12 W high power InGaAsP/AlGaInP 755 nm quantum well laser

High power laser diodes(LDs) with a lasing wavelength between 700 and 780 nm have great potential in various medical uses. Here, we report our recent efforts in developing an InGaAsP/AlGaInP-based commercial high power edge-emitting LD, which has 755 nm emission peak with a world-record continuous wave output power of 12.7 W, the highest reported so far. The lack of Al atoms in the active region significantly lowers the chance of catastrophic optical damage during high power laser operation. Meanwhile, with an accumulated 3800 h running time, our ongoing aging tests reveal excellent reliability of our devices.     

ZIF67衍生硫化钴/多孔碳复合催化剂的制备及其电催化性能

采用离子交换法与热处理相结合的方法,以ZIF67为前驱体,硫代乙酰胺为硫源,制备出硫化钴/多孔碳(CoS/C)复合催化材料,并探讨了硫化时间对复合催化剂的形貌、结构及其氧还原(ORR)性能的影响。采用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X射线衍射仪(XRD)、N2吸附-脱附测定仪、X射线光电子能谱分析(XPS)、拉曼光谱仪(Raman)和旋转圆盘电极(RDE)技术表征催化剂的物理特征和电催化性能。研究结果显示,在碱性条件下该复合催化剂具有与20%(w/w)的商业Pt/C催化剂相媲美的ORR活性,其半波电位仅比Pt/C催化剂低31 mV。随着硫化时间的增加,硫化钴颗粒逐渐增大,催化剂中碳材料的无序程度出现先减小后增大的趋势。在硫化时间为10 min时,复合催化剂在0.1 mol·L-1KOH中表现出良好的电催化活性,且在ORR过程中复合催化剂的平均转移电子数可达到3.72,接近于4,说明氧气在该催化剂表面发生的是四电子转移过程。     

高取代度羧甲基瓜尔胶溶液的微观结构及流变性能

利用环境扫描电子显微镜(ESEM)对粘度在5000mpa.s的高取代度羧甲基瓜尔胶及其降解产物的胶液微观结构进行了表征,并且与海藻酸钠胶液的微观结构相比,显示出不同程度的结构差异。这种结构差异导致其流变行为的差异。结果显示降解高取代度羧甲基瓜尔胶与海藻酸钠胶液的微观结构及流变性能接近,在物理性能和化学性能上较为符合活性染料印花糊料的要求。     

BiOBr/TiO_2异质结催化剂的制备及其可见光催化活性

将碱热法和溶剂热法相结合,制备了不同配比的BiOBr/TiO_2异质结催化剂,采用场发射扫描电子显微镜(FESEM)、透射电镜(TEM)、X射线衍射(XRD)、傅里叶变换红外光谱(FT-IR)、X射线光电子能谱分析(XPS)、紫外可见漫反射光谱(UV-Vis DRS)和光致发光光谱(PL)等技术对其结构、形貌和光学性能进行表征,并探讨BiOBr和TiO_2的配比对罗丹明B(RhB)脱色率的影响。结果显示,该异质结催化剂由锐钛矿相TiO_2纳米颗粒附着生长在BiOBr花状球表面构成;BiOBr和TiO_2摩尔比为1∶2的BiOBr/TiO_2催化剂在可见光照射下催化反应15min,RhB脱色率达96.5%;催化剂循环使用4次后,RhB脱色率仅降低7.94%,稳定性较好。Mott-Schottky曲线表明,该催化剂光催化活性的提升主要是由于在BiOBr和TiO_2界面上形成了p-n结,使电子-空穴对得到有效分离。光催化机理研究结果表明,O·-2是光催化反应过程中的主要活性物种,RhB的脱色主要是由于脱乙基和苯环开环氧化导致。     

