PLA/EMAG共混物的制备与表征

通过熔融共混挤出法制备了不同乙烯-丙烯酸甲酯-甲基丙烯酸缩水甘油酯(EMAG)含量下的聚乳酸(PLA)/EMAG共混物,考察共混体系中EMAG与PLA基体之间的相互作用,研究了PLA/EMAG共混物的结晶性能、力学性能、熔体指数、加工性能以及热稳定性.表征结果显示:EMAG中的环氧基团与PLA的端羟基或端羧基发生化学反应,形成反应性共混体系,PLA/EMAG共混物的韧性较纯PLA有大幅提高,在EMAG含量为15;时达到最大.     

A comparative study of the structure and crystallization of bulk metallic amorphous rod Pr60Ni30Al10 and melt-spun metallic amorphous ribbon Al87Ni10Pr3

Pr-based bulk metallic amorphous （BMA） rods （Pr60Ni30Al10） and Al-based amorphous ribbons （Al87Ni10Pr3） have been prepared by using copper mould casting and single roller melt-spun techniques, respectively. Thermal parameters deduced from differential scanning calorimeter （DSC） indicate that the glass-forming ability （GFA） of Pr60Ni30Al10 BMA rod is far higher than that of Al87Ni10Pr3 ribbon. A comparative study about the differences in structure between the two kinds of glass-forming alloys, superheated viscosity and crystallization are also made. Compared with the amorphous alloy Al87Ni10Pr3, the BMA alloy Pr60Ni30Al10 shows high thermal stability and large viscosity, small diffusivity at the same superheated temperatures. The results of x-Ray diffraction （XRD） and transmission electron microscope （TEM） show the pronounced difference in structure between the two amorphous alloys. Together with crystallization results, the main structure compositions of the amorphous samples are confirmed. It seems that the higher the GFA, the more topological type clusters in the Pr-Ni-Al amorphous alloys, the GFAs of the present glass-forming alloys are closely related to their structures.     

高压结晶PET/PC共混体系中大尺寸聚合物伸直链晶体的形态观察

 大尺寸聚合物伸直链晶体在低维体系物理学的研究中具有不可替代的重要作用。但以往高压合成的聚合物伸直链晶体，尺寸较小且合成时间过长，使其作用至今未能显现。加入10%（质量分数）聚碳酸酯（PC）于聚对苯二甲酸乙二醇酯（PET）中，在研究PET/PC共混体系高压结晶行为的过程中快速合成了大量生长厚度超过100 μm 的聚合物伸直链晶体，并采用扫描电子显微镜对其进行了深入研究。研究表明，高压结晶PET/PC共混体系中存在不同类型的大尺寸伸直链晶体：完善的伸直链晶体、沿平行或垂直于C轴方向发生断裂的伸直链晶体、内聚能密度较大而发生内聚破裂的伸直链晶体、不同断裂方式下呈不同形态的楔形状伸直链晶体以及弯曲的伸直链晶体。同时对不同形态伸直链晶体的形成机理作了阐述。     

Raman properties embeddedof GaSb nanoparticlesin SiO2 films

The Raman shifts of nanocrystalline GaSb excited by an Ar^ ion laser at wavelengths 514.5, 496.5, 488.0, 476.5,and 457.9nm are studied by an SPEX-1403 laser Raman spectrometer respectively, and they are explained by phonon confinement, tensile stress, resonant Raman scattering and quantum size effects. The Stokes and anti-Stokes Raman spectra of GaSb nanocrystals strongly support the Raman feature of GaSb nanocrystals. The calculated optical spectra compare well with experimental data on Raman scattering GaSb nanocrystals.     

乌桕类可可脂结晶过程中表现体积变化

为了解乌桕类可可脂(CTCBE)缓冷结晶横向胀罐爆裂原因，研究CTCBE结晶过程中的膨胀特性，采用流体静力法测试了不同等温结晶条件下CTCBE结晶形成的表观密度和表观体积及其横纵向膨胀状况。结果表明，CTCBE缓冷结晶后形成外部和中部两个晶区。在5-25℃的各等温结晶范围内，当结晶温度增加时，外部结晶区域减小、表观密度变化不大；中部结晶区域增大、表观密度明显减小，CTCBE的表观体积、横向、纵向膨胀率均增大，膨胀横向大于纵向。进一步表明CTCBE在自然缓冷固化的表观体积根本上由其结晶温度决定。为有效防止横向胀罐，自然缓冷固化温度应低于10℃。     

激光限制结晶技术制备nc-Si/SiO2多层膜

在等离子体增强化学气相淀积系统中，采用aSi:H层淀积和原位等离子体氧化相结合的逐层生长技术制备了aSi:H/SiO_2多层膜.在激光诱导限制结晶原理基础上，使用KrF准分子脉冲激光为辐照源，对aSi:H/SiO_2多层膜进行辐照，使纳米级厚度的aSi:H子层晶化.Raman散射谱和电子衍射谱的结果表明，经过激光辐照后纳米Si颗粒在原始的aSi:H子层内形成，晶粒尺寸可以根据aSi:H层的厚度精确控制.还研究了样品的光致发光（PL）特性以及激光辐照能量密度对PL性质的影响. 关键词： 脉冲激光 多层膜 限制结晶     

磁控溅射技术制备ZnO透光薄膜

采用RF磁控溅射方法,在玻璃衬底上制备了择优取向的ZnO薄膜;通过台阶仪、X射线衍射技术、原子力显微镜和分光光度计分别测量了不同溅射功率条件下淀积的ZnO薄膜厚度(淀积速率)、结晶质量、表面形貌与粗糙度、透光光谱,报道了该薄膜结晶质量、薄膜粗糙度与其在可见光区透光率的关系.     

超声波作用下的制冷剂水合物结晶过程研究

首先分析了超声波对制冷剂水合物成核生长的影响机理,然后进行了实验研究。结果表明,超声波对水合物的结晶生长有明显的影响,阶梯形的超声探头作用下的成核引导时间比指数形锥体引导时间长,促进水合物生长的超声波功率P范闱是58W相似文献