZrO2-Al2O3催化剂催化氧化C3H6和CO性能

采用共沉淀法合成了ZrO₂与Al₂O₃的不同质量比的ZrO₂-Al₂O₃复合氧化物,并以此为载体通过等体积浸渍法制备了1.5% Pt/ZrO₂-Al₂O₃（w/w）催化剂。以C₃H₆和CO为反应物的催化性能评价显示,在系列催化剂中以Pt/Zr（0.4）-Al催化剂催化氧化活性最为优异,其C₃H₆和CO的起燃温度（T₅₀）小于125℃,完全转化温度（T₉₀）小于150℃。采用XRD、低温N₂吸附、H₂-TPR、CO脉冲吸附等分析表征技术探索了催化剂物相结构、比表面积、颗粒尺寸等对催化活性的影响规律。结果发现,ZrO₂-Al₂O₃复合氧化物具有Al₂O₃材料的介孔织构和大比表面积特性,且产生了Al_xZr_1-xO_y固溶体新物相。适当的ZrO₂与Al₂O₃的质量比,是改善Pt与ZrO₂-Al₂O₃的相互作用强度,促进贵金属Pt的分散,提升Pt/ZrO₂-Al₂O₃催化剂的低温氧化活性的关键。     

整体式Co3O4/YSZ- -Al2O3＋CYZ催化剂上的甲烷催化燃烧

用质量比为3∶2的YSZ-γ-Al₂O₃和CeO₂-Y₂O₃-ZrO₂的混合物(以YSZA＋CYZ表示)作载体, 制备了不同Co₃O₄含量的整体式甲烷燃烧催化剂, 同时制备了分别以YSZA和CYZ为载体的催化剂作为对比, 研究了它们老化前后的反应性能, 并用BET, XPS, XRD, TPR等研究了催化剂的比表面、表面状态、晶相结构和还原性能. 结果表明, YSZ- -Al₂O₃和CeO₂-Y₂O₃-ZrO₂混合载体能有效地抑制CoAl₂O₄的生成, 并能充分发挥各自的优点, 因此负载一定量的钴后表现出很高的甲烷催化燃烧活性和抗老化性, 尤其是含8 wt% Co₃O₄的样品性能最佳, 有望成为实用的甲烷燃烧催化剂之一.     

MO(M=Cu和Ni)/TiO2/γ-Al2O3催化剂在CO+O2反应中的活性

采用X射线衍射(XRD)，程序升温还原(TPR)等表征手段考察了TiO₂改性对CuO(或NiO)在γ-Al₂O₃表面上分散以及还原性能的影响，同时检测了这些改性的催化剂在CO+O₂反应中的活性。结果表明:TiO₂的改性使得CuO和NiO在γ-Al₂O₃载体上的分散复杂化，产生了多种状态的氧化铜(氧化镍)物种。当负载量低于其在γ-Al₂O₃上的分散容量(0.56 mmol Ti⁴⁺/100 m² γ-Al₂O₃)时，TiO₂的加入主要是抑制了CuO和NiO在γ-Al₂O₃载体上的分散;而当负载量远大于其分散容量时，出现了CuO和NiO在晶相TiO₂(锐钛矿)上的分散。无论其负载量如何，TiO₂的加入促进了CuO的还原。因此，在250 ℃的CO+O₂反应中，改性的催化剂中具有更多的活性位，因而显示出更高的活性;相反，TiO₂的改性则抑制了NiO的还原。因此，在350 ℃的CO+O₂反应中，可还原的氧化镍的量明显少于未经改性的催化剂，导致改性催化剂的活性降低。     

La3+掺杂CaFe2O4材料的制备及室温检测超低浓度甲醛

采用静电纺丝法成功制备了La³⁺掺杂CaFe₂O₄材料。通过X射线衍射、扫描电子显微镜和X射线光电子能谱对La³⁺掺杂CaFe₂O₄材料的结构和形貌进行了表征。随后，研究了La³⁺的掺杂量（质量分数）对CaFe₂O₄气敏性能的影响。研究表明，3% La³⁺掺杂CaFe₂O₄材料在室温下对100 μL·L^-1甲醛的响应最高（R_a/R_g=14.1）。更为重要的是，对甲醛的最低检测限低至0.1 nL·L^-1，并且响应/恢复时间仅为4.3 s/8.4 s。     