基于可见光谱图的大豆外观品质判别方法

提出一种基于可见光谱图多模态词典特征低秩稀疏表示框架的大豆外观品质判别方法,以精确确定大豆品质等级。首先,提取大豆粒子可见光谱图像的多尺度空间梯度特征和色差分量(YCbCr)颜色空间特征;将上述提取的空间梯度特征和颜色空间特征看作视觉词汇,通过Kernel K-means聚类算法获取视觉词汇的核空间局部分布聚类中心,形成视觉词典;然后,使用低秩稀疏表示法耦合上述两种特征,用于消除高维异质模态词典描述符中冗余信息的影响;最后,在高维耦合空间中根据样本之间的度量对低秩稀疏耦合表示多模态词典特征进行分类。所提方法充分利用多模态多尺度空间梯度特征和YCbCr颜色空间特征来描述大豆粒子外观品质的语义特征归属。实验结果表明:建模集和预测集总的识别精度分别达92.7%和80.1%,所提方法的识别精度优于文献中提出的基于单一模态的视觉词典特征表示方法。     

High-Pressure Phase Transitions of Cubic Y_2O_3 under High Pressures by In-situ Synchrotron X-Ray Diffraction

High-pressure phase transitions of cubic Y_2O_3 are investigated using in situ synchrotron x-ray diffraction in a diamond anvil cell up to 36.3 GPa. The pressure-induced phase transitions of cubic Y_2O_3, which display apparent inconsistencies in previous studies, are verified to be from a cubic phase to a monoclinic phase and further to a hexagonal phase at 11.7 and 21.6 GPa, respectively. The hexagonal Y_2O_3 displays noticeable anisotropic compressibility due to its layered structure and it is stable up to the highest pressure in the present study. A third-order Birch–Murnaghan fit based on the observed pressure-volume data yields zero pressure bulk moduli of180(3), 196(7) and 177(7) GPa for cubic, monoclinic and hexagonal phases, respectively.     

Chryseobaterium s p. S 7溶藻过程光谱学特性及机理研究

藻类的大量繁殖对饮用水源、养殖业、旅游业以及人类健康造成了极大的影响。溶藻细菌作为一种生物控制手段,在控制藻类爆发方面显示出了极大的潜力。课题组前期分离获得一株金黄杆菌属溶藻菌Chryseobaterium sp.S7,研究发现该菌株具有明显的溶藻作用,作用方式为通过分泌溶藻物质进行间接溶藻,为进一步揭示该菌的溶藻特征及机理,以铜绿微囊藻为目标藻种,运用UV-Vis,EEMs,FTIR和FCM技术,分析Chryseobaterium sp.S7溶藻过程的光谱特性。实验结论如下：将菌株发酵液与藻液共培养7 d,利用UV-Vis和EEMs技术对藻细胞Chla含量与PC荧光值变化趋势进行分析,结果显示：藻细胞Chla含量在第1 d便开始下降,表明在短时间内,细菌胞外溶藻物质便可快速作用于藻细胞,第7 d时Chla去除率为59.37%。藻细胞PC荧光值也呈现下降趋势,与Chla变化趋势表现为一致性,表明在溶藻过程中伴有Chla和PC的减少。FTIR分析结果显示：藻细胞结构中的C=O, C-H,O-H键分别在1 647,2 927和3 475~3 437 cm-1处的吸收峰强度明显减弱,表明藻细胞内的多糖物质和蛋白质结构可能被破坏,处于2 500~1 700 cm-1范围的若干小吸收峰则进一步表明藻细胞解体的现象。分别在共培养第3 d和第7 d时对藻液进行PI特异染色,应用FCM对藻细胞PI特异性荧光和Chla,PC自发荧光特性进行分析,结果显示,在细菌S7的溶藻过程中,藻细胞PI特异性荧光逐渐增强,Chla、PC自发荧光呈下降趋势、表明藻细胞膜、Chla、PC三者破坏程度在溶藻过程中具有紧密的内在联系和较高的一致性。溶藻过程中藻细胞表现为多种形式的损伤,且损伤处于动态变化过程中,由Q1（Q5）区细胞按顺序逐步向Q4（Q8）区细胞移动。推测Chryseobaterium sp.S7可能的溶藻过程为：细菌将溶藻活性物质释放到细胞外,溶藻活性物质通过破坏铜绿微囊藻细胞膜中的多糖和蛋白质的结构,增加膜的通透性,进一步破坏胞体内的Chla,PC和DNA/RNA等物质,使藻体裂解死亡,最终形成细胞碎片。通过对Chryseobaterium sp.S7溶藻过程藻细胞的光谱学特性的分析,初步揭示了Chryseobaterium sp.S7的溶藻机理,为微生物控藻及修复技术提供了理论依据。     

