1-4丁炔二醇和乙二胺对离子液体电沉积Cu的影响

研究了1-4丁炔二醇和乙二胺作为添加剂对在离子液体1-甲基-3-甲基咪唑三氟甲磺酸盐中电沉积Cu的影响。紫外可见光吸收光谱结果表明,当采用1-4丁炔二醇作为添加剂时,1-4丁炔二醇吸附在工作电极表面且未与溶液中的Cu²⁺形成配合物。扫描电镜测试结果表明由于1-4丁炔二醇与离子液体的正离子的竞争吸附使得Cu的沉积电势发生正移并使镀层表面更加均匀平整。当采用乙二胺作为添加剂时,紫外可见光吸收光谱和循环伏安测试结果表明乙二胺与溶液中的Cu²⁺离子形成带有正电荷的络合离子使得Cu的沉积电势发生正移,扫描电镜和原子力显微镜测试结果表明得到了更加均匀的镀层。当同时加入1-4丁炔二醇和乙二胺时,Cu的沉积电势仍然发生正移并得到具有纳米粒径的镀层。     

Co3O4纳米片的制备及对H2O2电还原反应的催化性能简

通过恒电势电沉积和加热处理在泡沫镍基体上制备了Co3O4纳米片. 利用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X射线衍射(XRD)、傅里叶变换红外光谱(FTIR)和X射线光电子能谱(XPS)等手段对纳米片的形貌和结构进行了表征. 采用线性伏安扫描和计时电流技术研究了Co3O4纳米片电极对H2O2的电还原性能. 结果表明,在3.0 mol/L KOH 和 0.4 mol/L H2O2溶液中,当电压为-0.4 V(vs. Ag/AgCl)时,线性伏安扫描电流密度达到-0.386 A/cm2,在1000 s 测试时间内,计时电流密度衰减很小,表明Co3O4纳米片电极对H2O2具有很高的活性和稳定性.     

铂修饰的{001}面暴露的二氧化钛纳米片阵列的制备和光催化性能

采用有机溶剂热法在FTO衬底上制备{001}面暴露的单晶锐钛矿相TiO2纳米片阵列,通过FESEM和XRD研究样品的形貌和晶体结构. 与水热法制备的纳米片阵列相比,有机溶剂热法制备的样品取向性更好. 采用光沉积方法在纳米片阵列上沉积Pt,所得到的Pt纳米颗粒粒径更为均匀,并且更容易沉积在{001}面上. 所负载的Pt 纳米颗粒增强了TiO2纳米片的光吸收性能,同时大大减弱了光致发光强度. 在光催化性能测试中,具有最优负载量的样品催化性能提高了一倍. 与传统的Pt负载相比,{001}面的最优负载量显得相当小,这可能源于高活性{001}面的原子结构.     

碳纳米管透明导电薄膜的可控制备

碳纳米管具有优秀的导电性能、 透光性能和十分突出的柔性, 在柔性透明导电薄膜中有着良好的应用前景. 如何制备同时拥有良好导电性能和透光性能的碳纳米管薄膜是这一领域研究的核心问题. 本综述介绍了碳纳米管薄膜的制备方法, 并重点讨论了基于漂浮催化剂化学气相沉积法的碳纳米管薄膜的可控制备. 在生长过程中限制碳纳米管的团聚、 增加碳纳米管的长度、 降低杂质的含量是提高碳纳米管薄膜性能的主要策略.     

反式钙钛矿电池超薄空穴传输层研究进展

空穴传输层(HTLs)厚度对反式钙钛矿太阳能电池(PSCs)性能具有重大影响,因其显著影响太阳光透过和HTLs的空穴传输性能。几个纳米至十几个纳米厚度的超薄HTLs在减少伴生吸收、电荷传输损失和材料消耗等方面具有明显优势。目前,有许多成熟的制备超薄无机HTLs的方法,并在反式和叠层PSCs中得到广泛研究与应用。最近,一些关于有机超薄HTLs的新型制备方法也展现出良好的性能并逐渐引起相关领域研究者关注。在此,本文主要总结反式PSCs中超薄HTLs的研究进展与应用,关注其未来发展的挑战和方向,为该领域进一步的研究提供参考。     

石墨烯玻璃透明薄膜加热特性

Graphene has become a research focus in recent years owing to its excellent characteristics, and glass is a commonly used material with high transparency and low cost. Graphene glass combines the excellent properties of both graphene and glass; graphene glass has not only high thermal conductivity, high electrical conductivity, and good surface hydrophobicity but also exhibits superior electrothermal conversion and wide-spectrum high-light-transmittance characteristics. Therefore, the study of graphene glass films is of theoretical value and practical significance. In this study, a high-purity glass-based (JGS1 quartz glass) multilayer graphene film was developed based on an atmospheric-pressure chemical vapor deposition (APCVD) method, and its electrical characteristics, light transmittance, and electrical heating characteristics were experimentally investigated in detail. The results show that graphene glass with different surface resistance values obtained through direct growth on a high-purity quartz glass substrate using the APCVD method, not only has excellent uniformity and quality, but also has considerably flat and high transmittance across the entire visible light region and exhibits excellent heating performance and fast response time. For graphene glass with a surface resistance of 1500 Ω·sq^-1, the light transmittance can reach 74%, and the saturation temperature can rise to 185 ℃ by applying a bias voltage of 40 V. In addition, when the resistance value of the graphene glass is 420 Ω·sq^-1, the graphene glass reaches a high saturation temperature of 325 ℃ in 40 s, and the corresponding heating rate can exceed 18 ℃·s^-1, achieving a significantly higher heating rate than other heating films at the same voltage. Compared with the polyethylene-terephthalate- (PET-) based and silicon-based graphene films obtained by the transfer, graphene glass has a higher saturation temperature, shorter thermal response time, and faster heating rate. Furthermore, graphene glass exhibits better heating cycle stability and longer-term heating stability at a constant voltage. In addition, an experiment using the graphene glass to thermally tune the wavelength of a vertical-cavity surface-emitting laser was conducted and gave good results. The position of the laser peak controlled by the graphene glass was red-shifted by 1.78 nm by applying a voltage of 20 V, and the wavelength tuning efficiency reached 0.059 nm·℃^-1. Compared with PET-based and silicon-based graphene films, the actual electrical heating capacity of graphene glass increased by 195%. These experimental findings demonstrate that graphene glass transparent films with excellent electric heating characteristics can be used in various transparent electric heating fields and have relatively wide application prospects.     

