High power-added-efficiency AlGaN/GaN HEMTs fabricated by atomic level controlled etching

An atomic-level controlled etching(ACE)technology is invstigated for the fabrication of recessed gate AlGaN/GaN high-electron-mobility transistors(HEMTs)with high power added efficiency.We compare the recessed gate HEMTs with conventional etching(CE)based chlorine,Cl₂-only ACE and BCl³/Cl₂ACE,respectively.The mixed radicals of BCl₃/Cl₂were used as the active reactants in the step of chemical modification.For ensuring precise and controllable etching depth and low etching damage,the kinetic energy of argon ions was accurately controlled.These argon ions were used precisely to remove the chemical modified surface atomic layer.Compared to the HEMTs with CE,the characteristics of devices fabricated by ACE are significantly improved,which benefits from significant reduction of etching damage.For BCl₃/Cl₂ACE recessed HEMTs,the load pull test at 17 GHz shows a high power added efficiency(PAE)of 59.8%with an output power density of 1.6 W/mm at Vd=10 V,and a peak PAE of 44.8%with an output power density of 3.2 W/mm at Vd=20 V in a continuous-wave mode.     

Improved device performance of recessed-gate AlGaN/GaN HEMTs by using in-situ N2O radical treatment

The N₂O radicals in-situ treatment on gate region has been employed to improve device performance of recessed-gate AlGaN/GaN high-electron-mobility transistors (HEMTs). The samples after gate recess etching were treated by N₂O radicals without physical bombardment. After in-situ treatment (IST) processing, the gate leakage currents decreased by more than one order of magnitude compared to the sample without IST. The fabricated HEMTs with the IST process show a low reverse gate current of 10^-9 A/mm, high on/off current ratio of 10⁸, and high f_T×L_g of 13.44 GHz· μm. A transmission electron microscope (TEM) imaging illustrates an oxide layer with a thickness of 1.8 nm exists at the AlGaN surface. X-ray photoelectron spectroscopy (XPS) measurement shows that the content of the Al-O and Ga-O bonds elevated after IST, indicating that the Al-N and Ga-N bonds on the AlGaN surface were broken and meanwhile the Al-O and Ga-O bonds formed. The oxide formed by a chemical reaction between radicals and the surface of the AlGaN barrier layer is responsible for improved device characteristics.     

Negative bias-induced threshold voltage instability and zener/interface trapping mechanism in GaN-based MIS-HEMTs

We investigate the instability of threshold voltage in D-mode MIS-HEMT with in-situ SiN as gate dielectric under different negative gate stresses.The complex non-monotonic evolution of threshold voltage under the negative stress and during the recovery process is induced by the combination effect of two mechanisms.The effect of trapping behavior of interface state at SiN/AlGaN interface and the effect of zener traps in AlGaN barrier layer on the threshold voltage instability are opposite to each other.The threshold voltage shifts negatively under the negative stress due to the detrapping of the electrons at SiN/AlGaN interface,and shifts positively due to zener trapping in AlGaN barrier layer.As the stress is removed,the threshold voltage shifts positively for the retrapping of interface states and negatively for the thermal detrapping in AlGaN.However,it is the trapping behavior in the AlGaN rather than the interface state that results in the change of transconductance in the D-mode MIS-HEMT.     

Schottky forward current transport mechanisms in AlGaN/GaN HEMTs over a wide temperature range

The behavior of Schottky contacts in AlGaN/GaN high electron mobility transistors(HEMTs) is investigated by temperature-dependent current–voltage(T –I–V) measurements from 300 K to 473 K. The ideality factor and barrier height determined based on the thermionic emission(TE) theory are found to be strong functions of temperature, while present a great deviation from the theoretical value, which can be expounded by the barrier height inhomogeneities. In order to determine the forward current transport mechanisms, the experimental data are analyzed using numerical fitting method,considering the temperature-dependent series resistance. It is observed that the current flow at room temperature can be attributed to the tunneling mechanism, while thermionic emission current gains a growing proportion with an increase in temperature. Finally, the effective barrier height is derived based on the extracted thermionic emission component, and an evaluation of the density of dislocations is made from the I–V characteristics, giving a value of 1.49 × 107cm-2.