Multi-cracks problem for piezoelectric materials strip subjected to dynamic loading

This paper analyses and models the dynamic interaction among permeable multi-cracks in a piezoelectric strip under anti-plane shear waves by the Schmidt method. The Fourier transform is applied and then two pairs of triple integral equations can be solved using the Schmidt method. The results show that the stress and the electric displacement intensity factors of cracks depend on not only the crack length and the piezoelectric coefficient, but also the thickness of the piezoelectric strip, the distance between multi-cracks and the frequency of incident wave.     

Tl2O3/聚-N-乙烯基咔唑复合纳米线的研究

Stable monolayers of electropolymerized poly-N-vinylcarbazole (EPVK) and arachidic acid(AA) are obtained on a subphase of alkaline Tl2O3 colloidal solutions. As revealed by the atomic force microscope, there is phase separation in the mixed LB monolayers. Transmission electron microscopic observations reveal that ordered arrays of composite Tl2O3/Epvk nanowires are formed in the mixed monolayers. Formation of the composite nanowire arrays is attributed to the ordered adsorption of Tl2O3 colloidal particles along the polycationic EPVK chains. The composite nanowire array is 3.2nm wide with a spacing of 2.7nm.The composite nanowire arrays can also be formed when pure EPVK is used. Composite LB multilayers of Tl2O3/EPVK nanowire arrays are prepared. The bilayer spacing is 5.54nm.The present study is of importance to the fabrication of inorganic semiconductor/functional polymer composite nanowires.     

邻-甲氧基苯酚和α-,β-环糊精包合现象的理论与实验研究

通过紫外可见光谱法考察了水溶液中邻-甲氧基苯酚(o-Mop)和α-与β-环糊精(CD)的分子间相互作用, 利用Hildebrand-Benesi方程给出了两个包合物的稳定常数(K_s). 采用半经验PM3方法研究了α-,β-CD和o-Mop及其类似物苯酚(Phe)、丁香酚(Eug)之间的包络作用, 阐述了这些主客体包合作用过程中体系能量随主客体相对位置改变而变化的细节, 据此推断出主-客体包合物可能的分子结构, 计算了包合物的稳定化能(ΔE_s). 研究结果表明, 本文所选主客体体系而言, 当客体和同一种主体分子作用时, 超分子包合物的ΔE_s随着客体分子苯环上取代基团数目的增多而增加. 基于PM3方法优化得到的主-客体包合物在真空中的分子结构和通过实验方法在水溶液中测定的结构一致.     

A Mild and Efficient Deprotection of Geminal Diacetates Catalyzed by FeCl3 ·6H2O in Ionic Liquid

The selective deprotection of geminal diacetates promoted by FeCl3·6H2O in the ionic liquid [bmim] [BF4] canbe efficiently achieved in good yields. The ionic liquid and the catalyst can be recycled easily and the process is car ried out under mild conditions.     

十二烷基硫酸钠水溶液的动态表面吸附性质

利用MPTC型气泡压力张仪研究了十二烷基硫酸钠(SDS)溶液在不同NaCl 浓度下的动态表面吸附性质, 分析了离子型表面活性剂在表面吸附层和胶束中形成双电层结构产生表面电荷对动态表面扩散过程和胶束性质的影响. 结果表明, SDS在表面吸附过程中, 表面电荷的存在会产生5.5 kJ·mol^-1的吸附势垒(E_a), 显著降低十二烷基硫酸根离子(DS^-)的有效扩散系数(D_eff). 十二烷基硫酸根离子的有效扩散系数与自扩散系数(D)的比值(D_eff/D)仅为0.013, 这表明SDS与非离子型表面活性剂不同, 在吸附初期为混合动力控制吸附机制. 加入NaCl可以降低吸附势垒. 当加入不小于80 mmol·L^-1 NaCl后, E_a小于0.3 kJ·mol^-1, D_eff/D在0.8-1.2之间, 表现出与非离子型表面活性剂相同的扩散控制吸附机制. 同时, 通过分析SDS胶束溶液的动态表面张力获得了表征胶束解体速度的常数(k₂). 发现随着NaCl 浓度的增大, k₂减小, 表明SDS胶束表面电荷的存在会增加十二烷基硫酸根离子间的排斥力, 促进胶束解体.     

涂碳铝箔对磷酸铁锂电池性能影响研究

本文研究了使用涂碳铝箔作为正极集流体磷酸铁锂电池的性能。研究对比了使用普通铝箔和涂层铝箔的10 Ah软包磷酸铁锂电池的主要性能。研究表明:使用涂层铝箔不但可以提高磷酸铁锂材料的粘结性,而且使用导电涂层可以有效降低正极材料和集流体的接触内阻,从而减小电池内阻,提高电池倍率性能。与使用普通铝箔作为集流体相比,通过使用涂碳铝箔可以使得电池的内阻降低65%左右,但是,磷酸铁锂正极材料的克容量却偏低约5~10 mAh·g-1,首次效率也偏低4%左右;在快速放电15C倍率下,使用涂碳铝箔的电芯比使用普通铝箔容量提高约15%左右,10C放电倍率下,平台增加0.3~0.4 V;使用涂碳铝箔电芯的常温自放电率较高,但容量恢复率也较高;550周循环下,使用涂碳铝箔可以使得电池的循环性能提高约1%。而在电池低温性能方面,使用涂碳铝箔对低温性能并无改善。     

ICP-AES测定Ni-Cr合金在人工唾液中析出的Ni离子

在模拟口腔环境下用人工唾液浸泡Ni-Cr桥,150h后采用ICP-AES测定Ni-Cr桥在人工唾液中的Ni离子析出量.镍在0.01-7.5μg/mL内有良好的线性关系,相关系数为0.9998;方法检出限为0.0059μg/mL;标准加入法测定镍的回收率为92.3%-99.8%.     

高压下LiF和NaF的结构稳定性及其电子和光学性质的第一性原理研究

基于密度泛函理论，采用全势线性缀加平面波加局域轨道方法，计算模拟了LiF高压下的相变行为，预测其在450GPa附近发生由NaCl结构(B1)到CsCl结构(B2)的结构相变.同时还计算了高压下LiF不同相的电学特性，LiF的复介电函数以及介电常数随压强变化关系.通过比较能带结构的变化行为，得出LiF在53GPa附近还存在等结构相变，即由直接带隙结构变为间接带隙结构.将LiF的计算结果与另外一个同构化合物NaF进行了比较讨论. 关键词： LiF 压致相变 从头计算     

原始数据中束流相关本底的分离

束流相关本底处理的不确定性是在BES/BEPC上进行R值测量的主要误差来源之一,提出从原始数据中分离出束流相关样本的新方法, 并把此样本用于调节强子产生器LUARLW的参数,以减小强子探测效率的系统误差, 提高R值的测量精度.     

R值测量中强子事例选择的改进

强子事例的选择和强子探测效率是在BEPC/BES上进行R值测量的两项主要误差来源. 过去实验只选取等于或者大于2叉的强子事例, 因而0叉和1叉事例的丢失将导致强子事例数和强子探测效率的较大误差. 试图提出在R值测量中选取包含1叉强子事例在内的样本, 这将有助于更合理地调节强子事例产生器LUARLW的参数, 减小强子探测效率和R值测量的系统误差.