In situ synthesis of Ag-SiO2 Janus particles with epoxy functionality for textile applications

A facile method for the synthesis of silver-silica（Ag-SiO₂） Janus particles with functionalities suitable for textile applications is reported.Silica nanoparticles prepared by the Stober method were functionalized with epoxy,amine,and thiol groups,which were confirmed by Fourier transform infrared analysis.The functionalized silica nanoparticles were used to produce Pickering emulsions,and the exposed surface was used for the attachment of silver nanoparticles（AgNPs） via the low-temperature chemical reduction method.The morphology and structure of the Ag-SiO₂ Janus particles were characterized by scanning electron microscopy,scanning transmission electron microscopy,high-resolution transmission electron microscopy,energy-dispersive X-ray analysis,and UV-vis spectroscopy.Because of their specific functionalities,these Ag-SiO₂ Janus particles are proposed for applications on textile substrates,as they can overcome several drawbacks of direct application of AgNPs on textiles,such as leaching,agglomeration,and instability during storage.     

Methane dehydroaromatization with periodic CH4-H2 switch:A promising process for aromatics and hydrogen

Long-term stability test of Mo/HZSM-5-N catalysts(HZSM-5-N stands for nano-sized HZSM-5) in methane dehydroaromatization(MDA)reaction has been performed with periodic CH4-H2 switch at 1033-1073 K for more than 1000 h.During this test,methane conversion ranges from 13% to 16%,and mean yield to aromatics(i.e.benzene and naphthalene) exceeds 10%.N2-physisorption,XRD,NMR and TPO measurements were performed for the used Mo/HZSM-5 catalysts and coke deposition,and the results revealed that the periodic hydrogenation can effectively suppress coke deposition by removing the inert aromatic-type coke,thus ensuring Mo/HZSM-5 partly maintained its activity even in the presence of large amount of coke deposition.The effect of zeolite particle size on the catalytic activity was also explored,and the results showed that the nano-sized zeolite with low diffusion resistance performed better.It is recognized that the size effect was enhanced by reaction time,and it became more remarkable in a long-term MDA reaction even at a low space velocity.     

一类具有边界层性质的二次奇摄动边值问题

研究了一类具有边界层性质的二次奇摄动边值问题.在相对较弱的条件下,用合成展开法构造出该问题的形式近似式,并应用改进的Harten不动点定理和逆算子定理证明解的存在性及其渐近性质.最后,将所研究的问题和结论推广到更一般的高次情形.     

不同有机碱对铕-2-羟基喹啉-4-羧酸配合物发光性能的影响

分别在有机碱三乙胺、三丙胺和三丁胺的作用下,使用2-羟基喹啉-4-羧酸(H2hqc)与EuCl3·6H2O反应制备了3种配合物Eu(Hhqc)3(TEL)、Eu(Hhqc)3(TPL)和Eu(Hhqc)3(TBL)。通过元素分析、热重分析、摩尔电导率、紫外光谱、荧光光谱、荧光寿命和量子产率等对配合物进行了表征。所有配合物均在580,592,613,654,702 nm附近产生5条谱带,为Eu3+的特征发射,归属为5D0→7FJ(J=0,1,2,3,4)能级间的跃迁,荧光寿命分别为2.22,3.29,3.31 ms,量子产率分别为0.011,0.019,0.028。随着有机胺碳链长度的增加,配合物的荧光强度依次增大,表明有机碱参与了配合物的分子组成。     

Advances in high carbon dioxide separation performance of poly(ethylene oxide)-based membranes

Poly(ethylene-oxide)(PEO)-based membranes have attracted much attention recently for CO2 separation because CO2 is highly soluble into PEO and shows high selectivity over other gases such as CH4 and N2.Unfortunately,those membranes are not strong enough mechanically and highly crystalline,which hinders their broader applications for separation membranes.In this review discussions are made,as much in detail as possible,on the strategies to improve gas separation performance of PEO-based membranes.Some of techniques such as synthesis of graft copolymers that contain PEO,cross-linking of polymers and blending with long chains polymers contributed significantly to improvement of membrane.Incorporation of ionic liquids/nanoparticles has also been found effective.However,surface modification of nanoparticles has been done chemically or physically to enhance their compatibility with polymer matrix.As a result of all such efforts,an excellent performance,i.e.,CO2 permeability up to 200 Barrer,CO2/N2 selectivity up to 200 and CO2/CH4 selectivity up to 70,could be achieved.Another method is to introduce functional groups into PEO-based polymers which boosted CO2 permeability up to 200 Barrer with CO2/CH4 selectivity between 40 and 50.The CO2 permeability of PEO-based membranes increases,without much change in selectivity,when the length of ethylene oxide is increased.     

高压烧结制备Tb掺杂n型(Bi1–xTbx)2(Te0.9Se0.1)3合金及其微结构和热电性能

采用高压烧结技术制备了稀土元素Tb掺杂的n型Bi2Te2.7Se0.3基纳米晶块体热电材料.将高压烧结成型的样品于633 K真空退火36 h.研究了Tb掺杂量对样品的晶体结构和热电性能的影响.结果表明,高压烧结制备的样品为纳米结构, Tb掺杂使样品的晶胞体积变大,功率因子增大,热导率降低,从而使ZT值提高.Tb掺杂量为x=0.004是最优的掺杂量,该掺杂量的高压烧结样品经退火处理后,于373 K时ZT值达到最大为0.99,并且在323-473 K范围内, ZT值均大于0.8,这对用于温差发电领域具有重要意义.     

