High power-added-efficiency AlGaN/GaN HEMTs fabricated by atomic level controlled etching

An atomic-level controlled etching(ACE)technology is invstigated for the fabrication of recessed gate AlGaN/GaN high-electron-mobility transistors(HEMTs)with high power added efficiency.We compare the recessed gate HEMTs with conventional etching(CE)based chlorine,Cl₂-only ACE and BCl³/Cl₂ACE,respectively.The mixed radicals of BCl₃/Cl₂were used as the active reactants in the step of chemical modification.For ensuring precise and controllable etching depth and low etching damage,the kinetic energy of argon ions was accurately controlled.These argon ions were used precisely to remove the chemical modified surface atomic layer.Compared to the HEMTs with CE,the characteristics of devices fabricated by ACE are significantly improved,which benefits from significant reduction of etching damage.For BCl₃/Cl₂ACE recessed HEMTs,the load pull test at 17 GHz shows a high power added efficiency(PAE)of 59.8%with an output power density of 1.6 W/mm at Vd=10 V,and a peak PAE of 44.8%with an output power density of 3.2 W/mm at Vd=20 V in a continuous-wave mode.     

Improved device performance of recessed-gate AlGaN/GaN HEMTs by using in-situ N2O radical treatment

The N₂O radicals in-situ treatment on gate region has been employed to improve device performance of recessed-gate AlGaN/GaN high-electron-mobility transistors (HEMTs). The samples after gate recess etching were treated by N₂O radicals without physical bombardment. After in-situ treatment (IST) processing, the gate leakage currents decreased by more than one order of magnitude compared to the sample without IST. The fabricated HEMTs with the IST process show a low reverse gate current of 10^-9 A/mm, high on/off current ratio of 10⁸, and high f_T×L_g of 13.44 GHz· μm. A transmission electron microscope (TEM) imaging illustrates an oxide layer with a thickness of 1.8 nm exists at the AlGaN surface. X-ray photoelectron spectroscopy (XPS) measurement shows that the content of the Al-O and Ga-O bonds elevated after IST, indicating that the Al-N and Ga-N bonds on the AlGaN surface were broken and meanwhile the Al-O and Ga-O bonds formed. The oxide formed by a chemical reaction between radicals and the surface of the AlGaN barrier layer is responsible for improved device characteristics.