Fabrication of Zeolite A Rods with Irregular Macropores by Self-assembly of Zeolite A Microcrystals Using Microwave-assisted Hydrothermal Synthesis

Zeolite A rods by self-assembly of zeolite A microcrystal were successfully synthesized by microwave-assisted hydrotherrnal synthesis. The average size of zeolite crystals consisting of self-assembling materials was about 300 nm and the length of zeolite rods was in the range of 15--30μm.     

多齿胺膦钌配合物催化苯乙酮的氢转移氢化

利用Ｃ２－对称的双胺双膦钌（Ⅱ）配合物ＲｕＣｌ２（Ｐ２Ｎ２Ｈ４）为催化剂，研究了苯乙酮的氢转移还原反应。在苯乙酮、钌配合物和异丙氧基钾的摩尔比为２００：１：１２的条件下，于６５℃反应２ｈ后，苯乙酮的转化率高达９９％。讨论了苯乙酮的氢转移氢化机理。     

BaF2/La2O3催化剂上甲烷氧化偶联反应活性氧物种的原位红外光谱

用原位红外光谱研究了BaF2/La2O3催化剂上甲烷氧化偶联反应的活性氧物种.结果表明,催化剂经O2预吸附后,在1 108~1 118 cm-1处出现超氧物种O2-的O-O键伸缩振动峰.经18O2同位素交换实验后,原1 108~1 118 cm-1处谱峰的强度减弱,同时在1 086和1 051 cm-1处出现(O18O)-物种和18O2-物种的吸收峰.同位素交换实验进一步确证了1 108~1 118cm-1处谱峰确为O2-物种的吸收峰.在700℃下,O2-物种能够活化CH4生成C2H4,而且O2-物种的消耗量和C2H4的生成量呈很好的消长对应关系.超氧物种O2-是BaF2/La2O3催化剂上甲烷氧化偶联反应的活性氧物种.     

过渡金属配合物催化剂及其分子设计构思的发展与相互作用

讨论了某些不对称合成和α－烯烃定向配位聚合及α－烯烃氢甲酰化的过渡金属配合物向络合催化剂的发展与催化剂分子设计构思的发展及相互促进作用，并藉以说明过渡金属配合物定向络合物催化剂的分子设计已具备向计算机辅助设计发展的科学基础。     

双核钯配合物［Ph_2P（o－C_6H_4CO）PdCl］_2·2CH_2Cl_

合成了双氯桥双核钯配合物［Ｐｈ_２Ｐ（ｏ－Ｃ_６Ｈ_４ＣＯ）ＰｄＣｌ］_２·２ＣＨ_２Ｃｌ_２进行了元素分析、红外光谱表征和晶体结构测定，研究了其催化氢化性能。在３０～８０℃、氢分压１．０～５．０ＭＰａ的范围内。发现该配合物是催化氢化丙烯酸为丙酸的有效催化剂．晶体［Ｐｄ_２Ｃｌ_２（Ｃ_（１９）Ｈ_（１４）ＯＰ）_２］·２ＣＨ_２Ｃｌ_２属Ｐ１空间群，ａ＝０．９３０４（３）ｎｍ，ｂ＝１．０３９２（２）ｎｍ，ｃ＝１．１０６２（３）ｎｍ；ａ＝１０２．７８（２），Ｂ＝９７．３５（３），γ＝９５．２５（２），Ｖ＝１．０２６４ｎｍ~３，Ｍ＝１０３２．１７，２＝１，Ｄｃ＝１．６７０ｇ／ｃｍ~３，ｕ＝１３．６９５ｃｍ~（－１），Ｆ（０００）＝５１２，用１９４５个独立衍射精修结构，最终Ｒ＝０．０３６。     

氟化锶／氧化钕催化剂的甲烷氧化偶联性能及其吸附氧物种的原位FTIR光谱研究

氟化锶／氧化钕催化剂的甲烷氧化偶联性能及其吸附氧物种的原位ＦＴＩＲ光谱研究龙瑞强，万惠霖，赖华龙，蔡启瑞（厦门大学化学系固体表面物理化学国家重点实验室，厦门，３６１００５）关键词甲烷氧化偶联，氟化锶／氧化钕，吸附氧物种近年来，甲烷氧化偶联（ＯＣＭ）的...     