石墨烯纤维材料的化学气相沉积生长方法

石墨烯纤维材料是以石墨烯为主要结构基元沿某一特定方向组装而成或由石墨烯包覆纤维状基元形成的宏观一维材料。根据组成基元的不同可将石墨烯纤维材料分为石墨烯纤维和石墨烯包覆复合纤维。石墨烯纤维材料在一维方向上充分发挥了石墨烯高强度、高导电、高导热等特点,在智能纤维与织物、柔性储能器件、便携式电子器件等领域具有广阔的应用前景。随着化学气相沉积(Chemical Vapor Deposition,CVD)制备石墨烯薄膜技术的发展,CVD技术也逐渐应用于石墨烯纤维材料的制备。利用CVD法制备石墨烯纤维可避免传统纺丝工艺中繁琐的氧化石墨烯(Graphene Oxide,GO)还原过程。同时,通过CVD法直接将石墨烯沉积至纤维表面可以保证石墨烯与纤维基底之间强的粘附作用,提高复合纤维的稳定性,同时可实现对石墨烯质量的有效调控。本文综述了石墨烯纤维材料的CVD制备方法,石墨烯纤维材料优异的力学、电学、光学性质及其在智能传感、光电器件、柔性电极等领域的应用,并展望了CVD法制备石墨烯纤维材料未来的发展方向。     

亚硫酸盐无氰电沉积金新工艺及机制

直接以氯金酸作为主盐、 羟基乙叉二膦酸（HEDP）作为镀液稳定剂和镀层细化剂、 结合添加剂, 组成亚硫酸盐无氰镀金新工艺; 研究镀液稳定性、 镀层形态及金电沉积机制。结果表明, HEDP可明显提升镀液稳定性;不含HEDP的亚硫酸盐镀金液中, 镀层呈棒状晶粒并随沉积时间延长而逐渐生长,导致镀层外观随镀层厚度增加由金黄色转变为红棕色。镀液含有HEDP时, 金晶粒形态由棒状转变为棱锥状, 且棱锥状晶粒随沉积时间延长生长速率较小, 镀层厚度为1 μm时仍呈现金外观。电化学实验表明金电沉积不经历成核过程。     

电子功能外延薄膜的电沉积

电沉积作为一种在温和条件下从溶液中合成材料的技术已被广泛应用于在导体和半导体基底表面合成各种功能材料。电沉积一般由人为施加于基底的电刺激（如：施加电位/电流）来触发。这种电刺激通过氧化或还原靠近基底表面的溶液层内部的离子、 分子或配合物从而使该溶液层偏离其热力学平衡状态,随后引起目标产物在基底表面的沉积。在电沉积过程中, 许多实验参数都可能从不同的方面对沉积物的物化性质造成影响。迄今为止,已通过电沉积制备出多种单质（包括金属和非金属单质）、 化合物（例如：金属氧化物、金属氢氧化物、 金属硫化物等）以及复合材料。电沉积制备的这些材料大多为多晶、 织构或外延薄膜的形式。其中, 外延薄膜是一种具有特定的面外和面内晶体生长取向且其晶体取向受基底控制的类单晶薄膜。由于外延薄膜中高度有序的原子排列,它们常呈现出独特的电磁性质。本文总结了常见的电沉积合成路线及影响沉积物外延生长的关键实验因素。此外, 本文简要介绍了用于表征外延薄膜的技术。最后, 本文还讨论了一些采用电沉积制备的具有特殊电子、 电磁及光电特性的功能外延薄膜。     

纳米晶枝CuAu 合金催化剂对二氧化碳电催化还原性能的研究

利用可再生清洁能源将CO₂转化为CO和其他小分子是合成含碳燃料的可观方法之一。间歇性可再生能源存储的重要策略之一是将二氧化碳进行电化学还原。选择具有高活性和稳定性的电催化剂对于电化学还原CO₂至关重要。在这项研究中,我们使用简单的电沉积方法合成了具有纳米晶枝状结构的CuAu合金电极。各项表征显示原子比约为1:1的CuAu纳米枝晶对CO₂的电化学还原具有出色的催化活性。合成的主要产物是H₂和CO,这是合成气体是合成天然气,氨和甲醇合成的中间体。电化学阻抗谱（EIS）测量表明,相对于Cu和Au电沉积催化剂,CuAu纳米晶枝状催化剂具有相对低的电荷转移阻力。CuAu纳米枝晶催化剂是一种具有潜在的转化CO₂为合成气体的高活性电催化剂。