电沉积Fe-W-ZrO2纳米复合镀层的结构与腐蚀行为

采用复合电沉积工艺制备了Fe-W-ZrO₂纳米复合镀层. 分别用扫描电子显微镜(SEM)、扫描电子显微镜附带能谱仪(EDS)、X射线衍射(XRD)、恒电位仪等技术较系统地研究了Fe-W-ZrO₂纳米复合镀层的表面形貌、成分、结构、硬度和耐蚀性. 结果表明, 复合镀层的质量组成为Fe 38.3%(w)、W52.7%(w)、ZrO₂ 9.0%(w) 时, 在ZrO₂纳米粒子的弥散强化作用下, Fe-W非晶合金镀层的裂纹状况得到明显改善, 而且复合镀层成分分布均匀, 组织致密, 结构呈现明显的非晶态特征；复合镀层比Fe-W合金有更高的显微硬度；30 ℃下, Fe-W-ZrO₂纳米复合镀层在3.5%(w)NaCl和0.5 mol·L^-1 H₂SO₄溶液中的耐蚀性较Fe-W非晶合金镀层明显提高.     

Controllable Electrochemical Synthesis of Silver Dendritic Nanostructures and Their SERS Properties

Ag dendritic nanostructures were synthesized on fluorine-doped tin oxide covered glass sub-strates by the electrodeposition method. Results demonstrate that the size, diameter, crys-tallinity, and branch density of the Ag dendrites can be controlled by the applied potential,the surfactants and the concentration of AgNO₃. Three kinds of typical silver dendrites were applied as substrates of the surface enhanced Raman scattering (SERS) and one of them was able to clearly detect rhodamine 6G concentrations up to 0.1 nmol/L. The differences of the SERS spectra at these Ag dendrites confirmed that the shapes and interparticle spacings have great effect on Raman enhancement, especially the interparticle spacings.     

三维结构泡沫Co3O4的制备及电化学性能

通过电化学沉积方法在三维结构泡沫镍基体上沉积金属钴层, 利用固相氧化方法制备了三维结构泡沫Co3O4负极. XRD和SEM结果显示, 电化学沉积制备得到具有纳米结构的金属钴层, 经固相氧化处理, 在泡沫镍基体表面形成了Co3O4微米级的致密活性氧化层. 通过充放电和循环伏安以及电化学阻抗等方法研究了电极的电化学性能, 结果表明, 当放电电位区间为0.05~3.2 V时, 三维泡沫Co3O4于0.2 C倍率下充放电, 初始容量损失为29%, 经50次循环后, 质量比容量为824 mA·h/g, 三维泡沫结构提高了Co3O4电极的循环容量保持性能和倍率性能.     

退火前后镍钨硼合金电沉积层的结构与性能

采用电化学技术、XPS、DSC、XRD等方法研究Ni W B合金电沉积及热处理前后合金镀层的结构和显微硬度.结果表明,在Ni W B合金电沉积过程中伴随着化学沉积镍等过程以及Na2B4O7在镀层中的夹杂;Ni W和Ni W B合金电沉积层分别表现为纳米晶结构和非晶态结构;热处理过程中合金电沉积层发生晶粒粗化过程以及Ni W B合金镀层发生新相形成过程,产生Ni4W和镍硼化物如Ni2B、Ni3B等沉淀物;400 ℃热处理2 h后Ni W合金镀层有最大的显微硬度达919.8 kg•mm－2,而在500 ℃下Ni W B合金有最大的硬度达1132.2 kg•mm－2.     

Surface morphology and local magnetic properties of electrodeposited thin iron layers

Thin iron layers with different thickness were prepared by electrodeposition on the polycrystalline substrate. The surface morphology of the layers, their structure and local magnetic properties were studied using scanning tunneling microscopy (STM), X-ray diffraction (XRD) and conversion electron Mössbauer spectroscopy (CEMS). STM studies revealed the granular structure of the surface of the electrodeposited iron layers with the roughness up to 10 nm. XRD analysis proved that these layers were highly strained. The CEMS spectra showed an in-plane magnetic anisotropy in the iron layers. Isomer shift of the electrodeposited iron was different than that of the -Fe. This difference was attributed to the internal stresses existing in the electrodeposited layers.     

薄层电沉积的共轭溶解-沉积行为

在铅的薄层电沉积生长中,铅的枝晶沉积物由于氢气的扰动从阴极断裂.断裂的沉积物片段并非在薄层电解槽中保持不动,而是自发地朝阳极方向快速运动.研究表明,这种奇特的现象是由断裂沉积物两端发生的共轭溶解-沉积反应造成的.本文讨论了这种现象产生的机制.     

半导体硅上电沉积Cu/Co层状薄膜

由磁性层和非磁性层组成的人工调制层状结构多层膜,其物性和磁性都表现出与其它结构的多层膜显著不同的特点,如巨磁阻效应［’,‘l、易磁性方向的改变等”］．其性能的研究不但在磁性理论上具有重大意义,而且有望应用于高性能的磁阻敏感设备及提高磁记录密度等．因而近年来有关这方面的研究越来越引起人们的重视．目前,磁性多层膜的制备主要采用气相沉积、磁控溅射、分子束外延等真空技术．由于电沉积技术具有设备简单、操作方便等特点而成为制备多层膜的颇具活力的工艺．CO／Cll多层膜在C。层厚度较薄时具有较高室温巨磁阻（GMR）…     

电沉积Ni-PSZ梯度镀层过程中阴极电流效率的研究

采用动电位扫描,电化学交流阻抗及扫描电子显微镜研究电沉积Ｎｉ－ＰＳＺ梯度镀层过程中阴极电流效率的变化规律及其机理．结果表明,Ｎｉ－ＰＳＺ复合镀层对氢的析出反应具有催化作用,在镀液中加入ＰＳＺ微粒后,能增大镍还原过电位,降低氢析出过电位,从而不断降低电沉积梯度镀层过程中的阴极电流效率．在电沉积Ｎｉ的过程中,有中间吸附相Ｎｉ＋ａｄｓ生成,ＰＳＺ微粒的加入能优先催化Ｈａｄｓ,加速氢气析出     

纳米材料的电化学制取及应用

简介近年来纳米材料的电化学制备技术,纳米材料在电沉积、电池、电催化、传感器等领域中应用的新进展.     

Atomic Layer Electrodeposition of Pt on Nanoporous Au and its Application in pH Sensing

The preparation of nanoporous metal structures has received a substantial amount of attention because of the unique properties and various applications of these structures. In this work, the preparation of nanoporous Pt structures by modification of nanoporous gold (NPG) surfaces with Pt was achieved. An atomic layer electrodeposition (ALED) technique previously reported for the modification of flat Au surfaces with Pt was applied to the NPG surfaces to produce Pt‐modified NPG structures. The optimal ALED parameters, such as deposition potential, time, and number of cycles, for the preparation of Pt‐modified NPG structures were investigated. Scanning electron microscopy and energy‐dispersive X‐ray analysis confirmed the successful preparation of nanoporous Pt structures by ALED techniques. The Pt‐modified NPG performed well as a pH sensor with a Nernstian slope and negligible hysteresis. The method of preparing the nanoporous Pt structures reported in this work could be utilized in various applications such as electrocatalysis and electroanalysis.