SYNTHESIS OF AN AMPHIPHILIC PPESK-g-P(PEGMA) GRAFT COPOLYMER VIA ATRP AND ITS USE IN BLEND MODIFICATION OF PPESK MEMBRANES

Preparation of an amphiphilic graft copolymer having poly(phthalazinone ether sulfone ketone)(PPESK) as main chains was carried out by atom transfer radical polymerization(ATRP).The precursor,chloromethylated PPESK (CMPPESK),was prepared by using chioromethylether as chloromethylation agent.Then,poly(ethylene glycol) methyl ether methacrylate(PEGMA) was used as monomer to synthesize PPESK-g-P(PEGMA) by ATRP method under the catalysis of a cuprous chloride/2,2'-bipyridyl system.PPESK/PPESK-g-P(PEGMA) blen...     

三头季铵盐阳离子表面活性剂合成菱形十二面体介孔二氧化硅单晶

由于介孔二氧化硅单晶规整的外观形貌和有序的内部孔道结构性能, 使其在微激光器件领域具有十分重要的潜在应用. 试着用高电荷密度的阳离子三头季铵盐表面活性剂(C18-2-3-1)作模板剂, 用正硅酸四乙酯作无机前驱体, 在硫酸介质中通过调变有机-无机物种之间的协同组装作用, 成功地合成了具有简单立方相Pm3n结构的介孔二氧化硅单晶. 扫描电子显微镜(SEM)观察到这种介孔二氧化硅单晶具有菱形十二面体形貌, X射线衍射(XRD)和透射电子显微镜(TEM)测试结果证实这种介孔单晶属于简单立方Pm3n对称结构. 氮气吸附数据测得这种单晶具有较大的BET比表面积(550 cm2/g), 较大的孔体积(BJH 0.20 cm3/g)和孔径(BJH 2.4 nm).     

C(3)-酯基取代的1,5-苯并硫氮杂卓的合成、晶体结构及抑菌和构效关系的研究

设计、合成了三类C(3)酯基取代的1,5-苯并硫氮杂卓衍生物: 2,3/2,5-二氢和2,3,4,5-四氢-1,5-苯并硫氮杂卓-3-甲酸乙酯, 采用元素分析、IR、MS、1H NMR及X射线衍射法确定了标题化合物的分子结构．结构分析表明, 2,5-二氢-1,5-苯并硫氮杂卓-3-甲酸乙酯属单斜晶系, C2/c空间群, 晶胞参数为: a＝2.0319(4) nm, b＝1.4985(3) nm, c＝1.3659(3) nm, α＝90°, β＝120.49(3)°, γ＝90°, V＝3.5840(12) nm3, Z＝8, Dc＝1.397 g/cm3, μ＝0.351 mm－1, F(000)＝1560, R＝0.0478, Rw＝0.1304; 研究了2,3/2,5-二氢-1,5-苯并硫氮杂卓的合成反应条件, 发现该两种互变异构体分别是速度控制产物和平衡控制产物; 抑菌活性及抑真菌构效关系研究表明, 亚胺型的2,3-二氢-1,5-苯并硫氮杂卓具有明显的抑菌活性, 亚胺官能团是其抑真菌的药效团．     

纳米MnO2：水热法制备及盐对晶型和形貌的影响

在水热条件下,向反应体系中加入简单的无机盐,利用KMnO4和MnCl2反应生成不同晶型/形貌的一维MnO2纳米材料.用X-射线衍射(XRD)、场发射扫描电镜(FESEM)、透射电镜(TEM)、高分辨透射电镜(HRTEM)以及选区电子衍射(SAED)等对产物进行了结构和形貌的表征.结果显示,加入的简单无机盐不仅影响产物的晶型,同时也对产物的形貌也起到了控制作用.     

超临界二氧化碳中药物控制释放体系的一步法制备研究

用一步法首次制备了以N-异丙基丙烯酰胺类共聚物为基料的药物释放体系。在此法中,超临界二氧化碳同时作为聚合介质和渗透试剂。制得的聚合物微球用扫描电镜、差示扫描量热仪、透射电镜、X射线衍射仪等进行了表征,并用体外释放模拟考察了原位法制备的微凝胶对渗入的目标药物布洛芬的释放效果。     

Size control synthesis of sulfur doped titanium dioxide （anatase） nanoparticles, its optical property and its photo catalytic reactivity for CO2 ＋ H2O conversion and phenol degradation

Sulfur doped anatase TiO2 nanoparticles (3 nm−12 nm) were synthesized by the reaction of titanium tetrachloride, water and sulfuric acid with addition of 3M NaOH at room temperature. The electro-optical and photocatalytic properties of the synthesized sulfur doped TiO2 nanoparticles were studied along with Degussa commercial TiO2 particles (24 nm). The results show that band gap of TiO2 particles decreases from 3.31 to 3.25 eV and for that of commercial TiO2 to 3.2 eV when the particle sizes increased from 3 nm to 12 nm with increase in sulfur doping. The results of the photocatalytic activity under UV and sun radiation show maximum phenol conversion at the particle size of 4 nm at 4.80% S-doping. Similar results are obtained using UV energy for both phenol conversion and conversion of CO2+H2O in which formation of methanol, ethanol and proponal is observed. Production of methanol is also achieved on samples with a particle size of 8 and 12 nm and sulfur doping of 4.80% and 5.26%. For TiO2 particle of 4 nm without S doping, the production of methanol, ethanol and proponal was lower as compared to the S-doped particles. This is attributed to the combined electronic effect and band gap change, S dopant, specific surface area and the light source used.     

直接甲醇燃料电池的甲醇浓度控制方法

直接甲醇燃料电池(DMFC)直接以甲醇为阳极燃料,具有系统结构简单、体积能量密度高、燃料补充方便等特点,非常适合用于小型移动电源。甲醇浓度对DMFC性能和燃料利用效率的影响非常大,甲醇浓度高低直接决定DMFC输出性能的好坏,控制好DMFC中的甲醇浓度,对其寿命长短起着至关重要的作用。本文将目前已有的甲醇浓度控制方法分为有甲醇浓度传感器和无甲醇浓度传感器两大类,评述了这些浓度控制方法的研究现状和优缺点,并展望了甲醇浓度控制方法的趋势。     

功能纳米材料的化学控制合成、组装、结构与性能

维度限制使得纳米材料具有独特的物理和化学性质,如何对纳米构造单元的结构进行调控,并最终将纳米效应在宏观尺度上体现是当今纳米科技面临的挑战性问题,纳米材料的化学控制合成方法学、组装、结构与性能的研究是解决上述问题的基础．这篇综述文章从四个方面,分别介绍了单分散纳米晶以及纳米管、纳米线、空心纳米微球等系列低维纳米结构在合成方法与技术、“自下而上”的组装、基于微结构的性能表征与应用探索等领域取得的研究进展,试图总结出其中的规律性,同时也展现了纳米科学与技术的魅力和广阔的发展前景．     

控制电位电解法测定银合金中的银

利用控制阴极电位的方法,在氨性介质中,以EDTA作掩蔽剂对银合金中的银进行电解,消除了一定量的共存离子干扰,提高了银的回收率.在电解分析中,严格控制阴极电位,提高了方法的灵敏度.将该法用于银合金中银的测定,回收率为99.6%～99.8%,测定结果的相对标准偏差RSD为0.15%～0.17%(n=4).