硬X射线微束掠入射实验的控制和数据采集系统及其应用

在国内发展了硬X射线微束掠入射实验方法,并将此具有微米级高空间分辨率的方法应用于纳米厚度薄膜的微区分析。该实验方法对分析样品表面或薄膜在微小区域的不均匀组分、结构、厚度、粗糙度和表面元素化学价态等信息具有重要意义。基于X射线全反射原理,以微聚焦实验站的高通量、能量可调的单色微束X射线为基础,通过集成运动控制、光强探测、衍射和荧光探测,设计了掠入射实验方法的控制和数据采集系统。此系统采用分布式控制结构,并基于Experimental Physics and Industrial Control System （EPICS）环境设计SPEC控制软件。通过建立SPEC和EPICS的访问通道,实现SPEC软件对EPICS平台上设备的控制和数据获取。在所设计的控制和数据采集系统中,运动控制系统控制多维样品台电机的运动,实现定位样品位置和调节掠入射角;光强探测系统则监测样品出射光强度,通过样品台运动控制和光强探测的联控,实现样品台的扫描定位控制;通过衍射和荧光探测系统获取不同入射深度下样品的衍射峰强度和荧光计数。此外,为准确控制掠入射角角度,必须确定样品平面与X射线平行的零角度位置,对此给出一种自动定位零角度的方法,编写了该方法的控制算法,设计了相应的控制软件。零角度自动化定位的扫描结果表明,实验系统微区分析的空间分辨率达到2.8 μm,零角度定位精度小于±0.01°。利用该系统在上海光源微聚焦实验站首次实现了具有自动化准确控制零角度的微束掠入射X射线衍射和荧光同步表征的实验方法,实验中被测样品为10 nm Au/Cr/Si薄膜材料,Si基底最上层为10 nm厚的Au薄膜,其间为一层很薄的Cr粘附层。在不同掠入射角下测量样品的衍射信号,获取不同入射深度下样品的衍射峰强度,并实现在同一掠入射角下,同步采集样品的荧光计数信号,从而确定了样品表层的相结构信息以及荧光信号强度与入射角关系,实现了对纳米厚度薄膜在微小区域的相结构和组分分析。此外,通过该技术能够选取荧光计数最大值对应的入射角度,有助于提高后续发展的低浓度样品掠入射X射线吸收近边结构实验方法的信噪比。     

热声制冷机板叠内流动与换热的数值分析

本文采用基于压力修正算法的可压缩交变流动程序,采用适体坐标生成网格,AUSM 格式离散N-S方程和能量方程,计算了二维基本型热声制冷机板叠内的流动与换热情况,探讨了板叠附近的温度随时间的变化,分析了周期时均能量.由模拟结果可以看出,在气体冷端,能量由气体进入板叠,时均能量为正,在气体热端,能量由板叠进入气体,时均能量为负,板叠热端的时均能量稍大于板叠冷端的时均能量,板叠产生了冷量.但与输入功相比,板叠产生的冷量较小,因此系统的内能增加,气体冷端的温度增加.并且随着板叠的厚度的增加,板叠冷热端温差先增大后减小,并存在最佳板叠厚度使得冷热端的温差达到最大.