碳纳米管膜的高温纯化研究

为了获得纯度更高的碳纳米管膜, 保证材料发热稳定性, 需要对通过化学气相沉积法得到的碳纳米管膜进行二次纯化. 通过使用高温纯化炉, 在真空状态下, 从1700℃到3200℃分7挡温度对碳纳米管进行纯化, 并对其含碳量和方块电阻进行比较. 结果表明, 高温纯化后的碳纳米管膜含碳量从95.0%提高到99.9%, 解决了含碳量低的问题. 同时, 在高温纯化中发现碳纳米管膜方块电阻从纯化前3Ω降低到0.5Ω, 方块电阻的降低对碳纳米管膜具有十分重要的意义, 同样对碳纳米管膜后续产品的开发也有重要作用.     

硅和锗纳米线的原子排布和电荷分布的密度泛函紧束缚方法研究

低维硅锗材料是制备纳米电子器件的重要候选材料，是研发高效率、低能耗和超高速新一代纳米电子器件的基础材料之一，有着潜在的应用价值。采用密度泛函紧束缚方法分别对厚度相同、宽度在0.272 nm~0.554 nm之间的硅纳米线和宽度在0.283 nm~0.567 nm之间的锗纳米线的原子排布和电荷分布进行了计算研究。硅、锗纳米线宽度的改变使原子排布，纳米线的原子间键长和键角发生明显改变。纳米线表层结构的改变对各层内的电荷分布产生重要影响。纳米线中各原子的电荷转移量与该原子在表层内的位置相关。纳米线的尺寸和表层内原子排列结构对体系的稳定性产生重要影响。     

Cu2O/TiO2-Bi2WO6三元复合催化剂的制备及光催化性能研究

采用水热法制备花状Bi2 WO6,并利用超声分散法制备了Cu2 O/TiO2-Bi2 WO6复合光催化剂,通过FESEM、XRD、XPS、FI-IR、UV-vis DRS和PL对光催化剂进行了分析和表征.表征结果证明:花状Bi2 WO6表面负载着碎片状的TiO2和立方体Cu2 O形成Cu2 O/TiO2-Bi2 WO6复合光催化剂;以短链脂肪酸(SCFAs)为牺牲剂,考察复合光催化剂的光催化产生氢气和烷烃的性能.实验结果表明:Cu2 O/TiO2-Bi2 WO6复合光催化剂以乙酸为牺牲剂,主要产氢气和甲烷,降解率高达91.82;;以丙酸为牺牲剂,产物主要是乙烷和丁烷,降解率高达90.70;;以丁酸为牺牲剂,除了氢气,甲烷,乙烷,丙烷,丁烷外,气体产物还含有一定量的戊烷,其降解率高达91.50;.结合反应液中间产物的成分进行检测,由此推断出光催化反应的可能机理.     

狄拉克材料BaMnBi2的单晶制备和物理性质研究

在本工作中,我们成功制备了层状过渡金属磷族化合物BaMnBi2单晶样品,并研究了该化合物的磁学性质和电学输运性质.准二维化合物BaMnBi2具有四方晶体结构,主要包含有两个Bi四方格子层和一个共边的MnBi4四面体层.磁化率显示BaMnBi2在TN ＝288 K以下发生反铁磁相变,并表现出很强的磁各向异性.在反铁磁相变温度TN 以上,磁化率随温度呈线性关系,暗示体系在顺磁态具有很强的反铁磁关联.电阻率随温度变化曲线和在磁场下电阻率随角度的变化曲线都表明BaMnBi2具有准二维的电子结构.磁场导致的金属-绝缘体转变和低温下大的非饱和线性磁阻,与Bi四方格子层存在狄拉克费米子是一致的.     

Surface passivation in n-type silicon and its application in silicon drift detector

Based on the surface passivation of n-type silicon in a silicon drift detector(SDD), we propose a new passivation structure of SiO2/Al2O3/SiO2 passivation stacks. Since the SiO2 formed by the nitric-acid-oxidation-of-silicon(NAOS)method has good compactness and simple process, the first layer film is formed by the NAOS method. The Al2O3 film is also introduced into the passivation stacks owing to exceptional advantages such as good interface characteristic and simple process. In addition, for requirements of thickness and deposition temperature, the third layer of the SiO2 film is deposited by plasma enhanced chemical vapor deposition(PECVD). The deposition of the SiO2 film by PECVD is a low-temperature process and has a high deposition rate, which causes little damage to the device and makes the SiO2 film very suitable for serving as the third passivation layer. The passivation approach of stacks can saturate dangling bonds at the interface between stacks and the silicon substrate, and provide positive charge to optimize the field passivation of the n-type substrate.The passivation method ultimately achieves a good combination of chemical and field passivations. Experimental results show that with the passivation structure of SiO2/Al2O3/SiO2, the final minority carrier lifetime reaches 5223 μs at injection of 5×10¹⁵ cm^-3. When it is applied to the passivation of SDD, the leakage current is reduced to the order of nA.     

金属与金刚石薄膜接触的电学特性研究

用热丝辅助化学汽相沉积技术在Si衬底上合成了含少量受主型杂质的近于本征的金刚石薄膜，并研究了三种金属（Cu，Ag和Al）与它接触的电学特性，以及退火对接触特性的影响．结果表明Cu，Ag与金刚石薄膜接触的电学特性比较类似，而Al则明显不同；而且退火对它们的接触特性影响很大 关键词：     

Ag+掺杂的立方相Y2O3:Eu纳米晶体粉末发光强度研究

采用化学自燃烧法制备了不同Ag⁺掺杂浓度的Y₂O₃:Eu纳米晶体粉末样品(［Y³⁺］∶［Eu³⁺］∶［Ag⁺］=99∶1∶X，X=0—3.5×10^-2)，以及通过退火处理得到了相应的体材料.根据X射线衍射谱确定所得纳米和体材料样品均为纯立方相.实验表明在纳米尺寸样品中随着Ag离子浓度的增加，荧光发射强度随之增加，当X=2×10^-2时达到最大值，其发光强度比X=0时提高了近50%.当Ag离子浓度继续增加，样品发光强度保持不变.在相应的体材料样品中则没有观察到此现象.通过对各样品的发射光谱，激发光谱，X射线衍射图谱，透射电镜(TEM)照片和荧光衰减曲线的研究，分析了引起纳米样品荧光强度变化的原因是由于Ag离子与表面悬键氧结合，从而使这一无辐射通道阻断，使发光中心Eu³⁺的量子效率提高；Ag⁺的引入所带来的另一个效应是使激发更为有效.这两方面原因使发光效率得到了提高.     

6066Al/SiCp复合材料内耗性能研究

用粉末冶金方法制备了6066Al合金和不同SiCp含量的6066Al/SiCp复合材料,用多功能内耗仪在200～600 K温度区间内测试了所研究材料在升温过程中的内耗变化趋势,探讨了6066 Al /SiCp复合材料在不同温度区间的内耗机制.结果表明6066Al/SiCp的内耗值比6066Al合金内耗值高,特别是在高温阶段比6066Al合金内耗值高得多;6066Al/SiCp和6066Al合金在300～470 K时的内耗主要是位错与第二相颗粒交互作用引起的位错内耗,在高温下内耗主要由Al/Al、Al/SiC的界面微滑移引起.