CNx纳米管的制备、结构观察及低场致电子发射性能研究

采用高温热解法，以乙二胺为前驱液，在沉积有铁催化剂的p型硅（111）基底上制备出了定向生长的CNx纳米管.利用扫描电子显微镜、高分辨率透射电子显微镜和拉曼光谱对CNx纳米管进行了形貌观察和表征.CNx纳米管的高度在20?μm左右，直径在50—100nm之间，具有明显的“竹节状”结构，结晶有序度较差.对CNx纳米管薄膜进行低场致发射性能测试：外加电场为1.4V/μm，观察到20?μA /cm2发射电流，外电场升至2.54V/μm时发射电流达到1.280mA/cm2，在较高外电场下，没有发现电流“饱和”.这比 关键词： CNx纳米管 高温热解 “竹节状”结构 场致发射     

Effects of External Electric Field on Ferroelectric Superlattice with Two Alternating Layers

The effects of the external electric field on the ferroelectric superlattice with two alternating layers have been studied using the transverse Ising model based on the effective-field theory with the differential technique. The hysteresis loops and susceptibility of the system have been given. The stronger the external electric field, the smaller the susceptibility, reflecting that the polarization is weaker.     

CNx纳米管的制备、结构观察及低场致电子发射性能研究

采用高温热解法 ,以乙二胺为前驱液 ,在沉积有铁催化剂的p型硅 (1 1 1 )基底上制备出了定向生长的CNx 纳米管 .利用扫描电子显微镜、高分辨率透射电子显微镜和拉曼光谱对CNx 纳米管进行了形貌观察和表征 .CNx 纳米管的高度在 2 0 μm左右 ,直径在 5 0— 1 0 0nm之间 ,具有明显的“竹节状”结构 ,结晶有序度较差 .对CNx 纳米管薄膜进行低场致发射性能测试 :外加电场为 1 4V μm ,观察到 2 0 μA cm2 发射电流 ,外电场升至 2 5 4V μm时发射电流达到1 2 80mA cm2 ,在较高外电场下 ,没有发现电流“饱和” .这比相同实验条件下改变前驱液制备出的碳纳米管和硼碳氮纳米管的场发射性能优越 .还在“竹节状”结构的基础上对CNx 纳米管的场致电子发射机理进行了讨论     

铁电单晶Pb(Mg1/3Nb2/3)O3-PbTiO3的高场致应变及其在层叠式驱动器中的应用

通过研究(1-x)Pb(Mg1/3Nb2/3)O3-xPbTiO3 (PMNT)单晶在不同方向、不同组分下高场致应变的特性,确定了〈001〉取向PMNT单晶(29%≤x≤31%)为制作层叠式驱动器的最佳组分范围,这组分的单晶具有高场致应变、低滞后而且性能较稳定的特点.研究结果表明,在保证应变曲线的线性和低滞后的前提下,将近-2kV/cm的负电场能够运用于〈001〉方向的PMNT晶体上. 40层(每片晶片尺寸为7mm×7mm×0.7mm)PMNT层叠式驱动器在电场 -1.5-10kV/cm的驱动下,可以获得38.1μm的纵向位移,负载40N的重量后,位移量减为34μm.     

利用爆磁压缩发生器产生高功率脉冲高电压

 爆磁压缩发生器产生脉冲高电压技术可以用于产生高功率微波及强电磁脉冲的实验研究。给出了利用螺旋型爆磁压缩发生器（HEMG）驱动电爆炸丝功率调节系统产生高功率脉冲高电压的实验方法和主要的结果。在利用HEMG驱动电爆炸丝断路开关（EEOS）产生脉冲高电压实验中，获得了最高电压700~800kV,功率大于20GW的脉冲输出。     

硕果繁花荣九秩 仁风德范仰高贤——祝贺吴浩青先生九秩华诞暨执教69周年讲誌庆

著名电化学家、中国科学院资深院士吴浩青教授今年迎来他的九秩华诞．在半个多世纪来，吴老以他广博的学识和勤奋的精神为我国电化学事业作出了突出的贡献．     

Spin-Polarized Tunnelling Magnetoresistance Effects in La0.833K0.167MnO3／SrTiO3 Polycrystalline Perovskite Manganites

A sample of La0.833K0.167MnO3-SrTiO3 (LKMO/STO) is fabricated by the sol-gel method. The microstructure,magnetic and transportation properties have been studied. X-ray diffraction patterns indicate that the structure of LKMO/STO is a homogeneous solid solution phase. The resistivity of LKMO/STO shows the insulator behaviour, which is different from La0.833K0.167MnO3 (LKMO) whose resistivity shows metal-insulator transition with decreasing temperature. The low-field (moH = 0.02 T) magnetoresistance decreases from 11% to 0.2% with the increasing temperature from 4 K‘to 220K for the LKMO/STO sample. The magnitude of magnetoresistance in a strong field (μoH = 5.5 T) almost increases linearly with decreasing temperature and reaches the maximum of 65% at the low temperature of 4.2K, which is much higher than that oE LKMO (40%). The enhanced low-field magnetoresistance effects are quantitatively explained by the spin-polarized tunnelling at grain boundaries.     

金钢石的制备研究

本文研究了两种不同质异构体石墨—金刚石的转化条件，以及在实验室现有条件下，利用石墨材料制备金刚石颗粒的具体方法和试验结果。     

金属有机化学气相沉积法制备钛酸铅铁电薄膜

利用低压ＭＯＣＶＤ工艺分别在（００１）取向的ＬａＡｌＯ_３，ＳｒＴｉＯ_３和重掺杂硅单晶衬底上制备ＰｂＴｉＯ_３铁电薄膜，并通过Ｘ射线衍射谱对薄膜的微结构进行分析．Ｘ射线θ－２θ扫描显示硅衬底上得到了ＰｂＴｉＯ_３多晶薄膜，另两种衬底上得到了择优取向的ＰｂＴｉＯ_３薄膜．ＬａＡｌＯ_３衬底上的ＰｂＴｉＯ_３薄膜有ａ和ｃ两个取向，也就是薄膜中存在着９０°畴结构，而生长在ＳｒＴｉＯ_３衬底上的ＰｂＴｉＯ_３薄膜中只存在ｃ方向的择优取向．由于薄膜的尺度效应，发现ｃ轴晶格常数与块材相比均缩短．Ｘ射线的φ扫描验证了后两类薄膜的外延特性，利用同步辐射的高强度和高能量分辨率用摇摆曲线方法研究了这两种外延薄膜的品质，进一步证明了ＳｒＴｉＯ_３衬底上的ＰｂＴｉＯ_３薄膜的单畴特性．利用重掺杂的硅衬底作底电极，测量显示直接生长于硅衬底上的ＰｂＴｉＯ_３多晶薄膜具有良好的铁电性能 关键词：     

NaNO3掺杂Y2O3材料的制备及电流变性质

利用NaCO3和Y（NO3）3做主要原料，合成了一系列用稀土氧化物（Y2O3）作为基础材料的新型电流变材料——NaNO3掺杂Y2O3材料。对于这些材料的介电性质、微观结构和电流变性能的研究结果表明，NaNO3的掺杂可以明显地提高Y2O3材料的电流变活性。材料在二甲基硅油中的悬浮液的剪切应力随NaNO3在Y2O3中的掺杂程度有明显变化，当Na／Y（物质的量的比）为0．6时材料的电流变性能最好，