La_2O_3和WSi_2增强MoSi_2基复合材料的摩擦磨损性能研究

选用MRH-5A型环-块摩擦磨损试验机测定了3种载荷和2种转速条件下La2O3和WSi2增强MoSi2基复合材料在滑动干摩擦时的摩擦磨损性能,采用扫描电子显微镜分析了复合材料磨损表面形貌.结果表明:La2O3和WSi2增强MoSi2基复合材料的抗磨性能优于MoSi2及WSi2/MoSi2材料;当载荷与速度乘积(pv)值小于183.04N·m/s时,La2O3和WSi2增强MoSi2基复合材料的磨损质量损失仅为相同条件下MoSi2的1/4～1/6和WSi2/MoSi2的1/2;这是由于La2O3和WSi2复合增强相存在硬化和韧化协同作用所致;随着pv值增加,La2O3和WSi2增强MoSi2基复合材料依次呈现犁削、粘着磨损和疲劳磨损特征.     

纳米碳管/铝基复合材料的制备及摩擦磨损性能研究

利用粉末冶金法制备纳米碳管/铝基复合材料,研究不同纳米碳管含量对复合材料硬度和稳态摩擦磨损行为的影响,采用扫描电子显微镜观察复合材料的磨损表面形貌,并对其磨损机制进行探讨.结果表明:随着纳米碳管质量分数的增加,复合材料的硬度呈现先增大而后减小的趋势,含质量分数为2%的纳米碳管复合材料硬度比铝增加约80%;复合材料的摩擦系数逐渐降低,磨损率先减小而后增大;含质量分数为1%的纳米碳管复合材料磨损机制为磨粒磨损和粘着磨损,而含质量分数为2%的纳米碳管复合材料以剥层磨损和疲劳磨损为主.     

Synthesis and characterization of magnetic polymer microspheres with a core-shell structure

Non-porous magnetic polymer microspheres with a core-shell structure were prepared by a novel micro-suspension polymerization technique. A stable iron oxide ferrofluid was used to supply the magnetic core, and the polymeric shell was made of glycidyl methacrylate （GMA monomer） and ethylene dimethacrylate （cross-linker）. In the preparation, polyvinyl alcohol was used as the stabilizer, and a lauryl alcohol mixture as the dispersant. The influence of various conditions such as aqueous phase volume, GMA and initiator amounts, reaction time and stirring speed on the character of the microspheres was investigated. The magnetic microspheres were then characterized briefly. The results indicate that the microspheres with active epoxy groups had a narrow size distribution range from 1 to 10 μm with a volume-weighted mean diameter of 4.5 μm. The saturation magnetization reached 19.9 emu/g with little coercivity and remanence.     

PREPARATION AND CHARACTERIZATION OF SUPERPARAMAGNETIC FUNCTIONAL POLYMERIC MICROPARTICLES

Superparamagnetic poly(styrene-divinylbenzene-glycidyl methacrylate) (Pst-DVB-GMA) microparticles were prepared via a modified suspension polymerization process. A magnetic fluid was first prepared by a chemical co-precipitation method. Then magnetic microparticles were produced by mixing the monomers and the magnetic fluid with water in the presence of a stabilizer poly(vinyl pyrrolidone) (PVP) to form a suspension, and finally benzoyl peroxide was added to initiate the co-polymerization. The morphology and magnetic properties of the microparticles were examined by TEM and VSM. The spherically shaped microparticles, with a size range of 4 to 7 pm, showed distinct superparamagnetic characteristics. XRD was used to investigate the structure of the magnetite particles dispersed in the polymer matrix. The microparticles with epoxy groups on their surface can be applied directly to the seoaration of biomolecules.     

Ti-6Al-4V微弧氧化陶瓷膜的微观结构及摩擦磨损性能研究

在NaAlO2和Na3PO4混合电解液中,利用微弧氧化技术在Ti-6Al-4V表面制备了氧化物陶瓷膜.用扫描电子显微镜、X射线衍射仪及显微硬度仪分别对微弧氧化膜的微观结构、相组成及其断面硬度进行分析,并对氧化膜致密层的摩擦磨损性能进行研究.结果表明:氧化膜表面呈现出多孔结构,氧化膜疏松层与致密层无明显界限,氧化膜与基底以犬牙交错形式结合;氧化膜主要由TiAl2O5和TiO2相组成,还含有少量AlPO4相和Al2O3相,氧化膜疏松层中TiAl2O5相的含量明显高于致密层;氧化膜内距Ti-6Al-4V基底约21 μm处的硬度存在最大值,两侧硬度降低;微弧氧化膜与Si3N4球对摩时具有较高的摩擦系数,磨损率比Ti-6Al-4V降低2个数量级,说明氧化膜致密层具有良好的耐磨性能,其磨损机制为微区脆性断裂.     

几种酰胺类化合物作为添加剂对钢—钢和钢—铝摩擦副摩擦学性能的影响

采用四球摩擦磨损试验机和SRV摩擦磨损试验机考察了 4种酰胺化合物对钢 -钢和钢 -铝摩擦副摩擦磨损性能的影响 ,用X射线光电子能谱 (XPS)分析了丙烯酰胺润滑下铝合金磨斑表面元素的化学状态 .结果表明 :对钢 -钢摩擦副 ,酰胺类化合物表现出一定的抗磨减摩作用 ,对钢 -铝摩擦副 ,丙烯酰胺和乙酰胺表现出良好的抗磨减摩性能 .XPS分析结果显示 ,铝合金磨斑表面存在 3种价态的氮的化合物及 2种价态的铝 ,表明其磨损表面生成了复杂的反应膜     

有限元网格自动生成及自动调整技术

本文给出了一种任意平面域内三角形网格自动生成及自动调整算法，并编制了相应的程序。通过对带Ｕ形槽的三点变曲试件的分析，证明本文算法是可行的，并且具有稳定性能好、收敛速度快的优点。     

混合型裂纹的一个新的启裂准则

本文利用两个基本假设，给出了混合型裂纹的启裂准则。与实验结果的比较证明用本准则分析混合型裂纹问题是有效的。     

聚四氟乙烯对齿轮润滑成膜膏润滑性能的影响

作者以聚四氟乙烯(PTFE)为固体润滑剂填料对GM型齿轮润滑成膜膏进行了改进,并且研制出了两种新的成膜膏系列产品。经四球试验机、动静摩擦系数精密测定仪和SRV试验机评价的结果表明,添加PTFE的GM-2型成膜膏的承载能力和减磨性能都明显地比未添加的好;以PTFE为主要固体润滑剂填料的GM-3和MFC-1型两种润滑成膜膏也都具有良好的润滑性能,其中后者的性能与含PTFE的GM-2型成膜膏的接近。通过对摩擦轨迹的电子探针检测发现,PTFE在摩擦过程中于摩擦表面形成了转移膜,因而改善了润滑成膜膏的摩擦学性能。     

石墨对铜基自润滑材料高温摩擦磨损性能的影响

通过基体多元合金化和选用不同粒度的石墨颗粒,采用常规粉末冶金方法制备了铜基石墨固体自润滑材料,在大越式OAT-U型摩擦磨损试验机上考察了复合材料从室温到500℃温度条件下的摩擦磨损性能,利用扫描电子显微镜观察分析磨损表面形貌,进而探讨其摩擦磨损机理.结果表明:在室温条件下,石墨颗粒越小,则复合材料的摩擦系数越小,减摩自润滑效果越好;在室温至500℃条件下,选用合适的石墨粒度(0.3～0.5mm)和多元基体合金化,可使铜基石墨固体自润滑材料保持较好的自润滑特性.