基于抛光基材的热蒸镀铜箔生长高平整单层石墨烯薄膜

在石墨烯的化学气相沉积工艺中,铜箔是决定石墨烯薄膜质量的重要因素。传统铜箔由于制备工艺的限制,存在大量的缺陷,导致石墨烯薄膜的成核密度较高。本工作选用抛光铝板、抛光不锈钢板、微晶玻璃和SiO₂/Si作为基材,用热蒸镀法制备了不同粗糙度的铜箔,并详细讨论了以该系列铜箔生长高平整度石墨烯薄膜的条件及铜箔对石墨烯薄膜品质的影响。实验结果表明,铜箔以(111)取向为主,与基材分离后,表面具有纳米级平整度。在生长石墨烯后,从SiO₂/Si剥离的铜箔成核密度是4种基材中最小的。同时,从SiO₂/Si剥离的铜箔晶体结构变化最不明显,具有良好的结晶性,表面几乎不存在铜晶界缺陷。当压强为3 000 Pa,氢气和甲烷流速分别为300 mL/min和0.5 mL/min时,可以获得约1 mm横向尺寸的石墨烯单晶晶畴。     

Can a Procedure for the Growth of Single-layer Graphene on Copper be used in Different Chemical Vapor Deposition Reactors?

In the last decade, catalytic chemical vapor deposition (CVD) has been intensively explored for the growth of single-layer graphene (SLG). Despite the scattering of guidelines and procedures, variables such as the surface texture/chemistry of catalyst metal foils, carbon feedstock, and growth process parameters have been well-scrutinized. Still, questions remain on how best to standardize the growth procedure. The possible correlation of procedures between different CVD setups is an example. Here, two thermal CVD reactors were explored to grow graphene on Cu foil. The design of these setups was entirely distinct, one being a “showerhead” cold-wall type, whereas the other represented the popular “tubular” hot-wall type. Upon standardizing the Cu foil surface, it was possible to develop a procedure for cm²-scale SLG growth that differed only by the carrier gas flow rate used in the two reactors.     

电解铜箔表面电沉积Zn-Ni-P-La合金工艺

为了缓解我国高性能铜箔依靠进口的局面,进行了将类金属(P)和稀土金属(La)引入电解铜箔锌镍合金镀层中以获得高耐腐蚀性铜箔的实验。 利用电子能谱(XPS)、X射线衍射(XRD)、扫描电子显微镜(SEM)等技术手段分析镀层质量。 在最佳工艺下获得非晶态Zn-Ni-P-La合金镀层,镀层表面平整均匀、结晶致密,未钝化的情况下,铜箔镀件在180 ℃烘箱中保持1 h不变色,表现出较理想的抗氧化和抗腐蚀能力。 表明镀层中适量的P和稀土La对改善镀层质量有着重要的作用,具有较好的工业应用前景。     

线-铝箔电极电晕放电激励器的推力理论与实验研究

空气电晕放电离子风激励器无需旋转部件, 仅通过消耗电能就能直接产生驱动力, 它是一种新型的动力技术, 备受国内外航空航天界的广泛关注. 目前对空气电晕放电离子风激励器的推力产生机理虽有各种解释, 但是现有理论均不能统一各种条件下的实验结果, 仍需要开展进一步的分析与研究. 本文以线-铝箔电极电晕放电激励器为研究对象, 通过实验研究发现作用在线电极与铝箔电极上的静电力不对称, 而且改变铝箔电极纵向高度和气压均能影响激励器的推力大小; 通过理论分析, 考虑电晕层与空间电荷的影响, 建立了线-铝箔电极电晕放电激励器的推力计算模型, 其计算值与实测值比较一致. 基于上述实验现象与理论建模分析, 本文认为线-铝箔电极电晕放电激励器的推力主要来源于线电极电晕产生的空间电荷对电极系统产生了不对称静电力作用, 使激励器出现净静电力作用.     

断裂过程区应力应变场的数学分析

本文将条状分离区看作是位错连续分布区域,利用复变函数理论及切比雪夫多项式级数展开提出了一种统一的数学分析的方法,用以对均匀材料裂纹前方分离过程区的非线性效应进行有效的,精确的解析分析。避免以前各种模型一般都需要借助于有限元法或其他离散方法才能得到数值解答的难点。本文利用这一新方法,对断裂过程区是内聚力模型,条状屈服区模型的裂纹问题,受约束金属薄膜的裂纹问题,进行了分析计算,并与已有的结果进行了比较,得到了满意的结果。     