钴掺杂MoSe2共生长中氢气的作用分析及磁电特性研究

采用原位共生长化学气相沉积法,以Co3O4、MoO3、Se粉末为前驱物,710℃下在SiO2衬底上生长掺钴MoSe2纳米薄片,分析讨论氢气含量对其生长及调节机理的影响.表面形貌分析表明,氢气的引入促进了成核所需的氧硒金属化合物以及横向生长中需要的CoMoSe化合物分子的生成;AFM(Atomic Force Microscope)结果表明氢气有利于生长单层二维超薄掺钴MoSe2.随着Co3O4前驱物用量的增加,样品的拉曼和PL(Photoluminescence)谱图分别表现出红移和蓝移现象,带隙实现从1.52—1.57 eV的调制.XPS(X-ray photoelectron spectroscopy)结果分析得到Co的元素组分比为4.4%.通过SQUID-VSM(Superconducting QUantum Interference Device)和器件电学测试分析了样品的磁电特性,结果表明Co掺入后MoSe2由抗磁性变为软磁性;背栅FETs器件的阈值电压比纯MoSe2向正向偏移5 V且关态电流更低;为超薄二维材料磁电特性研究及应用拓展提供了基础探索.     

微氧化烧结制备掺杂Y2O3的SiC陶瓷及含镉模拟废水处理

采用了微氧化烧结制备了不同Y₂O₃质量分数（0%、2%、4%、6%）的多孔SiC陶瓷，通过对陶瓷的晶体结构、微观形貌、物理性能和Cd²⁺的去除率测试发现：添加了Y₂O₃的SiC陶瓷出现了较多的第二相Y₂SiO₇、Y₅Si₃C_0.5，随着Y₂O₃的质量分数增加逐渐升高，主相的衍射峰的强度有降低。扫描电子显微镜测试发现，SiC陶瓷的尺寸在2.5 μm，Y₂O₃引入后，SiC陶瓷的晶粒尺寸降低，高温烧结时液相的含量增加，熔体粘度降低，晶粒结合更加紧密，Y₂O₃的引入提高了多孔陶瓷的体积密度，Y₂O₃质量分数为6%SiC的体积密度最大为2.21 g/cm³。热导率随着Y₂O₃质量分数的增加呈现出先升高后降低的趋势。金属Cd²⁺的过滤测试表明：随着Y₂O₃质量分数增加，Cd²⁺的残留质量浓度、膜通量和去除率先降低后升高，当掺杂质量分数为4%时，Cd²⁺残留质量浓度最低为0.042 mg/L，膜通量达到了最大值572 L/（m²·h），去除率最大为99.95%，相比未掺质量分数杂体系的去除率提高了0.14%。随着溶液pH值的逐渐增大，金属Cd²⁺的残留质量浓度逐渐降低、去除率逐渐升高，pH≥9时最终均趋于稳定。综合来看，多孔SiC陶瓷的助烧剂Y₂O₃最佳掺量为4%。     

AgAlSe2晶体高压相变的第一性原理研究

基于密度泛函理论,采用广义梯度近似法,研究了黄铜矿结构AgAlSe₂在高压下的晶体结构、晶格动力学稳定性与电子结构.结果显示:在0 GPa时AgAlSe₂的晶格参数与实验值吻合,在13.9 GPa附近,质量密度、Se-Ag键长、Se-Al键长、晶格常数a突然增大,相对晶胞体积V/V₀、晶格常数c突然减小,声子谱出现虚频,结构变得不稳定,带隙发生突变,数值呈减小趋势.表明AgAlSe₂晶体在13.9 GPa附近发生结构相变.该研究为AgAlSe₂晶体在理论上所能承受的高压提供信息支撑.     

SiO2@Gd2O3∶Tb3+核壳微球的可控合成及发光性能研究

采用简便的尿素辅助沉淀法将Gd2O3∶Tb3+成功包覆在二氧化硅微球表面合成了尺寸均匀的球形SiO2@Gd2O3∶Tb3核壳发光材料,解决了稀土发光材料普遍存在的形貌可控性差和颗粒尺寸不均一等问题.利用XRD、SEM、红外光谱和荧光光谱等表征测试了样品的形貌、结构和发光性能.SEM照片和尺寸分布图显示,SiO2@Gd2O3∶Tb3+粒子呈现均匀球形形貌,分散性良好,粒径约(608 +18) nm.XRD图谱分析表明,600℃煅烧后,壳层Gd(OH)3CO3完全转变为立方相Gd2O3,结晶性良好,无杂相生成.同时,结合红外光谱推测了SiO2@Gd2O3∶Tb3核壳微球的形成机理,并得出Gd2O3∶Tb3+壳层主要以Si-O-Gd键形式连接在二氧化硅微球表面.在240 nm紫外光激发下,SiO2@Gd2O3∶Tb3核壳微球呈现绿光发射,其中,位于540 nm处的主峰归属于Tb3+的5D4→7F5能级跃迁.不同Tb3掺杂浓度下的发射光谱表明,当Tb3+掺杂浓度为4mol;时,SiO2@Gd2O3∶Tb3+核壳微球的发射强度达到最大值,寿命为1.55 ms,色坐标位于绿色区域,展现了良好的绿光发光性能.