用浸渍法制备了A l2O3,S iO2和MgO等不同性质载体负载的锰氧化物催化剂,考察了其对CO氧化反应的性能,并用XRD、XPS、TPR和XAFS等方法对催化剂进行了详细表征.活性测试结果表明,不同载体负载的样品的活性次序为:MnOx/A l2O3>MnOx/MgO>MnOx/S iO2.XRD结果表明,在S iO2和A l2O3上,负载量为15%的催化剂中没有检测到Mn氧化物的衍射峰,说明Mn物种在载体表面分散性很好,而在MgO上检测到Mg6MnO8物种.XAFS等表征结果表明,A l2O3和S iO2负载的样品中Mn主要以高分散的Mn2O3形式存在,MgO负载的样品中Mn的分散性相对较差,且与载体发生强相互作用.结合XPS和TPR结果,Mn氧化物与载体相互作用强弱的顺序为:MnOx/MgO>MnOx/A l2O3>MnOx/S iO2.负载Mn氧化物催化剂的活性与分散度没有直接对应关系,而是显示了明显的载体效应.     

H4SiW12O40/TiO2/SiO2复合光催化剂的制备及性能研究

溶胶-凝胶法制备了TiO2/S iO2光催化剂,利用所得TiO2/S iO2光催化剂为基体,浸渍烧结法制备了H4S iW12O40/TiO2/S iO2表面负载修饰型复合光催化剂。TG-DSC、XRD、SEM、BET对催化剂的物化结构进行了表征,分析了TiO2和H4S iW12O40催化活性组分在S iO2载体表面上的键联机理。光催化性能测试是以低浓度酸性品红染料的水溶液为降解目标物,试验结果表明H4S iW12O40的负载修饰可以改进TiO2/S iO2光催化剂的催化活性,酸性品红的降解效率最高可以增加45%。     

WO3-TiO2/SiO2的制备、表征及光催化甲烷和水的反应性能

以表面改性法制备出TiO2／SiO2，进而以浸渍法制备出负载型复合半导体材料WO3-TiO2／SiO3，利用XRD、BET、TPR、UVDRS、IR和TPD等技术对材料的表面性质与构造、光响应性能和化学吸附性能进行了表征，并研究了该材料光催化甲烷和水合成甲醇和氢的反应性能．结果表明：载体有效分散表面物种并使其能隙增大；WO3与TiO2复合所形成的组合活性基元可调变吸光带边并促进对甲烷和水的化学吸附；在100℃以上，光激发WO3-TiO2／SiO2表面产生的光生空穴，促使分子吸附态的甲烷解离并向甲醇转化，形成一定的“光-表面-热”协同作用促使反应顺利进行，对甲醇的选择性达到83％以上．     

TiO_2-Al_2O_3载体的制备方法对其负载的磷化镍催化剂加氢脱氮反应性能的影响

采用共沉淀法和原位溶胶-凝胶法制备了TiO2-Al2O3复合载体,其负载的磷化镍催化剂采用等体积浸渍法和H2原位还原法制备.通过N2吸附(BET)、X射线衍射(XRD)、透射电镜(TEM)、程序升温还原(TPR),X射线光电子能谱(XPS)和等离子体发射光谱(ICP-AES)表征技术对催化剂进行了表征,并通过喹啉的加氢脱氮反应评价了催化剂的加氢脱氮性能.结果表明,原位溶胶-凝胶法制成的复合载体基本保留了原有的γ-Al2O3的孔特征,具有较大的比表面积和较宽的孔分布,TiO2主要以表面富集的形式分散在管状的γ-Al2O3表面,其负载的磷化镍催化剂还原后所形成的活性相为Ni2P和Ni12P5;而共沉淀法制成的复合载体比表面积较小,孔径分布更加集中,TiO2趋于在块状的Al2O3表面均匀分散,其负载的磷化镍催化剂具有更好的可还原性,还原后所形成的活性相为Ni2P.不同的载体制备方法和不同的钛铝比对催化剂加氢脱氮性能影响较大,当n(Ti)/n(Al)=1/8时,共沉淀法载体负载的催化剂表现出最佳的加氢脱氮性能,在340℃,3 MPa,氢油体积比500,液时空速3 h-1的反应条件下,喹啉的脱氮率可以达到91.3%.     

