Electrochemical formation and composition analysis of Zn x Cd1-x Se solid solutions

The direct growth of ZnSe–CdSe solid solution onto metallic cathodes by electrodeposition from acidic aqueous sulphate solutions is described. The plating process is studied by simple voltammetry, while the structure and composition of the electrolytic deposits are investigated by X-ray diffraction. The experimental d-spacing values of the as-grown mixed lattice are compared to data from reference Zn _x Cd_1-x Se pellets of standard composition, produced by a sintering method. The findings are supplemented with energy-dispersive X-ray (EDX) elemental analysis. Thereupon, the variation of the mole fraction x in Zn _x Cd_1-x Se, and the solid phase constitution of the electrodeposits are determined and correlated to the electrochemical conditions of growth. The resulting films contain admixtures of CdSe compound and metallic Cd.     

Enhanced electrodeposition of indium hexacyanoferrate thin films through improved plating solution stability

An ordinary plating solution for indium hexacyanoferrate (InHCF) thin film deposition, mainly composed of equal concentrations of In³⁺ and [Fe(CN)₆]^3–, usually forms precipitates rapidly when either concentration is higher than few millimolar. This contributes to the plating solution's instability. Moreover, electrodeposited capacities are limited accordingly. In this work, the plating solution's stability and the electrodeposition of InHCF were greatly enhanced by adding a large amount of K⁺ and/or H⁺. It was found that a 10-mM plating solution added with 1 M HCl and 1 M KCl could be stored as fresh over a one-week period, whereas an unmodified plating solution became useless within a couple of minutes. Also, such cationic additions, especially adding H⁺, increased the electrodeposited capacity ca. 18 times at least, as compared with that obtained from the unmodified plating solution. Furthermore, related enhancing mechanisms were proposed and verified. To sum up, this study offers a means for better InHCF electrodeposition and should promote the applications of InHCF films. Electronic Publication     

镧与镍共沉积的研究

由于含稀土的合金新材料具有多种特殊功能，因此，其制备技术已为人们所关注．制备含稀土合金的方法有高温烧结法、真空蒸发法、离子溅射法及电化学法等．其中电化学法设备简单，容易获得不同组份的表层材料，但是，由于稀土元素的电位很负，从电解质水溶液中沉积稀土及其合金是相当困难的，以往曾有采用熔融盐电解质或非水电解质制备稀土合金的一些报导[1，2]，而从电解质水溶液中电沉积稀土合金的报导甚少．本研究采用适宜的络合剂，实现了从电解质水溶液中电沉积Ni－La合金，镀层中钠含量最高达22．58％（质量分数，下同）．通过XPS及…     

Electropreparation of Poly(benzophenone‐4) Film Modified Electrode and Its Electrocatalytic Behavior Towards Dopamine,Ascorbic Acid and Nitrite

The oxidation of benzophenone‐4 (2‐hydroxy‐4‐methoxybenzophenone‐5‐sulfonic acid) at glassy carbon electrode gives rise to stable redox active electropolymerized film during repetitive potential cycling between 0 to 1.3 V (Ag/AgCl). Cyclic voltammogram of poly(benzophenone‐4) film shows a redox couple with well‐defined peaks. The redox response of the modified electrode was found to be depending on the pH of the contacting solution. The peak potentials were shifted to a less positive region with increasing pH and the dependence of the peak potential was found to be 51 mV/pH. The electrocatalytic behavior of poly(benzophenone‐4) film modified electrode towards oxidation of dopamine, ascorbic acid and reduction of nitrite was investigated. The oxidation of dopamine and ascorbic acid occurred at less positive potential on poly(benzophenone‐4) film compared to bare glassy carbon electrode. For dopamine, the overpotential was reduced about 180 mV. Feasibility of utilizing poly(benzophenone‐4) film coated electrode in analytical estimation of dopamine, ascorbic acid and nitrite was also demonstrated.     