~1H MAS NMR characterization of hydrogen over silica-supported rhodium catalyst

Hydrogen species in both SiO2 and Rh/SiO2 catalysts pretreated in different atmospheres (H2, O2, helium or air) at different temperatures (773 or 973 K) were investigated by means of 1H MAS NMR. In SiO2 and O2-pretreated catalysts, a series of downfield signals at -7.0, 3.8-4.0, 2.0 and 1.5-1.0 were detected. The first two signals can be attributed to strongly adsorbed and physisorbed water and the others to terminal silanol (SiOH) and SiOH under the screening of oxygen vacancies in SiO2 lattice, respectively. Besides the above signals, both upfield signal at -110 and downfield signals at 3.0 and 0.0 were also detected in H2-pretreated catalyst, respectively. The upfield signal at -110 originated from the dissociative adsorption of H2 over rhodium and was found to consist of both the contributions of reversible and irreversible hydrogen. There also probably existed another dissociatively adsorbed hydrogen over rhodium, which was known to be p hydrogen and in a unique form of "delocalized hydrogen". It wa     

碱金属盐对ZSM-5分子筛晶化的影响

Effect of different alkali metal salts on the crystal size and the crystallization rate of ZSM-5 zeolite was de-tailedly investigated in this paper. The samples prepared by adding the different alkali metal salts were character-ized by using XRD， TEM， TG-DSC， BET and IR techniques. The XRD results showed that， for the nanosized ZSM-5 zeolite， the characteristic peaks broadened on the XRD patterns in comparison with the microsized ZSM-5 zeolite. The SEM results verified that the crystal size of zeolites prepared by adding different alkali metal salts had different results， and adding NaCl， NaC₂H₃O₂ and KCl showed the better effect of reducing crystal size， which are about of 40～60nm size. The crystallization curve of adding the different alkali metal salts suggested that the crystallization rate was significantly affected by the anions in the alkali metal salt besides the cations. Moreover， the crystal size likewise depended on the anion in the alkali metal salt. In addition， the BET results suggested that the nanosized ZSM-5 zeolite possessed a larger outer surface area in comparison with the microsized ZSM-5 zeolite. The thermostability of the samples was determined by TG-DSC technique， indicating that the nanosized ZSM-5 zeolite had a poor thermostability as compared with the microsized ZSM-5 zeolite. The possible difference of the samples with different crystal sizes on IR spectra was also given.     

介孔Co-Al2O3催化剂上甲烷部分氧化制合成气

采用一锅法制备了介孔Co-Al2O3催化剂,并首次用于甲烷部分氧化制合成气反应. 结果表明,与普通浸渍法相比,一锅法制备的Co-Al2O3催化剂表现出更为优异的催化性能. 合成的介孔Co-Al2O3催化剂具有大的比表面积和孔体积,以及规整有序的六方介孔孔道,Co物种高度分散,从而导致还原后高的金属分散度,而介孔孔道对金属纳米颗粒的约束作用可有效增强金属的抗烧结能力.     

水滑石负载钯催化剂上的醇无氧脱氢反应

 研究了多种载体负载 Pd 催化剂上苯甲醇无氧脱氢反应. 结果发现, 以兼具较强酸性和碱性的水滑石 (HT) 为载体时, Pd 催化剂具有优异的苯甲醇转化活性和苯甲醛选择性, 当 Pd 含量为 0.32%~0.55% 时催化性能最佳. Pd/HT 催化剂可重复使用, 且对于含推电子取代基的芳香醇、2-噻吩甲醇、α,β-不饱和醇与环状脂肪醇等的直接脱氢反应均具有较好催化性能. HT 表面的 Pd(II) 物种反应后转变为平均粒径为 2.0~2.5 nm 的 Pd 纳米粒子或纳米簇. 具有较高分散度的 Pd(II) 物种易转变为较小的 Pd 纳米粒子, 从而具有较佳的催化性能. 本文推测, 催化剂表面的碱性位可促进苯甲醇 O–H 键的活化, 形成 Pd-苯甲氧基中间体, 该中间体进一步脱氢生成苯甲醛和 Pd-H 物种; 而催化剂表面的质子酸位可与 Pd-H 作用, 促进 H2 的脱除.