B2O3-Bi2O3-ZnO-Al2O3玻璃助烧剂对BaTiO3陶瓷烧结条件、晶体结构和介电性能的影响

通过调节B₂O₃‐Bi₂O₃‐ZnO‐Al₂O₃(BBZA)玻璃的添加量研究其对钛酸钡(BaTiO₃)陶瓷烧结条件、晶体结构和介电性能的影响。结果表明：添加适量的BBZA玻璃能够有效地将BaTiO₃陶瓷烧结温度由1350℃降至950℃,并使其致密化。同时,添加BBZA玻璃后,BaTiO₃的晶体结构随着烧结温度的升高而发生转变(立方相→四方相)。另外,BBZA玻璃的引入使BaTiO₃陶瓷的居里峰得到了有效的抑制和拓宽。陶瓷微观形貌显示,玻璃相均匀分布在BaTiO₃晶粒表面。优化的BaTiO₃陶瓷制备条件如下：BBZA添加量(质量分数)为2.0%,烧结温度为950℃。在该条件下制备的BaTiO₃陶瓷介电常数达到1364,介电损耗低至1.2%。     

B2O3-Bi2O3-ZnO-Al2O3玻璃助烧剂对BaTiO3陶瓷烧结条件、晶体结构和介电性能的影响

通过调节B₂O₃-Bi₂O₃-ZnO-Al₂O₃(BBZA)玻璃的添加量研究其对钛酸钡(BaTiO₃)陶瓷烧结条件、晶体结构和介电性能的影响。结果表明：添加适量的BBZA玻璃能够有效地将BaTiO₃陶瓷烧结温度由1 350℃降至950℃,并使其致密化。同时,添加BBZA玻璃后,BaTiO₃的晶体结构随着烧结温度的升高而发生转变(立方相→四方相)。另外,BBZA玻璃的引入使BaTiO₃陶瓷的居里峰得到了有效的抑制和拓宽。陶瓷微观形貌显示,玻璃相均匀分布在BaTiO₃晶粒表面。优化的BaTiO₃陶瓷制备条件如下：BBZA添加量(质量分数)为2.0%,烧结温度为950℃。在该条件下制备的BaTiO₃陶瓷介电常数达到1 364,介电损耗低至1.2%。     

BaO-Al2O3-B2O3系密封玻璃的结构与性质

The BaO-Al₂O₃-B₂O₃ glasses manufactured for solid oxide fuel cell(SOFC) sealing were studied. The effect of different n_BaO/n_B2O3 on crystal, thermal properties, density and infrared spectra of this system has been discussed. The results show that the trends of crystallization, glass transformation temperature, dilatometric softening temperature and density increase with n_BaO/n_B2O3 values. But a typical property deviation occurs when n_BaO/n_B2O3 is 0.875, and its coefficient of thermal expansion has the maximum at this point. The changes of properties can attribute to the conversion of boron from tetrahedral coordination to trigonal, breakage of the local glass network and interaction between the network modifiers. These can be proved by infrared spectra of glasses. Thermal properties of some studied samples are suitable for the sealing of SOFC using Sm doped ceria electrolyte and operating at 400～600 ℃.     

The Al2O3-Fe2O3 Mixed Oxidic System, I. Preparation and Characterization

A series of Al₂O₃-Fe₂O₃ mixed oxidic solids with composition ranging from 0 to 100% of Fe₂O₃ were prepared and examined for structural characteristics. XRD diagrams showed the presence of α-Al₂O₃ and hematite phases. The analysis of M?ssbauer spectra revealed the existence of two iron containing phases. The specific surface area of the mixture decreases by the addition of iron and depends on the crystal phases of the mixture. This revised version was published online in June 2006 with corrections to the Cover Date.     

Eu3+掺杂SiO2-B2O3-NaF玻璃的制备及发光性质

The Eu-doped SiO₂-B₂O₃-NaF glass was prepared by sol-gel process, using tetraethoxy Silicane, boric acid and sodium fluoride as starting materials, 0.10 mol·L^-1 EuCl₃ solution as the dopant. The luminescent properties of Eu³⁺ doped SiO₂-B₂O₃-NaF phosphors were investigated. The phosphors showed prominent luminescence in pink, the strong emission of Eu³⁺ comes from electronic transition of ⁵D₀- ⁷F₁（591 nm）and ⁵D₀- ⁷F₂（615 nm）,which derived from two transition modes of magnetic-dipole and electric-dipole .The peak intensity of 591nm in SiO₂-B₂O₃-NaF matrix is much stronger than it in the other matrixes, it means that SiO₂-B₂O₃-NaF has sensitization on the transition of ⁵D₀- ⁷F₁ (Eu³⁺). If there are broad bonds in the range of 275～380 nm in the excitation spectrum of Eu³⁺ -doped SiO₂-B₂O₃-NaF glass, the emission peak intensity should be intensified. It is because the electron migration CT band of O^2--Eu³⁺. For all Eu³⁺ concentrations used, the investigation found that when the mass of fraction got to 29.19×10^-3, the luminescence intensity reached the summit. And there is a phenomenon of concentration quenching. Investigation with the same concentration of Eu³⁺ at different annealed temperature, we found that the sample annealed at 400 ℃, the luminescence intensity achieved its maximum value, and Eu³⁺ in this matrix had a phenomenon of temperature quenching. The structural characterization of these luminescent materials was carried by used XRD and TEM. The result showed that the phosphor was in amorphous phase.     