碟形超声变幅杆的设计

优化超声变幅杆的形状结构可有效地提高水域声场分布和空化区域,提升对水域超声空化效果。通过模拟分析发现传统超声变幅杆在水域中具有声场分布均匀性差、变幅杆端部声压高等特征,不利于声波在水域中传播。基于此,提出并优化设计了一种具有碟形结构的变幅杆,位于变幅杆的最大振幅处的碟形结构,有更大的振动位移;模拟表明其水域声场和声压均衡度显著优于传统变幅杆,铝箔空化腐蚀实验进一步证实了其水域中的声压分布均匀性。同时,实验通过铝箔的空化腐蚀、KI剂量测定及工件表面油渍去除对比了传统变幅杆和碟形变幅杆,分析表明碟形变幅杆所在水域中有较大的空化腐蚀区域,腐蚀速率明显提升,声化学反应速率提高,油渍去除程度增强,说明了设计的碟形变幅杆能够促进空化泡的产生,增加水域空化区域。     

Electrospray ionization with aluminum foil: A versatile mass spectrometric technique

In this study, we developed a novel electrospray ionization (ESI) technique based on household aluminum foil (Al foil) and demonstated the desirable features and applications of this technique. Al foil can be readily cut and folded into desired configuration for effective ionization and for holding sample solution in bulk to allowing acquisition of durable ion signals. The present technique was demonstrated to be applicable in analysis of a wide variety of samples, ranging from pure chemical and biological compounds, e.g., organic compounds and proteins, to complex samples in liquid, semi-solid, and solid states, e.g., beverages, skincare cream, and herbal medicines. The inert, hydrophobic and impermeable surface of Al foil allows convenient and effective on-target extraction of solid samples and on-target sample clean-up, i.e., removal of salts and detergents from proteins and peptides, extending ESI device from usually only for sample loading and ionization to including sample processing. Moreover, Al foil is an excellent heat-conductor and highly heat-tolerant, permitting direct monitoring of thermal reactions, e.g., thermal denaturation of proteins. Overall, the present study showed that Al-foil ESI could be an economical and versatile method that allows a wide range of applications.     

A magnetised foil as inclined π-flipper for time-of-flight neutron beams

A prototype instrument with an inclined ferromagnetic foil was built which was capable of π-flipping over a broad wavelength range of polarised thermal neutrons in a time-of-flight beam. It was found that, for a single foil, polarised neutrons could be flipped in a wavelength range of 0.2-0.5 nm with an efficiency of 93%. With improved mechanical setup this range probably can even be extended to 0.1-1.0 nm. Foil flippers can have some major advantages for polychromatic SESANS over resonance flippers, but the technical realisation with four foils in series will be challenging.     

涂碳铝箔对磷酸铁锂电池性能影响研究

本文研究了使用涂碳铝箔作为正极集流体磷酸铁锂电池的性能。研究对比了使用普通铝箔和涂层铝箔的10 Ah软包磷酸铁锂电池的主要性能。研究表明:使用涂层铝箔不但可以提高磷酸铁锂材料的粘结性,而且使用导电涂层可以有效降低正极材料和集流体的接触内阻,从而减小电池内阻,提高电池倍率性能。与使用普通铝箔作为集流体相比,通过使用涂碳铝箔可以使得电池的内阻降低65%左右,但是,磷酸铁锂正极材料的克容量却偏低约5~10 mAh·g-1,首次效率也偏低4%左右;在快速放电15C倍率下,使用涂碳铝箔的电芯比使用普通铝箔容量提高约15%左右,10C放电倍率下,平台增加0.3~0.4 V;使用涂碳铝箔电芯的常温自放电率较高,但容量恢复率也较高;550周循环下,使用涂碳铝箔可以使得电池的循环性能提高约1%。而在电池低温性能方面,使用涂碳铝箔对低温性能并无改善。     

预嵌锂用穿孔集流体对锂离子电容器电化学性能的影响

将石墨涂覆于传统铜箔(CCC)与穿孔铜箔(PCC)集流体表面,通过内部短路的方式进行预嵌锂处理,再以商业化的活性炭及预锂化的石墨分别为正、负极材料组装成锂离子电容器(LIC)。以PCC为集流体的LIC在0.1和2.0 A?g~(-1)的电流密度下,能量密度分别为118.2和51.7 Wh?kg~(-1),并且在0.5 A?g~(-1)的电流密度下循环1000次后的能量密度保持率为90%;以CCC为集流体的LIC在0.1和2.0 A?g~(-1)的电流密度下的能量密度分别为125.5和43.3 Wh?kg~(-1),在同等电流密度下2.0-3.8 V之间循环1000次后的能量密度保持率仅为73.2%。进一步研究表明,石墨采用PCC在预嵌锂的过程中避免了金属锂沉积,生成了均一且稳定的固体电解质膜(SEI),有效防止充放电过程中SEI膨胀,活性物质与集流体间粘结力降低,活性物质脱落等现象发生。因此,LIC通过PCC完成预嵌锂后的自放电及内阻更小,具有更佳的倍率性能和循环性能。