MoO3-TiO2/SiO2上光促表面催化甲烷和水合成甲醇和氢气

用分步等体积浸渍法制备了负载型复合半导体催化剂MoO3-TiO2/SiO2,通过XRD,BET,TPR,IR,UVDRS和TPD等手段对其进行了表征,结果表明,活性组分在载体表面高度分散,并具有量子尺寸效应,吸光阈值显著蓝移;TiO2在SiO2表面分散可增强MoO3与载体的相互作用,调变吸光性能,所形成的表面活性基元能够有效地吸附活化甲烷和水.在100℃下利用固定床环隙反应器借助紫外光的激发,通过“光-表面-热”协同作用,气相甲烷和水在MoO3-TiO2/SiO2表面生成了甲醇和氢,选择性达到85.6%.     

糠醛液相加氢用Mo改性Ni-B/TiO2-Al2O3(S)非晶态合金催化剂

以溶胶-凝胶法制备复合载体TiO2-Al2O3(S)负载非晶态Ni-B合金用于催化糠醛液相加氢反应, 并研究了Mo对催化剂的改性作用. 采用ICP(等离子发射光谱)、DSC(差示扫描量热)、N2吸附、TPR(程序升温还原)和TPD(程序升温脱附)等技术对催化剂进行了表征. 研究结果表明, 与单一氧化铝载体相比, 复合载体负载的Ni-B合金催化性能明显提高, 这是由于在同样的制备条件下, 复合载体负载的Ni-B中Ni含量更高, 同时TiO2分散到了γ-Al2O3的孔中, 堵住了部分细孔, 有利于产物糠醇扩散出来, 防止深度加氢. Mo能提高Ni-B/TiO2-Al2O3(S)的热稳定性, 增大Ni的负载量, 使部分氧化态物种变得易于被还原, 表面出现新的加氢活性中心, 并增加化学吸附中心数, 减弱吸氢强度, 因而显著提高了Ni-B/TiO2-Al2O3(S)的活性; Mo添加使Ni-B/TiO2-Al2O3(S)的平均孔径及总孔容均增大, 有利于产物糠醇扩散出来, 还能使糠醇更易从催化剂的表面脱附, 防止其深度加氢, 因而提高了糠醇的选择性. 当Mo含量为1.25%时, 糠醛转化率、糠醇选择性都达到了100%.     

一种TiO2修饰的Pd/Al2O3选择性加氢用催化剂的研究

 研制了一种用TiO2修饰的Pd/Al2O3(Pd/Al2O3-TiO2)选择性加氢催化剂,并采用N2吸附,XRD,SEM,FT-IR,TPD和TPR等手段对催化剂进行了表征,考察了催化剂的催化性能. 结果表明,Pd/Al2O3-TiO2催化剂具有较小的比表面积; 低的表面酸性,且以弱酸中心为主; TiO2在Al2O3表面呈高度分散,并集中于载体到一定的深度; 用含钛溶液浸渍次数以1次为佳. 载体中TiO2的添加使得PdO更易于被还原. 用这种复合氧化物作载体制备的催化剂表现出更高的加氢活性和选择性,优于单纯以Al2O3作载体的催化剂.     

一种新型结构的CO2重整CH4催化剂的制备与催化性能研究

研制高效、稳定的Ni基催化剂一直是CO2重整CH4反应过程的重点之一。本文采用微波技术和真空浸渍法制备了ZrO2单层分布的负载型ZrO2／Al2O3复合载体和活性物种单层分布的Ni／ZrO2／Al2O3催化剂，并利用XRO、FT-IR、TPR、TPD、BET等技术研究了新型结构催化剂的分散状态、体相结构、表面性能、催化活性及稳定性。结果表明，催化剂在CO2重整CH4反应体系中具有良好的催化活性和稳定性。     

TiO2-Al2O3复合氧化物负载NiMo加氢脱硫催化剂的研究

采用溶胶凝胶技术，从Al2O3载体的表面改性出发，制备了TiO2-Al2O3复合载体。采用此改性载体制备了NiMo／TiO2-Al2O3催化剂；用中压固定床微反装置考察了载体改性对制备的催化剂的噻吩加氢脱硫(HDS)活性的影响．用透射电镜、NH3-TPD及吡啶红外光谱法对改性载体和催化剂进行了表征．结果表明，经钛溶胶改性的载体制备的催化剂与原有载体制备的催化剂相比，催化剂活性提高了20％．改性载体表面负载的钛溶胶以纳米尺寸的TiO2微粒形态存在．     

