铁路货车心盘材料的耐磨性研究

对比研究了货车心盘用ZG25MnNb钢、AAR-C级钢及经过表面强化处理的锻钢20Mn、锻钢Q345和铸钢ZG25的耐磨性能；采用金相显微镜分析了材料金相结构对其耐磨性能的影响。结果表明，对货车心盘用钢材进行表面强化能够显著改善其耐磨性能ZG25MnNb钢和经表面强化处理的锻钢20Mn的耐磨性较优；表面硬度高而组织细小的材料组成的摩擦副的耐磨性较好。     

（Ti,Al）N Film on Normalized T8 Carbon Tool Steel Prepared by Pulsed High Energy Density Plasma Technique

Under optimized operating parameters, a hard and wear resistant （Ti,Al）N film is prepared on a normalized T8 carbon tool steel substrate by using pulsed high energy density plasma technique. Microstructure and composition of the film are analysed by x-ray diffraction, x-ray photoelectron spectroscopy, Auger electron spectroscopy and scanning electron microscopy. Hardness profile and tribological properties of the film are tested with nano- indenter and ring-on-ring wear tester, respectively. The tested results show that the microstructure of the film is dense ahd uniform and is mainly composed of （Ti,Al）N and A1N hard phases. A wide transition interface exists between the film and the normalized T8 carbon tool steel substrate. Thickness of the film is about lO00nm and mean hardness value of the film is about 26 GPa. Under dry sliding wear test conditions, relative wear resistance of the （Ti, Al）N film is approximately 9 times higher than that of the hardened T8 carbon tool steel reference sample. Meanwhile, the （Ti,Al）N film has low and stable friction coefficient compared with the hardened T8 carbon tool steel reference sample.     

铁道车辆用新型减振材料的摩擦磨损行为研究

对铁道车辆摩擦减振系统所用斜楔和磨耗板新型材料进行了磨损试验研究,并分析了其摩擦磨损行为.结果表明,T10与ADI球铁、奥贝灰铸铁和高分子材料配副的耐磨性均优于45#钢与ADI球铁配副,磨耗板材料的相对耐磨性均优于斜楔,T10与高分子材料配副具有最佳的摩擦磨损性能.     

氧化锆口腔种植体的动态植入过程分析与设计

在牙科种植领域常使用的种植体材料多为纯钛或钛合金, 然而钛金属种植体存在美学缺陷及潜在的致敏可能等问题. 氧化锆陶瓷由于其高强度、美观性与生物相容性被认为是钛金属种植体的理想替代品, 但目前国内对于氧化锆种植体的研究仍处于起步阶段. 本文通过对氧化锆种植体及骨组织进行有限元建模, 并对种植体的动态植入过程进行仿真, 分析了骨组织内部的应力-应变状况. 结果发现, 随着植入深度的增加, 种植体与骨组织的接触面积增大, 松质骨内应力增加. 考虑到骨组织的具体结构, 将松质骨内的最大应力-应变作为分析的主要对象, 结合损伤分析, 对种植体模型进行了优化. 此外, 还设计了3种具有自攻刃设计的种植体模型, 分别进行应力应变分析后确定了最优设计. 之后建立了具有自攻刃设计的种植体模型, 并模拟了临床的3种植入方案: 螺纹成形、螺纹切割、螺纹成形与切割进行分析, 通过分析得到螺纹成形与切割种植方案更为安全的结论. 本文结果可以指导氧化锆种植体的结构设计以及植入时的条件设定等, 为我国自主研发的氧化锆种植体进行了理论指导, 为其早日进行临床应用指明了方向.      