Fe2O3/Al2O3二元气凝胶合成高质量单壁纳米碳管

通过溶胶和超临界干燥方法制得了Fe₂O₃/Al₂O₃二元气凝胶，其比表面积和孔隙体积分别为246 m²·g^-1和1.89 cm³·g^-1，并具有较宽的孔径分布。以Fe₂O₃/Al₂O₃二元气凝胶作催化剂，通过甲烷催化裂解成功地合成了高质量的单壁纳米碳管。利用FESEM、TEM和HRTEM、Raman光谱等分析手段研究了反应温度对单壁纳米碳管生长的影响。结果表明在900 ℃时合成单壁纳米碳管的质量较高，并且合成的炭产物为毡状，该炭产物主要为高质量的单壁纳米碳管。     

The Al2O3-Fe2O3 Mixed Oxidic System, II. Catalytic Decomposition of N2O

N₂O decomposition was examined over a series of Al₂O₃-Fe₂O₃ mixed oxidic solids with composition ranging from 0 to 100% of Fe₂O₃. The catalytic activity of the solids runs parallel to the number of atoms of iron in the Al_2−x Fe_xO₃ solid solution phase. Two compensation effects are present. The first corresponds to catalysts rich in alumina, and the second one to catalysts rich in hematite. This revised version was published online in June 2006 with corrections to the Cover Date.     

The Ternary System Li2O-Al2O3-B2O3: Compounds and Phase Relations

The ternary system Li₂O-Al₂O₃-B₂O₃ is reinvestigated with solid-state reaction and X-ray powder diffraction technique to clarify some long-standing uncertainties. The phase relations are constructed based on the phase identifications of 51 ternary samples. Six ternary compounds, Li₂AlB₅O₁₀, LiAlB₂O₅, Li₃AlB₂O₆, Li₂AlBO₄, LiAl₇B₄O₁₇ and a compound with a composition close to 0.66Li₂O·0.06Al₂O₃·0.28B₂O₃, are observed or confirmed in this system, and the thermal stability of these ternary compounds is also discussed on the basis of DTA experimental results.     

La2O3对Ni/γ-Al2O3甲烷化催化剂的助催化作用

我国将稀土作为助剂引入镍基甲烷化催化剂,大大提高了催化剂的活性和热稳定性,并已投入工业应用［1－3］．稀土对不同镍催化剂反应性能及其作用机理的研究已有一些报导［3－7］．谢有畅等观察到镍负载在经单层La2O3改性的γ－Al2O3表面,其晶粒要比没有La2O3时小得多．Rotgerink等认为添加La后反应速率的增加不只是由于几何效应,而是La对甲烷化本身有促进作用,单位镍表面的活性是随La含量不同而改变的,活性增加的同时表观活化能也增加［5］．作为助剂的La2O3在氢还原和反应过程中的变化及其作用的研究和讨论较少,目前一般认为添…     

Ho3+/Yb3+共掺ZnO-Al2O3-GeO2-SiO2玻璃陶瓷的制备和上转换发光性质

综合ZnO-Al₂O₃-SiO₂系和锗酸盐玻璃陶瓷的优点,采用熔融-晶化法首次制备了Ho³⁺/Yb³⁺共掺以ZnAl₂O₄为主晶相的ZnO-Al₂O₃-GeO₂-SiO₂系玻璃陶瓷。因[GeO₄]四面体和[SiO₄]四面体都是玻璃网络形成体,讨论了GeO₂取代SiO₂对玻璃陶瓷样品硬度及发光性能的影响,最终确定GeO₂的取代量为10.55%（w/w）时,玻璃陶瓷综合性能最佳。在980 nm泵浦光的激发下,发现强的绿色（546 nm）和弱的红色（650 nm）上转换发光,并研究了不同Ho³⁺/Yb³⁺掺杂比对样品上转换发光的影响,最终结果表明当Ho³⁺/Yb³⁺掺杂比为1：11（n/n）时样品荧光强度最强,在绿色上转换发光材料方面具有潜在的应用。