Structural disorder in Ba0.6Sr0.4Al2O4

The structural disorder in Ba_0.6Sr_0.4Al₂O₄ (space group P6₃22) was investigated by X-ray powder diffraction and selected-area electron diffraction (SAED). The initial structural model was determined using direct methods, and it was further modified by the combined use of Rietveld method and maximum-entropy method (MEM). MEM-based pattern fitting method was subsequently applied, resulting in the final reliability indices of R_wp=9.61%, R_p=6.96%, R_B=1.40% and S=1.25. The electron density distribution was satisfactorily expressed by the split-atom model in which the strontium/barium and oxygen atoms were split to occupy the lower symmetry sites. The diffuse scattering in SAED was mainly attributable to the positional disorder of oxygen atoms.     

Selective Transport of Lead(II) and Strontium(II) Through a Crown Ether-Based Polymer Inclusion Membrane Containing Dialkylnaphthalenesulfonic Acid

New polymer inclusion membranes (PIMs) containing 18-membered crownethers and dialkylnaphthalenesulfonic acid are proposed for Sr2+ and Pb2+removal from nitric acid solutions. The influence of source phasecomposition and stripping agents was characterized and permeabilitycoefficients were calculated. The PIMs are easy to prepare and may be usefulin separation and concentration procedures for these cations from complexmixtures such as nuclear waste. Long-term stability was obtained for atleast several weeks of constant use during which no significant change ofpermeability was observed.     

Reaction Mechanisms of Strontium Ferrites Synthesis

The reactions between strontium and iron nitrates have been studied in an open atmosphere system using three different molar ratios, 1:1 (I), 1:2 (II) and 2:1 (III) at different temperatures as pointed out from the DTA data. The reaction mechanism was discussed based on the chemical composition characterized by means of thermal analysis, X‐ray diffraction patterns, infrared spectra and magnetic susceptibility. It was found that the reaction products depend on both temperature of reaction and the ratio between reactants. The reaction products were found to be composed of a variety of iron compounds that possess different valences: SrFeO_2.86, SrFeO_2.97, SrFe₂O₄, SrFe₁₂O₁₉, Sr₂Fe₂O₅ and Sr₇Fe₁₀O₂₂ in addition to some accessory reaction products namely α‐Fe₂O₃ and FeO(OH).     

Crystallisation of Ba1-xSrxZn2Si2O7 from BaO/SrO/ZnO/SiO2 glass with different ZrO2 and TiO2 concentrations

The effect of different nucleation agents such as ZrO₂ and TiO₂ was investigated for a first time with respect to their crystallisation behaviour in the glass system BaO-SrO-ZnO-SiO₂. In all studied glasses, a Ba_1-xSr_xZn₂Si₂O₇ (0.1 ≤ x ≤ 0.9) solid solution crystallized. This phase was first described in 2015 to possess a similar structure as the high temperature phase of BaZn₂Si₂O₇ and a thermal expansion close to zero or even negative. It may find applications e.g. as cook panels, telescope mirrors, and furnace windows. Kinetic parameters of the crystallisation process were determined by supplying different heating rates in a differential scanning calorimeter (DSC). The results were evaluated using the equations of Ozawa and Kissinger with respect to the activation energies. Furthermore, the Ozawa method was used for the determination of Avrami parameters, which provides further information on the nucleation and crystallisation processes. Scanning electron microscopy including electron backscatter diffraction (EBSD) was used to characterise the microstructure, to determine the crystallite size and the crystal orientation. For the characterisation of the occurring crystalline phases, X-ray diffraction was used.     

甲烷氧化偶联纳米SrTiO3催化剂的原位ESR和TPSR表征

采用溶胶-凝胶法制备了纳米钙钛矿型复合氧化物SrTiO3催化剂,并用X射线粉末衍射、透射电子显微镜、原位电子自旋共振和程序升温表面反应等技术对催化剂进行了表征,测定了催化剂对甲烷氧化偶联(OCM)反应的催化性能.结果表明,与相同组成的常规SrTiO3催化剂相比,纳米SrTiO3催化剂具有较好的低温(～650℃)催化性能.通过增大Sr/Ti比可进一步优化纳米SrTiO3的催化性能.纳米SrTiO3催化剂表面的吸附氧物种和F中心均具有活化及催化甲烷分子生成C2烃产物的活性,但吸附氧物种易使OCM反应中间体和产物深度氧化,而F中心具有低温活化甲烷分子及高选择性生成C2烃产物的特性.纳米氧化物粒子因表面原子配位不饱和(配位数低),其表面存在较多的F中心。     

Crystal structure of a highly hydrated tristrontium phosphate,Sr9(PO4)6·16H2O

The crystal structure of a highly hydrated tristrontium phosphate, nonastrontium hexakis(phosphate) hexadecahydrate, Sr₉(PO₄)₆·16H₂O, has been determined by single crystal X-ray diffraction. The crystals are monoclinic,a=15.203(2),b=6.488(1),c=18.984(7) Å, =98.42(2)^o, space groupP2/c (No. 13),Z=2,V=1852.3 ų,d _c =2.951 Mg·m^–3. The structure was refined by full-matrix least-squares techniques toR=0.038,R _w =0.051, for 2329 reflections with I3(I). The structure can be described in terms of a layer-type arrangement parallel to (100). One layer consists of a compact assembly of columns of Sr and PO₄ ions in a pseudohexagonal arrangement resembling an apatitic structure. A second layer containing all the water molecules and one PO₄ ion that occupies the interstitial space may be referred to as the hydrated layer. The structure has an overall similarity to that of octacalcium phosphate and can be considered as a model for amorphous calcium phosphate.Certain commercial materials and equipment are identified in this paper to specify the experimental procedure. In no instance does such identification imply recommendation or endorsement by the National Institute of Standards and Technology or the ADA Health Foundation or that the material or equipment identified is necessarily the best available for the purpose.     

