铈铝复合载体对钼基催化剂耐硫甲烷化催化性能的研究

采用共沉淀法、浸渍法和沉积沉淀法制备了CeO₂-Al₂O₃复合载体,比较了不同复合载体浸渍钴钼后的耐硫甲烷化催化性能,并优化了复合载体中CeO₂的含量。结合N₂物理吸附、XRD、H₂-TPR等表征手段对复合载体及其负载的钴钼催化剂进行物相和结构分析发现,在Al₂O₃中添加CeO₂可以明显提高合成气的耐硫甲烷化活性,其中,沉积沉淀法制备的25% CeO₂-Al₂O₃复合载体负载钴钼后具有最佳催化活性。     

氧化铈在生物分析与传感检测中的应用研究进展

铈是镧系元素中活性最高的一种稀土元素,氧化铈已广泛应用于抛光剂、脱色剂、催化剂、发光增强剂等领域。Ce3+/Ce4+之间自发的氧化还原循环可在氧化铈晶面上产生许多氧空位（V?）,加快反应中的电荷转移,使氧化铈具有很高的催化活性和储放氧能力。混合价态自发的氧化还原循环以及由此产生的氧空位对氧化铈的性质有着重大影响,使其表现出独特的抗菌、抗炎、抗肿瘤和模拟酶等生物医学活性,可用于多种疾病的诊疗。此外,氧化铈还可单独使用或与其他材料掺杂、复合来构建灵敏的传感材料,应用于多种物质的分析与检测,并已成为国内外研究的热点。该文首先阐明了氧化铈作为传感材料的理论基础,然后分别从电化学传感、比色传感、荧光传感和化学发光传感四个方面对国内外氧化铈传感检测领域的应用进展进行了归纳,最后对氧化铈传感器的研发现状进行总结并对未来发展进行了展望,为高性能传感器的研发提供了参考。     

Density functional theory study of formaldehyde adsorption and decomposition on Co-doped defective CeO_2(110) surface

Formaldehyde as an air pollutant to adverse health effects for humanity has been getting attention. The adsorption and dissociation of formaldehyde(HCHO) on the Co_xCe_(1-x_O_(2-δ)(110) surface were investigated by the density functional theory(DFT) calculations. We calculated the oxygen vacancy formation energy as the function of its site around dopant Co in detail. The results showed that Co doping was accompanied by compensating oxygen hole spontaneous formation.The adsorption configurations and bindings of HCHO at different locations on the Co_xCe_(1-x)O_2(110) were presented.Four possible pathways of oxidation of formaldehyde on the catalytic surface were explored. The results suggested that formaldehyde dissociation at different adsorption sites on the doped CeO_2(110) — first forming dioxymethylene(CH_2O_2)intermediate, and then decomposing into H_2O, H_2, CO_2, and CO molecules. It was found that the presence of cobalt and oxygen vacancy significantly prompted the surface activity of CeO_2.     

Powder preparation and UV absorption properties of selected compositions in the CeO2-Y2O3 system

Several approaches have been investigated to prepare fluorite-type compositions within the (1−x) CeO₂-xYO_1.5 system. The optical properties of the resulting modified-ceria materials have been characterized in order to evaluate their potential abilities as inorganic UV absorbers. Diffuse reflectance analyses reveal a strong optical absorption between 390 and 400 nm for all substituted compositions and the spectral selectivities are estimated suitable for the targeted application. Additionally, time resolved microwave conductivity (TRMC) and phenol photodegradation analyses do not indicate any photocalatytic activity for these compositions. Aqueous colloidal suspensions of the Ce_0.7Y_0.3O_1.85 UV absorber have been carried out.     

Ce-Pt-Pd/不锈钢丝网催化剂的制备与催化性能

采用阳极氧化技术在不锈钢丝网上自生长了一层结构致密的阳极氧化膜,并以此为载体,制备出一种高活性、高稳定性的负载型Ce-Pt-Pd催化剂.考察了该系列催化剂对甲苯、丙酮和乙酸乙酯的氧化活性,并用扫描电镜、X射线光电子能谱和程序升温氧化技术对催化剂进行了表征.结果表明,不锈钢丝网载体表面自生长的氧化物膜十分有利于活性组分的负载,制得的催化剂具有较高的催化燃烧有机化合物的活性和稳定性.     