ZnS:Mn摩擦发光特性的研究

本文报道了ZnS:Mn具有良好摩擦发光性能。研究了ZnS:Mn发光中心Mn^2 及其含量以及样品的灼烧温度、灼烧时间等条件对样品发光特性的影响。优化浓度配比和制备条件制备出了较高摩抢擦发光效率的ZnS:Mn摩擦发光材料。摩擦发光机理可能是由于机械能使ZnS:Mn的电子从基态激发到激发态所致,而具有较高的摩擦发光效率可能来源于ZnS:Mn具有较宽的激发能量范围。     

等离子熔敷Cr7C3金属陶瓷增强复合涂层组织与耐磨性研究

利用等离子熔敷技术,以Fe-Cr-C合金粉末为原料在正火态C级钢表面制备出Cr7C3金属陶瓷增强复合涂层,分析了复合涂层的显微组织结构,评价了复合涂层在室温干滑动磨损条件下的耐磨性.结果表明:等离子熔敷Cr7C3金属陶瓷增强复合涂层的组织均匀、与基材之间为完全冶金结合,涂层显微组织为规则块状Cr7C3金属陶瓷相均匀分布于Cr7C3与γ-Fe固溶体构成的共晶基体上,其硬度较高;涂层在室温干滑动磨损条件下表现出优异的耐磨性,复合涂层磨损质量损失随载荷增加变化缓慢.     

Microstructure and Properties of Cr3Si/γ-Fe Composite Coating Prepared by Plasma Transferred Arc Cladding Technique

Under optimized operating parameters, a wear and corrosion resistant Cr3 Si/γ-Fe composite coating is fabricated on a normalized 0.45% carbon steel substrate by using the plasma transferred arc （PTA） cladding technique with Fe-Cr-Si elemental powder blend as the precursor material. Mierostructure, microhardness, dry-sliding wear resistance and electrochemical corrosion characteristic of the coating are evaluated. Test results show that the composite coating is mainly composed of primary Cr3Si dendrites and the interdendritic supersaturated iron-base solid solution γ-Fe. Between the Cr3Si/γ-Fe composite coating and the normalized 0.45% carbon steel substrate, there is a narrow metallurgical bonding zone. The Cr3Si/γ-Fe composite coating exhibits high microhardness, excellent wear and corrosion resistance under test conditions.     

PVK掺杂稀土铕配合物的电致发光中的能量传递过程

将Michler‘s Ketone(MK)作为协同配体与一种β－双酮类稀土配合物Eu(fod)3的氯仿溶液混合，两者有效配合生成一种新的稀土配合物Eu(fod)3MK，它的吸收谱中有一Michler‘s Ketone和Eu(fod)3都不具有的新的吸收峰，吸收边在450nm附近。这一新的吸收峰与PVK的发射谱有很好的重叠，从而使能量可以有效地通过Forster能量转移方式由PVK传递给稀土配合物。将这种新的稀土配合物掺杂到导电聚合物PVK中，并以它们为发光层制成电致发光器件。结果表明：加入协同配体后的光致发光和电致发光中，PVK的发射均被有效抑制。这说明MK贩加入大大提高了由聚合的基质向稀土配合物进行能量传递的效率。     

脉冲高能量密度等离子体沉积(Ti,Al)N薄膜组织及其性能研究

利用脉冲高能量密度等离子体技术在室温条件下在45＃钢基材表面沉积了高硬度耐腐蚀(Ti, Al)N薄膜. 利用扫描电子显微镜、X射线衍射、X射线光电子能谱、俄歇电子能谱分析了薄膜的显微组织.利用纳米压痕仪测试了薄膜的纳米硬度.测试了薄膜在05mol/L H2SO4水溶液中的耐蚀性. 测试结果表明：薄膜主要组成相为(Ti, Al)N，同时含有少量的AlN,薄膜的纳米硬度高达26 GPa,薄膜具有良好的耐蚀性，与1Cr18Ni9Ti奥氏体不锈钢相比，耐蚀性提高了一个数量级. 关键词： 脉冲高能量密度等离子体 薄膜 纳米硬度 耐蚀性     

ZnO薄膜的制备和发光特性的研究

用射频磁控溅射的方法在石英衬底上沉积了氧化锌薄膜，在室温下测量了样品的XRD曲线、吸收光谱以及光致发光光谱。探讨了气氛中氧气与氩气比对制备薄膜的影响，从XRD谱中可以看出，样品具有较好的结晶状态。另外，样品在紫外有较强的吸收，而其光致发光也是较强的紫外发射，这表明带间跃迁占了主导地位，以上结果说明：用溅射方法制备的ZnO薄膜结晶质量较好，富锌状态有所改善。