负载型纳米ZrO2-Al2O3复合载体中ZrO2的负载量对Ni基催化剂性能的影响

采用真空浸渍法在负载型纳米ZrO2-Al2O3复合载体上负载NiO,并用X射线衍射考察了NiO在复合载体上的分散周值.结果表明,该分散阈值与ZrO2-Al2O3复合载体中ZrO2的负载量有关,当ZrO2的负载量为0.60 g/g时,NiO的分散阈值达到最高值0.315 g/g.热重-微分热重和程序升温脱附结果表明,NiO在不同ZrO2负载量的复合载体表面形成不同的相互作用和分布状态,复合载体中ZrO2的负载量影响催化剂表面活性中心的种类和对CO2的吸附.同时考察了不同ZrO2负载量的复合载体Ni基催化剂在CO2重整CH4反应中的活性和稳定性.     

制备高比表面负载型催化剂的一种新方法

In this paper, a new way to increase the specific surface areas of supported catalysts has been suggested. The results for MoO_3/ZrO_2, WO_3/ZrO_2, CuO/ZrO_2, SO_4~(2-)/ZrO_2, NiO/ZrO_2, Fe_2O_3/ZrO_2, Fe_2(SO_4)_3/ZrO_2, MoO_3/TiO_2, WO_3/TiO_2, SO_4~(2-)/TiO_2, NiSO_4/TiO_2, NiO/TiO_2, V_2O_5/TiO_2 etc. systems show that the specific surface areas of the samples, prepared by impregnating some hydroxides then calcinating at high temperature, are much larger than those of the samples prepared with a traditional method——impregnating their oxides calcinated at the same temperature. Using this way, the specific surface areas of some supported catalysts can increase by several times. The surface areas of some supports such as zirconia and titania are not large enough, and they are easy to sinter at high temperature. In these cases, the advantage of of this preparation method is fully displayed, and the specific surface areas of the resulting zirconia-or titania-supported catalysts can compare favourably with those of the catalysts prepared from some classical supports (such ar γ-Al_2O_3, SiO_2).In addition, it has been proved by means of XPS, XRD, LRS, and DTA that as an active component disperse on a support as a monolayer and its content comes up to its monolayer dispersion capacity, the specific surface area of the obtained catalyst would be the largest. We suggest a mechanism that an active component covered on a support can not only segregate its particles, but also hinder the surface diffusion of support, and as a result, its crystalline growth, an accompanying phase transformation and inter-crystalline sintering are all retarded.     

负载型光催化材料CeO2-TiO2/SiO2的表面结构与光响应性能

采用表面改性法制备了负载型光催化材料CeO2-TiO2/SiO2,并用X射线衍射,比表面积测定,红外光谱,程序升温还原和紫外可见漫反射光谱技术对固体材料的结构和光响应性能进行了表征.结果表明,CeO2与TiO2在材料表面存在相互修饰作用,CeO2能拓展TiO2的光响应范围,使TiO2吸光区域由紫外拓宽至可见光区,从而提高材料的光能利用率;Ti4 可以进入CeO2晶格,形成Ce-O-Ti键合,使得Ti4 平均配位数增加,同时提高了CeO2体相晶格氧的活性;TiO2有助于提高CeO2在载体表面的分散程度,减小CeO2的微晶尺寸,提高固体材料的能隙值和氧化还原能力.     

TiO2-SiO2复合气凝胶：常压干燥制备及性能表征

以廉价的四氯化钛和工业水玻璃为原料,通过溶胶-凝胶法制得TiO2-SiO2复合湿凝胶,用三甲基氯硅烷(TMCS)/乙醇(EtOH)/正己烷(Hexane)混合溶液对湿凝胶进行改性,常压干燥制备了TiO2-SiO2复合气凝胶.利用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、红外光谱(FTIR)、X射线衍射(XRD)及N2吸附/脱附法对复合气凝胶的形貌和性质进行了分析.结果表明,TiO2-SiO2复合气凝胶具有连续多孔结构,150℃干燥后复合气凝胶的比表面积为1 076 m2·g-1,孔体积为4.96 cm3·g-1;经550 ℃热处理后,复合气凝胶仍然具有高的孔隙率,比表面积为856 m2·g-1,孔体积为3.46 cm3·g-1.吸附和光催化降解罗丹明B的结果表明,复合气凝胶同时具有较好的吸附和光催化性能,其吸附/光催化协同作用活性优于纯SiO2气凝胶和锐钛矿TiO2粉末;且重复利用四次降解率仍然可达到89%.     