不同CuO/CeO2催化剂上CO低温氧化反应

 分别用热解硝酸铈法和浸渍法制备了不同物性的CeO2粉体和相应的CuO/CeO2催化剂,并用XRD, HRTEM和TPR等对样品进行了表征,利用微反-色谱装置考察了其催化CO低温氧化的活性. 结果表明,热解温度影响CeO2的物性(形貌、粒度大小及分布等). 相同条件下,不同物性的CeO2载体上CuO的负载情况不同, 500 ℃热解获得的CeO2载体上非晶态CuO负载量最高,相应的CuO/CeO2催化剂活性也较高. 非晶态CuO一部分进入CeO2晶格,另一部分高度分散于CeO2表面上. 焙烧温度较低时(≤ 600 ℃), 催化剂活性受焙烧温度的影响较小,而高温(800 ℃)焙烧后,催化剂则因载体粒度增大和CuO烧结团聚等因素导致催化活性明显降低.     

Zr‐doped CeO2 Hollow slightly‐truncated nano‐octahedrons: One‐pot synthesis,characterization and their application in catalysis of CO oxidation

Zirconium‐doped ceria hollow slightly‐truncated nano‐octahedrons (HTNOs) (Ce_1‐xZr_xO₂) were synthesized by a one‐pot, facile hydrothermal method. The morphology and crystalline structure were characterized with powder X‐ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM) and the high resolution transmission electron microscopy (HRTEM). The composition and chemical valence on the surface of the as‐prepared Ce_1‐xZr_xO₂ powders were detected by X‐ray photoelectron spectroscopy (XPS) and energy dispersive spectrometry (EDS). The surface area and pore size distribution of as‐obtained Zr‐doped ceria HTNOs were measured by N₂ adsorption‐desorption measurement. Mechanisms for the growth of Zr‐doped ceria HTNOs are proposed as both oriented attachment and Ostwald ripening process and the formation of the hollow structure is strongly dependent on the addition of Zr⁴⁺ ions. Furthermore, the as‐obtained Zr‐doped ceria HTNOs revealed superior catalytic activity and thermal stability toward CO oxidation compared to pure ceria. It may provide a new path for the fabrication of inorganic hollow structures on introducing alien metal ions.     

Ce1—xM′xCa0.2O1.8—0.4x（M=Y,La和Gd）的水热合成及离子导电性质研究

采用水热法合成了系列双掺杂的萤石结构Ce1-xLnxCa0.2O1.8-0.4x固溶体,并研究了3种稀土离子对固溶体导电性的影响,发现掺杂离子半径接近Ce^4 时,体系电导率增大而活化能降低,同时发现水热合成的Ce1-xLnxCa0.2O1.8-0.4x样品的平均粒度按着掺入离子Y^3 ,Gd^3 ,La^3 的顺序逐渐减小,分别为32,20和15nm,这种变化是由于Y^3 半径比La^3 和G ^3 更接近Ce^4 ,因而在水热合成过程中, 掺Y^3 的体系更有利于晶粒的生长,得到的晶体粒度较大。     

氧化铈气凝胶担载氧化铜催化剂上的一氧化碳氧化

 以一氧化碳氧化为探针反应,考察了氧化铈气凝胶担载氧化铜催化剂的催化活性,研究了催化剂中氧化铜的含量、载体及催化剂的焙烧温度对催化剂活性的影响．结果表明,氧化铈气凝胶担载的氧化铜催化剂对一氧化碳氧化反应呈现出高催化活性,适当温度下焙烧载体及催化剂有利于提高催化剂的催化活性;随着催化剂中氧化铜含量的增加,一氧化碳完全转化的温度降低,但当w（CuO）＞12％时,过量的氧化铜以体相形式而不是以高分散形式存在,对催化剂活性的影响很小．     

Investigation of the relationship between the ionic conductivity and the local structures of singly and doubly doped ceria compounds using EXAFS measurement

The oxide ionic conductivity measurements of singly and doubly doped ceria compounds were carried out. Singly and doubly doped ceria used in this study were Ce_0.8Ln_0.2O_1.9 (Ln=Y, Sm, Nd, or La) and Ce_0.8La_0.1Y_0.1O_1.9, respectively. Lattice constants of these compounds were in proportion to the ionic radius of the dopant(s). The doubly doped ceria compound showed oxide ionic conductivity comparative to the average of that of each corresponding singly doped sample. This finding indicates that the conductivity is influenced by both dopants in the doubly doped compounds. The extended X-ray absorption fine structure (EXAFS) study showed that the coordination number of oxide ions at the nearest neighbor of cation was related to the ionic conductivity. It was found that the conductivity gave the highest value when oxygen vacancies were randomly distributed in the lattice. This indicates that the local structure seriously affects oxide ionic conduction in singly and doubly doped ceria compounds.