铜在HOPG上电沉积过程的现场ECSTM研究

用自制的电化学扫描隧道显微镜（ＥＣＳＴＭ）现场研究Ｃｕ在ＨＯＰＧ上的电沉积过程．结果表明Ｃｕ在ＨＯＰＧ上的电沉积为三维成核的过程．当电位较低或Ｃｕ２＋离子浓度较低时，铜在本体金属生长主要沿着台阶方向．过电位较高时，铜的成核数目增加，沉积层的晶粒有所细化．同时，非现场ＥＣＳＴＭ比较研究表明，ＳＴＭ针尖对针尖局部区域的电沉积起屏蔽作用，针尖所在区域Ｃｕ的沉积速度比其它区域明显减小     

Electroreduction of α-glucose on CNT/graphite electrode modified by Zn and Zn–Fe alloy

Electroreduction of -glucose to form sorbitol on Zn/CNTs and Zn alloy/CNTs electrodes has been investigated in this paper. Carbon nanotubes (CNTs) used in this paper are grown directly on graphite disks by chemical vapor deposition. Zn and Zn alloy are electrodeposited on the activated CNTs/graphite electrode by pulse galvanostatic method. The micrographs of Zn/CNTs and Zn alloy/CNTs electrodes are characterized by scanning electron microscopy. The results show that the current efficiency of -glucose reduction on CNTs electrodes is much better than that on flat Zn electrodes. The order of the current efficiency on different electrodes is as follows: Zn/CNT (0.58) Zn–Fe/CNT (0.57)>Zn–Ni/CNT (0.43) Zn/graphite (0.42)>Zn (0.40). It indicates that CNTs have good potential application in electrosynthesis. Additionally, effects of some operating parameters, such as pH, temperature and -glucose concentration, on the current efficiency of -glucose reduction are also discussed.     

Electrodeposition of nanocrystalline zinc from acidic sulfate solutions containing thiourea and benzalacetone as additives

Nanocrystalline zinc coatings were produced by pulse electrodeposition in acid sulfate bath containing thiourea and benzalacetone additives and characterized by X-ray diffraction and scanning electron microscopy techniques. The influence of benzalacetone concentration and pulse peak current density on the grain size and crystallographic orientation of zinc deposits was investigated. Zinc electrodeposited from additive-free solutions or with one of the two additives is not composed of nanosized crystals. The mixture additives of thiourea and benzalacetone give rise to the formation of particle-like nanocrystalline zinc with a (10ī1) random orientation. A change in peak current density from 2 to 1 A/cm² only increases the grain size from 60 to 62 nm.     

Potentiodynamic deposition of Prussian blue from a solution containing single component of ferricyanide and its mechanism investigation

Potentiodynamic techniques were used for the direct electrodeposition of Prussian blue nano-clusters from an acidic solution of ferricyanide. Electrochemical, EQCM, IR, AFM, and UV/vis measurements were carried out to characterize deposited nano-sized Prussian blue and to explore the formation mechanism. Results showed that ferricyanide could partially dissociate to free ferric and cyanide ions. The driving force of this dissociation is the formation of PB and the evolution of HCN. The optimal potential window for the potentiodynamic formation of PB from an acidic solution (pH 1.6) is between –0.5 V and 0.4 V. In addition, the influence of surface adsorption of CN^- ions on the formation of PB was discussed.Dedicated to Professor W. Vielstich on the occasion of his 80th birthday.     

高活性钛镀铂电极

在电沉积过程中采用超声波振荡技术，选择最佳条件可制备牢固高活性然镀铂电极，超声波振荡技术改善他镀层与基底的粘结力。电极活性与双层电容有关，并旭因于表面粗糙度。     

模板组装Fe纳米线阵列及其微结构

铝在硫酸溶液中经直流阳极氧化,得到多孔铝阳极氧化膜(AAO). 以AAO膜为模板,通过交流电沉积的方法,在AAO模板孔内成功组装了Fe纳米线.TEM分析表明,Fe纳米线的长度约为2.5 μm,其长度分布十分均匀；粗细均匀,直径约为25 nm. XRD实验分析证实,所制备的Fe纳米线为α-Fe.选区电子衍射（SAED）实验分析表明,α-Fe纳米线具有单晶结构.