二氧化钛薄膜的低温制备及其性能表征

通过水煮法在较低温度下制备了均匀、透明的TiO2-SiO2复合薄膜,利用XRD、AFM和UV-Vis光谱等手段对薄膜的物相、表面形态结构和透明性进行了表征,分析了SiO2的添加对薄膜性质的影响.并利用紫外光照降解罗丹明B溶液评价了薄膜的光催化活性及其影响因素.实验结果表明,通过水煮法在较低温度下制备的薄膜具有较高的光催化活性,适量SiO2的添加能够提高薄膜的光催化活性.     

新型WO3/HMS催化剂的制备及其对环戊烯选择氧化反应的催化性能

 采用草酸络合方法将WO3固载到六方介孔全硅分子筛HMS上,制得新型WO3/HMS非均相催化剂. 利用SEM,TEM,N2吸附,XRD及激光拉曼光谱等手段对催化剂进行了表征,研究了催化剂在环戊烯选择性氧化合成戊二醛反应中的催化性能. 结果表明,在WO3/HMS催化下环戊烯和H2O2的转化率均可达100%,戊二醛的选择性可达72%. WO3以高分散状态存在于催化剂表面. 单次反应后钨的溶脱量(5.5 μg/ml)很小,对反应几乎没有影响. 催化剂具有较高的稳定性,可以重复套用6次. 失活后的催化剂可通过简单焙烧的方式再生.     

钛硅复合氧化物局域结构的研究

用XAFS（X-ray absorption fine structure）分析了由溶胶-凝胶、液相浸渍和化学气相沉积等三种方法制备的二氧化钛和二氧化硅复合氧化物的Ti K边结构.结果表明:溶胶-凝胶法制得的复合氯化物中的钛分散很好,液相浸渍法次之,而化学气相沉积法最差.不论哪种方法,随钛含量（或钛硅原子比）的增加,边前特征峰A2降低,钛的第一配位层Ti－O的配位数和键长增加;在复合载体中既有钛中心对称的八面体6配位TiO6的结构也有钛中心对称性差的四面体4配位TiO4或五面体5配位结构,并且随钛含量增加,钛的局域结构越来越接近锐钛矿型二氧化钛.根据XAFS、XRD、IR表征结果,提出了钛硅复合氧化物模型.     

负载型镍基非晶态催化剂催化氯代硝基苯加氢合成氯代苯胺

分别以碳纳米管(CNTs), SiO_2, TiO_2, γ-Al_2O_3, TiO_2-SiO_2和活性炭(AC)为载体(M),以Ni和B为活性组分,采用浸渍-化学还原法制备了一系列负载型Ni-B非晶态合金催化剂(Ni-B/M).采用电感耦合等离子体光谱(ICP), XRD, TEM和DSC研究了Ni-B/CNTs的非晶性质,Ni的担载量及其热稳定性.将Ni-B/M用于催化三种氯代硝基苯液相加氢合成氯代苯胺的反应.结果表明,Ni-B/M在反应中表现出较高的活性和良好的选择性,其中Ni-B/CNTs可使三种氯代硝基苯的转化率均高于99.8%,加氢脱氯率小于3%.讨论了CNTs和Ni-B之间的相互作用对催化剂性能的影响.     

Effect of TiO2 Nanoparticles on Photochromism of WO3 Colloids

IntroductionWO3has received considerable attention becauseof its photochromic and electrochromic properties[1—10].Since the photochromic process of WO3can be com-pletely reversible by exposing it to oxygen,it has beenconsidered to be one of the most prom…     

抗积炭CH_4/CO_2重整用Ni/Al_2O_3催化剂

甲烷转化制备的合成气是合成液体燃料和含氧有机化合物的原料 .甲烷转化制合成气的方法有甲烷蒸汽重整、甲烷部分氧化和甲烷、二氧化碳重整 3种 [1～ 3] .对于 CH4/CO2 重整反应 ,调节进料比可制备出 H2 /CO≤ 1、富含 CO的合成气 ,它适于羰基合成和 F- T合成 .这种方法一方面充分利用碳资源 ,缓解能源危机 ;一方面可减少温室气体的排放 ,改善人类的居住环境 .目前倍受关注 .CH4/CO2 重整制合成气 ,Rh、Ru、Pd、Ir等贵金属有很高的活性和稳定性 [4] .但其价格昂贵 ,高温易流失 ,商业化困难 .Ni基催化剂的活性与贵金属相当 ,但它易积…