A new high‐pressure strontium germanate,SrGe2O5

The Sr–Ge–O system has an earth‐scientific importance as a potentially good low‐pressure analog of the Ca–Si–O system, one of the major components in the constituent minerals of the Earth's crust and mantle. However, it is one of the germanate systems that has not yet been fully examined in the phase relations and structural properties. The recent findings that the SrGeO₃ high‐pressure perovskite phase is the first Ge‐based transparent electronic conductor make the Sr–Ge–O system interesting in the field of materials science. In the present study, we have revealed the existence of a new high‐pressure strontium germanate, SrGe₂O₅. Single crystals of this compound crystallized as a co‐existent phase with SrGeO₃ perovskite single crystals in the sample recovered in the compression experiment of SrGeO₃ pseudowollastonite conducted at 6 GPa and 1223 K. The crystal structure consists of germanium–oxygen framework layers stacked along [001], with Sr atoms located at the 12‐coordinated cuboctahedral site; the layers are formed by the corner linkages between GeO₆ octahedra and between GeO₆ octahedra and GeO₄ tetrahedra. The present SrGe₂O₅ is thus isostructural with the high‐pressure phases of SrSi₂O₅ and BaGe₂O₅. Comparison of these three compounds leads to the conclusion that the structural responses of the GeO₆ and GeO₄ polyhedra to cation substitution at the Sr site are much less than that of the SrO₁₂ cuboctahedron to cation substitution at the Ge sites. Such a difference in the structural response is closely related to the bonding nature.     

nFe3+/nSr2+和nOH-/nNO3-对锶铁氧体纳米片结构及磁性能的影响

采用改进的水热法成功合成了单分散的纯相锶铁氧体纳米片。借助DLS、XRD、FTIR、SEM、EDS和VSM等分析测试手段对SrFe₁₂O₁₉铁氧体粉体的粒度、结构、形貌和磁性能进行表征。研究结果表明,在240℃保温5 h,物质的量之比n_Fe³⁺/n_Sr²⁺(R_F/S)和n_OH^-/n_NO3^-(R_O/N)分别为5和2时,所得产物为单分散的纯相六角SrFe₁₂O₁₉铁氧体纳米片。随着R_F/S和R_O/N的变化,合成样品中有少量SrCO₃和Fe₂O₃杂相存在,这主要与反应条件和离子比例有关。磁性能测试结果显示,所得纯相的六角SrF₁₂O₁₉铁氧体纳米片具有优异的磁性能,其饱和磁化强度和矫顽力分别达到60.91 emu·g^-1和94.83 kA·m^-1,使其在医疗、催化和生物等高技术领域具有潜在的应用。     

Eu,Dy共掺杂SrAl2O4长余辉材料制备新工艺

活化Al-Sr合金粉末水解制备SrAl₂O₄长余辉材料的前驱体,并采用高温固相反应法制备出Eu,Dy共掺杂的SrAl₂O₄长余辉材料,对其微观结构和发光特性进行了研究。实验结果表明:前驱体中Al、Sr元素在微观状态下分布均匀,所制成的长余辉发光材料的发射主峰位于520nm附近,为典型的Eu²⁺离子4f5d-4f的特征发射,初始亮度达到18cd/m²,余辉时间长达46h。     

Cerium effect on the phase structure, phase stability and redox properties of Ce-doped strontium ferrates

Nanostructured perovskite-type Sr_1−aCe_aFeO_3−x, (0?a<0.15) powders have been prepared by citrate-nitrate smoldering auto-combustion. Their phase structure and stability, surface and morphological properties, reduction behavior and interaction with oxygen have been investigated by X-ray Powder Diffraction combined with Rietveld Analysis, ⁵⁷Fe Mössbauer and X-ray Photoelectron Spectroscopies, N₂-adsorption method, Temperature Programmed Reduction and Oxidation experiments. Our results reveal that citrate-nitrate auto-combustion method is effective in obtaining single phase Sr_1−aCe_aFeO_3−x. The Sr_1−aCe_aFeO_3−x structure is cubic only for a?0.06, while for a<0.06 remains tetragonal. Moreover, for a?0.06 after semi-reductive treatment under inert gas, an expanded cubic phase is obtained instead of the brownmillerite-type structure, which is known to have ordered vacancies. Stabilization of octahedral Fe³⁺ by cerium doping appears to be the main factor in determining the structural properties of Sr_1−aCe_aFeO_3−x. The highest oxygen consumption for Ce-doped SrFeO₃ occurs for a=0.06. Preliminary impedance measurements show that Sr_0.94Ce_0.06FeO_3−x has the lowest area-specific resistance.